Photoelectrochemical hydrogen generation with linear gradient Al composition dodecagon faceted AlGaN / nGaN electrode

We demonstrated photoelectrochemical cells (PECs) with dodecagon faceted AlGaN/n-GaN heterostructure electrode for H2 generation, where the AlGaN/n-GaN heterostructure has a linear gradient Al composition (LGAC). The separation efficiency of the photo-generated electron–hole pairs in the electrode performs a key function in the H2 generation efficiency of PEC cells. The linear gradient Al composition, AlGaN, could create more internal field and light absorption because of the linear graded band gap. Therefore, the zero-bias photocurrent density of PEC cells with dodecagon facet LGAC AlGaN/n-GaN heterostructure electrode is around 5.9 times larger than that of dodecagon faceted n-GaN electrode. ©2014 Optical Society of America OCIS codes: (230.0230) Optical devices; (230.0250) Optoelectronics; (230.2090) Electro-optical devices. References and links 1. S. Ida, K. Yamada, T. Matsunaga, H. Hagiwara, Y. Matsumoto, and T. Ishihara, “Preparation of p-type CaFe2O4 photocathodes for producing hydrogen from water,” J. Am. Chem. Soc. 132(49), 17343–17345 (2010). 2. J. Z. Zhang, “Metal oxide nanomaterials for solar hydrogen generation from photoelectrochemical water splitting,” MRS Bull. 36(1), 48–55 (2011). 3. A. Fujishima and K. Honda, “Electrochemical photolysis of water at a semiconductor electrode,” Nature 238(5358), 37–38 (1972). 4. A. Wolcott, W. A. Smith, T. R. Kuykendall, Y. Zhao, and J. Z. Zhang, “Photoelectrochemical Study of Nanostructured ZnO Thin Films for Hydrogen Generation from Water Splitting,” Adv. Funct. Mater. 19(12), 1849–1856 (2009). 5. K. Fujii, T. K. Karasawa, and K. Ohkawa, “Hydrogen Gas Generation by Splitting Aqueous Water Using n-Type GaN Photoelectrode with Anodic Oxidation,” Jpn. J. Appl. Phys. 44(18), L543–L545 (2005). 6. S. Y. Liu, J. K. Sheu, C. K. Tseng, J. C. Ye, K. H. Chang, M. L. Lee, and W. C. Lai, “Improved hydrogen gas generation rate of n-GaN photoelectrode with SiO2 Protection layer on the ohmic contacts from the electrolyte,” J. Electrochem. Soc. 157(2), B266–B268 (2010). 7. J. K. Sheu, Y. K. Su, G. C. Chi, M. J. Jou, C. C. Liu, and C. M. Chang, “Indium tin oxide ohmic contact to highly doped n-GaN,” Solid-State Electron. 43(11), 2081–2084 (1999). 8. Q. Ding, F. Meng, C. R. English, M. Cabán-Acevedo, M. J. Shearer, D. Liang, A. S. Daniel, R. J. Hamers, and S. Jin, “Efficient Photoelectrochemical Hydrogen Generation Using Heterostructures of Si And Chemically Exfoliated Metallic Mos2,” J. Am. Chem. Soc. 136(24), 8504–8507 (2014). 9. B. Kaiser, D. Fertig, J. Ziegler, J. Klett, S. Hoch, and W. Jaegermann, “Solar Hydrogen Generation with Wide-Band-Gap Semiconductors: Gap(100) Photoelectrodes and Surface Modification,” ChemPhysChem 13(12), 3053–3060 (2012). 10. A. Pareek, R. Purbia, P. Paik, N. Y. Hebalkar, H. G. Kim, and P. H. Borse, “Stabilizing effect in nano-titania functionalized CdS photoanode for sustained hydrogen generation,” Int. J. Hydrogen Energy 39(9), 4170–4180 (2014). 11. A. J. Nozik and R. Memming, “Physical chemistry of semiconductor-liquid interfaces,” J. Phys. Chem. 100(31), 13061–13078 (1996). 12. I. Waki, D. Cohen, R. Lal, U. Mishra, S. P. DenBaars, and S. Nakamura, “Direct water photoelectrolysis with patterned n-GaN,” Appl. Phys. Lett. 91(9), 093519 (2007). 13. J. Li, J. Y. Lin, and H. X. Jiang, “Direct hydrogen gas generation by using InGaN epilayers as working electrodes,” Appl. Phys. Lett. 93(16), 162107 (2008). #223682 $15.00 USD Received 23 Sep 2014; revised 30 Oct 2014; accepted 30 Oct 2014; published 13 Nov 2014 (C) 2014 OSA 15 December 2014 | Vol. 22, No. S7 | DOI:10.1364/OE.22.0A1853 | OPTICS EXPRESS A1853 14. J. Wu, W. Walukiewicz, K. M. Yu, J. W. Ager III, E. E. Haller, H. Lu, and W. J. Schaff, “Small band gap bowing in In1−xGaxN alloys,” Appl. Phys. Lett. 80(25), 4741 (2002). 15. M. Ono, K. Fujii, T. Ito, Y. Iwaki, A. Hirako, T. Yao, and K. Ohkawa, “Photoelectrochemical reaction and H2 generation at zero bias optimized by carrier concentration of n-type GaN,” J. Chem. Phys. 126(5), 054708 (2007). 16. I. Waki, D. Cohen, R. Lal, U. Mishra, S. P. DenBaars, and S. Nakamura, “Direct water photoelectrolysis with patterned n-GaN,” Appl. Phys. Lett. 91(9), 093519 (2007). 17. S. Y. Liu, J. K. Sheu, J. C. Ye, S. J. Tu, C. K. Hsu, M. L. Lee, C. H. Kuo, and W. C. Lai, “Characterization of n-GaN with naturally textured surface for photoelectrochemical hydrogen generation,” J. Electrochem. Soc. 157(12), H1106–H1109 (2010). 18. W. H. Tu, Y. K. Hsu, C. H. Yen, C. I. Wu, J. S. Hwang, L. C. Chen, and K. H. Chen, “Au nanoparticle modified GaN photoelectrode for photoelectrochemical hydrogen generation,” Electrochem. Commun. 13(6), 530–533 (2011). 19. Y. G. Lin, Y. K. Hsu, A. M. Basilio, Y. T. Chen, K. H. Chen, and L. C. Chen, “Photoelectrochemical activity on Ga-polar and N-polar GaN surfaces for energy conversion,” Opt. Express 22(S1), A21–A27 (2014). 20. S. Jung, S. N. Lee, K. S. Ahn, and H. Kim, “Surface Fermi Level Pinning of Semipolar (11 ̅22) n-type GaN Surfaces Grown on m-Plane Sapphire Substrates,” Electron. Mater. Lett. 9(5), 609–613 (2013). 21. K. Fujii, Y. Iwaki, H. Masui, T. J. Baker, M. Iza, H. Sato, J. Kaeding, T. Yao, J. S. Speck, S. P. Denbaars, S. Nakamura, and K. Ohkawa, “Photoelectrochemical Properties of Nonpolar and Semipolar GaN,” Jpn. J. Appl. Phys. 46(10A), 6573–6578 (2007). 22. K. Fujii, M. Ono, T. Ito, Y. Iwaki, A. Hirako, and K. Ohkawa, “Band-edge energies and photoelectrochemical properties of n-type AlxGa1-xN and InyGa1-y N alloys,” J. Electrochem. Soc. 154(2), B175–B179 (2007). 23. Y. R. Wu, R. Shivaraman, K. C. Wang, and J. S. Speck, “Analyzing the physical properties of InGaN multiple quantum well light emitting diodes from nano scale structure,” Appl. Phys. Lett. 101(8), 083505 (2012). 24. C. K. Li, M. Rosmeulen, E. Simoen, and Y. R. Wu, “Study on the Optimization for Current Spreading Effect of Lateral GaN/InGaN LEDs,” IEEE Trans. Electron. Dev. 61(2), 511–517 (2014). 25. O. Ambacher, J. Majewski, C. Miskys, A. Link, M. Hermann, M. Eickhoff, M. Stutzmann, F. Bernardini, V. Fiorentini, V. Tilak, B. Schaff, and L. F. Eastman, “Pyroelectric properties of Al(In)GaN/GaN heteroand quantum well structures,” J. Phys. Condens. Matter 14(13), 3399–3434 (2002). 26. J. Simon, V. Protasenko, C. Lian, H. Xing, and D. Jena, “Polarization-Induced Hole Doping in Wide-Band-Gap Uniaxial Semiconductor Heterostructures,” Science 327(5961), 60–64 (2010). 27. Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “Self-screening of the quantum confined Stark effect by the polarization induced bulk charges in the quantum barriers,” Appl. Phys. Lett. 104(24), 243501 (2014). 28. Z. H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “InGaN/GaN multiple-quantum-well light-emitting diodes with a grading InN composition suppressing the Auger recombination,” Appl. Phys. Lett. 105(3), 033506 (2014). 29. Z.-H. Zhang, S. T. Tan, Z. Kyaw, W. Liu, Y. Ji, Z. Ju, X. Zhang, X. W. Sun, and H. V. Demir, “p-doping-free InGaN/GaN light-emitting diode driven by three-dimensional hole gas,” Appl. Phys. Lett. 103(26), 263501 (2013). 30. Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, X. Zhang, L. Wang, Z. Kyaw, X. W. Sun, and H. V. Demir, “Polarization self-screening in [0001] oriented InGaN/GaN light-emitting diodes for improving the electron injection efficiency,” Appl. Phys. Lett. 104(25), 251108 (2014). 31. Y. Zhao, R. M. Farrell, Y. R. Wu, and J. S. Speck, “Valence band states and polarized optical emission from nonpolar and semipolar III-nitride quantum well optoelectronic devices,” Jpn. J. Appl. Phys. 53(10), 100206 (2014). 32. H.-H. Huang and Y.-R. Wu, “Light Emission Polarization Properties of Semipolar InGaN/GaN Quantum Well,” J. Appl. Phys. 107(5), 053112 (2010).


Introduction
Solar hydrogen (H 2 ) generation via water splitting poses an advantageous challenge for developing clean eco-friendly energy systems [1].The photoelectrochemical method of generating H 2 is one of the most desirable renewable routes to address this challenge [2].Fujishima et al. have reported water splitting into H 2 and O 2 with TiO 2 electrode under ultraviolet (UV) light illumination [3].Since then, several metal-oxide semiconductors have been widely investigated [4].Besides metal-oxide semiconductors, various semiconductors have been demonstrated as water splitting photoelectrochemical cells (PECs) photoelectrode or photocatalyst, such as GaN [5][6][7], MoS 2 /Si [8], GaP [9], and CdS [10].Semiconductors for use in PECs H 2 generation should possess a conduction band potential that is less than that of the cathode reduction half-reaction, and its valence band-edge potential must be higher than that of the anode oxidation half-reaction [11].GaN-based materials have suitable band gap that fits the criteria for photoelectrochemical H 2 generation [12,13].In addition, III-nitride materials are potentially resistant to aqueous solutions [14].Tuning the band gap of GaN-based material from 3.4 eV to 0.7 eV by adding indium content would result in the PECs fitting the solar spectrum for enhancing light absorption.Moreover, Ono et al. have also reported that n-GaN electrode PECs split water without extra bias [15].However, the photocurrent density is not sufficiently high to produce adequate hydrogen gas within a short time.Increasing the area of GaN surface would be one method to enhance the photocurrent of PECs for water splitting.Waki et al. have reported on GaN area increase by introducing a select area GaN growth technique [16].The group created faceted GaN strips on a patterned n-GaN template to increase the area of GaN and, consequently, the photocurrent of PECs.However, Liu et al. have reported that PECs with a naturally textured rough n-GaN electrode did not exhibit photo-current enhancement compared with a smooth surface n-GaN electrode under illumination [17].This result should be attributed to the highly defective low-temperature growth of textured n-GaN electrode.Moreover, Tu et al. have reported that the photocurrent of PECs with p-GaN electrode could be enhanced by introducing Au nanoparticles on the p-GaN electrode, because the Au nano-particles could bend down the energy band of p-GaN larger than p-GaN in direct contact with the solution [18].Therefore, the band bending of the GaN electrode would also affect the photocurrent of the PECs.In this study, we aimed to demonstrate a faceted AlGaN/n-GaN heterostructure with linear gradient Al composition (LGAC) AlGaN layer as the electrode of PECs.The optoelectrical characteristics of the fabricated PEC cell with flat n-GaN, faceted n-GaN, and facet LGAC AlGaN/n-GaN heterostructure electrode will be discussed.

Experiments
All samples were grown on a (0001) sapphire substrate by vertical MOCVD.In n-GaN and heterostructure AlGaN/n-GaN epitaxy, trimethylgallium (TMGa), trimethylaluminum (TMAl), and ammonia are the source materials for Ga, Al, and N, respectively.Silane is an n-type doping source of the III-nitride material.A 25 nm thick, low-temperature GaN nucleation layer was first deposited on the substrate at 520 °C after a standard H 2 etch-back process at 1060 °C.A 1.5 μm thick, high-temperature undoped GaN (u-GaN) was deposited at 1050 °C after the NH 3 / H 2 etch-back process.A 2 μm thick, Si-doped GaN layer (n-GaN) with doping concentration of 1 × 10 19 cm −3 was then grown on the u-GaN layer.The samples were then removed from reactor and then a 250 nm thick SiO 2 deposited on n-GaN.Standard photolithography was then used to define a circular disk pattern of 3 μm diameter and 3 μm spacing between two neighboring disks.An inductively coupled (ICP) plasma etcher was used to etch the exposed SiO 2 regions to form a SiO 2 -pillar mask.Subsequently, a faceted n-GaN layer was grown on the n-GaN template with the SiO 2 pillar mask where the faceted n-GaN has thickness and doping concentration of 5 μm and 1 × 10 19 cm −3 , respectively.A 100 nm thick undoped AlGaN layer with and without gradient Al composition was grown on the faceted n-GaN layer to form the faceted AlGaN/n-GaN heterostructure.We varied the TMAl flow rate linearly from 40 sccm to 5 sccm to create AlGaN layers with a linear gradient Al composition from 20% at the AlGaN/GaN interface to 2.5% on the surface.And we keep the TMAl flow rate of 40 sccm to create constant 20% Al composition of AlGaN layer.We performed scanning electron microscopy (SEM) to observe the surface morphology of samples.Transmission electron microscope (TEM) was performed to index dodecagonal planes of faceted n-GaN structure.
For ohmic contact of the faceted AlGaN/n-GaN heterostructure, a portion of the AlGaN layer was removed via ICP dry etching to expose the n-GaN layer.A bilayer metal Cr (50 nm) / Au (80 nm) was then deposited on the n-GaN and exposed n-GaN to form an ohmic contact.The PECs with flat n-GaN electrode was named as PECs I for comparison.The PECs with faceted n-GaN, constant Al composition (CAC) AlGaN/n-GaN, and LGAC AlGaN/n-GaN electrode were named as PECs II, III, and VI, respectively.A potentiostat (Autolab-PGSTAT128N) was employed to supply the external bias.The current density was measured to evaluate the electrical properties of the PECs.A 300 W Xe lamp was utilized as light source, and 1 mol/L NaCl was used as electrolyte at room temperature.The light illumination power at position of PECs is 2.2 W/cm 2 .An Ag/AgCl reference electrode and a platinum (Pt) wire counter electrode were used to measure the potential.The bias voltage was applied to the working electrode with respect to the Ag/AgCl reference electrode.Hydrogen gas was generated at the Pt wire counter electrode.

Results and discussions
Figure 1 shows surface morphology SEM images of faceted n-GaN, CAC AlGaN/n-GaN, and LGAC AlGaN/GaN electrode.The n-GaN layer with facets presented epitaxy lateral overgrowth (ELO) on top of the SiO 2 pillars at standard growth conditions, as shown in Fig. 1.Therefore, faceted dodecagon V-shaped pits were created on top of the SiO 2 pillars.As the growth time elapsed, the bottom of the dodecagon V-shaped pits decreased because of the ELO process.However, the growth rate of dodecagon V-shaped pit facet surfaces is considerably less than that of the (0001) surface.Therefore, the facet surfaces of dodecagon V-shaped pits would eventually coalesce with the facet surfaces of the neighboring V-shaped pits, and the (0001) surface disappeared.Finally, we could obtain a dodecagon faceted n-GaN structure layer having the average size of the bottom and top dodecagon V-shaped pits of 1.02 and 6.2 μm, respectively.Moreover, the dodecagon faceted n-GaN structure layer was consisted with rough and smooth facets as indicated in Fig. 1(a).We have done the TEM on the sample of faceted GaN structure to index the faceted GaN planes.Two TEM samples were prepared by Focus Ion Beam (FIB) to cut along line 1 and line 2 from the dodecagon faceted n-GaN structure as indicated by the Fig. 1(a).TEM analysis was then performed in a FEI Tecnai F20 TEM operated at 200 kV.TEM bright field (BF) images and their corresponding selected area diffraction patterns (SADPs) were recorded.The rotation angle between images and SADPs was calculated to be 90 clockwise (SADP fixed) from the over-focused shadow image which contains the image inside the transmitted beam.The rough surface of the dodecagon faceted n-GaN structure is identified to be {1 1 −2 2} by a pair of TEM BF cross-section image cut along the line 1 presented in Fig. 1(a) and its corresponding SADP, as indicated in Fig. 1 (d).The smooth surface of the dodecagon faceted n-GaN structure is identified to be {-1 1 0 1} by a pair of TEM BF cross-section image cut along the line 2 presented in Fig. 1(a) and its corresponding SADP, as indicated in Fig. 1(e).Both {1 1 −2 2} and {-1 1 0 1} should belong to the semi-polar surface.The {1 1 −2 2} facets have a rougher surface than the {-1 1 0 1}.To date, the details for the formation of rough {1 1 −2 2} surfaces are not yet understood and need to be investigated.The following AlGaN layer growth for the CAC AlGaN/GaN and LGAC AlGaN/GaN heterostructures should not change the dodecagon facet shape of the faceted n-GaN layer.Figure 2 demonstrates the dark and illuminated current densities of PECs I, II, III, and VI as a function of external bias voltage (V ext ).All PECs show similar dark current density (J d ) -V ext characteristics and possess cathodic currents associated with proton reduction onset potential of around -0.8 V.Under illumination and at a photocurrent density of 2 mA/cm , the voltage of PECs II (-0.035V) is larger than that of PECs I (-0.27V).In addition, the zero-bias voltage photocurrent density of PEC II (2.34 mA/cm 2 ) is less than that of PECs I (6.06 mA/cm 2 ).However, the photocurrent of PECs II is larger than PECs I when the applied V ext is larger than 0.6 V.The PECs with dodecagon faceted n-GaN electrode have the least and the largest zero bias photocurrent density and voltage at 2 mA/cm 2 , respectively.Lin et al. have reported that the polarization direction of GaN would affect the energy band bending of the GaN and electrolytes junction [19].Ga-polar n-GaN with polarization pointing to GaN would have larger band bending than the N-polar n-GaN with polarization pointing out off the GaN surface.This trend imparts Ga-polar n-GaN with more effective carrier separation and less carrier recombination than the N-polar n-GaN.Moreover, Jung et al. have reported that the surface Fermi level of semipolar (11)(12)(13)(14)(15)(16)(17)(18)(19)(20)(21)(22) n-GaN/metal contact pinned around 0.82 eV below the conduction band energy [20]  However, the photocurrent density (J p )-V ext characteristics of PECs with dodecagon faceted n-GaN electrode could be improved by adding an AlGaN layer.PECs III presents a voltage at 2 mA/cm 2 and zero bias photocurrent of -0.32 V and 8.62 mA/cm 2 , respectively.PECs III shows more negative voltage at 2 mA/cm 2 than of PECs II and I. Furthermore, the zero-bias photocurrent density of PECs III is around 3.7 and 1.5 times larger than those of PECs II and I, respectively.In addition, the photocurrent density of PECs III is larger than those of PECs I and II for an applied bias ranging from -0.6 V to 2.0 V. Fujii et al. [22] have reported that the energy differences between the conduction band-edge energy and the energy of the H 2 evolving half-reaction increases with Al composition.The electrons in the conduction band of Al x Ga 1−x N are expected to have higher energy for H 2 gas production than those in GaN.Thus, easier H 2 gas evolution at the counter electrode is expected when Al x Ga 1−x N is used than when GaN is used with the same number of electrons.Moreover, the group also revealed that the onset voltage of PECs with AlGaN electrode would have negative voltage with increasing Al composition of AlGaN.Although the larger band gap of AlGaN is directly linked to lower photo absorption, the internal field of AlGaN/GaN heterostructure from the piezoelectric polarization effect would enhance the generated electron-hole pair separation and suppress the carrier recombination process in the AlGaN layer.Therefore, the PECs with dodecagon faceted AlGaN/n-GaN electrode (PECs III) has considerably better zero-bias photocurrent density and more negative voltage at 2 mA/cm 2 than the PECs with flat n-GaN and dodecagon facet n-GaN electrodes.
The J p -V ext characteristic of PECs with dodecagon facets AlGaN/n-GaN heterostructure electrode could be further improved by band engineering of the AlGaN layer with linear gradient Al composition.The PECs IV has the largest zero-bias photocurrent density of 13.77 mA/cm 2 and has almost the same voltage of −0.36 V at 2 mA/cm 2 as PECs III.The zero-bias photocurrent density of PECs IV is around 1.6, 5.9, and 2.3 times larger than those of PECs III, II, and I, respectively.Therefore, the PECs IV should have larger amount gas generation than the PECs I at zero-bias as indicated in Fig. 3. Figure 4   Unlike the linear upward bending band of CAC AlGaN/GaN heterostructure electrode of PECs, the LGAC AlGaN/GaN hetero-structure electrode PECs have a curve-bending band as shown in Fig. 3 (a).The LGAC AlGaN/GaN heterostructure electrode shows more rapid band bending up at the interface of the AlGaN/GaN than CAC AlGaN/GaN heterostructure electrode.In addition, the band bending of LGAC AlGaN/GaN heterostructure electrode slows down and flattens near the electrode surface.Therefore, the E c and E v electric field is not constant in the whole LGAC AlGaN layer but gradually reduces from AlGaN/GaN interface toward the surface.Since small band offsets E c Δ and E v Δ due to the composition changes in each section of LGAC AlGaN layer, there were E c and E v electric field pikes at each section junction after taking the derivation of E c and E v .However, the pikes electric field directions at conduction band and valence band are different.The overall electric field of LGAC AlGaN/GaN heterostructure is larger than that of CAC AlGaN/GaN heterostructure in the region between 1000 nm and 1045 nm.For the conduction band, the overall E c electric field is smaller including those E c electric field pikes due to the band offset.However, because the electron mobility is much higher than holes, the diffusion length is much longer to avoid recombination.The advantage part is in the valence band, the E v electric field pikes direction (induced by the valence band offset) is the same as the depletion field direction.As mentioned, the hole mobility is much lower than electron.Therefore, the hole needs a larger electric field to be pulled away from the AlGaN/GaN interface especially near the AlGaN/GaN interface where a large two dimensional electron gas is there.In the LGAC case, the hole is much easier to move away due to the larger electric field near AlGaN/GaN interface and also those additional E v electric field pikes.Therefore, the PECs with LGAC AlGaN/GaN hetero-structure electrode should have better photo-generated electron-hole pair separation efficiency than that with CAC AlGaN/GaN heterostructure electrode.Moreover, the LGAC AlGaN layer might have better light absorption than the AlGaN layer because of the extra light absorption wavelength from 334 nm to 362 nm.Therefore, PECs IV has the largest zero-bias photocurrent density and has almost the same voltage at 2 mA/cm 2 as PECs III.

Conclusions
In summary, we demonstrated PECs with dodecagon faceted n-GaN, CAC AlGaN/GaN hetero-structure and LGAC AlGaN/n-GaN heterostructure electrode for H 2 generation.The separation efficiency of the photo-generated electron-hole pairs in the electrode performs a key function for H 2 generation efficiency of PECs.Dodecagon faceted n-GaN electrode has less zero-bias photocurrent density than flat n-GaN electrode because of the reduced polarization field and surface Fermi level pinning effect to reduce photo-generated electron-hole pair separation efficiency.Adding an AlGaN layer on the dodecagon faceted n-GaN electrode would help improve the zero-bias photocurrent density by 3.7 times because of the assistance of internal spontaneous and piezoelectric polarization fields.Furthermore, the LGAC AlGaN could create more internal field and light absorption because of the linear graded band gap.Therefore, zero-bias photocurrent density of PECs with dodecagon faceted LGAC AlGaN/n-GaN heterostructure electrode is around 5.9 times larger than that with dodecagon faceted n-GaN electrode.

Fig. 1 .
Fig. 1.Surface morphology SEM images of (a) faceted n-GaN, (b) CAC AlGaN/n-GaN, and (c) LGAC AlGaN/GaN electrode (d) The TEM cross-section image cut on the rough surface of the dodecagon faceted n-GaN structure and its corresponding SADP with z = [1-100].(e) The TEM cross-section image cut on the smooth surface of the dodecagon faceted n-GaN structure and its corresponding SADP with z = [11-20].

Fig. 2 .
Fig. 2. (a) Dark and (b) illuminated current densities of PECs I, II, III, and IV as a function of Potential vs. Ag/AgCl (V ext ).
(a) shows the numerical simulated schematic band diagrams of electrolyte and dodecagon faceted n-GaN, dodecagon faceted CAC AlGaN/n-GaN heterostructure, and dodecagon faceted LGAC AlGaN/n-GaN heterostructure electrode interface at zero-bias.And we have taken the derivation of conduction band (E c ) and valance band (E v ) to find the electric field profiles at conduction band and valence band of all PECs samples as shown in Fig. 4(b).The details of the simulation software have been reported by the Wu et al. and Li et al. [23,24].The Fermi level is zero in the whole junction at zero bias.The band-offset ratio ( c E / g E Δ Δ ) is 63%.The basic parameters especially the setting of polarization value can be found in report of Ambacher et al. [25].#223682 -$15.00USD Received 23 Sep 2014; revised 30 Oct 2014; accepted 30 Oct 2014; published 13 Nov 2014 (C) 2014 OSA According to Ref. 25, since GaN is the substrate, the polarization of different x% Al composition is the function of x%.For the linear gradual Al composition AlGaN layer case, we divided 100nm thick AlGaN layer into 33 sections where each section's Al composition gradually changes from 20% to 5% in the growth direction.As shown in the insect of Fig. 3, each section of E c and E v of LGAC AlGaN has small band offsets E c Δ and E v Δ due to the composition changes.The polarization charge difference induced at each interface can be obtained by taking the divergence of P(x) along the growth direction, i.e. pol P(x) = ρ ∇ .In our setting, the equivalent negative polarization charge density is induced as Simon et al. [26] and Zhang et al. [27-30] suggested.And the polarization charge at the semipolar plane is changed as well due the induced of shear strain and projection angle [31,32].Two {-1 1 0 1}, {1 1 −2 2} planes have close polarization charge because of similar tilt angle of 60 degree as shown in Fig. 1 (d) and (e).The flat n-GaN electrode/electrolyte interface shows a rapid band bending upward with depletion thickness of 27 nm and the largest electric field.The dodecagon faceted n-GaN electrode/electrolyte interface has less upward band bending and electric field than that of flat n-GaN electrode/electrolyte interface because of polarization reduction and surface Fermi level pinning effect.The dodecagon faceted CAC AlGaN/n-GaN heterostructure electrode/electrolyte interface demonstrated the whole 100 nm thick CAC AlGaN layer having linear band bending up and constant E c and E v electric field because of the assistance of the internal spontaneous and piezoelectric polarization field.Therefore, PECs with dodecagon faceted CAC AlGaN/GaN electrode having much thicker thickness of the constant E c and E v electric field region than that with n-GaN and dodecagon faceted n-GaN electrode would improve the light absorption and separation efficiency of the photo-generated electron-hole pair in the AlGaN layer, which would consequently improve the zero-bias current density and have more negative voltage at 2 mA/cm 2 of PECs III.

Fig. 3 .
Fig. 3. Gas generation picture of the PECs I and IV under illumination.Left side of picture is PECs IV and right side of picture is PECs I.Both PECs are generating H2 gas at the Pt cathode (see Media 1).

Figure 5
Figure 5 shows the surface morphology SEM images of PECs I to IV after J p -V ext characteristics measurement.High-density tiny pits were formed on the surface of PEC cells with flat n-GaN electrode (PECs I) after photoelectrochemical etching.In addition, the photoelectrochemical-etched facets n-GaN electrode also show high density tiny pits on all facets of {-1 1 0 1}, {1 1 −2 2}, and (0001) surface.The {-1 1 0 1} surfaces of the etched dodecagon faceted n-GaN electrode present similar surface morphology to etched flat n-GaN electrode.However, the {1 1 −2 2} surfaces of etched dodecagon faceted n-GaN electrode seem to present a rougher surface than {-1 1 0 1}.Rougher photoelectrochemical etched {1 1 −2 2} facets should be attributed to the rough surface of the as grown {1 1 −2 2} facets.Furthermore, adding AlGaN layer on the dodecagon faceted n-GaN enlarged the photoelectrochemical etching pits size of the facet surface.The enlarged pits size of dodecagon faceted AlGaN/n-GaN heterostructure indicates high photoelectrochemical reaction rate on the facet surface.This finding also implies that PECs III has a larger photo current density with applied bias than PECs II and I.Moreover, the dodecagon faceted AlGaN/n-GaN heterostructure electrode also shows rougher PEC etched surfaces of {1 1 −2 2} than that of {-1 1 0 1}.Finally, the dodecagon faceted LGAC AlGaN/n-GaN hetero-structure electrode PECs have the roughest etched facet surfaces.In addition, the boundary of the etched {-1 1 0 1} and {1 1 −2 2} faceted LGAC AlGaN/n-GaN hetero-structure electrode was barely recognized.The

Fig. 5 .
Fig. 5. Surface morphology SEM images of (a) PECs I, (b) PECs II, (c) PECs III, and (d) PECs IV after the J p -V ext characteristics measurement.