Abstract
This study reports a high-performance tin (Sn)-coated vertically aligned carbon nanofiber array anode for lithium-ion batteries. The array electrodes have been prepared by coaxial sputter-coating of tin (Sn) shells on vertically aligned carbon nanofiber (VACNF) cores. The robust brush-like highly conductive VACNFs effectively connect high-capacity Sn shells for lithium-ion storage. A high specific capacity of 815 mAh g-1 of Sn was obtained at C/20 rate, reaching toward the maximum value of Sn. However, the electrode shows poor cycling performance with conventional LiPF6 based organic electrolyte. The addition of fluoroethylene carbonate (FEC) improve the performance significantly and the Sn-coated VACNFs anode shows stable cycling performance. The Sn-coated VACNF array anodes exhibit outstanding capacity retention in the half-cell tests with electrolyte containing 10 wt.% FEC and could deliver a reversible capacity of 480 mAh g-1 after 50 cycles at C/3 rate.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
M. Winter, and J. O. Besenhard, Electrochim. Acta 45, 31, (1999).
C. K. Chan, H. Peng, G. Liu, K. McIlwrath, X. F. Zhang, R. A. Huggins, and Y. Cui, Nat. Nanotechnol. 3, 31 (2008).
M. Zhao, Q. Zhao, J. Qiu, H. Xue, and H. Pang, RSC Adv. 6, 95449 (2016).
B. Wang, B. Luo, X. Li, and L. Zhi, Materials Today 15, 544 (2012).
L. Sun, X. Wang, R. A. Susantyoko, and Q. Zhang, Carbon 82, 282 (2015).
B. A. Cruden, A. M. Cassell, Q. Ye, and M. Meyyappan, J. Appl. Phys. 94, 4070 (2003).
A. V. Melechko, V. I. Merkulov, T. E. McKnight, M. Guillorn, K. L. Klein, D. H. Lowndes, and M. L. Simpson, J. Appl. Phys. 97, 041301 (2005).
S. A. Klankowski, G. P. Pandey, B. A. Cruden, J. Liu, J. Wu, R. A. Rojeski, and Jun Li, J. Power Sources 276, 73 (2015).
G. P. Pandey, S. A. Klankowski, Y. Li, X. S. Sun, J. Wu, R. A. Rojeski, and J. Li, ACS Appl. Mater. Interfaces 7, 20909 (2015).
D. Wang, X. Li, J. Yang, J. Wang, D. Geng, R. Li, M. Cai, T.-K. Sham, and X. Sun, Phys. Chem. Chem. Phys. 15, 3535 (2013).
Z. Yang, A. A. Gewirth, and L. Trahey, Appl. Mater. Interfaces 7, 5667 (2015).
S. Hong, M.-H. Choo, T. H. Kwon, J. Y. Kim and S.-W. Song, Adv. Mater. Interfaces 3, 1600172 (2016).
D. M. Seo, C. C. Nguyen, B. T. Young, D. R. Heskett, J. C. Woicik and B. L. Lucht, J. Electrochem. Soc. 162, A7091 (2015).
R. Tian, Y. Zhang, Z. Chen, H. Duan, B. Xu, Y. Guo, H. Kang, H. Li and H. Liu, Sci. Rep. 6, 19195 (2016).
Y. Dong, S. Das, L. Zhu, T. Ben and S. Qiu, J. Mater. Chem. A 4, 18822 (2016).
D.-H. Nam, J. W. Kim, J.-H. Lee, S.-Y. Lee, H.-A-S. Shin, S.-H. Lee, and Y.-C. Joo, J. Mater. Chem. A 3, 11021 (2015).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Pandey, G.P., Jones, K., Brown, E. et al. High Performance Tin-coated Vertically Aligned Carbon Nanofiber Array Anode for Lithium-ion Batteries. MRS Advances 3, 3519–3524 (2018). https://doi.org/10.1557/adv.2018.520
Published:
Issue Date:
DOI: https://doi.org/10.1557/adv.2018.520