1 . 3-μ m InAs quantum-dot micro-disk lasers on V-groove patterned and unpatterned ( 001 ) silicon

We report comparison of lasing dynamics in InAs quantum dot (QD) micro-disk lasers (MDLs) monolithically grown on V-groove patterned and planar Si (001) substrates. TEM characterizations reveal abrupt interfaces and reduced threading dislocations in the QD active regions when using the GaAs-on-V-grooved-Si template. The improved crystalline quality translates into lower threshold power in the optically pumped continuous-wave MDLs. Concurrent evaluations were also made with devices fabricated simultaneously on latticematched GaAs substrates. Lasing behaviors from 10 K up to room temperature have been studied systematically. The analyses spotlight insights into the optimal epitaxial scheme to achieve low-threshold lasing in telecommunication wavelengths on exact Si (001) substrates. © 2016 Optical Society of America OCIS codes: (140.5960) Semiconductor lasers; (140.3948) Microcavity devices; (230.5590) Quantum-well, -wire


Introduction
Fusing photonic circuits with the advanced silicon technology can break the cost barrier of optoelectronics, essential to enabling the transition from copper to optical interconnects in future data centers [1].In this regard, an on-chip light source represents a vital component, but has been a major obstacle hindering the development of silicon photonics.Although attempts have been made to overcome the indirect bandgap limitation in Si and group-IV compatible alloys, a highly efficient silicon-based laser that is on par with state-of-the-art III-V lasers remains elusive [2,3].Integration of III-V laser diodes on silicon is arguably the most viable path to leverage the economies of scale of silicon while maintaining the highest efficiency and yield [4,5].Over the last few decades, various approaches to achieve III-V photonics on silicon have been pursued, including flip-chip integration, bonding technology, and heteroepitaxial growth.Despite the fact that direct epitaxy of III-V lasers on silicon is a truly monolithic approach desirable in the long term, this technology has lagged far behind [1] because of the fundamental challenges in mitigating issues brought by the lattice mismatch and thermal mismatch between III-V materials and silicon.The high sensitivity of semiconductor lasers to crystalline defects generated in heteroepitaxy makes the task formidable.Recent advances in growing high performance InAs quantum dot (QD) lasers on Si substrates revealed the great potential of utilizing dense and spatially isolated quantum dots to circumvent crystal defects in heteroepitaxy, marking a big step towards potential commercial success of integrated silicon photonics [6][7][8][9][10][11][12].To eliminate antiphase-domains (APDs), all the work reported so far, however, strongly relies on the use of offcut Si substrates.Previously, we have introduced GaAs on V-groove patterned silicon (GoVS) templates using CMOS-compatible, exact (001) silicon wafers without offcut [13,14] and demonstrated 1.3-μm InAs QD micro-disk lasers (MDLs) [15][16][17].Compared to the use of planar Si substrates, growing quantum-dot lasers on V-groove patterned Si substrates may benefit from t importance t characteristics disk lasers on study of the d Benchmarking devices fabri assessment li epitaxial temp  eated by a solution.nanowires wth of the growth on m) GaAs wth of a 1 V blanket prominent suggested substrates s without aries-free ive GaAs y (MBE).followed by a five-stacked InAs dot-in-a-well (DWELL) structure [22] sandwiched by 50 nm Al 0.4 Ga 0.6 As cladding layers.

Experime
Characterization of crystal defects was carried out by TEM imaging using a JEOL2010F field-emission microscope operating at 200 keV.Taken along the [110] zone axis, the brightfield cross-sectional TEM images in Figs.1(a) and 1(b) present the complete structures of the MDLs grown on GoVS and planar Si, respectively.We observe much reduced defects threading upwards in the GoVS template.Figures 1(c) and 1(d) show a zoomed-in view of the active region consisting of five-stacked InAs DWELLs.As opposed to the clean structure on the GoVS template, dislocation lines frequently penetrate through the active region on the planar Si template.In addition, the TEM images revealed a great difference in interface abruptness of the DWELL structures.While the interface is well defined and flat on the GoVS template, surface undulations were uncovered on the planar Si.Plan-view TEM measurements indicated a threading dislocation density of 1.4 × 10 8 cm −2 in the active region on the GoVS template, while three times the value (5.0 × 10 8 cm −2 ) was observed on the planar Si.Typical plan-view TEM images on the V-groove patterned and unpatterned Si are shown in Figs.1(e) and 1(f), respectively.Figure 2 compares room temperature PL of the as-grown epitaxial structure on the three substrates.At a low pump power density of 20 W/cm 2 in Fig. 2(a), non-radiative recombination acts as the dominant quenching mechanism, precluding efficient luminescence from QDs.The difference in the luminescence closely reflects varied defect levels in the GaAs templates.Compared to the reference QDs on the GaAs substrate, the integrated PL intensity of the QDs was degraded by more than a factor of 9 on the planar Si, whereas one third degradation was observed on the GoVS template.This suggests superior optical efficiency using V-grooved Si, compared to simple planar Si.At a high pump power density of 4700 W/cm 2 in Fig. 2(b), we observe only slightly weaker luminescence on the planar Si than on the GoVS template.This is probably because at such a high pumping level, defects are mostly saturated.In Fig. 3(a), a high-resolution TEM image of an InAs quantum dot on the GoVS template is presented, showing a typical dot size of ∼21 nm in diameter and ∼6 nm in height.Low temperature lasing characteristics were measured with the samples mounted in a helium gas flow cryostat and cooled to 10 K.The representative lasing spectra at 3 times threshold are presented in Figs.4(a)-4(c).The spectra comprise of whispering-gallery modes (WGMs) of different radial and azimuthal orders.Dotted arrows were used to connect WGMs with the same radial order.The free spectral range (FSR) was extracted to be around 30 nm.While distinct lasing peaks were observed for all three samples, the MDL on GaAs exhibited the most significant suppression of background emission, indicating the most efficient coupling of the emitter to the surrounding cavity.In contrast, the MDL on planar Si exhibited the smallest extinction ratio of ~12 dB.This is presumably attributed to the highest density of defects in the epitaxial layer compared with the other two, such that the quenching effect from non-radiative recombination is more prominent.Furthermore, the deep levels associated with the dislocations can also leach away the photogenerated carriers that are generated outside the active region.Light-in light-out (L-L) lasing curves in the log-log scale at 10 K for the three samples are presented in Figs.4(d)-4(f).The S-shaped nonlinear characteristics clearly indicate the evolution from spontaneous emission to lasing.Thresholds were determined through a linear fit to the higher-power region of the L-L curves in linear scale, as shown in the insets of Figs.4(d)-4(f).The thresholds of the dominant mode were determined to be ~50, 85, and 150 µW for the MDLs on the GaAs substrate, the GoVS template, and the planar Si template, respectively.
Figures 5(a)-5(c) display representative room temperature lasing emission spectra of the MDLs on the GaAs substrate, the GoVS, and the planar Si template, respectively.Note that a pronounced background emission was observed on planar Si.From the linear L-L curve shown in the insets in Figs.5(a)-5(c), the lasing thresholds were extracted to be ~100, 135, and 265 µW for the MDLs on the GaAs substrate, the GoVS template, and the planar Si template, respectively.Statistical analysis over some sampling of micro-disks were performed to reach a fair comparison.Histograms of the thresholds over a number of devices at 10 K and 300 K for the MDLs on the three templates are presented in Figs.6(a)-6(f).The overall lasing thresholds of the MDLs on the GoVS template were much lower compared to those on planar Si.Notably, at 300 K, the threshold of the best working device on the GoVS template (135 µW) yielded a ~2-fold reduction compared to the best one on the planar Si template (265 µW), and was only around 1.35 times that of the best reference MDL (100 µW) on GaAs.The low-threshold laser operation under room temperature continuous-wave optical pumping presents a solid evidence of the high optical properties of the III-V crystals monolithically grown on Si.Currently, our epitaxial structure does not adopt any dislocation filtering layers.It has been reported that four sets of In 0.18 Ga 0.82 As/GaAs strained-layer superlattices (SLSs) may further reduce the dislocation density in the hetero-epitaxy of GaAs on Si [12].We therefore expect better device performance by adding effective dislocation filters in the GaAs on Si buffer, as well as by improving the uniformity of the QDs to enhance active modal gains.An important aspect of integrating active devices on Si is that the Si substrate is not only used as a substrate carrier but also can be used as waveguiding material because of the low optical material losses.The GoVS templates used in this work do not include any absorptive germanium buffer or other dislocation filter layers.Thus, it allows coupling from the laser active regions to Si waveguides and suggests potential opportunity to be incorporated in the well-developed silicon-on-insulator (SOI) technology in Si photonics.However, one concern for mode coupling into underlying patterned Si waveguide is that the V-grooves would add a significant amount of scattering loss.A. Liu et al. recently proposed one approach to achieve waveguide coupling by growing III-V cavity in selectively V-groove patterned regions on the handle wafer of a SOI substrate [11].The optical mode is butt-coupled to a silicon rib waveguide and the optical coupling can be maximized by aligning the height of the active quantum dot region with the Si waveguide layer.

Conclusions
In conclusion, low-threshold micro-disk lasers with compact optical cavities were demonstrated on (001) Si substrates using different epitaxial schemes.A comprehensive comparison of the lasing dynamics was made in devices with the same active structures and geometries but fabricated on different GaAs-on-Si templates, from 10 K up to room temperature.Compared to GaAs on Si by conventional blanket heteroepitaxy, the GoVS template using V-groove patterned heteroepitaxy exhibited improved material quality and thereby greatly enhanced optical efficiency, as reflected by the superior lasing characteristics.The somewhat forgiving nature of QD lasers is also demonstrated by room temperature lasing of MDLs grown on simple GaAs on planar Si templates.This work therefore closes the gap between III-V lasers epitaxially grown on lattice-matched substrates and dissimilar Si substrates, illuminating a promising path towards low-threshold on-chip laser sources for high-density, high-speed data interconnections.
Fig. 1 planar GoVS disloc We first prepa (MOCVD), o The V-groove SiO 2 stripe-m MOCVD sele inside the V-GaAs nanowi planar Si, a nucleation lay µm GaAs bu heteroepitaxy double steppe single domain through an A any specified epilayers wer substrate, mic 1-µm GaAs b

Fig. 2 .
Fig. 2. Room temperature PL of the as-grown structure on GoVS template, GaAs substrate and planar Si template at pump power densities of (a) 20 W/cm 2 and (b) 4700 W/cm 2 .

Fig. 5 .
Fig. 5. Laser emission spectra at 300 K for MDLs on (a) GaAs substrate, (b) GoVS template, and (c) planar Si template.Inset: L-L curve in linear scale, the dashed line represents a linear fit to the experimental data.

Fig. 6 .
Fig. 6.Histograms of the lasing thresholds over a number of devices at 10 K for MDLs on (a) GaAs substrate, (b) GoVS template, and (c) planar Si template.Histograms of the threshold over a number of devices at 300 K for MDLs on (d) GaAs substrate, (e) GoVS template, and (f) planar Si template.