Rheological Characteristics of Castor oil used as Biodegradable Lubricant

In this article I have presented the rheological characteristics of castor oil used as a biodegradable lubricant. The rheograms of castor oil have quite different slopes. The highest slope is at shear speed 3.3s-1, and the smallest slope is at 120s-1. From the representation of the dependence of the dynamic viscosity on the correlation coefficients at all the temperatures at which the castor oil has been was studied, the correlation coefficients have values close to the one value. The correlation coefficients have values between 0.985-0.990.


INTROdUCTION
Lately, due to environmental issues and more restrictive environmental laws, there has been a strong demand for "environmentally friendly" lubricants with as little negative impact as possible. In this context, lubricants obtained from plants are in the attention of tribologists, their main advantages being the relatively inexhaustible source, nontoxicity and biodegradability [1][2][3][4][5][6] . The problem is that, in addition to these advantages, the disadvantages are not to be neglected either: poor lubricating properties, instability to oxidation. Vegetable and animal oils are considered liquid lubricants and are chemically glycerin compounds with fatty acids. They consist of fatty acid fragments bound by an ester with glycerol (the result being triglycerides) [7][8][9][10][11][12] . May also contain in the raw state: phospholipids (8%), glycolipids (5%), sterile esters and sterols (5%), mono or diglycerides and free fatty acids (2%), waxes and other hydrocarbons (1%), but by various processes they can be totally or partially eliminated. Refined vegetable oils have a fairly uniform chemical composition compared to mineral ones and can be classified according to the fatty acids contained: Vegetable oils with high oleic acid content can be considered as highly monounsaturated, thus having better properties at low temperatures compared to other saturated vegetable oils.
Castor oil is obtained from the seeds of the castor plant, of which several varieties are known, the most cultivated being Ricinus communis and Ricinus sanguineus. The plant is native to India and has been acclimatized to South America, the USA, Italy, Turkey and France. In Romania it has been cultivated since 1930, with satisfactory results, but being a tropical plant requires a warmer, longer period of time for ripening. The regions where castor has been best cultivated are: Dobrogea, Southern Muntenia and Oltenia, Baragan and especially in Calcareous soils. Castor oil is obtained by cold and hot pressing the grains, the yields generally differ from the theoretical ones, the qualitative assessment of the seeds being made after the manufacturing yields. Under correct technical conditions, an oil yield of 39… 40% is obtained from almost all assortments. Due to the high viscosity, high flammability and strong polar character, with high adhesion to the metal, castor oil has long been used simply or mixed with mineral oils to lubricate aircraft engines. Castor oil obtained by cold pressing is used in medicine, and that obtained by hot pressing for industrial uses. Castor oil is also obtained by extraction with gasoline without light fractions, but with some difficulties and can only be used for technical purposes. Castor oil contains 80-85% glycerides of hydroxyoleic oil, the rest being glycerides of palmitic and stearic acids. When castor oil comes from wet and partially degraded castor beans and is dark in color, it must be refined. The high viscosity causes some difficulties in the refining process.
The object of this paper is to determine the rheological behaviour for castor oil at shear rates ranging between 3 and 120s -1 and temperatures ranging between 40 and 100 o C.

MATERIAL ANd METHOdS
The castor oil used in this work is provided by a company in Bucharest, Romania. In this paper we studied only castor oil not additives.
Castor oil have been investigated using a Haake VT 550 Viscotester developing shear rates ranging between 3 and 120s -1 and measuring viscosities from 104 to 106 mPa.s when the HV 1 viscosity sensor is used. The temperature ranged between 40 and 100 0 C and the measurements were made from 10 to 10 0 C. The accuracy of the temperature was 0.1 0 C 5-13 . Figure 1 shows the dependence of the dynamic viscosity of the shear speed at all the temperatures at which the castor oil has been was studied. The curves obtained exhibit an exponential decrease at low temperatures and at high temperatures the decrease becomes less significant.  Figure 2 shows the reograms of castor oil at all temperatures at which the oil was studied. From the graphical representation of the dependence of the shear rate and the shear voltage, straight lines are obtained which have different slopes depending on the temperature at which the oil was studied. The highest slope is at 40 0 C and the smallest at 100 0 C.  Figure 3 shows the log dependence of dynamic temperature viscosity at all shear rates. The straight with the highest slope is at the shear speed 3.3s -1 , and the smallest slope is at 120s -1 .  Figure 4 shows the dependence of the dynamic viscosity as on the correlation coefficients at all the temperatures at which the castor oil was studied. All correlation coefficients have values close to the one value.

CONCLUSION
In this article I have presented the rheological characteristics of castor oil used as a biodegradable lubricant. The rheograms of castor oil have quite different slopes. The highest slope is at shear speed 3.3s -1 , and the smallest slope is at 120s -1 .
From the representation of the dependence of the dynamic viscosity on the correlation coefficients at all the temperatures at which the castor oil has been was studied, the correlation coefficients have values close to the one value. The correlation coefficients have get values between 0.985-0.990.