Abstract
YBa2Cu3O7-x (YBCO) films grown by pulsed laser deposition (PLD) on (100) LaAlO3 (LAO) substrates show a strong thickness dependence on the electrical properties. For example, for films in excess of 0.3 µm, the critical current density decreases with increasing thickness. In contrast, nano-composite films consisting of a series of multiple layers of YBa2Cu3O7-x and (Ba0.05, Sr0.95)TiO3 (BSTO) thin films having a total thickness of 5 µm show improved electrical properties. In order to understand this phenomenon, a detailed microstructural characterization has been undertaken. Transmission electron microscopy (TEM) observations show that cracks, stacking faults, c-∥ crystals and secondary phase precipitates are present on the single-layer films, while a high-quality microstructure is observed for the nanocomposite multiple-layer films although defects at YBCO/BSTO interface are still present. In addition, nanocomposite films have a reduced surface roughness. In this complex microstructure, the YBCO/BSTO interfaces and the lattice mismatch strain play a crucial role in controlling the nature of the defects and stability of phases. In order to understand the role of the BSTO layer has on the microstructure, the interfacial mismatch strain and defects are analyzed by high-resolution transmission electron microscopy (HRTEM) in combination with the Moiré fringe technique.
Similar content being viewed by others
References
R. Gross, P. Chaudhari, M. Kawasaki, M. B. Ketchen, and A. Gupta, Appl. Phys. Lett. 57, 727(1990).
J. Gao, W. A. M. Aarnink, G. J. Gerritsma, and H. Rogalla, Physica C, 171, 126(1990).
S. R. Foltyn, Q. X. Jia, P. N. Arendt, L. Kinder, Y. Fan, and J. F. Smith, Appl. Phys. Lett. 75, 3692(1999).
A. Ignatiev, Q. Zhong, P.C. Chou, X. Zhang, J. R. Liu, and W. K. Chu, Appl. Phys. Lett. 70, 1474(1997).
V. F. Solovyov, H. J. Weismann, L. J. Wu, M. Suenaga, and R. Feenstra, IEEE Trans. Appl. Supercond. 9, 1467(1999).
T. R. Dinger, T. K. Worthington, W. J. Gallagher, and R. L. Sandstrom, Phys. Rev. Lett. 58, 2678(1987).
G. W. Nieh, L. Anthony, J. Y. Josefowicz, and F. G. Krajenbrink, Appl. Phys. Lett. 56, 2138(1990).
Y. Enomoto, T. Murakami, M. Suzuki, and K. Moriwaki, Jap. J. Appl. Phys. 26, L1248(1987).
A. H. Carim, S. N. Basu, and R. E. Muenchausen, Appl. Phys. Lett. 58, 871(1991).
Robert Hughes, Patrick Turner and John Preston. US Patent No. S–994276 (2001).
D. Chambonnet, D. Keller, C. Belouet, Physica C, 302, 198(1998).
Martin J. HΫtch, Microsc. Microanal. Microstruct. 8, 41(1997).
H.Y. Zhai, I. Rusakava, R. Fairhurst and W. K. Chu, Phil. Mag. Let, 81, 683(2001).
T. Kitamura, I. Hirabayashi, S. Tanaka, Y. Sugawara, Y. Ikuhara, Appl. Phys. Lett., 68, 2002(1996).
T. Scherer, P. Marienhoff, R. Herwig, M. Neuhaus and W. Jutzi, Physica C, 197, 79(1992).
Acknowledgments
We thank Prof. J.D. Embury for useful discussions and Mr. F. Pearson and Mr. A. Duft for the microscopy facilities maintenance. We are grateful to NSERC and Materials Manufacturing Ontario for financial support.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Luo, Y., Hughes, R.A., Preston, J.S. et al. Microstructure and Current Transport Properties of YBa2Cu3O7-x/(Ba0.05, Sr0.95)TiO3 Multiple-Layer Thin Films. MRS Online Proceedings Library 795, 7–12 (2003). https://doi.org/10.1557/PROC-795-U11.46
Published:
Issue Date:
DOI: https://doi.org/10.1557/PROC-795-U11.46