Abstract
Here, we describe a porous 3-dimensional collagen scaffold material that supports capillary formation in vitro, and promotes vascularization when implanted in vivo. Collagen scaffolds were synthesized from type I bovine collagen and have a uniform pore size of 80 μm. In vitro, scaffolds seeded with primary human microvascular endothelial cells suspended in human fibrin gel formed CD31 positive capillary-like structures with clear lumens. In vivo, after subcutaneous implantation in mice, cell-free collagen scaffolds were vascularized by host neovessels, whilst a gradual degradation of the scaffold material occurred over 8 weeks. Collagen scaffolds, impregnated with human fibrinogen gel, were implanted subcutaneously inside a chamber enclosing the femoral vessels in rats. Angiogenic sprouts from the femoral vessels invaded throughout the scaffolds and these degraded completely after 4 weeks. Vascular volume of the resulting constructs was greater than the vascular volume of constructs from chambers implanted with fibrinogen gel alone (42.7±5.0 μL in collagen scaffold vs 22.5±2.3 μL in fibrinogen gel alone; p<0.05, n = 7). In the same model, collagen scaffolds seeded with human adipose-derived stem cells (ASCs) produced greater increases in vascular volume than did cell-free collagen scaffolds (42.9±4.0 μL in collagen scaffold with human ASCs vs 25.7±1.9 μL in collagen scaffold alone; p<0.05, n = 4). In summary, these collagen scaffolds are biocompatible and could be used to grow more robust vascularized tissue engineering grafts with improved the survival of implanted cells. Such scaffolds could also be used as an assay model for studies on angiogenesis, 3-dimensional cell culture, and delivery of growth factors and cells in vivo.
Citation: Chan EC, Kuo S-M, Kong AM, Morrison WA, Dusting GJ, Mitchell GM, et al. (2016) Three Dimensional Collagen Scaffold Promotes Intrinsic Vascularisation for Tissue Engineering Applications. PLoS ONE 11(2): e0149799. https://doi.org/10.1371/journal.pone.0149799
Editor: Jui-Yang Lai, Chang Gung University, TAIWAN
Received: December 4, 2015; Accepted: February 4, 2016; Published: February 22, 2016
Copyright: © 2016 Chan et al. This is an open access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.
Data Availability: All relevant data are within the paper.
Funding: This work was supported by grants from the National Health and Medical Research Council of Australia (#1061912- GJD, GSL; and #1003113- GJD), the Research Endowment Fund- St Vincent’s Hospital Melbourne (SYL, GMM) and the Jack Brockhoff Foundation (GMM). The Centre for Eye Research Australia and the O’Brien Institute Department of St Vincent’s Institute of Medical Research receive Operational Infrastructure Support from the Victorian Government.
Competing interests: The authors have declared that no competing interests exist.
Introduction
Engineered tissues are emerging as a viable approach to address the scarce supply of heterologous donor organs available for transplantation. However, vascularization is one of the great challenges that tissue engineering faces in order to generate sizeable tissue and organ substitutes that contain living cells [1]. In vascularized tissues, it is estimated that cells must be located within 150–200 μm of the nearest capillary to survive and function optimally [2]. In addition to access to oxygen and nutrients, vascular networks are needed for the removal of carbon dioxide and other cellular waste products during metabolism [2]. Therefore, engineering functional tissues with clinically relevant thickness will require approaches to incorporate vascular networks.
Several strategies have been explored to enhance tissue vascularization, including controlled release of proangiogenic factors such as vascular endothelial growth factor (VEGF) and fibroblast growth factor-2 [3,4], but such approaches could be limited by the short half-life of proangiogenic factors. Recent studies have reported that by allowing vascular cells to form rudimentary microvascular networks on biologically-derived scaffolds in vitro, it is possible to achieve enhanced integration of the implanted graft with host vasculature [5–8]. This pre-vascularization strategy generated ‘perfusable’ constructs that might improve survival of implanted cells when transplanted in vivo.
Collagen is a major extracellular matrix (ECM) component that has been widely used for constructive remodelling to facilitate cell growth and differentiation. The widespread use of collagen across many clinical applications is due to its bio-inductive, and desirable mechanical and degradable properties [9,10]. Collagen-based biomaterials in various formats have been employed as cellular scaffolds for tissue repair and regeneration [11]. Scaffolds made of collagen can support physiological processes in the course of healing and provide a platform for the development of 3-dimensional (3D) functionally intact tissue constructs with vascular in-growth, a component which is indispensable for survival of scaffold implanted cells. Type I bovine collagen has been used to create porous biomaterials as a means for regenerating bladder tissues in an experimental model of bladder exstrophy [12,13] and is readily available. It is therefore a suitable base material to fabricate a porous collagen scaffold.
In this current study, we sought to determine whether the collagen scaffold material could support in vitro vascularization with human endothelial cells and facilitate extrinsic and intrinsic vascularization when implanted in vivo. We employed the murine subcutaneous implant model to characterize the time course of endogenous cell infiltration and degradation of the collagen scaffold in vivo. We then employed a more complex rat tissue engineering chamber model to assess the potential of the collagen scaffolds to promote intrinsic vascularization and as a bioactive cue for sustaining the proangiogenic paracrine activity of human adipose-derived stem cells (ASCs) in vivo.
Materials and Methods
Synthesis and characterization of collagen scaffolds
The base collagen solutions were prepared as described previously [12]. Porous collagen scaffolds with an average pore size of 80 μm were generated from a lyophilized collagen solution (final concentration of 7 mg/mL). Briefly, 0.56 g of Type I bovine collagen isolated from cow skin was added to 80 mL of 0.5 M acetic acid solution (Merck Millipore, Darmstadt, Germany). The collagen solution was first frozen at -20°C for 24 hours, and then underwent a concentrated and lyophilized procedure to produce an interconnected porous structure. The pre-formed porous collagen scaffolds were then treated with N-Ethyl-N'-(3-dimethylamino-propyl) carbodiimide (Sigma-Aldrich, MO, USA), a crosslinking agent, for 4 hours and washed with phosphate buffered saline (PBS) three times. The scaffolds were then lyophilized again to improved mechanical strength (Table 1). Collagen scaffolds in the shape of a disc with a dimension of 8 mm diameter and 2 mm thickness (Fig 1A) were prepared for this study. The surface and cross-section morphology of the scaffolds were examined by a scanning electron microscope (Fig 1B).
(A) A 3D collagen scaffold measured to a diameter of 8 mm and a thickness of 2 mm. (B) Representative images captured by scanning electron microscopy on the surface (left) and through a cross section (right) of collagen scaffold.
To assess the mechanical properties of the collagen sponge, the collagen sample was fully swollen in PBS solution before the mechanical strength measurements (tensile tests). In these tests we mounted the collagen onto the load cell using adhesive sponge gasket between the load cell and sample. The collagen membranes were cut into pieces (1 × 6 cm, n = 5) and the tensile strengths of the samples were measured up to the point at which they broke. The mechanical parameters of the samples were calculated and recorded automatically by using a material-testing system (MTS; Eden Prairie, USA) at a crosshead speed of 5 mm/min.
The porosity of the collagen sponge was determined using Archimedes’ principle [14]. The exterior volume (Vs) of the plug (1 cm × 1 cm) was measured using a Vernier caliper. The sample was then immersed in a pycnometer containing 99% ethanol solution. The actual volume (Va) of the sample was calculated using the formula:
Where Ww is the weight of the ethanol and the pycnometer, Wo is the dry weight of the pycnometer, Wt is the combined weight of the ethanol, the pycnometer and the plug sample, Wp is the combined weight of the dry pycnometer and dry plug sample, and 0.789 g/cm3 is the density of 99% ethanol solution. The porosity of the plug was then determined using the following formula:
Porosity values are expressed as means ± standard deviations (n = 5).
The water content (WC) of the collagen sponge was determined by swelling the sponge in a pH 7.4 PBS at room temperature. After the sponge was equilibrated with PBS, the wet sponge was blotted using filter paper to remove the water adherent to the sponge surface. The WC of the sponge was calculated as following formula:
Where Ww and Wd are the weights of the wet and dry sponge, respectively. The WC are expressed as means ± standard deviations (n = 5).
Culture of human endothelial cells on collagen scaffolds and assessment of vascularization in vitro
Primary human dermal blood microvascular endothelial cells (hMECs) and growth media (EGM-2-MV) were purchased from Lonza (MD, USA). hMECs (5x105 cells) were resuspended in 25 μL of human fibrinogen (15 mg/mL in PBS, Sigma-Aldrich) and dripped onto the upper surface of collagen scaffolds sitting flat on a petri dish. Following passive uptake of the cell/fibrinogen mixture, 25 μL of human thrombin (25 U/mL in PBS, Sigma-Aldrich) was added to form the fibrin gel. Scaffolds were then transferred to a 24-well plate containing 2 mL growth media and cultured for the specified time. Media was replaced after 2 days. At day 3, scaffolds were harvested and fixed in 4% paraformaldehyde for 24 hours before subjection to tissue processing and embedding in paraffin.
Culture of human ASCs on collagen scaffolds in vitro
Isolation and culture of human ASCs.
Human ASCs were isolated as previously described [15] following approval by St Vincent’s Hospital Human Ethics Committee (HREC5203). Fat tissues were collected as part of routine medical surgery and patients have given written informed consent for use of their tissues for research purpose. Briefly, aspirated fat tissues were washed with PBS containing 100 mg/mL streptomycin and 100 U/mL penicillin (Invitrogen, CA, USA), and minced into small pieces. Tissue fragments were washed once with PBS and then digested in 3 volumes of Dulbecco’s Modified Eagle's Medium (DMEM; Invitrogen) containing 0.5 mg/mL collagenase I (250 U/mg; Worthington Biochemical, NJ, USA) overnight with continuous shaking at 37°C. On the second day, cells were collected by centrifugation (800 xg for 10 minutes), seeded in culture flasks and cultured overnight at 37°C with 5% CO2 in growth media (DMEM supplemented with 10% fetal bovine serum (FBS, Sigma-Aldrich), 2 mM glutamine (Invitrogen), 100 mg/mL streptomycin and 100 U/mL penicillin (Invitrogen)). On the third day, attached cells were rinsed 3 times with PBS and cultured in growth media until confluent. Confluent cells were subcultured by trypsinization at a 1:4 ratio. We have confirmed that >95% of the isolated cells express mesenchymal surface markers CD29, CD44 and CD90 by flow cytometry [15].
Generating the GFP-expressed ASCs by lentiviral gene delivery.
The packaging system for the production of lentiviral consisted of the following vectors: pCMV-ΔR8.91 plasmid, pMD.G (envelope element) and pLKO_AS2/GFP (transfer vector). These vectors were obtained from the National RNAi Core Facility (Taipei, Taiwan) as described previously [15]. Briefly, 6×105 293FT cells (Invitrogen) were seeded in a 6-cm culture dish and cultured for 24 hours. A mixture of the 3 vectors (2.5 μg of pCMV-ΔR8.91, 0.3 μg of pMD.G, and 2.5 μg of pLKO_AS2/GFP) was prepared and transfected into 293FT cells using Lipofectamine 2000 (Invitrogen). The virus-containing media were collected at 48 hours after transfection. For lentivirus transduction, human ASCs were seeded in 6-well plates (1×105 per well) in growth media. After overnight incubation, cells were treated with virus-containing media containing 8 μg/mL polybrene (Sigma-Aldrich). The culture medium was removed at 24 hours post-infection and GFP positive cells were enriched (>99%) by FACSAria (BD Biosciences, CA, USA).
Scanning electron microscopy (SEM)
Twenty-four hours after cell seeding, the scaffolds were directly subjected to SEM (Philips XL30 SEM, FEI Company, OR, USA) with an accelerating voltage of 24 kV at Melbourne Advanced Microscopy Facility (Parkville, VIC, Australia).
Proliferation assay to assess cell growth in vitro
The growth of GFP-expressed human ASCs cultured in 3D collagen scaffolds or on collagen coated (0.5 mg/mL; Invitrogen) plate was assessed by using alamarBlue assay. Briefly, GFP-expressed human ASCs (1x106 cells) were seeded in collagen scaffolds as 3D culture or in 12-well tissue culture plates as 2D culture, and cultured over a period of 3 weeks. At day 0, 2, 7, 14 and 21, scaffolds were cut into small pieces and incubated with alamarBlue® solution (Invitrogen) in a proportion of 1:10 (10 μL of alamarBlue® reagent to 100 μL of culture media) for 1 hour at 37°C in a humidified atmosphere containing 5% CO2. Fluorescence signals were measured at an excitation wavelength at 530–560 nm and an emission wavelength at 590 nm using a polarstar microplate reader (BMG Labtech, Australia) at 37°C.
Animal use
Ethics approval for this work was obtained from the St Vincent’s Hospital Animal Ethics Committee (#021/13), in accordance with the requirements of the Australian National Health and Medical Research Council guidelines for the care and health of animals. The animals were supplied from Animal Resources Centre, Perth, Australia. No mice or rats became ill prior to the experimental endpoint. Minor stress induced by operation was looked for daily by observing the motility, grooming and feeding behaviour. All surgery was performed under general anaesthesia (2% isoflurane), and all efforts were made to minimize suffering. In the experimental endpoint, the mice or rats were euthanized using Lethobarb (200 mg/kg, intraperitoneal injection).
Murine subcutaneous scaffold implantation to assess vascular infiltration in vivo
The collagen scaffolds filled with normal saline were implanted subcutaneously on either side of the dorsum of male C57B/L6 mice (10–12 weeks) under general anaesthesia (2% isoflurane). Scaffolds were then harvested at 1, 2, 4 and 8 weeks post-implantation to evaluate the time course of vascular infiltration and degradation of scaffold. At harvest, scaffolds were cleaned of connective tissues and immediately fixed in 4% paraformaldehyde overnight before being subjected to tissue processing and embedding in paraffin.
Rat tissue engineering chamber to assess vascular infiltration in vivo
An in vivo rat tissue engineering chamber was employed as previously described [16]. Male Sprague Dawley rats weighing between 300–400 g were anesthetized with an inhalation of isoflurane. The femoral vessels were exposed through a longitudinal incision made on the medial thigh. Intact left and right femoral artery and vein were separated from each other and from the surrounding tissues over approximately a 2 cm distance and placed within an acrylic polymer chamber (internal dimensions of 10×8×4 mm; Department of Chemical and Biomolecular Engineering, University of Melbourne, Australia) by passing the intact vascular pedicle through openings at either end of the chamber, creating a flow-through model with an intact femoral circulation. A lid was attached to the chamber base to create a protected volume space for tissue growth. Each rat was implanted with two chambers (left and right femoral vessels); one containing a collagen scaffold impregnated with 100 μL of human fibrinogen gel (15 mg/mL; Sigma-Aldrich) and one with 100 μL of human fibrinogen gel alone to serve as a control.
To determine whether collagen scaffolds can be used to deliver cells with proangiogenic paracrine activity, scaffolds were seeded with human ASCs and implanted into the rat tissue engineering chambers. Male nude rats (CBH-rnu, 190–225 g) were purchased from the Animal Resources Centre (Perth, Australia) and were used for implantation of chambers containing either a collagen scaffold or a collagen scaffold pre-cultured for 48 hours with 1x106 GFP-expressed human ASCs.
At 2–4 weeks post-implantation, tissue constructs were harvested from the animals under general anesthesia. Tissues were blotted dry and weighed. The volume of tissue constructs was determined by a volume displacement measurement method [17,18]. Tissues were fixed in 4% paraformaldehyde overnight. Tissue constructs were then divided into four equal transverse sections and paraffin embedded for routine histology and immunohistochemistry.
Immunohistochemistry
Paraffin embedded sections (5 μm) were stained with eosin-hematoxylin (H&E) and Masson’s Trichrome to examine general tissue morphology. To identify hMECs in scaffolds cultured in vitro, endogenous peroxidase activity of sections was quenched with 3% H2O2 for 5 minutes. Sections were then subjected to enzymatic-mediated antigen retrieval with 0.1% Proteinase K (pH 7.8, Dako, Hamburg, Germany) for 8 minutes. The sections were blocked with 10% goat serum (Sigma-Aldrich) for 30 minutes, and then incubated with mouse anti-human CD31 (10.3 μg/mL, Dako) for 60 minutes. Sections were then incubated with biotinylated rabbit-anti-mouse secondary antibody (2.9 μg/mL; Dako) for 60 minutes and avidin-biotinylated-peroxidase complex (Vectastain Elite ABC kit, Vector Laboratories, Peterborough, UK) for 30 minutes.
To identify blood vessels in scaffolds implanted in mice, endogenous peroxidase activity of sections was quenched with 3% H2O2 for 10 minutes. Sections were then subjected to enzymatic-mediated antigen retrieval with 0.1% Proteinase K (pH 7.8, Dako, Hamburg, Germany) for 3 minutes. The sections were blocked with protein block solution (Dako) for 30 minutes, and then incubated with rat anti-mouse CD31 (3 μg/mL, BD Biosciences, North Ryde, Australia) for 60 minutes. Sections were then incubated with biotinylated rabbit anti-rat IgG (4 μg/mL, Dako) for 30 minutes, followed by avidin-biotinylated-peroxidase complex (Vectastain Elite ABC kit, Vector Laboratories).
To identify blood vessels in tissue constructs harvested from rat tissue engineering chambers, sections were treated with 3% H2O2 and proteinase K (Dako) prior to incubation with biotinylated Griffonia Simplicifolia lectin (6.67 μg/mL, B-1105, Vector Laboratories) overnight at 4°C. The incubation of lectin was then followed by HRP-streptavidin (1.78 μg/mL; Dako) treatment for 30 minutes.
To identify human cells, sections underwent heat-mediated antigen retrieval in citric acid buffer (pH 6.0, 30 minutes at 95°C) followed by 3% H2O2 for 5 minutes. Sections were then sequentially incubated in serum-free blocking solution (Thermo Fisher Scientific, MA, USA) for 10 minutes, rabbit anti-Ku80 antibody (0.06 μg/mL; Abcam, MA, USA) or mouse anti-human CD31 (4.1 μg/mL, Dako) overnight at 4°C, biotinylated goat-anti-rabbit secondary antibody (7.5 μg/mL; Vector Laboratories) or biotinylated rabbit-anti-mouse secondary antibody (2.9 μg/mL; Dako) for 60 minutes and avidin-biotinylated-peroxidase complex (Vectastain Elite ABC kit, Vector Laboratories) for 30 minutes. In all sections, peroxidase activity was visualized with diaminobenzidine chromogen (Dako) and sections were counterstained with hematoxylin before mounting in DPX mounting medium (VWR International, Poole, UK).
Morphometric analysis of vascularization
Quantification of tissue vascularization and scaffold degradation were performed using video microscopy with a computer-assisted stereo investigator system (MBF Bioscience, VT, USA)[18,19]. For each sample, three cross-sectional sections—200 μm apart (scaffolds from in vivo murine subcutaneous implantation) or 4 complete transverse sections (tissue constructs from in vivo rat tissue engineering chambers) were counted with a 20x magnification objective. Using systematic random sampling, 12-point grids (400 μm x 400 μm) were superimposed on randomly selected fields representing 25% of the total area and each point within the grid was recorded as positive or negative on the basis of CD31 staining vessels, lectin staining vessels or scaffold. Percentage of vascular volume were determined by dividing the number of points in each of the selected fields that fell randomly on vessels (CD31 or lectin positive capillaries including the lumens) or scaffolds by the total number of points counted for that tissue section and multiplied by 100. Absolute vascular volume or scaffold of rat tissue was calculated by multiplying the percentage of vascular volume or percentage of scaffold material by the total tissue volume at harvest determined by volume displacement. All counting was completed by a trained operator masked to the identity of the tissue samples.
Statistical analysis
Data are expressed as mean ± standard error of the mean (SEM). The mean data were analysed with unpaired t-test or one-way analysis of the variance (ANOVA) with Tukey multiple comparison post-hoc test where appropriate. A value of p<0.05 was regarded as statistically significant.
Results
Formation of capillary structures in collagen scaffolds seeded with human endothelial cells in vitro
To assess whether collagen scaffolds can provide a viable platform for the growth of endothelial cells, hMECs were cultured in fibrin filled scaffolds for 3 days. CD31+ capillary-like structures were formed throughout the scaffolds cultured with hMECs for 3 days (n = 2, Fig 2A and 2B).
(A) Human dermal microvascular endothelial cells formed CD31+ capillaries with clear luminal structures at 3 days in culture. (B) A higher magnification of an inset box in (A) with capillary-like structures identified by arrows. Scale bar = 100 μm.
Collagen scaffold induces intrinsic vascularisation in a murine subcutaneous implantation model
We assessed the degree of vascular infiltration of scaffolds harvested from mice at 1, 2, 4 and 8 weeks post-implantation (n = 4–6 from each time point). The scaffolds reduced in size the longer the implantation period (Fig 3A). Histological sections of scaffolds implanted for 1 week showed evenly distributed pores with minimal cell infiltration. The number of infiltrated cells gradually increased with longer implantation periods (2–8 weeks; Fig 3B). Within the scaffolds, CD31+ capillary-like structures with clear lumens were observed at 2, 4 and 8 weeks but not at 1 week (Fig 3C). Quantification of CD31+ vessels within the scaffolds confirmed that vascularization was minimal at 1 week but gradually increased from 2 weeks and reached a maximum percent vascular volume at 4 weeks (4.6±0.9% at 2 weeks, 8.2±0.7% at 4 weeks, 6.7±0.9% at 8 weeks; p<0.05 for each comparison vs. 0.04±0.04% at 1 week, n = 3–6; Fig 3D). The increase in CD31+ cells in the scaffold was accompanied by gradual degradation of scaffold material over time (22.7±3.7% at 4 weeks, 31.3±3.5% at 8 weeks; p<0.05 for each comparison vs 83.4±1.5% at 1 week, n = 3–6; Fig 3E). The extent of scaffold degradation plateaued at 4 weeks and collagen scaffold material could still be found at 8 weeks post-implantation.
(A) Appearance of scaffolds harvested from mice at 1 and 4 weeks. Representative images of scaffold sections stained with haematoxylin and eosin (B) or endothelial cell marker CD31 (C) at 1, 2, 4 and 8 weeks post-implantation. Percentage of vascular volume (D) and percent of remaining collagen scaffold (E) at 1, 2, 4 and 8 weeks post-implantation (n = 3–6 mice). *p<0.05 and **p<0.01 by one-way ANOVA with Turkey post-hoc test. Scale bar = 100 μm.
Collagen scaffold induces intrinsic vascularisation in a rat tissue engineering model
An in vivo rat tissue engineering chamber was employed to assess the ability of collagen scaffolds to support an angiogenic response and new tissue formation (Fig 4A and 4B). Newly formed blood vessels were identified by lectin staining (Fig 4C). Compared to control chambers which contained fibrinogen gel alone, the absolute vascular volume was significantly higher in constructs generated from chambers containing collagen scaffolds infiltrated with fibrinogen gel (42.7±5.0 μL in collagen scaffold vs 22.5±2.3 μL in control; p<0.05, n = 7; Fig 4D). The percentage of vascular volume was similar between groups (40.7±2.5% in collagen scaffold vs 39.9±4.1% in control; p>0.05, n = 7). No significant difference in total chamber tissue weight and volume was found between groups (Fig 4E) and collagen scaffolds were completely degraded by 4 weeks post-implantation.
(A) The polyacrylic chambers containing collagen scaffolds infiltrated with fibrinogen gel (circled) or fibrinogen gel alone were placed around the femoral artery and vein in the groin region of rats. Scale bar = 5 mm. (B) Representative photomicrograph of new tissues generated in the tissue engineering chambers contained collagen scaffold infiltrated with fibrinogen gel (left) or fibrinogen gel alone (right) at 4 weeks post-implantation. (C) Representative images of tissue sections stained with blood vessel marker lectin. Top two figures: fibrinogen alone (-scaffold), bottom two figures collagen scaffold with fibrinogen (+scaffold). (D) The absolute vascular volume in vascularized tissues at 4 weeks post-implantation (n = 7). (E) The weight and volume of tissue constructs harvested at 4 weeks post-implantation (n = 7). **p<0.01 by unpaired t-test. Scale bars = 100 μm.
Collagen scaffolds provide a bioactive cue for human ASCs in vitro and in vivo
Twenty-four hours after seeded onto the collagen scaffold, human ASCs were found distributed evenly throughout the collagen scaffold (Fig 5A). SEM showed that adhered human ASCs exhibited spindle shape morphology, and cell-cell and cell-scaffold interactions were observed around the porous structure of the collagen scaffolds (Fig 5A). Moreover, the proliferation of proangiogenic human ASCs [20] cultured in 3D collagen scaffolds and 2D culture was assessed over a period of 21 days. Those ASCs cultured in 2D (1x106 cells/well in 12-well plate) were confluent at 2 days after seeding but did not proliferate further for the next 21 days due to contact inhibition. In contrast, human ASCs cultured in 3D collagen scaffolds continued to proliferate throughout the 21 days in culture (Fig 5B and 5C).
(A) Representative images captured from 3D collagen scaffolds seeded with human ASCs for 24 hours: haematoxylin and eosin (H&E) staining and scanning electron microscopy (SEM). The white arrow demonstrates human ASCs attached to the collagen scaffold. (B) Representative images of GFP-expressed human ASCs cultured in collagen scaffolds for 7 and 21 days. Scale bar = 200 μm. (C) The proliferation rate of GFP-expressed human ASCs cultured in 3D collagen scaffolds and on 2D collagen-coated plates (n = 3). **p<0.01 vs 2D culture by unpaired t-test.
To determine whether collagen scaffolds support the proangiogenic function of GFP-labelled human ASCs in vivo, the formation of new vascularized tissue in the rat tissue engineering chambers was compared between chambers containing scaffolds seeded with and without GFP-labelled human ASCs. At 2 weeks post-implantation, the absolute vascular volume was significantly higher in the ASCs group compared to control group (42.9±4.0 μL in the collagen scaffold with human ASCs vs 25.7±1.9 μL in collagen scaffold alone; p<0.05, n = 4; Fig 6A). The percent vascular volume was increased in the ASC/scaffold group over the control scaffold group (32.1±5.0% in the collagen scaffold with human ASCs vs 25.9±1.7% in collagen scaffold alone; p>0.05, n = 4). No significant difference in total chamber tissue weight and volume was found between groups (Fig 6B and 6C). Staining with human-specific Ku80 showed that human ASCs were still present in the residual collagen scaffolds at 2 weeks post-implantation (Fig 6D) but human cells had also migrated into the neotissues outside the scaffold aligning close to the new blood vessels (Fig 6E). However, no human-specific CD31 positive cells were detected in the tissue constructs (data not shown).
(A) The absolute vascular volume in tissue constructs harvested at 2 weeks post-implantation (n = 4). The total weight (B) and volume (C) of chamber tissue constructs harvested at 2 weeks post-implantation (n = 4). Human ASCs were identified by human-specific Ku80 (brown nucleus staining) in (D) the collagen scaffold and (E) the tissue construct harvested at 2 weeks post-implantation. **p<0.01 by unpaired t-test.
Discussion
The present study demonstrated that the 3D collagen scaffolds can support extrinsic and intrinsic vascularization using two different in vivo animal models, the murine subcutaneous implant model (extrinsic vascularization) and the rat tissue engineering chamber model (intrinsic vascularization). The collagen scaffolds support endothelial cell survival and permitted significant capillary formation within their pores in vitro. Furthermore, the collagen scaffolds also provide structural and mechanical support for 3D cell culture in vitro and can be employed as a bioactive cue for the delivery of human cells in vivo.
Collagen is one of the major ECM proteins that interacts with various growth factors and cells, and has a chemotactic activity to endothelial cells [21] in the wound healing process [22]. Theoretically, collagen scaffolds can be employed as cell carriers and as reservoirs for growth factors without compromising their activity which would be of great value to promote angiogenesis and vascular stabilization for tissue engineering [23,24]. Indeed, we have previously shown that exogenously added neuron cancer stem cells start to adhere to the scaffolds at day 1 and form a colony at day 3 [25]. In the present study, we have further demonstrated the cell compatibility of these collagen scaffolds with human endothelial cells and human ASCs. The human endothelial cells can be grown in the collagen scaffold and formed CD31+ capillary-like structures in vitro suggesting that the scaffolds can form a pre-vascularized platform for cell-based tissue growth for subsequent implantation. We also showed a greater growth of human ASCs when cultured in the porous 3D collagen scaffolds rather than the conventional 2D cell culture format. This was attributed to the interconnection of pores within the scaffolds providing more space to accommodate cell growth and allowing diffusion of nutrient, oxygen and metabolites through the scaffolds. Therefore, the collagen scaffolds provide a biological ECM microenvironment that supports growth of several human cell types including endothelial cells, ASCs and neuronal cancer stem cells [25].
The collagen scaffolds employed in the present study might well provide a bioactive cue for infiltrating cells, including endogenous endothelial cells, to induce vascularization of the implants. The porous structure of the collagen scaffolds allows the diffusion of nutrients as well as migration of cells [24], which are important features for vascularization. Xiao et al. [26] have recently shown that endothelial cells tend to accumulate around the pore interconnection of porous scaffolds, and it is the site where the cells migrate into the inner part of the scaffolds to induce vascularization. As such, the porous structure of scaffolds facilitates vascularization, and the collagen scaffolds are biocompatible when implanted in vivo in small animals. The murine subcutaneous implant model is often used to study the biocompatibility of scaffolds [27] as well as angiogenesis during wound healing [28]. An infiltration of host cells into the collagen scaffolds was seen at week 1 and an accumulation of host cells at the central region occurred from week 2. This time-dependent increased in cell infiltration correlated with an increasing number of CD31+ capillaries indicating vascularization of the implanted scaffolds. The gradual increased in vascularization of the implanted scaffolds was also found to be accompanied by the degradation of scaffold matrix over 8 weeks without adverse inflammatory response. These findings suggest that such scaffolds can integrate with the host tissues and provide a biodegradable environment for in vivo vascularization during a wound healing response [24].
Fibrin gel has often been used as a hydrogel in many applications of tissue engineering [29] such as skeletal muscle tissue [30] and cardiac tissue [31,32]. Fibrin gel can be derived from human fibrinogen and can potentially be applied clinically. Autologous fibrin gel can be synthesized from the patient’s own blood to minimise immune reaction [29] and this makes fibrin gel an attractive hydrogel for tissue repair and regeneration. Moreover, fibrin, an active component of the fibrinogen gel, has also been shown to be a pro-angiogenic factor that can enhance angiogenesis via triggers the angiogenic such as VEGF [33,34]. However, fibrin gel has poor mechanical properties render it susceptible to cell-mediated contraction and mechanical strain when implanted in vivo [35]. Brougham et al. [35] recently addressed this problem by incorporating fibrin into a collagen-glycosaminoglycan matrix hence reducing the degree of cell-mediated contraction as well as improving the viability of vascular smooth muscle cells. Similarly, we showed that incorporating fibrin gel into the collagen scaffolds yielded a greater vascular volume in the tissue constructs generated in an in vivo tissue engineering chamber compared with fibrin gel alone. The increase in vascular volume was likely due to larger chamber tissue volume of the constructs from the collagen scaffold group as the percentage of vascular volume was similar between groups. Thus, the structural support provided by the collagen scaffolds would synergise the growth of tissues in fibrin gel.
An alternative approach to using soluble growth factors to promote intrinsic vascularization would be seeding scaffolds with pro-angiogenic cells [5–8]. Human ASCs have been known to release a variety of pro-angiogenic cytokines and growth factors including interleukins, VEGF, angiogenin, and fibroblast growth factor-2 under normoxic [36] and hypoxic [37] conditions. The level of cytokines and growth factors released from human ASCs has been found to be sufficient to promote proliferation of human endothelial cells [36,37] and promote angiogenesis in vivo [36]. Moreover, Wang et al. [20] recently developed a biocompatible polytetrfluoroethylene filtration membrane to study the pro-angiogenic activity of human ASCs. This device was used to encapsulate human ASCs to insulate the implanted cells from the host microenvironment while allowing diffusion of soluble factors secreted from the cells. When implanted subcutaneously in rats, ASC-laden devices resulted in higher number of blood vessels in the tissue surrounding the devices and expressed higher levels of cytokines and growth factors such as interleukin-10 and VEGF in comparison to acellular devices [20], confirming a pro-angiogenic effect of human ASCs in vivo. We found that ASC-laden collagen scaffolds resulted in a higher volume of blood vessels in tissue constructs in comparison to scaffolds without ASCs. At 2 weeks post-implantation, some implanted human ASCs remained in the collagen scaffolds while others have migrated out of the scaffolds into the neotissues and localized in close proximity to the host blood vessels. However, immunostaining with human-specific endothelial marker CD31 did not detect positive cells in the tissue constructs suggesting that the increase in vascular volume was likely attributed to the paracrine activity of the implanted human ASCs on host tissues, rather than the differentiation of ASCs into endothelial cells.
Conclusions
We have demonstrated a 3D porous collagen scaffold material that is versatile, biocompatible, biodegradable and has bioactivity that mimics the functions of natural ECM to support vascularization in vitro and in vivo in different species (rat and mouse) and experimental models (subcutaneous implant and tissue engineering chamber). Unique properties of the collagen scaffolds which (1) provide structural support for cell infiltration and angiogenesis, (2) can be used as a cell carrier for in vivo implantation, and (3) offer mechanical support to grow more robust vascularized tissue grafts for tissue and organ repair.
Acknowledgments
Authors thank Ms Malarmathy Ramachandran and Mr Sze Woei Ng for assistance with histological analysis and Ms Priyadharshini Sivakumaran for cell preparation.
Author Contributions
Conceived and designed the experiments: ECC SMK GMM SYL GSL. Performed the experiments: ECC AMK SYL GSL. Analyzed the data: ECC AMK GMM SYL GSL. Contributed reagents/materials/analysis tools: SMK WAM. Wrote the paper: ECC WAM GJD SYL GSL.
References
- 1. Novosel EC, Kleinhans C, Kluger PJ (2011) Vascularization is the key challenge in tissue engineering. Adv Drug Deliv Rev 63: 300–311. pmid:21396416
- 2. Kannan RY, Salacinski HJ, Sales K, Butler P, Seifalian AM (2005) The roles of tissue engineering and vascularisation in the development of micro-vascular networks: a review. Biomaterials 26: 1857–1875. pmid:15576160
- 3. Conconi MT, Ghezzo F, Dettin M, Urbani L, Grandi C, et al. (2010) Effects on in vitro and in vivo angiogenesis induced by small peptides carrying adhesion sequences. J Pept Sci 16: 349–357. pmid:20552562
- 4. Nomi M, Miyake H, Sugita Y, Fujisawa M, Soker S (2006) Role of growth factors and endothelial cells in therapeutic angiogenesis and tissue engineering. Curr Stem Cell Res Ther 1: 333–343. pmid:18220878
- 5. Tian L, George SC (2011) Biomaterials to prevascularize engineered tissues. J Cardiovasc Transl Res 4: 685–698. pmid:21892744
- 6. Sukmana I (2012) Bioactive polymer scaffold for fabrication of vascularized engineering tissue. J Artif Organs 15: 215–224. pmid:22527978
- 7. Chiu LL, Montgomery M, Liang Y, Liu H, Radisic M (2012) Perfusable branching microvessel bed for vascularization of engineered tissues. Proc Natl Acad Sci U S A 109: E3414–3423. pmid:23184971
- 8. Montano I, Schiestl C, Schneider J, Pontiggia L, Luginbuhl J, et al. (2010) Formation of human capillaries in vitro: the engineering of prevascularized matrices. Tissue Eng Part A 16: 269–282. pmid:19702510
- 9. Yannas IV, Tzeranis DS, Harley BA, So PT (2010) Biologically active collagen-based scaffolds: advances in processing and characterization. Philos Trans A Math Phys Eng Sci 368: 2123–2139. pmid:20308118
- 10. Abou Neel EA, Bozec L, Knowles JC, Syed O, Mudera V, et al. (2013) Collagen—emerging collagen based therapies hit the patient. Adv Drug Deliv Rev 65: 429–456. pmid:22960357
- 11. Glowacki J, Mizuno S (2008) Collagen scaffolds for tissue engineering. Biopolymers 89: 338–344. pmid:17941007
- 12. Roelofs LA, Eggink AJ, Hulsbergen-van de Kaa CA, Wijnen RM, van Kuppevelt TH, et al. (2008) Fetal bladder wall regeneration with a collagen biomatrix and histological evaluation of bladder exstrophy in a fetal sheep model. Fetal Diagn Ther 24: 7–14. pmid:18504374
- 13. Roelofs LA, Kortmann BB, Oosterwijk E, Eggink AJ, Tiemessen DM, et al. (2014) Tissue engineering of diseased bladder using a collagen scaffold in a bladder exstrophy model. BJU Int 114: 447–457. pmid:25302355
- 14. Wan Y, Xiao B, Dalai S, Cao X, Wu Q (2009) Development of polycaprolactone/chitosan blend porous scaffolds. J Mater Sci Mater Med 20: 719–724. pmid:18987952
- 15. Higuchi M, Dusting GJ, Peshavariya H, Jiang F, Hsiao ST, et al. (2013) Differentiation of human adipose-derived stem cells into fat involves reactive oxygen species and Forkhead box O1 mediated upregulation of antioxidant enzymes. Stem Cells Dev 22: 878–888. pmid:23025577
- 16. Lim SY, Sivakumaran P, Crombie DE, Dusting GJ, Pebay A, et al. (2013) Trichostatin A enhances differentiation of human induced pluripotent stem cells to cardiogenic cells for cardiac tissue engineering. Stem Cells Transl Med 2: 715–725. pmid:23884641
- 17. Scherle W (1970) A simple method for volumetry of organs in quantitative stereology. Mikroskopie 26: 57–60. pmid:5530651
- 18. Lim SY, Hsiao ST, Lokmic Z, Sivakumaran P, Dusting GJ, et al. (2012) Ischemic preconditioning promotes intrinsic vascularization and enhances survival of implanted cells in an in vivo tissue engineering model. Tissue Eng Part A 18: 2210–2219. pmid:22651554
- 19. Zhang Y, Sivakumaran P, Newcomb AE, Hernandez D, Harris N, et al. (2015) Cardiac Repair With a Novel Population of Mesenchymal Stem Cells Resident in the Human Heart. Stem Cells 33: 3100–3113. pmid:26184084
- 20. Wang K, Yu LY, Jiang LY, Wang HB, Wang CY, et al. (2015) The paracrine effects of adipose-derived stem cells on neovascularization and biocompatibility of a macroencapsulation device. Acta Biomater 15: 65–76. pmid:25575852
- 21. Kuraitis D, Hou C, Zhang Y, Vulesevic B, Sofrenovic T, et al. (2011) Ex vivo generation of a highly potent population of circulating angiogenic cells using a collagen matrix. J Mol Cell Cardiol 51: 187–197. pmid:21569777
- 22. Schultz GS, Wysocki A (2009) Interactions between extracellular matrix and growth factors in wound healing. Wound Repair Regen 17: 153–162. pmid:19320882
- 23. Jiang B, Akar B, Waller TM, Larson JC, Appel AA, et al. (2014) Design of a composite biomaterial system for tissue engineering applications. Acta Biomater 10: 1177–1186. pmid:24321351
- 24. Chan BP, Leong KW (2008) Scaffolding in tissue engineering: general approaches and tissue-specific considerations. Eur Spine J 17 Suppl 4: 467–479. pmid:19005702
- 25. Chen CH, Kuo SM, Liu GS, Chen WN, Chuang CW, et al. (2012) Enhancement of neurite outgrowth in neuron cancer stem cells by growth on 3-D collagen scaffolds. Biochem Biophys Res Commun 428: 68–73. pmid:23047009
- 26. Xiao X, Wang W, Liu D, Zhang H, Gao P, et al. (2015) The promotion of angiogenesis induced by three-dimensional porous beta-tricalcium phosphate scaffold with different interconnection sizes via activation of PI3K/Akt pathways. Sci Rep 5: 9409. pmid:25797242
- 27. Haase T, Krost A, Sauter T, Kratz K, Peter J, et al. (2015) In vivo biocompatibility assessment of poly(ether imide) electrospun scaffolds. J Tissue Eng Regen Med.
- 28. Chan EC, Peshavariya HM, Liu GS, Jiang F, Lim SY, et al. (2012) Nox4 modulates collagen production stimulated by transforming growth factor beta1 in vivo and in vitro. Biochem Biophys Res Commun 430: 918–925. pmid:23261430
- 29. Dietrich M, Heselhaus J, Wozniak J, Weinandy S, Mela P, et al. (2013) Fibrin-based tissue engineering: comparison of different methods of autologous fibrinogen isolation. Tissue Eng Part C Methods 19: 216–226. pmid:22889109
- 30. Bitto FF, Klumpp D, Lange C, Boos AM, Arkudas A, et al. (2013) Myogenic differentiation of mesenchymal stem cells in a newly developed neurotised AV-loop model. Biomed Res Int 2013: 935046. pmid:24106724
- 31. Birla RK, Borschel GH, Dennis RG, Brown DL (2005) Myocardial engineering in vivo: formation and characterization of contractile, vascularized three-dimensional cardiac tissue. Tissue Eng 11: 803–813. pmid:15998220
- 32. Kofidis T, Lenz A, Boublik J, Akhyari P, Wachsmann B, et al. (2003) Pulsatile perfusion and cardiomyocyte viability in a solid three-dimensional matrix. Biomaterials 24: 5009–5014. pmid:14559014
- 33. Morin KT, Tranquillo RT (2013) In vitro models of angiogenesis and vasculogenesis in fibrin gel. Exp Cell Res 319: 2409–2417. pmid:23800466
- 34. Shiose S, Hata Y, Noda Y, Sassa Y, Takeda A, et al. (2004) Fibrinogen stimulates in vitro angiogenesis by choroidal endothelial cells via autocrine VEGF. Graefes Arch Clin Exp Ophthalmol 242: 777–783. pmid:15103470
- 35. Brougham CM, Levingstone TJ, Jockenhoevel S, Flanagan TC, O'Brien FJ (2015) Incorporation of fibrin into a collagen-glycosaminoglycan matrix results in a scaffold with improved mechanical properties and enhanced capacity to resist cell-mediated contraction. Acta Biomater.
- 36. Hsiao ST, Asgari A, Lokmic Z, Sinclair R, Dusting GJ, et al. (2012) Comparative analysis of paracrine factor expression in human adult mesenchymal stem cells derived from bone marrow, adipose, and dermal tissue. Stem Cells Dev 21: 2189–2203. pmid:22188562
- 37. Stubbs SL, Hsiao ST, Peshavariya HM, Lim SY, Dusting GJ, et al. (2012) Hypoxic preconditioning enhances survival of human adipose-derived stem cells and conditions endothelial cells in vitro. Stem Cells Dev 21: 1887–1896. pmid:22165914