High-dispersive mirrors for high power applications

We report on the development and manufacturing of two different types of high-dispersive mirrors (HDM). One of them provides a record value for the group delay dispersion (GDD) of −4000 fs 2 and covers the wavelength range of 1027-1033 nm, whereas the other one provides −3000 fs 2 over the wavelength range of 1020-1040 nm. Both of the fabricated mirrors exhibit a reflectance of >99.9% and are well suited for intracavity applications. Mirrors of the second type have been successfully employed in a Kerr-lens mode-locked Yb:YAG thin-disk oscillator for the generation of 200-fs pulses with multi-10-W average power. ©2012 Optical Society of America OCIS codes: (320.5520) Pulse compression; (310.1620) Interference coatings; (310.4165) Multilayer design; (310.5696) Refinement and synthesis methods. References and links 1. T. Südmeyer, S. V. Marchese, S. Hashimoto, C. R. E. Baer, G. Gingras, B. Witzel, and U. Keller, “Femtosecond laser oscillators for high-field science,” Nat. Photonics 2(10), 599–604 (2008). 2. X. Liu, D. Du, and G. Mourou, “Laser ablation and micromachining with ultrashort laser pulses,” IEEE J. Quantum Electron. 33(10), 1706–1716 (1997). 3. D. Linde, K. Sokolowski-Tinten, and J. Bialkowski, “Laser-solid interactions in the femtosecond time regime,” Appl. Surf. Sci. 109–110, 1–10 (1997). 4. C. R. E. Baer, C. Kränkel, C. J. Saraceno, O. H. Heckl, M. Golling, R. Peters, K. Petermann, T. Südmeyer, G. Huber, and U. Keller, “Femtosecond thin-disk laser with 141 W of average power,” Opt. Lett. 35(13), 2302– 2304 (2010). 5. T. Südmeyer, C. Kränkel, C. R. E. Baer, O. H. Heckl, C. J. Saraceno, M. Golling, R. Peters, K. Petermann, G. Huber, and U. Keller, “High-power ultrafast thin disk laser oscillators and their potential for sub-100femtosecond pulse generation,” Appl. Phys. B 97(2), 281–295 (2009). 6. D. Bauer, F. Schättiger, J. Kleinbauer, D. H. Sutter, A. Killi, and T. Dekorsy, “Energies above 30 μJ and average power beyond 100 W directly from a mode-locked thin-disk oscillator,” in Advanced Solid-State Photonics, OSA Technical Digest (CD) (Optical Society of America, 2011), paper ATuC2. 7. O. Pronin, J. Brons, C. Grasse, V. Pervak, G. Boehm, M.-C. Amann, V. L. Kalashnikov, A. Apolonski, and F. Krausz, “High-power 200 fs Kerr-lens mode-locked Yb:YAG thin-disk oscillator,” Opt. Lett. 36(24), 4746–4748 (2011). 8. F. Krausz and M. Ivanov, “Attosecond physics,” Rev. Mod. Phys. 81(1), 163–234 (2009). 9. R. Szipöcs, K. Ferencz, C. Spielmann, and F. Krausz, “Chirped multilayer coatings for broadband dispersion control in femtosecond lasers,” Opt. Lett. 19(3), 201–203 (1994). 10. F. X. Kärtner, N. Matuschek, T. Schibli, U. Keller, H. A. Haus, C. Heine, R. Morf, V. Scheuer, M. Tilsch, and T. Tschudi, “Design and fabrication of double-chirped mirrors,” Opt. Lett. 22(11), 831–833 (1997). 11. V. Laude and P. Tournois, “Chirped mirror pairs for ultrabroadband dispersion control,” in Digest of Conference on Lasers and Electro-Optics (CLEO_US) (Optical Society of America, 1999), pp. 187–188. 12. N. Matuschek, F. X. Kärtner, and U. Keller, “Analytical design of double-chirped mirrors with custom-tailored dispersion characteristics,” IEEE J. Quantum Electron. 35(2), 129–137 (1999). 13. F. Gires and P. Tournois, “Interféromètre utilisable d'impulsions lumineuses modulées en fréquence,” C.R. Acad. Sci. Paris 258, 6112–6115 (1964). 14. R. Szipocs, A. Koházi-Kis, S. Lako, P. Apai, A. P. Kovács, G. DeBell, L. Mott, A. W. Louderback, A. V. Tikhonravov, and M. K. Trubetskov, “Negative Dispersion Mirrors for Dispersion Control in Femtosecond #160519 $15.00 USD Received 23 Dec 2011; revised 31 Jan 2012; accepted 31 Jan 2012; published 8 Feb 2012 (C) 2012 OSA 13 February 2012 / Vol. 20, No. 4 / OPTICS EXPRESS 4503 Lasers: Chirped Dielectric Mirrors and Multi-cavity Gires-Tournois Interferometers,” Appl. Phys. B 70(S1), S51–S57 (2000). 15. B. Golubovic, R. R. Austin, M. K. Steiner-Shepard, M. K. Reed, S. A. Diddams, D. J. Jones, and A. G. Van Engen, “Double Gires-Tournois interferometer negative-dispersion mirrors for use in tunable mode-locked lasers,” Opt. Lett. 25(4), 275–277 (2000). 16. F. X. Kärtner, U. Morgner, R. Ell, T. Schibli, J. G. Fujimoto, E. P. Ippen, V. Scheuer, G. Angelow, and T. Tschudi, “Ultrabroadband double-chirped mirror pairs for generation of octave spectra,” J. Opt. Soc. Am. B 18(6), 882–885 (2001). 17. T. R. Schibli, O. Kuzucu, J.-W. Kim, E. P. Ippen, J. G. Fujimoto, F. X. Kaertner, V. Scheuer, and G. Angelow, “Toward single-cycle laser systems,” IEEE J. Sel. Top. Quantum Electron. 4(9), 990–1001 (2003). 18. G. Tempea, V. Yakovlev, B. Bacovic, F. Krausz, and K. Ferencz, “Tilted-front-interface chirped mirrors,” J. Opt. Soc. Am. B 18(11), 1747–1750 (2001). 19. G. Steinmeyer, “Brewster-angled chirped mirrors for high-fidelity dispersion compensation and bandwidths exceeding one optical octave,” Opt. Express 11(19), 2385–2396 (2003). 20. V. Pervak, F. Krausz, and A. Apolonski, “Dispersion control over the UV-VIS-NIR spectral range with HfO2/SiO2 chirped dielectric multilayers,” Opt. Lett. 32, 1183–1185 (2007). 21. V. Pervak, A. V. Tikhonravov, M. K. Trubetskov, S. Naumov, F. Krausz, and A. Apolonski, “1.5-octave chirped mirror for pulse compression down to sub-3 fs,” Appl. Phys. B 87(1), 5–12 (2007). 22. V. Pervak, C. Teisset, A. Sugita, S. Naumov, F. Krausz, and A. Apolonski, “High-dispersive mirrors for femtosecond lasers,” Opt. Express 16(14), 10220–10233 (2008). 23. M. Trubetskov, A. Tikhonravov, and V. Pervak, “Time-domain approach for designing dispersive mirrors based on the needle optimization technique. Theory,” Opt. Express 16(25), 20637–20647 (2008). 24. V. Pervak, I. Ahmad, J. Fulop, M. K. Trubetskov, and A. V. Tikhonravov, “Comparison of dispersive mirrors based on the time-domain and conventional approaches, for sub-5-fs pulses,” Opt. Express 17(4), 2207–2217 (2009). 25. V. Pervak, I. Ahmad, M. K. Trubetskov, A. V. Tikhonravov, and F. Krausz, “Double-angle multilayer mirrors with smooth dispersion characteristics,” Opt. Express 17(10), 7943–7951 (2009). 26. V. Pervak, I. Ahmad, S. A. Trushin, Zs. Major, A. Apolonski, S. Karsch, and F. Krausz, “Chirped-pulse amplification of laser pulses with dispersive mirrors,” Opt. Express 17(21), 19204–19212 (2009). 27. S. V. Marchese, C. R. E. Baer, R. Peters, C. Kränkel, A. G. Engqvist, M. Golling, D. J. H. C. Maas, K. Petermann, T. Südmeyer, G. Huber, and U. Keller, “Efficient femtosecond high power Yb:Lu2O3 thin disk laser,” Opt. Express 15(25), 16966–16971 (2007). 28. S. V. Marchese, T. Südmeyer, M. Golling, R. Grange, and U. Keller, “Pulse energy scaling to 5 microJ from a femtosecond thin disk laser,” Opt. Lett. 31(18), 2728–2730 (2006). 29. G. Palmer, M. Siegel, A. Steinmann, and U. Morgner, “Microjoule pulses from a passively mode-locked Yb:KY(WO(4))(2) thin-disk oscillator with cavity dumping,” Opt. Lett. 32(11), 1593–1595 (2007). 30. I. Pupeza, T. Eidam, J. Rauschenberger, B. Bernhardt, A. Ozawa, E. Fill, A. Apolonski, T. Udem, J. Limpert, Z. A. Alahmed, A. M. Azzeer, A. Tünnermann, T. W. Hänsch, and F. Krausz, “Power scaling of a high-repetitionrate enhancement cavity,” Opt. Lett. 35(12), 2052–2054 (2010). 31. M. K. Trubetskov and A. V. Tikhonravov, “Robust synthesis of multilayer coatings,” in Optical Interference Coatings, OSA Technical Digest (Optical Society of America, 2010), paper TuA4. 32. V. Pervak, M. K. Trubetskov, and A. V. Tikhonravov, “Robust synthesis of dispersive mirrors,” Opt. Express 19(3), 2371–2380 (2011). 33. OptiLayer software, http://www.optilayer.com 34. A. V. Tikhonravov, M. K. Trubetskov, and G. W. Debell, “Application of the needle optimization technique to the design of optical coatings,” Appl. Opt. 35(28), 5493–5508 (1996). 35. A. V. Tikhonravov, M. K. Trubetskov, and G. W. DeBell, “Optical coating design approaches based on the needle optimization technique,” Appl. Opt. 46(5), 704–710 (2007). 36. C. Y. Teisset, H. Fattahi, A. Sugita, L. Turi, X. Gu, O. Pronin, V. Pervak, F. Kraus, and A. Apolonski, “700 nJ b road-band MHz optical parametricamplifier,” in Ultra Fast Optics and High Field Short Wavelength Conference Program, Arcachon, (2009). 37. http://www.novawavetech.com 38. T. V. Amotchkina, A. V. Tikhonravov, M. K. Trubetskov, D. Grupe, A. Apolonski, and V. Pervak, “Measurement of group delay of dispersive mirrors with white-light interferometer,” Appl. Opt. 48(5), 949–956 (2009). 39. V. L. Kalashnikov and A. Apolonski, “Energy scalability of mode-locked oscillators: a completely analytical approach to analysis,” Opt. Express 18(25), 25757–25770 (2010).

High-power oscillators are not the only application of HDMs that can benefit from optics with high dispersion, low losses and negligible thermal effects. Enhancement cavity technology [30] relies on such optics as well. Due to the high reflectivity of HDM (99.97%) one can use such mirrors in enhancement cavities requiring total losses to be suppressed to the level of 0.1-0.2% per roundtrip.
As a first application, we apply this novel HDM for power-scalable Kerr-lens modelocking of an Yb:YAG thin-disk laser. We obtained 200-fs pulses at 17 W average power and 270-fs pulses at 45 W at 40 MHz repetition rate by using the prototypical HDM described in this paper for dispersion control inside of the cavity.

Design and production
The total group delay (GD) introduced in the HDM structure is a result of two combined effects: a penetration effect [9] and a resonance effect or the so called Gires-Tournois interferometer dispersive mirrors [13][14][15]. Our HDMs are designed to provide −3000 fs 2 and −4000 fs 2 of GDD in the wavelength ranges centered at 1030 nm. The delay related to penetration effect is ~30%. The resonance effect provides of ~70% of GDD. The combination of penetration and resonance effects allows to enhance the GDD by factor of ~2 without increasing the total physical thickness of the structure. Manufacturing HDMs is highly challenging due to the high sensitivity of the mirror's performance to deviations in layer thicknesses from their design value. Such a sensitivity to deposition errors has so far been the limiting factor of their use in Yb:YAG disk oscillators. Despite these challenges, HDMs could be demonstrated to compensate a significant amount of GDD in systems operating at the micro joule level [22,26]. In order to design HDMs, a novel robust synthesis technique [31,32] was applied. First we designed HDMs (called HDM1) with group delay dispersion (GDD) of −4000 fs 2 in the wavelength region from 1025 nm to 1035 nm and theoretical reflectance of 99.97% ( Fig. 1) for an 11 MHz Yb:YAG thin-disk oscillator. Commercially available OptiLayer software [33][34][35] has been used to design the HDMs. HDM1 permitted the stable operation of the laser up to intracavity pulse energies of 50-60 µJ and durations of ~1 ps at a repetition rate of 11 MHz [36]. The measured GDD of the HDM1 design is shown in Fig. 1 together with the theoretical GDD and the corridor of GDD errors. For the HDM1, the GDD measurements are in a good agreement with the theoretical GDD. Figure 1 reveals that the actual layer thickness accuracy during this deposition may be estimated as better than 0.5 nm, since most of the measured GDD data lie within the 68.3% corridor of errors. High thickness accuracy during deposition allowed us to fabricate HDM designs in a highly reproducible and reliable way. During the experiments with Yb:YAG oscillator, we found out that the emission bandwidth of Yb:YAG gain media may be truncated by the spectral bandwidth of HDM1. Another problem was connected with a high sensitivity of HDM1 to deposition errors that caused not unsatisfactory production yield of the HDM1 design. To overcome these issues, we had to improve the design of the mirror. To this end, we reduced slightly the nominal value of GDD in order to obtain more robust and broader design. The advanced HDM (named HDM2) works in the wavelength range of 1020-1040 nm, and has a nominal GDD of -3000 fs 2 and average theoretical reflectance of 99.985% (in the absence of scattering losses), see Fig. 2.  To proof manufacturability of designs we performed an error yield analysis. It allows us to estimate how many designs with random deviations from target layer thicknesses will still fulfill our requirements. The error yield analysis is a statistical procedure, therefore the yield estimations may change for different runs with the same parameters. In order to have more stable results, we performed 1000 tests (corresponding to 1000 independent coating runs). The results of error yield analysis of HDM1 and HDM2 are summarized in Table 1. For example, in case of 0.3% relative errors for HDM1 from 1000 virtual coating runs only 163 runs (corresponding to 16.3%) will fulfill requirements. In case of HDM2 -237 coating runs (corresponding to 23.7%) will be successful. Similar behavior is observed for the absolute errors and larger relative errors (0.5%). Therefore HDM1 demonstrates smaller production yield for both absolute and relative errors. In order to experimentally demonstrate manufacturability of the HDM, we have produced designs discussed above. The HDMs consist of layers with thicknesses in the range from 15 nm to 800 nm. Time-controlled deposition is one of the most suitable layer thickness control techniques available for production of dispersive mirrors. In accordance with the error yield analysis, in order to realize designed HDMs, accuracy of the layer thicknesses better than 0.5 nm is required. The desired precision can be reached with a state-of-the-art magnetron sputtering machine (Helios, Leybold Optics GmbH, Alzenau, Germany), which is currently one of the most precise plants available for production of dispersive optics [20][21][22][23][24][25][26]32]. The GDD values measured with white-light interferometer [38] are indicated by red crosses in Figs. 1-2. The measured values for HDM2 lie much closer to the calculated curve (see Fig. 2) in comparison to HDM1 (see Fig. 1). The difference between theoretical and measured GDD can be explained by higher sensitivity of the HDM1 design to errors in layer thicknesses and has been predicted by the error yield analysis. Both measurements are in a good agreement with the conclusion obtained from the error yield analysis.

Pulse analysis, applications, and perspectives
Modern high-energy thin-disk femtosecond oscillators mostly utilize two main perspective gain medias Yb:YAG and Yb:Lu 2 O 3 . The latter has an emission bandwidth of approximately 12 nm FWHM centered at 1034 nm. For oscillators operated at a negative cavity GDD, the maximum pulse energy that is achievable in the regime of stable operation is predicted to be given by [39]: E~β A eff /γ, where β is the net GDD, A eff is the average mode area, E is the energy of pulse and γ is the net self-phase modulation coefficient. According to this formula the achievable pulse energy increases linearly with the magnitude of negative group-delay dispersion. To test the utility of the design, we simulated the propagation of a chirp-free Gaussian pulse of 200-fs pulse duration with spectrum as the one shown in Fig. 3 (upper inset) through a hypothetical delay line consisting of the designed mirrors with the target GDD removed. bounces, affect negligibly the contrast of the pulse (see pulse in logarithmic scale, on Fig. 3), leaving its shape and duration almost unchanged. The main practical limitations for scaling of output power appeared to be the thermal effect and damage threshold of intracavity elements, including HDM. We have compared temperature changes on the surface of available mirrors at 47 W in a continuous wave operation of the laser. The output coupler has reflectivity of 94.5%, thus the intracavity power is by factor of 18 larger than the output power of the oscillator. We have measured temperature of mirrors around beam spot with thermal camera. Both HDM1 and HDM2 demonstrate relatively low temperature: maxima 311 K and 314 K, respectively. In case we switch power off, the temperature is drop to 298 K for whole surface of the mirror. The high-reflectance mirror (quarter-wave stack) made from the same alternating materials as HDM has maximum temperature of 312 K. The temperatures of all available mirrors have changed in the range from 311 K to 350 K.
HDM2 mirrors were successfully implemented in Kerr-lens mode-locked Yb:YAG thindisk oscillator [7]. It delivers 270-fs 1.1-µJ pulses at an average power of 45 W and a repetition rate of 40 MHz with an optical-to-optical efficiency of 25% (see Fig. 4).

Conclusions and discussion
For the first time, we demonstrate HDMs with GDDs as high as −3000 fs 2 and −4000 fs 2 at a central wavelength of 1030 nm ±5nm. The measured reflectance are >99.91% and >99.97% for HDM1 and HDM2, respectively. The novel robust synthesis technique was applied to the design of a high-dispersive mirror. The HDM2 were successfully implemented in an Yb:YAG disk oscillator with 270-fs pulses at an average power of 45 W and a repetition rate of 40 MHz. Beyond high-power oscillators the unique combination of high dispersion, low losses and negligible thermal effects are also expected to benefit enhancement cavity technology as well.