Structure , nonlinear properties , and photosensitivity of ( GeSe 2 ) 100x ( Sb 2 Se 3 ) x glasses

Chalcogenide glasses from (GeSe2)100-x(Sb2Se3)x system were synthesized, with x varying from 5 to 70, in order to evaluate the influence of antimony selenide addition on nonlinear optical properties and photosensitivity. Nonlinear refractive index and two photon absorption coefficients were measured both at 1064 nm in picosecond regime using the Z-scan technique and at 1.55 μm in femtosecond regime using an original method based on direct analysis of beam profile change while propagating in the chalcogenide glasses. The study of their photosensitivity at 1.55 m revealed highly glass composition dependent behavior and quasi-photostable compositions have been identified in femtosecond regime. To better understand these characteristics, the evolution of the glass transition temperature, density and structure with the chemical composition were determined. © 2014 Optical Society of America OCIS codes: (160.2750) Glass and other amorphous materials; (160.4760) Optical properties; (190.4400) Nonlinear optics, materials; (300.6450) Spectroscopy, Raman.


Introduction
Chalcogenide glasses, based on S, Se or Te elements in combination with suitable elements from 14 th or 15 th group of the periodical system (Ge, As, Sb, etc.), are known to present high linear refractive index, photosensitivity to light exposure [1][2][3][4], and to be highly nonlinear [5][6][7].Indeed, they present great Kerr nonlinearities at femtosecond time scale which can reach values several orders of magnitude larger than that of silica glass, variable two-photon absorption depending on their bandgap and insignificant free carrier absorption [8].For these reasons, chalcogenide glasses have been studied under the scope of the development of alloptical signal processing based on nonlinear effects for telecommunication systems [9][10][11][12][13].For mentioned integrated optical devices, a key prerequisite is an identification of appropriate bulk glass composition regarding the nonlinear figure of merit (FOM) for photonic applications.Thus, among the variety of chalcogenide glasses compositions, materials presenting high nonlinear refractive index represented by n2 (m 2 /W), low two photon absorption (TPA) defined by nonlinear absorption coefficient β (m/W), leading to optimized FOM = n2 / λβTPA, along with negligible linear absorption m  are of interest.Given the diversity of vitreous compositions available, it is necessary to predict the overriding factors which could lead to the best figure of merit.
For crystalline semiconductors according to the theoretical works based on a two-band model assuming a sharp absorption edge proposed by Sheik-Bahae et al., it was reported that TPA starts to occur when the photon energy (h) is above the half bandgap energy Eg while n2 is an increasing function of photon energy until ℎ = 0.5 in case of direct gap or close to Eg for indirect gap [14].Consequently, the figure of merit fluctuates inside this energy range.
The sulfide and selenide glasses are considered as indirect gap amorphous materials and thus, the two-band model is not absolutely valid without a rough approximation [15].The distribution of electronic states of amorphous semiconductors remains not perfectly described [16].It can be noted that the exact determination of optical bandgap Eg, with no well-defined band edges due to the presence of tails and localized electronic states encroached up on the bandgap, is still subject of discussion.Consistent with the approximate onset of significant absorption, the optical gap is generally taken at  = 1000 cm -1 for which the absorption changes from the one controlled by Tauc's relation (where the density of states can be approximated to parabolic bands of extended states) to an exponential Urbach's tail absorption involving both, tail states and extended states.As absorption coefficient is following Tauc's relation in region of ℎ ≥ , the optical gap Eg can be also evaluated from Tauc's law typically used in case of amorphous chalcogenide thin films.
The presence of Urbach's tail related to both, thermal effects and static disorder, leads to TPA below the half bandgap energy.Far below the bandgap energy, the linear properties,  and n0 (linear refractive index), do not exhibit strong dependences on Eg; unlike the nonlinear properties [17].Naturally for a given λlaser, the TPA increases from sulfide glasses to selenide glasses following the bandgap energy decrease.In case of telecommunication wavelength, an energy bandgap larger than ~1.6 eV is required for a negligible TPA.Some increase of TPA in selenide glasses can be tolerated if n2 is growing faster.Sanghera et al. used the classical anharmonic oscillator model to describe the nonlinear data and claimed a linear dependence of n2 versus .providing a predictive capability for nonlinear refractive index [8].
Moreover, if one considers a microscopic approach, the correlation between the local structure (polarity and covalent-ionic nature of the bonds) and the optical nonlinearities in chalcogenide glasses is not completely established yet.However, the polarizable electronic lone pairs (S, Se, As, Sb) seem to have a direct influence on the nonlinear refractive index.For high optical nonlinearities, As-S(Se,Te) and Ge-(As)-S(Se,Te) glass systems were mainly studied [18][19][20][21][22].The substitution of S with Se or Te was realized in order to increase the n2 from 2-7⋅10 -18 m 2 /W for As2S3 glass to 11-30⋅10 -18 m 2 /W for As2Se3 glass at near-infrared wavelengths, see for instance [19,20,23,24].Nevertheless, according to Harbold et al. [19,20], nonlinear refractive index of sulfide and selenide glasses based on As-S(Se) and Ge-As-S(Se) systems is not only dependent on the lone pair electron density of the chalcogen and arsenic, but also on two-photon resonant enhancement accompanied by TPA when the photon energy of the operating laser approaches half of the optical bandgap energy of the material.Thus, in Ge-As-Se system for a fixed ratio of Ge/As = 0.5, a deficit of selenium, which decreases the electronic lone pair density, seems to increase n2.It was shown that in Ge-As-Se glass set, where the normalized photon energy (  ) varies from 0.41 to 0.45, the highest value of n2 was found for normalized photon energy equal to 0.45 with a major detrimental impact on the TPA following the bandgap energy decrease compared to stoichiometric composition.Consequently, the best FOM was obtained for the stoichiometric glass.In case of Ge-As-Se system glasses rich in Ge (Ge/As ratio varying from 1.1 to 2.8), Gopinath et al.
showed that variations of the nonlinear refractive index cannot be satisfactorily explained considering the n2 dependence on lone pair electron density.As the normalised photon energy varies only from 0.38 for stoichiometric glass to 0.41 for the glass with the highest deficit of selenium, the TPA is probably not really large for Ge rich glasses and the  remains in the range of 0.4 to 0.5 cm/GW.Glasses with a strong deficit of Se, present particular structure containing homopolar bonds (Ge(As)-Ge or As-As) that may possibly play a non-negligible role if one considers the microscopic approach.We focused our attention on Ge-Sb-Se system regarding the substitution of As with Sb that may increase the nonlinear properties of the corresponding amorphous chalcogenides due to the enlargement of hyperpolarisability.The corresponding amorphous chalcogenides will have also lower bandgap energy related to this substitution.Further, the use of antimony is beneficial regarding its lower toxicity in comparison with arsenic.Finally, presence of antimony in amorphous chalcogenides is known to reduce photosensitivity of the material.Only few compositions were investigated in the Ge-Sb-Se system, Ge28Sb12Se60 (commercially known as AMTIR-3 or IG5, Eg 1.8 eV) with n2 = 9.4⋅10 -18 m 2 /W at 1.5 m or some Se over-stoichiometric glasses for which the Ge/Sb vary from 1.1 to 5 measured at 1.064 m [5,25].The tailoring of the glass chemical composition in Ge-Sb-Se system would lead to the optimization of FOM thanks to stronger increasing of n2 comparing with TPA.
In this paper, beyond the description of basic physico-chemical properties we focused on nonlinear properties of selected bulk chalcogenide glasses from Ge-Sb-Se system.Within this ternary glass system, a careful analysis of trends in physico-chemical properties is performed by studying their compositional dependences along a characteristic cut-line of glass-forming region.Some authors claim that the knowledge of Z (mean coordination number reflecting the global connectivity of glass) and the glass composition (chemical short-range order) is needed to have a balanced view of the evolution of physico-chemical properties in ternary system [26,27].In our case, we consider a variation of composition on the cut-line (GeSe2)100-x(Sb2Se3)x to investigate the introduction of antimony versus properties of glasses.Nonlinear refractive index and two-photon absorption of studied glasses are measured using Z-scan technique in picosecond regime at 1064 nm and at 1.55 µm in femtosecond regime using an original method.Photosensitivity of Ge-Sb-Se glasses is also studied at 1.55 µm in femtosecond regime.

Materials and experimental methods
For this study, chalcogenide glasses from pseudo-binary (GeSe2)100-x(Sb2Se3)x system (where x varied from 5 to 70) were synthesized.For reader's convenience, individual chemical compositions are shown in ternary Ge-Sb-Se diagram (Fig. 1, adopted from [28]).Ge-Sb-Se glasses were prepared from commercial elements (Ge, Sb and Se) of high purity (5N) using the conventional melting and quenching technique.Despite the high purity of selenium, it presented a surface oxidation (SeO2); therefore selenium was purified before mixing with other elements by distillations under dynamic and static vacuum.At first, all the elements were weighted in appropriate amounts, placed in a silica glass ampoule, which was evacuated and sealed.The elements were melted during 30 minutes at 850 °C in a rocking furnace.Then, the temperature was maintained at 800 °C during 10 hours.After quenching, glass rods were annealed 20 °C below their glass transition temperature during 6 hours, and finally slowly cooled down to room temperature.For optical characterization, resulting glass rods (25 mm diameter) were sliced and polished.
A scanning electron microscope with an energy-dispersive X-ray analyzer (EDS, JSM 6400-OXFORD Link INCA) was used for the determination of Ge-Sb-Se bulk glasses chemical composition and uniformity.Thermal characteristics of Ge-Sb-Se glasses were determined by DSC (Q20 DSC, TA Instruments).DSC measurements were performed with 10 mg powdered samples, heated up to 450°C at heating rate of 10 °C.min -1 .
The structure of bulk glasses was analyzed using micro-Raman spectroscopy.Raman spectra were recorded at room temperature under 785 nm laser excitation with an InVia reflex spectroscope (Renishaw) coupled to an Olympus BFXM free space x20 microscope.Transmittance spectra were measured with a visible-near-IR spectrophotometer (PerkinElmer).Linear refractive indices spectral dependencies (not shown here) as well as optical bandgap values of (GeSe2)100-x(Sb2Se3)x glasses were obtained from the analysis of variable angle spectroscopic ellipsometry (VASE) data measured using an ellipsometer with automatic rotating analyzer (J. A. Woollam Co., Inc.).The measurement parameters are as follows: spectral region 300-2300 nm with wavelengths steps of 20 nm, angles of incidence 50°, 60°, and 70°.For the analysis of VASE data, we used Cody-Lorentz model which includes both the correct band edge function and weak Urbach absorption tail; this model is appropriate for the description of amorphous chalcogenides optical functions [4].
Nonlinear refractive indices and two photon absorption coefficients were first measured using Z-scan technique [29] at 1064 nm [30].The excitation is provided by a linearly polarized mode-locked Nd:YAG laser (1064 nm, pulse duration of 15 ps, 10 Hz).The measurement was performed using a 4f system.The image receiver is a 1000 x 1018 pixels cooled CCD camera (-30 °C) operating with a fixed gain.The sample is moved in the common focus region belonging to both lenses along the beam propagation direction (Z axis).Open and closed Z-scan normalized transmittance are numerically processed from the acquired images by integrating over all the pixels in the first case and over a circular numerical filter in the second one (giving a linear aperture transmittance equal to 0.7).The incident intensity can be varied by a polarizing system at the entry of the setup.In this work and when the material is highly absorbing, the intensity at the center of the beam and in the focus of the Z-scan system is kept around I0 = 0.4 GW/cm 2 .
Nonlinear optical properties of studied chalcogenide glasses were further determined in femtosecond regime.An optical parametric oscillator (OPO, Chameleon, Coherent Inc.) is tuned to 1.55 µm and focused in a bulk glass sample.Pulses duration is 200 fs, while repetition rate is 80 MHz, which gives peak power of 12.5 kW at the average output power of 200 mW.A NIR camera and two power meters monitor the output beam profile and sample transmission, respectively.Both, two photon absorption coefficient and nonlinear Kerr coefficient, are deduced from direct transmission analysis (DTA).The TPA coefficients β are deduced from the analysis of samples transmission as a function of beam intensity.For this measurement, the beam waist is positioned mid-way between the entrance and output faces of the sample (typically 2 mm long) to minimize the influence of diffraction and self-focusing.In a second step, the beam waist is placed exactly at the entrance face of the sample and beam profile at the output face is monitored with the camera.From the modifications of the output beam diameter between linear and nonlinear regime, the Kerr coefficient n2 sign and amplitude are deduced.To this end, the experimental observations are compared with simulations based on numerical resolution of the nonlinear Schrödinger equation.Moreover, from the same experimental arrangement, the damage threshold intensities are evaluated for the different glass compositions.At last, to study the photosensitivity of the materials, the long term evolution of the beam profile at the exit face of the chalcogenide samples is observed.

Physico-chemical properties
The bulk (GeSe2)100-x(Sb2Se3)x samples were amorphous, as confirmed by X-ray diffraction patterns, excluding (GeSe2)30(Sb2Se3)70 material, which was crystalline and was not used for further structural and optical characterization.Chemical composition of fabricated (GeSe2)100-x(Sb2Se3)x glasses as determined using EDS is in good agreement with nominal one; the differences are about 1 at.% -this value corresponds to the EDS measurements uncertainty (Table 1).No crystallization peaks were observed in DSC curves (in measured temperature region) except for glass with x = 70 which is close to glassy domain edge (Fig. 1).Globally, glass transition temperature (Tg) decreases monotonously when antimony concentration increases (Fig. 2).This trend follows changes of vitreous network connectivity occurring when antimony is incorporated in chalcogenide glasses.We note that antimony coordination is 3 (in [SbSe3/2] pyramids), whereas germanium is known to be in a tetrahedral environment ([GeSe4/2] tetrahedra).On the other hand, density of (GeSe2)100-x(Sb2Se3)x glasses clearly increases with rising x (Fig. 2).Considering atomic masses of elements (Ar(Ge) = 72.64,Ar(Sb) = 121.76,Ar(Se) = 78.96)), the density of glasses increases coherently with antimony introduction.
When increasing Sb content in the glassy matrix, changes in Raman spectra are observed.First of all, intensities of Raman bands peaking at ~200 and ~215 cm -1 decrease with increasing Sb content.Looking at decomposition of Raman spectra (Fig. 4), one can note that the ratio between the intensity of the A1 and the A1 c contributions decreases with increasing Sb content, meaning that corner linked tetrahedra are the first bonds broken by Sb introduction.The network slowly evolves from a tetrahedra dominated network to a pyramidal one.Peak intensity corresponding to Ge-Ge bonds vibrations (~170 and ~270 cm -1 ) also decreases when Sb content increases.Raman intensity at ~140 cm -1 which is significant for a type E vibrational mode of Se polymeric chains, decreases when Sb content increases.Finally, a broadening of the main band is observed; this broadening is due to the increase of ~190 cm -1 contribution corresponding to Sb-Se bond vibration in [SbSe3/2] pyramids.A Raman feature peaking at ~160 cm -1 appears when Sb2Se3 content reaches 40%, corresponding to Sb-Sb bond vibration in Se2Sb-SbSe2 entities.Note that the Ge-based entities in this region (at ~170 cm -1 ) are dominated by the Sb-based entities, probably due to their higher polarizability, leading to masking effects, as observed in case of Ge-Sb-Te and Ge-Sb-S system [45,46].The broad high frequency band of low intensity (~230-330 cm -1 ) also tends to disappear when increasing Sb content, meaning that its introduction induces probably a diminution of homopolar Se-Se bond in the glassy matrix.
In order to understand in more detail structural changes occurring in (GeSe2)100-x(Sb2Se3)x glasses with increasing Sb2Se3 content, relative intensities of vibrational modes were investigated as follows.The Sb2Se3 content dependence of the intensity ratio of the A1 c to the A1 modes was plotted, corresponding qualitatively to the ratio between number of edgesharing tetrahedra to corner-sharing ones present in the glassy matrix (Fig. 5).In Ge rich GexSe1-x glasses, the formation of edge-sharing polyhedra is favored, as observed by Sugai [35].As shown in Fig. 5, intensity ratio of edge-shared to corner-shared entities increases with x.Decrease of GeSe2 component concentration in the glassy network thus tends to favor presence of edge-shared [GeSe4/2] tetrahedra and to reduce the number of corner-shared [GeSe4/2] tetrahedra within the network, in agreement with Petit's study [25].Glasses rich in Sb2Se3 thus contain a large number of Ge2Se8/2 entities.Furthermore, number of Se-Se bonds slowly increases compare to Ge-Se bonds from edge and corner-shared tetrahedra (Fig. 5).Intensity ratio of Ge-Ge vibrational mode located at ~170 cm -1 ([Ge2Se6/2] entities) to the sum of edge and corner-shared Ge-based tetrahedra also slightly increases when Sb2Se3 content is higher than 30%.Introduction of Sb2Se3 will then favor formation of homopolar Ge-Ge and Se-Se bonds at the expense of Ge-Se bonds.Intensity ratio of Raman 270 cm -1 feature (assigned to Ge-GemSe4-m structural motifs) to 170 cm -1 feature (attributed to Ge2Se6/2 entities) decreases with increasing content of Sb, leading to the conclusion that the formation of [Ge2Se6/2] entities may be preferred when introducing Sb into glassy structure.Note that for higher Sb2Se3 content in the glasses, calculated intensities of individual contributions suffer due to higher uncertainties coming from global shape of the spectra.Finally, intensity ratio of Raman 155 cm -1 band (Sb-Sb bonds vibrations) to 190 cm -1 feature (Sb-Se vibrations) slightly increases when increasing Sb2Se3 content (Fig. 5).Thus, Sb-Sb bonds may be preferentially formed at high Sb concentrations in (GeSe2)100-x(Sb2Se3)x glasses.
To conclude, GeSe2 glassy network is composed mainly of GeSe4/2 units linked by corner or edge.Introduction of Sb2Se3 in the amorphous matrix seems to induce a progressive change in the network, first favoring edge-shared [GeSe4/2] entities.Then, at intermediate Sb2Se3 contents, glassy network contains significant number of [SbSe3/2] pyramids.Finally, at high Sb concentration in (GeSe2)100-x(Sb2Se3)x glasses, number of Se2Sb-SbSe2 structural motifs seems to be present.Evolution of n2 values in a system can be related to structure of the glass.As proposed by Harbold, nonlinear refractive index is not only dependent on lone pair electron concentration but mainly also on bandgap energy [47].One can assume that change in nonlinear properties depends on the composition and structure of the glass, related to bandgap energy variation from one glass to another one.Petit et al. first demonstrated that in Ge-Sb sulfo-selenide glasses, the increase in nonlinear refractive index could be attributed to the increase of number of Sb-Se and Ge-Se bonds [48].A more recent study of ternary Ge-Sb-Se glasses [25] reported that n2 of Se over-stoichiometric glasses, from Ge23Sb7Se70 to Ge16Sb14Se70, increases when Sb/Ge ratio increases for a Se fixed composition.It should be mentioned that the number of Se-Se bonds is increasing when the Sb/Ge increases, which can also play a secondary role for n2.Nevertheless, in case of Ge(13+x)Sb7Se80-x (x = 0, 10, 15, 22) glass set, the Ge/Sb ratio increase induces an increase of n2 until the composition becomes Se understoichiometric, for which the presence of Ge-Ge homopolar bonds starts to be not negligible and the [GeSe4/2] edge linked tetrahedra content stops to increase.The two main effects of an increase of Ge/Sb in discussed over-stoichiometric glass set is the increase of [GeSe4/2] tetrahedra number connected by edges compare to those connected by corners and the strong decrease of of number of Se-Se bonds.It was also shown that n2 value is related to the number of heteropolar bonds within the glassy matrix and is more influenced by the increase of Sb-Se bonds number than by the increase of Ge-Se ones [25].

Nonlinear optical properties
Nonlinear characterization of studied Ge-Sb-Se glasses are first studied in picosecond regime using the Z-scan technique at 1.064 µm.Results are summarized in Table 3 together with results obtained at 1.55 µm in femtosecond regime.For a comparison, nonlinear characteristics of classical chalcogenide compositions (As2S3, As2Se3, and Ge28Sb12Se60 glasses) measured by other authors are included in Table 3 as well.Linear refractive indices (calculated by VASE) are also shown.
Qualitatively, substitution of sulfur by selenium in chalcogenide glasses leads to a significant increase of n2 values.The values of n2 presented in this work are in good agreement with data measured by Petit et al. at 1.064 µm for Ge28Sb7Se65 glass using a similar picosecond laser source [25].Concerning the determination of two photon absorption coefficients at 1.064 µm, it is globally growing in studied (GeSe2)100-x(Sb2Se3)x glasses with increasing content of antimony which is in accordance with the shift of the bandgap to lower energies.One can find large discrepancies between individual values of two photon absorption coefficient (Table 3): β~0.2-2 and ~4.4-19 cm.GW -1 at 1.064 µm for As2S3 and As2Se3 glasses, respectively.Among studied (GeSe2)100-x(Sb2Se3)x glasses, the highest FOM was found for (GeSe2)90(Sb2Se3)10 composition, reaching value of ~1.2, which is significantly larger comparing with other Ge-Sb-Se glasses measured at 1.064 µm.Nevertheless, the measured β values seem to be overestimated compared to value obtained at 1.55 µm, decreasing strongly the FOM at 1.064 µm.
Table 3: Linear (n0) and nonlinear (n2) refractive indices, n2/n2(SiO2) ratios, two photon absorption coefficients (β), nonlinear figures of merit (FOM) of (GeSe2)100-x(Sb2Se3)x glasses determined at 1.064 and 1.550 µm.For a comparison, data for Ge28Sb12Se60, As2Se3, and As2S3 glasses taken from other authors are given.Note that literature data could differ from this work in measurement method and measurement wavelength (MZI is for Mach-Zehnder interferometry, SRTBC is for spectrally resolved two-beam coupling).

Sample n0 n2
(10 -18 m 2 .W -1 ) Nonlinear properties of studied glasses at 1.55 µm have been investigated using the setup described above.TPA coefficients have first been evaluated by fitting the measured samples transmission T as a function of the input beam intensity I0 using Eq. ( 1): In Eq. ( 1),  is the linear absorption coefficient and L is the sample thickness.Deduced values for β are reported in Table 3.Note that, as expected, TPA is lower than at 1.06 µm.The technique to evaluate the Kerr coefficient at 1.55 µm is based on the analysis of the beam profile variation when the nonlinear effect is present.In linear regime, beam size enlarges due to diffraction over propagation while in nonlinear regime, i.e. at high laser power, the Kerr effect can either further defocus the beam (n2<0) or gives some focusing (n2>0).
For the experiment, the laser beam from the OPO tuned at 1.55 µm is focused to (typically) 26 µm FWHM spot at the entrance face of the sample to be analyzed.In the studied Ge-Sb-Se glasses, a clear decrease of the beam size diameter is observed at the output face at high power compare to low power, as illustrated in Fig. 6.It shows unambiguously that n2 is positive.For studied glasses, significant beam size change is thus predicted between linear (n2 = 0) and nonlinear regime.To accurately determine n2, linear loss and evaluated TPA are also taken into account in the simulations.The deduced n2 values are presented in Table 3.It shows that Kerr effect is stronger in glass with higher Sb2Se3 content and β coefficient follows the same trend.FOM as high as 1.9-2.0can be reached for intermediate compositions.For (GeSe2)x(Sb2Se3)100-x glasses with 5<x<50, estimated values of n2 coefficient vary from 6.5⋅10 -18 to 2.0⋅10 -17 m 2 .W -1 at 1.55 µm.This is in good agreement with data measured for Ge28Sb12Se60 glass by Lenz et al. at 1.5 µm using a similar femtosecond laser source [5].The n2 of Ge-Sb-Se glasses are at least 20% larger than those of Ge-As-Se glasses of analogous stoichiometric composition; that is to say Ge25As10Se65 and Ge12.5As25Se62.5 (n2 = 6.0⋅10 -18 and 1.7⋅10 -17 m 2 .W -1 ) [19,52].Note that an accurate n2 value could not be measured in glass with the highest Sb2Se3 content due to poor reproducibility of the measurements.Within Ge-Sb-Se system, we show that an increase of antimony clearly leads to increasing values of the nonlinear refractive indices n2.n2 at 1.55 m is estimated to be up to ~750 times the value of fused silica (n2(SiO2)~0.027⋅10 -1 m 2 .W -1 ) [53].Regarding structural evolution of Ge-Sb-Se glasses with addition of antimony, one can associate the increase in nonlinear refractive index values, as observed by Petit et al. [25], mainly to the increase in Sb-Se bonds number.Damage peak intensity thresholds of studied glasses have also been assessed using the same optical set-up.It spans to about 2.5 GW.cm -2 for low Sb content glasses down to 1.6 GW.cm -2 for (GeSe2)40(Sb2Se3)60.
From the values reported in Table 3, we note that there are usually large discrepancies between n2 values obtained for the same glass composition (for example 14-30⋅10 -18 m 2 .W -1 in case of As2Se3 glass) obtained by different measurement techniques (Z-scan, Mach-Zehnder interferometry or spectrally resolved two-beam coupling).The uncertainty of the measurement techniques and probably the different glass purities (which may affect transmission and bandgap energy) can also induce discrepancies in n2 values.Moreover, the deduced n2 and β values also depend on the incident intensity due to several features such as free carrier refraction and absorption changes [54] and possible higher order nonlinearities as intensity rises.These are sources of errors when evaluating nonlinear coefficients.Experimentally it is demonstrated that there is a decrease of the effective nonlinear coefficients with increasing intensity.This behavior has also be seen in crystalline semiconductors [55].

Photosensitivity
Additionally to the instantaneous self-focusing due to the Kerr effect, a slow and irreversible variation of the output beam size can be observed for some glass compositions at high intensity when illumination time is long.To quantify this effect, the same optical arrangement as for the evaluation of the Kerr coefficient is used.Fig. 8 shows the time evolution of the output beam FWHM normalized to the initial FWHM in different (GeSe2)100x(Sb2Se3)x glasses when illuminated with intensities of about half the peak intensity damage threshold.In the (GeSe2)95(Sb2Se3)5 glass, the output beam FWHM does not evolve significantly over the observation time of 80 minutes.The absence of photosensitivity is not surprising due to the large energy bandgap of this composition compare to the photon energy.To the contrary, for (GeSe2)90(Sb2Se3)10 and (GeSe2)80(Sb2Se3)20 glasses, a gradual self-focusing is clearly observed.In the latter composition, it even leads to a 15 µm FWHM spot at the output face of the sample which is remarkably smaller than the one at the entrance face (26 µm).This photosensitivity is thus associated with an increase of the index of refraction in the illuminated area.At the end of the photoinduction process, the beam size slightly enlarges when the laser beam power is reduced but a permanent self-focusing persists.This irreversible self-focusing effect is attributed to a permanent photoinduced refractive index change that adds up to the Kerr effect.Remarkably, as the Sb2Se3 content is further increased, the permanent self-focusing tends to disappear and even changes to a defocusing effect for highest Sb2Se3 content.For instance, (GeSe2)70(Sb2Se3)30 composition shows no discernible change in beam size while experiments with (GeSe2)60(Sb2Se3)40 glass reveal an increasing output beam FWHM over time which is the sign of a defocusing effect due to the photosensitivity.We also note that the irreversible index change becomes weaker and appears slower in any composition for lower laser power.Beam size change is unnoticeable at an average power lower than 50 mW (intensity of about 0.3 GW.cm -2 ).Moreover, it is important to note that no photosensitivity is observed if a CW source with the same average power of 200 mW and the same wavelength than the femtosecond laser is used.This leads to the conclusion that the photosensitivity is not related to thermal effects but to optical nonlinearities.
We thus observed an evolution of the output beam size in nonlinear regime for long interaction time (80 min) which is very dependent on glass composition.The experiments suggest that the irreversible index variations are related to nonlinear absorption that gives either photodarkening in self-focusing medium or photobleaching in self-defocusing medium.To confirm this hypothesis, samples transmission T in nonlinear regime is studied over time.
The experimental setup is slightly modified with the insertion of two powermeters, one to monitor the input power and the other one for the output power.Evolution of the transmission, normalized to the initial one (T0), of three characteristic glass compositions is presented in Fig. 9 for peak intensities similar to Fig. 8. First, we observe that a fast dynamic is present at the beginning of the transmission curves.Indeed, in few seconds after switching on irradiating laser, a fast increase of the transmission is observed.These fast transmission variations could be due to defects leading to charge carrier trapped in localized levels; and after the first few seconds, this localized levels could no longer lead to a two-photon absorption limiting transmission.Following this fast transmission increase, weak variations of transmission are also observed on a longer time scale.For instance, a decrease in transmission is observed in the case of self-focusing samples (for example (GeSe2)80(Sb2Se3)20 glass) while an increase of transmission is observed in the case of self-defocusing sample ((GeSe2)50(Sb2Se3)50.This is consistent with a photodarkening effect frequently associated with an increase of the refractive index whereas photobleaching is usually accompanied with a decrease of the index.Note that for the focusing samples, burning of the input glass surface is observed experimentally when illumination time approaches 80 min.This damage is certainly due to the increase of absorption connected with photodarkening.At last, intermediate compositions close to (GeSe2)70(Sb2Se3)30 sample does not show any significant slow transmission evolution with time (Fig. 9) which is in agreement with observations made for beam profile analysis (Fig. 8) where only weak change in beam size was observed.Note that the double kinetic observed in our sample transmission has also been recently reported in Ge-As-Se thin films.A fast transient photodarkening and a slower photobleaching effect was reported [56].To better understand the behavior observed in our samples, a more complete study on structural properties of irradiated samples is under progress.écrire x=50 à la place de 40 Mettre la bonne courbe x=30 à la place

Conclusion
Physico-chemical properties of (GeSe2)100-x(Sb2Se3)x chalcogenide glasses as well as their structural properties are reported.Raman spectra are presented for various glassy compositions and reveal a progressive change when increasing Sb2Se3 content in the system, first favoring edge-shared [GeSe4/2] edge linked entities.Sb2Se3 rich compositions appear to contain slightly higher number of Sb-Sb, Ge-Ge and Se-Se structural motifs.
Nonlinear properties of (GeSe2)100-x(Sb2Se3)x chalcogenide glasses are studied both at 1064 nm and at 1.55 µm.Evolution of n2 and β are measured for different x values.Globally, nonlinear refractive index increases with increasing antimony content and figure of merit as high as 1.9-2.0can be obtained at 1.55 µm.Furthermore, photosensitivity attributed to TPA is shown to be very dependent on composition.It is noteworthy that for glasses with intermediate Sb2Se3 content (at x = 30-40), photosensitivity is strongly reduced.At high power, a striking time varying transmission is also reported which is described with two dissimilar time constants.For instance, a fast photobleaching along with a slow photodarkening is observed in glasses with low Sb2Se3 content.

Fig. 5 .
Fig. 5. Intensity ratios for various Raman active vibration modes.ISe-Se corresponds to the sum of ~230 and ~260 cm -1 contributions from homopolar Se-Se bonds.IES and ICS are intensities of A1 c and A1 bands, respectively (ES is for edge-shared and CS for cornershared tetrahedra).ISb-Sb and ISb-Se correspond to ~155 cm -1 and ~190 cm -1 contributions, respectively.

Fig. 6 .
Fig. 6.Measured evolution of beam FWHM at the output of a 2.21 mm long (GeSe2)60(Sb2Se3)40 sample when input light beam intensity is switched from linear regime to nonlinear regime (I0 = 1.4 GW/cm 2 ) at t = 10 s.Inserts show two corresponding observed images.Furthermore, n2 values at 1.55 µm are determined by comparison of experimental beam self-focusing observations with predictions obtained by numerical solution of the nonlinear Schrödinger equation.As an illustration, Fig. 7 shows the calculated beam size (FWHM) at the exit face of a 2.26 mm long chalcogenide glass as a function of the n2 coefficient for a 25.7 µm FWHM input beam for two different input intensities.For studied glasses, significant beam size change is thus predicted between linear (n2 = 0) and nonlinear regime.To accurately determine n2, linear loss and evaluated TPA are also taken into account in the simulations.The deduced n2 values are presented in Table3.It shows that Kerr effect is stronger in glass with higher Sb2Se3 content and β coefficient follows the same trend.FOM as high as 1.9-2.0can be reached for intermediate compositions.For (GeSe2)x(Sb2Se3)100-x glasses with 5<x<50, estimated values of n2 coefficient vary from 6.5⋅10 -18 to 2.0⋅10 -17 m 2 .W -1 at 1.55 µm.This is in good agreement with data measured for Ge28Sb12Se60 glass by Lenz et al. at 1.5 µm using a similar femtosecond laser source[5].The n2 of Ge-Sb-Se glasses are at least 20% larger than those of Ge-As-Se glasses of analogous stoichiometric composition; that is to say Ge25As10Se65 and Ge12.5As25Se62.5 (n2 = 6.0⋅10 -18 and 1.7⋅10 -17 m 2 .W -1 )[19,52].Note that an accurate n2 value could not be measured in glass with the highest Sb2Se3 content due to poor reproducibility of the measurements.Within Ge-Sb-Se system, we show that an increase of antimony clearly

Fig. 8 .
Fig. 8. Evolution of output beam size with time for (GeSe2)100-x(Sb2Se3)x glasses for intensities about half the damage intensity threshold.

Table 1 . Theoretical and real chemical composition (evaluated by EDS) of fabricated (GeSe2)100-x(Sb2Se3)x glasses (±0.5 at.%), their cut-off wavelengths determined as wavelengths at which absorption coefficient is equal to 10 and 1000 cm -1 , and optical bandgap (Eg, ±0.01 eV) values extracted by Cody- Lorentz model from VASE data and as energy where  = 1000 cm -1 (Eg 03 ).
Table 1 contains also cut-off wavelengths showing linear increase with introduction of Sb2Se3.The bandgap energy determined by Cody-Lorentz model from VASE data (±0.01 eV) decreases with introduction of Sb2Se3 in good agreement with Eg 03 values.