Abstract
The use of porous ultra-low-k materials between interconnections for sub 45nm technologies has introduced some barrier diffusion and mechanical problems. In order to avoid the problems caused by the porosity, a hybrid dense material (porogen and matrix) can be used in an alternate integration scheme. In this approach, the porogen is removed after CMP steps by a thermal cure or UV assisted thermal cure. In this work, we have first characterized the impact of the temperature and the duration of the thermal cure on the material. The crosslinking degree increases and the porogen amount decreases with increasing cure temperature. The most important impact of the curing duration happens between 350°C and 400°C. The increase of the curing duration leads to an increase of the porogen loss and a decrease of the refractive index. Secondly, in order to assess the structure of the layer as a function of the depth, the material was etched in a 0.05% HF solution and then characterized. According to the temperature and duration of the cure, the etch-rate can vary as a function of the material depth. This variation is related to a complex gradient inside the material.
Similar content being viewed by others
References
S. Maîtrejean, X. Houziaux, M. Fayolle, et al, Admeta, Tokyo, Mat. Res. Soc. Symp. Proc., 2005, accepted.
M. Verdier, M. Montagna, S. Maitrejean, G. Passemard, Mater. Res. Soc. Symp. Proc. 795 (2004) 1.
N. Chérault, G. Carlotti, N. Casanova, P. Gergaud, et al, to be published in Microelec. Eng (2005).
P. Leduc, M. Savoye, S. Maitrejean, D. Scevola, V. Jousseaume, G. Passemard, Proc. of the IITC, 2005.
V. Jousseaume, M. Assous, A. Zenasni, S. Maitrejean, B. Remiat, et al, Proceedings of the IEEE 2005 International Interconnect Technology Conference (2005) 60–62.
V. Jousseaume, J. Beynet, B. Remiat, F. Gaillard, G. Lumia, G. Didier et al, Proc. of Advanced Metallization Conference, (2005) accepted.
A. Van der Lee, Solid State Sciences, 2 (2) 2000, 257–278
S. Y. Chang, T-J Chou, Y-C. Lu, et al, J. Electrochem. Soc. 151 (2004), 146.
D. Rebiscoul, B. Puyrenier, L. Broussous, et al, Micro. Elec. Eng., (2006) submitted.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Rebiscoul, D., Trouvé, H., Remiat, B. et al. Morphological and Structural Evolution of an Ultra-low-k Dielectric During the Porogen Removal. MRS Online Proceedings Library 914, 204 (2005). https://doi.org/10.1557/PROC-0914-F02-04
Received:
Accepted:
Published:
DOI: https://doi.org/10.1557/PROC-0914-F02-04