Ultra-broadband quantum infrared spectroscopy

Spectroscopy in the mid-infrared region is an indispensable tool for identifying molecular types in various ﬁelds, including physics, chemistry, and medical sciences. However, conventional infrared light sources, detectors, and noise from blackbody radiation have been the obstacles to miniaturization and higher sensitivity of infrared spectrometers. Quantuminfraredspectroscopy,whichusesvisibleandinfraredphotonpairsinaquantumentangledstate,hasattracted attentionasanewsensingtechnologythatenablesinfraredspectroscopywithdetectorsinthevisiblerange.However, thebandwidthofconventionalquantumentangledlightsourcesisatmost1 µ m or less, which hinders broadband measurements, which are important in spectroscopic applications. Here we have realized an ultra-broadband entangled state of visible–infrared photons with wavelengths from 2 to 5 µ m, harnessing a specially designed nonlinear crystal with chirped poling structure inside. Furthermore, we constructed a nonlinear quantum interferometer using the ultra-broadband quantum entangled photons and realized broadband infrared spectroscopy of inorganic and organic materials using a visible detector made of silicon. Our results show that quantum infrared spectroscopy can achieve ultra-broadband spectroscopic measurements and pave the way for the highly sensitive, ultra-compact infrared spec-trometers using quantum entangled photons. © 2024 Optica Publishing Group under


INTRODUCTION
Infrared (IR) spectroscopy is a versatile tool in a broad range of fields from astronomy to medicine [1].The transmission spectrum reflects the vibrational modes unique to the molecules in a sample and is thus widely used to discriminate materials.The current state-of-the-art IR spectroscopy technique is Fourier transform IR (FTIR) spectroscopy.However, the relatively low efficiency of available IR sources and detectors has been an obstacle for the development of FTIR spectroscopy, such as efforts to miniaturize FTIR systems.One way to solve the problem is by improving mid-IR (MIR) thermal light sources and detectors.Quantum cascade lasers (QCLs) in the MIR region have been investigated, but the bandwidth of off-the-shelf QCLs is still limited [2].Further, high-sensitivity MIR detectors often require cryogenic cooling and are subject to export control [3].
A shortcoming of these demonstrations of QIRS is the limited spectral coverage [4][5][6][7][8][9][10][11].To address this problem, the broadband group-velocity phase matching aimed to use for QIRS has been demonstrated; however, the bandwidth was still smaller than 1 µm [22].Alternatively, wavelength tunable QIRS systems have been recently realized by tuning the angle of a nonlinear crystal [5,23] or the crystal temperature [24], but with the drawback of a long measurement time required for the wavelength tuning process.
Here, we experimentally demonstrate the QIRS with an ultrabroadband frequency-entangled photon pair source using chirped quasi-phase-matched periodically poled magnesium doped stoichiometric lithium tantalate (PPMg:SLT).We successfully observed an ultra-broad spectrum of visible signal photons from 595 to 725 nm, which corresponds to wavelengths of the idler photons from 2.0 to 5.0 µm with a bandwidth of 3.0 µm.Then we constructed a quantum nonlinear interferometer in the low-gain regime where the average photon flux is below one photon pair per correlation time for the biphotons.We successfully observed a quantum interferogram and obtained an MIR broadband spectrum of the idler photons.Finally, we performed ultra-broadband QFTIR spectroscopy over the range of 2.5 to 4.5 µm with a bandwidth of 2.0 µm for solid and liquid samples.This demonstration of ultra-broadband QFTIR spectroscopy covering the whole MIR region, using a visible light source and detector, paves the way for its use in a wide range of fields from materials science to medical applications.

DEVELOPMENT OF AN ULTRA-BROADBAND CHIRPED QPM DEVICE
To realize the ultra-broadband visible and MIR entangled photonpair source, we developed a chirped quasi-phase-matching (QPM) device [25,26] with a spatially modulated QPM structure to generate broadband two-photon states by continuously varying the phase-matching condition.For comparison, we also experimentally evaluated a non-chirped QPM device with uniform poling periods suitable for generating photon pairs at specific wavelengths with relatively narrow spectral bandwidths.In the following, we compare the experimentally obtained emission spectra of visible photons from both devices with theoretical calculations to confirm that photon pair generation occurs in the desired spectral regions.The QPM device uses PPMg:SLT [25][26][27][28][29][30][31][32][33][34].This nonlinear optical material is not subject to instability in short-wavelength pumping [35], has a transmission region from ultraviolet to mid-infrared wavelengths [36], and has a high damage threshold of the order of GW/cm 2 .
Figure 1(a) shows a schematic view of the non-chirped QPM device.The dimensions of the device are 1 × 1 × 10 mm 3 .The spatial frequencies of the polarization reversals for the segment , corresponding to the inverse of the poling periods, are set based on a previously reported equation [33].1/ is set to 12.9 µm.The QPM structure is designed to generate a photon pair with a visible wavelength of 612 nm and an infrared wavelength of 4100 nm via collinear type-0 spontaneous parametric down-conversion (SPDC), assuming a crystal temperature of 30 • C and an excitation wavelength of 532.45 nm.The refractive index of Mg:SLT is modeled by the Sellmeier equation [25].The calculated emission spectrum of the photon pair, shown in Fig. 1(b), is centered at the designed wavelengths and has a spectral width of 0.4 nm full width at half maximum (FWHM) for a visible signal photon.The experimentally observed emission spectrum of the signal photons has a peak with a FWHM of 0.7 nm, centered at the designed wavelength, as shown in Fig. 1(c).Compared to the simulation result, the experimental data have a slightly larger spectral width due to the finite wavelength resolution of the visible spectrometer (0.17 nm).
Figure 1(d) shows the chirped QPM device consisting of 50 segments with different poling periods for simultaneously generating photon pairs with a variety of combinations of wavelengths.The dimensions of the device are 1 × 1 × 10 mm 3 .The QPM structure is designed so that the emission spectrum of a photon pair is continuously distributed in the wavelength range of 595 to 725 nm in the visible region and 2 to 5 µm in the infrared region.For the device used in this work, the number of segments n is 50, and 1/ (1) and 1/ (n) are set to 9.58 and 13.33 µm, respectively, corresponding to a chirp rate of 39.1.
Figure 1(e) shows numerical simulation results for the emission spectrum of a photon pair generated from the chirped device, assuming a pump wavelength of 532.45 nm and a crystal temperature of 55.1 • C. In this simulation, we considered that each segment has a finite length and is assumed to be a step function to reflect the actual QPM structure.The calculation results show that the spectral intensity of SPDC photons generated from the chirped device is distributed over a much wider bandwidth than that from the non-chirped device.Visible signal photons are generated in the wavelength range of 595-725 nm, and infrared idler photons in the wavelength range of 2.0-5.0 µm.Fine ripples are seen throughout the spectrum, which can be attributed to quantum interference between the photon-pair generation processes in the different segments [37].In the experiment, we measured the emission spectrum of visible signal photons generated from the chirped QPM device using the visible spectrometer.Here, the pump power was set to 150 mW and the emission spectrum was accumulated 60 times with an exposure time of 1 s.As shown in Fig. 1(f ), we succeeded in observing broadband generation of SPDC photons, ranging from 595 to 725 nm, equal to the bandwidth of the numerical simulation (126 nm).
To evaluate the SPDC photon generation rate for the chirped QPM device, we measured the pump power dependence of the signal photon count rate, which increased linearly with increasing pump power.The generation rate for the signal photons collected through the multimode fiber to the single photon detector, was estimated to be larger than 2.5 × 10 4 photons/mW.These results clearly show that the chirped QPM device is a highly efficient entangled photon pair source suitable for broadband quantum infrared spectroscopy.

EXPERIMENTAL DEMONSTRATION OF ULTRA-BROADBAND QIRS A. Experimental Setup
We constructed the QIRS system by a Michelson-type nonlinear quantum interferometer using the Mg:SLT QPM device and confirmed that a quantum interferogram can be obtained over the entire bandwidth of the generated photon pairs.Figure 2(a) shows the interferometer.In the experimental setup in Fig. 2(a), a pump light passes through the QPM device twice so that quantum interference between two photon-pair generation processes occurs.The QPM device is placed in an oven and set to the optimum operating temperature by a temperature controller (OV30D+TC-038D, HC Photonics).A continuous-wave laser with a wavelength of 532.45 nm (Cobolt Samba, output power 300 mW, linewidth ≤ 1 MHz) is used as the pump source.The polarization of the pump light is adjusted by a halfwave plate (HWP).After being reflected by a dichroic mirror with a 567 nm cutoff wavelength (DM1, DMLP567 Thorlabs), the pump light is focused on the center of the QPM device with a lens (Len, f = 200 mm) generating visible-MIR photon pairs.The focused beam diameter is 100 µm.The visible signal photons and the pump light are transmitted through the second dichroic mirror with a 2000 nm cutoff wavelength (DM2, Optical Coatings Japan) and again focused onto the QPM device by a concave mirror (CM).The infrared idler photons are reflected by DM2 and spatially separated from the pump light and the signal photons.After being collimated by an off-axis parabolic mirror (OAPM, f = 150 mm), the idler photons pass through a germanium window (G), are reflected by an end mirror (Mi), and are finally refocused by the OAPM onto the QPM device.Mi is placed on a high-precision translational stage (FS-1020UPX, Sigma Koki) to adjust the idler path length.Then, quantum interference between the photon pair generation processes occurs when the spatial modes of the first SPDC photons match those of the second SPDC photons.The signal photons pass through DM1 and a long-pass filter with a 550 nm cut-on wavelength and a short-pass filter (SPF) with a 1000 nm cut-on wavelength.To filter out the unwanted luminescent light, a band pass filter (BPF) with a center wavelength of 609 nm and a bandwidth of 20 nm is placed in the case of a non-chirped device, and a BPF with a center wavelength of 665 nm and a bandwidth of 150 nm is placed in the case of a chirped device.After the filters, a pinhole is used to spatially select the center-most part of the signal beam.The pinhole (P) aperture is set at 150 µm for the non-chirped device and 200 µm for the chirped device.Finally, the signal photons are coupled to a multimode fiber guided to a Si avalanche photodetector (SPCM-AQRH-14FC, Excelitas Tech.) and the photon count is recorded with a photon counter (SR400, Stanford Research systems).It is noted that a visible spectrum is also recorded with a dispersive visible spectrometer (SR500i+DU416A-LDC-DD, Andor).The grating groove density and the grating blaze of the spectrometer are 300 l/mm and 1000, respectively.As a result of quantum interference between the photon-pair generation processes, the signal photon count varies depending on the optical path length difference L inside the nonlinear quantum interferometer.In the subsequent measurements, quantum interferograms, i.e., visible signal photon counts, are recorded as a function of L by translating Mi with a step size of 100 nm (corresponding to L of 200 nm) up to a total translation distance W .At each step, signal counts are integrated for 2 s.
By calculating the Fourier spectrum of the quantum interferogram measured in this way, the spectral intensity of the infrared idler photons contributing to quantum interference can be obtained [6,8].Figure 2(b) shows a quantum interferogram taken with the nonchirped QPM device.The pump power was set to 180 mW and the average signal photon count was 4.1 × 10 4 counts/2s.We observed a distinct interferometric signal showing a periodic oscillation within an approximately 1-mm-wide envelope.The visibility of the signal was V = (P max − P min )/(P max + P min ) = 9.1%, where P max and P min are the maximum and minimum photon count rates, respectively.As shown in the inset, the oscillation period of the interferogram was about 4 µm, corresponding to the design wavelength of 4100 nm for the idler photons generated by the non-chirped QPM device.We performed a Fourier transform of the quantum interferogram shown in Fig. 2(b) using a fast Fourier transform (FFT) algorithm [6,8].The wavenumber resolution of the Fourier spectrum δk is determined by the reciprocal of the total translation distance, δk = W −1 .In this measurement, W was set to 1.8 mm and the corresponding resolution was δk = 5.6 cm −1 .The obtained Fourier amplitude spectrum is shown in Fig. 2

(c).
A spectral peak is centered around 4100 nm with a FWHM of 0.7 nm.This spectral width is compatible with the numerically calculated idler photon generation bandwidth of 0.4 nm [Fig.1(b)], indicating that all the spectral components of the photon pair contribute to quantum interference.
Next, we measured a quantum interferogram using the chirped QPM device as a broadband photon-pair source.The total translation distance W was set to 2.5 mm, resulting in a wavenumber resolution δk of 4 cm −1 in the Fourier spectrum.The quantum interferogram is shown in Fig. 2(d).The average signal photon count was 8.0 × 10 5 counts/2s for a pump power of 150 mW.The visibility was V = 11.0%.The observed quantum interferogram had a highly asymmetric shape and the duration of the signal was much longer than that of the non-chirped QPM device [Fig.2(b)].This can be attributed to the chromatic dispersion of the QPM device and germanium window (G) placed on the idler path.
Figure 2(e) shows the Fourier amplitude spectrum of the quantum interferogram in Fig. 2(d).The spectrum is continuously distributed over the entire wavelength range from 2.0 to 5.0 µm, where idler photon generation by the chirped QPM is expected.The FWHM of the spectrum is 2800 nm, which is in good agreement with the numerically calculated generation bandwidth of the idler photon (2700 nm) as shown in Fig. 1

Fig. 1 .
Fig. 1.Optical characteristics of non-chirped and chirped QPM devices.The material of QPM devices is Mg-doped stoichiometric lithium tantalate (Mg:SLT).The crystal length is 10 mm.The height and width are 1 mm.(a) Schematic view of a non-chirped QPM device.The wavelengths of visible and MIR photon pairs are 612 and 4100 nm, respectively.(b) Numerical simulation results for expected signal (visible) spectrum for visible and MIR photon pairs generated from the non-chirped QPM device.The lower and upper horizontal axes show signal (visible) and idler (MIR) wavelengths, respectively.(c) Experimental signal (visible) spectrum for visible and MIR photon pairs generated from the non-chirped QPM device.(d) Schematic view of a chirped QPM device.The wavelengths of visible and MIR photon pairs are 595 to 725 nm and 2000 to 5000 nm.(e) Numerical simulation results for expected signal (visible) spectrum for visible and MIR photon pairs generated from the chirped QPM device.(f ) Experimental signal (visible) spectrum for visible and MIR photon pairs generated from the chirped QPM device.

Fig. 3 .
Fig. 3. Transmittance measurement of three various samples with an ultra-broadband QFTIR spectroscopy.(a) Transmittance of UVFS, (b) transmittance of polystyrene film, and (c) transmittance of ethanol, calculated from Fourier amplitude obtained by QFTIR spectroscopy.The black line shows the experimental results.The dotted red line shows the reference measured by IRTracer-100 (wavenumber resolution: 4.0 cm −1 ).The insets show the quantum interferogram obtained from the interference between two visible and MIR photon pair generation processes by a chirped QPM device when the samples are inserted.