氧化石墨烯高压膜的制备及其在水处理中的应用研究进展

孔繁鑫, 刘倩, 杨智云, 陈进富, 郭春梅. 氧化石墨烯高压膜的制备及其在水处理中的应用研究进展[J]. 环境工程学报, 2021, 15(12): 3811-3829. doi: 10.12030/j.cjee.202108183
引用本文: 孔繁鑫, 刘倩, 杨智云, 陈进富, 郭春梅. 氧化石墨烯高压膜的制备及其在水处理中的应用研究进展[J]. 环境工程学报, 2021, 15(12): 3811-3829. doi: 10.12030/j.cjee.202108183
KONG Fanxin, LIU Qian, YANG Zhiyun, CHEN Jinfu, GUO Chunmei. Research progress on the application of graphene oxide in preparation of high-pressure membranes for water purification[J]. Chinese Journal of Environmental Engineering, 2021, 15(12): 3811-3829. doi: 10.12030/j.cjee.202108183
Citation: KONG Fanxin, LIU Qian, YANG Zhiyun, CHEN Jinfu, GUO Chunmei. Research progress on the application of graphene oxide in preparation of high-pressure membranes for water purification[J]. Chinese Journal of Environmental Engineering, 2021, 15(12): 3811-3829. doi: 10.12030/j.cjee.202108183

氧化石墨烯高压膜的制备及其在水处理中的应用研究进展

    作者简介: 孔繁鑫(1985—),男,博士,副教授。研究方向:膜法水处理技术。E-mail:kfx11@cup.edu.cn
    通讯作者: 孔繁鑫, E-mail: kfx11@cup.edu.cn
  • 基金项目:
    国家自然科学基金资助项目 (51708556);北京市优秀人才青年骨干个人项目(2017000020124G102);中国石油大学青年拔尖人才项目(2462019BJR004);环境模拟与污染控制国家重点联合实验室开放课题(K03ESPCT);污染控制与资源化研究国家重点实验室开放课题(PCRRF17011)
  • 中图分类号: X703

Research progress on the application of graphene oxide in preparation of high-pressure membranes for water purification

    Corresponding author: KONG Fanxin, kfx11@cup.edu.cn
  • 摘要: 氧化石墨烯(GO)是一种理想的二维结构分离膜材料。从GO结构性质入手,探讨了GO混合基质膜和GO层压膜(GO膜)的制备及其在水处理中的研究现状与前景。分析了GO的添加方式对混合基质膜性能的影响,未来需要进一步对GO表面的活性基团进行改性以提高其分散性和与聚合物的相容性,并加强GO及改性GO的添加方式对膜性能影响的研究。GO混合基质膜在一定程度上可克服传统聚合物膜的Trade-off 效应,技术成熟度较高、应用前景较好。GO膜在水溶液中的不稳定性是其在水处理中应用中的瓶颈,在系统分析提高GO膜稳定性的方法的基础上,进一步指出需要探讨采用新型交联剂或多种稳定方法同步强化其稳定性的可行性,同时其在实际应用中的稳定性及长期运行效果需要进一步研究和验证,以利于开拓其应用。
  • 加载中
  • 图 1  GO结构示意图

    Figure 1.  The schematic diagram of GO structure

    图 2  GO在膜制备中的2种应用

    Figure 2.  Two typical fabrication routes for membrane with GO

    图 3  GO混合基质膜的4种制备形式

    Figure 3.  Four typical preparation methods for the mixed matrix membrane with GO

    图 4  GO添加至基膜制备混合基质膜

    Figure 4.  Schematic diagram for fabrication of mixed matrix membranes with GO incorporated substrate

    图 5  GO添加至单体溶液制备混合基质膜

    Figure 5.  Schematic diagram for fabrication of mixed matrix membranes with the addition of GO to monomer solution

    图 6  GO中间层加入混合基质膜的制备示意图[52]

    Figure 6.  Schematic diagram for fabrication of mixed matrix membranes with the GO as the intermediate layer[52]

    图 7  GO以表层方式加入混合基质膜

    Figure 7.  Schematic diagram for the preparation of PA membrane with surface deposition of GO

    图 8  GO膜的分离机理[61]

    Figure 8.  Separation mechanism for the GO-based membrane [61]

    图 9  GO膜制备新方法

    Figure 9.  Novel methods for preparation of GO-based membrane

    图 10  GO溶胀示意图

    Figure 10.  Schematic diagram for the swelling of GO nanosheets

    图 11  稳定GO膜的制备方法

    Figure 11.  Fabrication method of the stable GO-based membrane

    图 12  以金属离子作为交联剂制得GO膜的特性

    Figure 12.  Characteristics of GO-based membrane with metal ions as crosslinker

    图 13  通过LBL法在PAN基板上制造聚阳离子/GO膜的示意图[96]

    Figure 13.  Schematic diagram of polycation/GO membrane on PAN substrate by LBL method[96]

    图 14  rGO膜的制备示意图[115]

    Figure 14.  Preparation of nanoporous rGO membrane[115]

    图 15  原位组装PrGO膜及脱盐过程示意图[117]

    Figure 15.  Schematic diagram for the PrGO membrane by the in-situ assembly of PrGO and the desalination process[117]

    表 1  GO制备方法的对比

    Table 1.  Comparison of preparation methods for GO-based membrane

    制备方法优点缺点
    真空过滤法操作简单GO片层连接较弱,膜稳定性较差
    层层自组装法膜稳定性好,性能优异制备时间较长,操作繁琐
    旋涂法能有效控制GO膜的厚度操作条件较高,无法大量制备
    制备方法优点缺点
    真空过滤法操作简单GO片层连接较弱,膜稳定性较差
    层层自组装法膜稳定性好,性能优异制备时间较长,操作繁琐
    旋涂法能有效控制GO膜的厚度操作条件较高,无法大量制备
    下载: 导出CSV

    表 2  不同交联剂制备的GO膜及性能

    Table 2.  The fabrication methods and performance of GO-based membrane with different crosslinkers

    交联剂基膜交联方法机制交联效果
    N-异丙基丙烯酰胺N,N'-亚甲基双丙烯酰胺[22]聚偏二氟乙烯膜将两种交联剂加入GO溶液后进行抽滤三者在水性条件下的自由基聚合过程中能形成GO-聚合物网络水通量:33.5 L·(m2·h)−1
    NaCl截留:98.5%
    且具有较好氯稳定性
    多巴胺[80]聚偏二氟乙烯膜使用多巴胺溶液涂敷聚偏二氟乙烯膜多巴胺有强粘附能力增强了GO分离层和基底之间的连接,增加了膜稳定性
    多巴胺[81]多孔α-Al2O3将多巴胺涂敷在多孔α-Al2O3基膜上多巴胺有强粘附能力水通量:32.1 kg·(m2·h)−1
    截留:99.7%
    336 h后截留和通量几乎恒定
    对苯二胺[82]聚丙烯腈膜通过LBL法将GO和对苯二胺交联对苯二胺中的胺与GO中的环氧基之间的环氧开环反应,产生羟基和仲胺截留率提高了12%,稳定性显著增强
    乙二胺[99]溴化聚苯醚膜在乙二胺中加入不同量的GOGO上的-COOH与乙二胺上的-NH反应交联膜在水中浸泡1个月后,仍保持其通量和脱盐能力
    尿素[85]醋酸纤维素膜GO和尿素混合,过滤尿素上的-NH与GO上的-COOH反应膜通量提高了1.6~2.4倍
    二羧酸[87]聚丙烯微滤膜二羧酸与GO混合,
    过滤
    二羧酸与GO上的羧基交联渗透量增加了2倍,GO溶胀度
    下降了4.3%
    阳离子[88,91]醋酸纤维素膜;聚偏二氟乙烯膜;陶瓷膜GO分别与不同阳离子溶液混合制膜阳离子通过静电力和配位键提高GO纳米片的键合强度膜完整性能保持1个月以上,且能通过调节阳离子浓度来调节GO层间距
    四硼酸钠[92]聚偏二氟乙烯膜在GO溶液中加入四硼酸钠混合两者反应形成
    —B—O—C—共价键
    膜的临界破坏载荷增加了10倍,在破坏性洗涤实验中保持良好的稳定性
    均苯三甲酰氯[100]聚砜膜层层组装法酰氯基团与GO上羧基和羟基反应形成酯键亚甲基蓝:46%~66%
    罗丹明-WT:93%~95%
    水通量:27.2~93.8 L·(m2·h)−1
    卟啉[95]PC膜GO与卟啉混合后过滤通过静电作用和π−π作用Na2SO4:87.7%
    水通量:9.3 L·(m2·h)−1
    聚阳离子[96]聚丙烯腈膜层层组装法静电作用甲基蓝:99.2%
    水通量(每0.1 MPa下):6.42 kg·(m2·h)−1
    聚乙烯亚胺[97]聚丙烯腈膜层层组装法静电作用MgCl2:86%
    聚氧化铝[98]聚偏二氟乙烯膜层层组装法静电作用腐殖酸:99.6%
    TOC:90%~95%
    聚丙烯胺盐酸盐[101]聚丙烯腈膜层层组装法静电作用蔗糖:99%
    交联剂基膜交联方法机制交联效果
    N-异丙基丙烯酰胺N,N'-亚甲基双丙烯酰胺[22]聚偏二氟乙烯膜将两种交联剂加入GO溶液后进行抽滤三者在水性条件下的自由基聚合过程中能形成GO-聚合物网络水通量:33.5 L·(m2·h)−1
    NaCl截留:98.5%
    且具有较好氯稳定性
    多巴胺[80]聚偏二氟乙烯膜使用多巴胺溶液涂敷聚偏二氟乙烯膜多巴胺有强粘附能力增强了GO分离层和基底之间的连接,增加了膜稳定性
    多巴胺[81]多孔α-Al2O3将多巴胺涂敷在多孔α-Al2O3基膜上多巴胺有强粘附能力水通量:32.1 kg·(m2·h)−1
    截留:99.7%
    336 h后截留和通量几乎恒定
    对苯二胺[82]聚丙烯腈膜通过LBL法将GO和对苯二胺交联对苯二胺中的胺与GO中的环氧基之间的环氧开环反应,产生羟基和仲胺截留率提高了12%,稳定性显著增强
    乙二胺[99]溴化聚苯醚膜在乙二胺中加入不同量的GOGO上的-COOH与乙二胺上的-NH反应交联膜在水中浸泡1个月后,仍保持其通量和脱盐能力
    尿素[85]醋酸纤维素膜GO和尿素混合,过滤尿素上的-NH与GO上的-COOH反应膜通量提高了1.6~2.4倍
    二羧酸[87]聚丙烯微滤膜二羧酸与GO混合,
    过滤
    二羧酸与GO上的羧基交联渗透量增加了2倍,GO溶胀度
    下降了4.3%
    阳离子[88,91]醋酸纤维素膜;聚偏二氟乙烯膜;陶瓷膜GO分别与不同阳离子溶液混合制膜阳离子通过静电力和配位键提高GO纳米片的键合强度膜完整性能保持1个月以上,且能通过调节阳离子浓度来调节GO层间距
    四硼酸钠[92]聚偏二氟乙烯膜在GO溶液中加入四硼酸钠混合两者反应形成
    —B—O—C—共价键
    膜的临界破坏载荷增加了10倍,在破坏性洗涤实验中保持良好的稳定性
    均苯三甲酰氯[100]聚砜膜层层组装法酰氯基团与GO上羧基和羟基反应形成酯键亚甲基蓝:46%~66%
    罗丹明-WT:93%~95%
    水通量:27.2~93.8 L·(m2·h)−1
    卟啉[95]PC膜GO与卟啉混合后过滤通过静电作用和π−π作用Na2SO4:87.7%
    水通量:9.3 L·(m2·h)−1
    聚阳离子[96]聚丙烯腈膜层层组装法静电作用甲基蓝:99.2%
    水通量(每0.1 MPa下):6.42 kg·(m2·h)−1
    聚乙烯亚胺[97]聚丙烯腈膜层层组装法静电作用MgCl2:86%
    聚氧化铝[98]聚偏二氟乙烯膜层层组装法静电作用腐殖酸:99.6%
    TOC:90%~95%
    聚丙烯胺盐酸盐[101]聚丙烯腈膜层层组装法静电作用蔗糖:99%
    下载: 导出CSV
  • [1] 赵向阳, 许锋. 膜技术在饮用水处理行业的研究进展及应用[J]. 广东化工, 2017, 44(16): 152-153. doi: 10.3969/j.issn.1007-1865.2017.16.067
    [2] PERSSON K M, GEKAS V, TRAGARDH G. Study of membrane compaction and its influence on ultrafiltration water permeability[J]. Journal of Membrane Science, 1995, 100(2): 155-162. doi: 10.1016/0376-7388(94)00263-X
    [3] GIN D L, NOBLE R D. Designing the next generation of chemical separation membranes.[J]. Science, 2011, 332(6030): 674-676. doi: 10.1126/science.1203771
    [4] DU Y C, HUANG L J, WANG Y X, et al. Recent developments in graphene-based polymer composite membranes: Preparation, mass transfer mechanism, and applications[J]. Journal of Applied Polymer Science, 2019, 136(28): 47761. doi: 10.1002/app.47761
    [5] TANG C Y, ZHE Y, HAO G, et al. Potable water reuse through advanced membrane technology[J]. Environmental Science & Technology, 2018, 52(18): 10215-10223.
    [6] XU R, QIN W, ZHANG B, et al. Nanofiltration in pilot scale for wastewater reclamation: long-term performance and membrane biofouling characteristics[J]. Chemical Engineering Journal, 2020, 395: 125087. doi: 10.1016/j.cej.2020.125087
    [7] PENDERGAST M T M, HOEK E M V. A review of water treatment membrane nanotechnologies[J]. Energy & Environmental Science, 2011, 4(6): 1946-1971.
    [8] MOHAMMAD A W, TEOW Y H, ANG W L, et al. Nanofiltration membranes review: Recent advances and future prospects[J]. Desalination, 2015, 356: 226-254. doi: 10.1016/j.desal.2014.10.043
    [9] KOROS W J, ZHANG C. Materials for next-generation molecularly selective synthetic membranes[J]. Nature Materials, 2017, 16(3): 289-297. doi: 10.1038/nmat4805
    [10] EPSZTEIN R, SHAULSKY, QIN M, et al. Activation behavior for ion permeation in ion-exchange membranes: Role of ion dehydration in selective transport[J]. Journal of Membrane Science, 2019, 580(15): 316-326.
    [11] YANG Y, WANG H, LI J, et al. Novel functionalized nano-TiO2 loading electrocatalytic membrane for oily wastewater treatment[J]. Environmental Science & Technology, 2012, 46(12): 6815-6821.
    [12] LEE A, ELAM J W, DARLING S B. Membrane materials for water purification: Design, development, and application[J]. Environmental Science: Water Research & Technology, 2016, 2(1): 17-42.
    [13] WEI Y, ZHAGN Y, GAO X, et al. Multilayered graphene oxide membrane for water treatment: A review[J]. Carbon, 2018, 139: 964-981. doi: 10.1016/j.carbon.2018.07.040
    [14] FATHIZADEH M, XU W L, ZHOU F, et al. Graphene oxide: a novel 2-Dimensional material in membrane separation for water purification[J]. Advanced Materials Interfaces, 2017, 4(5): 1-16.
    [15] SONG N, GAO X, MA Z, et al. A review of graphene-based separation membrane: Materials, characteristics, preparation and applications[J]. Desalination, 2018, 437: 59-72. doi: 10.1016/j.desal.2018.02.024
    [16] YOON H W, CHO Y H, PARK H B. Graphene-based membranes: Status and prospects[J]. Philosophical Transactions, 2016, 374(2060): 1-23.
    [17] KANG Y, XIA Y, WANG H, et al. 2D laminar membranes for selective water and ion transport[J]. Advanced Functional Materials, 2019, 29(29): 1902014. doi: 10.1002/adfm.201902014
    [18] SUN P, WANG K, ZHU H. Recent Developments in graphene-based membranes: structure, mass-transport mechanism and potential applications[J]. Advanced Materials, 2016, 28(12): 2287-2310. doi: 10.1002/adma.201502595
    [19] LERF A, HE H Y, FORSTER M, et al. Structure of graphite oxide revisited[J]. The Journal of Physical Chemistry, 1998, 102(21/22/23/24): 4477-4482.
    [20] 黄铁凡. 交联型GO膜的结构调控和应用[D]. 杭州: 浙江大学, 2015.
    [21] 徐宇曦. 功能化石墨烯的制备、组装及其应用[D]. 北京: 清华大学, 2011.
    [22] KIM S, OU R, HU Y, et al. Non-swelling graphene oxide-polymer nanocomposite membrane for reverse osmosis desalination[J]. Journal of Membrane Science, 2018, 562: 47-55. doi: 10.1016/j.memsci.2018.05.029
    [23] 董航, 张林, 陈欢林, 等. 混合基质水处理膜: 材料、制备与性能[J]. 化学进展, 2014, 26(12): 2007-2018.
    [24] CHONG J Y, WANG B, MATTEVI C, et al. Dynamic microstructure of graphene oxide membranes and the permeation flux[J]. Journal of Membrane Science, 2018, 549: 385-392. doi: 10.1016/j.memsci.2017.12.018
    [25] HEGAB H M, ZOU L. Graphene oxide-assisted membranes: Fabrication and potential applications in desalination and water purification[J]. Journal of Membrane Science, 2015, 484: 95-106. doi: 10.1016/j.memsci.2015.03.011
    [26] BASKORO F, WONG C B, RAJESH KUMAR S, et al. Graphene oxide-cation interaction: inter-layer spacing and zeta potential changes in response to various salt solutions[J]. Journal of Membrane Science, 2018, 554: 253-263. doi: 10.1016/j.memsci.2018.03.006
    [27] GANESH B M, ISLOOR A M, ISMAIL A F. Enhanced hydrophilicity and salt rejection study of graphene oxide-polysulfone mixed matrix membrane[J]. Desalination, 2013, 313(7): 199-207.
    [28] ZINADINI S, ZINATIZADEH A A, RAHIMI M, et al. Preparation of a novel antifouling mixed matrix PES membrane by embedding graphene oxide nanoplates[J]. Journal of Membrane Science, 2014, 453(3): 292-301.
    [29] ZHAO C, XU X, CHEN J, et al. Effect of graphene oxide concentration on the morphologies and antifouling properties of PVDF ultrafiltration membranes[J]. Journal of Environmental Chemical Engineering, 2013, 1(3): 349-354. doi: 10.1016/j.jece.2013.05.014
    [30] LAI G S, LAU W J, GOH Q S, et al. Graphene oxide incorporated thin film nanocomposite nanofiltration membrane for enhanced salt removal performance[J], Desalination, 2016, 387(1): 14-24.
    [31] NASSERI S, EBRAHIMI S, SAEEDI R, et al. Synthesis and characterization of polysulfone/graphene oxide nano-composite membranes for removal of bisphenol A from water[J]. Journal of Environmental Management, 2018, 205(1): 174-182.
    [32] ZHAO H, WU L, ZHOU Z, et al. Improving the antifouling property of polysulfone ultrafiltration membrane by incorporation of isocyanate-treated graphene oxide[J]. Physical Chemistry Chemical Physics, 2013, 15(23): 9084-9092. doi: 10.1039/c3cp50955a
    [33] XIE Q, ZHANG S, HONG Z, et al. A novel double-modified strategy to enhance the performance of thin-film nanocomposite nanofiltration membranes: Incorporating functionalized graphenes into supporting and selective layers[J]. Chemical Engineering Journal,2019, 368: 186-201.
    [34] YIN J, ZHU G, DENG B. Graphene oxide (GO) enhanced polyamide (PA) thin-film nanocomposite (TFN) membrane for water purification[J]. Desalination, 2016, 379: 93-101. doi: 10.1016/j.desal.2015.11.001
    [35] 陈贤鸿, 傅倍佳, 钟明强, 等. 氧化石墨烯掺杂反渗透混合基质膜制备及性能[J]. 化工学报, 2018, 69(1): 437-442.
    [36] HU R, ZHANG R, HE Y, et al. Graphene oxide-in-polymer nanofiltration membranes with enhanced permeability by interfacial polymerization[J]. Journal of Membrane Science, 2018, 564: 813-819. doi: 10.1016/j.memsci.2018.07.087
    [37] ZHAO W, LIU H Y, MENG N, et al. Graphene oxide incorporated thin film nanocomposite membrane at low concentration monomers[J]. Journal of Membrane Science, 2018, 565: 380-389.
    [38] 芦瑛, 赵海洋, 张林, 等. 含氧化石墨烯混合基质反渗透复合膜的制备及性能研究[J]. 中国工程科学, 2014, 16(7): 84-88. doi: 10.3969/j.issn.1009-1742.2014.07.015
    [39] BANO S, MAHMOOD A, KIM S J, et al. Graphene oxide modified polyamide nanofiltration membrane with improved flux and antifouling properties[J]. Journal of Materials Chemistry A, 2015, 3(5): 2065-2071. doi: 10.1039/C4TA03607G
    [40] ALI M E A, WANG L, WANG X, et al. Thin film composite membranes embedded with graphene oxide for water desalination[J]. Desalination, 2016, 386: 67-76. doi: 10.1016/j.desal.2016.02.034
    [41] XIA S, YAO L, ZHAO Y, et al. Preparation of graphene oxide modified polyamide thin film composite membranes with improved hydrophilicity for natural organic matter removal[J]. Chemical Engineering Journal, 2015, 280: 720-727. doi: 10.1016/j.cej.2015.06.063
    [42] WANG X, WNAG H, WNAG Y, et al. Hydrotalcite/graphene oxide hybrid nanosheets functionalized nanofiltration membrane for desalination[J]. Deslination, 2019, 451: 209-218. doi: 10.1016/j.desal.2017.05.012
    [43] YANG L L, XI L, YAN S L, et al. Single-walled carbon nanotubes-carboxyl-functionalized graphene oxide-based electrochemical DNA biosensor for thermolabile hemolysin gene detection[J]. Analytical Methods, 2015, 7: 5303-5310. doi: 10.1039/C5AY01062D
    [44] ZHANG H, LI B, PAN J, et al. Carboxyl-functionalized graphene oxide polyamide nanofiltration membrane for desalination of dye solutions containing monovalent salt[J]. Journal of Membrane Science, 2017, 539: 128-137. doi: 10.1016/j.memsci.2017.05.075
    [45] KANG Y, OBAID M, JANG J, et al. Novel sulfonated graphene oxide incorporated polysulfone nanocomposite membranes for enhanced-performance in ultrafiltration process[J]. Chemosphere, 2018, 207: 581-589. doi: 10.1016/j.chemosphere.2018.05.141
    [46] WEN P, CHEN Y, HU X, et al. Polyamide thin film composite nanofiltration membrane modified with acyl chlorided graphene oxide[J]. Journal of Membrane Science, 2017, 535: 208-220. doi: 10.1016/j.memsci.2017.04.043
    [47] ZHANG Y, RUAN H, GUO C, et al. Thin-film nanocomposite reverse osmosis membranes with enhanced antibacterial resistance by incorporating p-aminophenol-modified graphene oxide[J]. Separation and Purification Technology, 2020, 234: 116017. doi: 10.1016/j.seppur.2019.116017
    [48] ALI F A, ALAM J, SHUKLA A K, et al. Graphene oxide-silver nanosheet-incorporated polyamide thin-film composite membranes for antifouling and antibacterial action against Escherichia coli and bovine serum albumin[J]. Journal of Industrial and Engineering Chemistry, 2019, 80: 227-238. doi: 10.1016/j.jiec.2019.07.052
    [49] LIU Y, LIU J, JIANG J, et al. Synthesis of novel high flux thin-film nanocomposite nanofiltration membranes containing GO-SiO2 via interfacial polymerization[J]. Industrial & Engineering Chemistry Research, 2019, 58: 22324-22333.
    [50] ABADIKHAH H, KALALI E N, KHODI S, et al. Multifunctional thin-film nanofiltration membrane Incorporated with reduced graphene oxide@TiO2@Ag nanocomposites for high desalination performance, dye retention, and antibacterial properties[J]. ACS Applied Materials & Interfaces, 2019, 11(26): 23535-23545.
    [51] LAI G S, LAU W J, GOH P S, et al. A novel interfacial polymerization approach towards synthesis of graphene oxide-incorporated thin film nanocomposite membrane with improved surface properties[J]. Arabian Journal of Chemistry, 2019, 12(1): 75-87. doi: 10.1016/j.arabjc.2017.12.009
    [52] SHI J, WU W, XIA Y, et al. Confined interfacial polymerization of polyamide-graphene oxide composite membranes for water desalination[J]. Desalination, 2018, 441: 77-86. doi: 10.1016/j.desal.2018.04.030
    [53] LI Y, LI C, LI S, et al. Graphene oxide (GO)-interlayered thin-film nanocomposite (TFN) membranes with high solvent resistance for organic solvent nanofiltration (Osn)[J]. Journal of Materials Chemistry A, 2019, 7: 13315-13330. doi: 10.1039/C9TA01915D
    [54] CHOI W, CHOI J, BANG J, et al. Layer-by-layer assembly of graphene oxide nanosheets on polyamide membranes for durable reverse-osmosis applications[J]. ACS Applied Materials & Interfaces, 2013, 5(23): 12510-12519.
    [55] FRANCOIS P, TOUSLEY M E, ELIMELECH M. Thin-film composite polyamide membranes functionalized with biocidal graphene oxide nanosheets[J]. Environmental Science & Technology Letters, 2013, 1(1): 71-76.
    [56] WANG J L, GAO X L, WANG J, et al. O-(Carboxymethyl)-chitosan nanofiltration membrane surface functionalized with graphene oxide nanosheets for enhanced desalting properties[J]. ACS Applied Materials & Interfaces, 2015, 7(7): 4381-4389.
    [57] KOVTUN A, ZAMBIANCHI M, BETTINI C, et al. Graphene oxide–polysulfone filters for tap water purification, obtained by fast microwave oven treatment[J]. Nanoscale, 2019, 11: 22780-22787. doi: 10.1039/C9NR06897J
    [58] JOSHI R K, CARBONE P, WANG F C, et al. Precise and ultrafast molecular sieving through graphene oxide membranes[J]. Science, 2014, 343(6172): 752-754. doi: 10.1126/science.1245711
    [59] WANG K, AUSRI I R, CHU K Y, et al. Pressure-driven solvent transport and complex ion permeation through graphene oxide membranes[J]. Advanced Materials Interface, 2019, 6(12): 1802056. doi: 10.1002/admi.201802056
    [60] FEI W W, XUE M M, QIU H, et al. Heterogeneous graphene oxide membrane for rectified ion transport[J]. Nanoscale, 2019, 11(3): 1313-1318. doi: 10.1039/C8NR07557C
    [61] PERREAULT F, ANDREIA F D, ELIMELECH M. Environmental applications of graphene-based nanomaterials[J]. Chemical Society Reviews, 2015, 44(16): 5861-5896.
    [62] ZHANG M, SUN J, MAO Y, et al. Effect of substrate on formation and nanofiltration performance of graphene oxide membranes[J]. Journal of Membrane Science, 2019, 574: 196-204. doi: 10.1016/j.memsci.2018.12.071
    [63] 张瑛洁, 戴继悟. 氧化石墨烯改性复合纳滤膜的研究进展[J]. 水处理技术, 2017, 43(9): 1-5.
    [64] NAN Q, LI P, CAO B. Fabrication of positively charged nanofiltration membrane via the layer-by-layer assembly of graphene oxide and polyethylenimine for desalination[J]. Applied Surface Science, 2016, 387: 521-528. doi: 10.1016/j.apsusc.2016.06.150
    [65] ZHU Y, MURALI S, CAI W, et al. Graphene-based materials: Graphene and graphene oxide: Synthesis, properties, and applications[J]. Advanced Materials, 2010, 22(35): 3906-3924. doi: 10.1002/adma.201001068
    [66] WANG T, LU J, MAO L, et al. Electric field assisted layer-by-layer assembly of graphene oxide containing nanofiltration membrane[J]. Journal of Membrane Science, 2016, 515: 125-133. doi: 10.1016/j.memsci.2016.05.053
    [67] QI B Y, HE X F, ZENG G F, et al. Strict molecular sieving over electrodeposited 2D-interspacing-narrowed graphene oxide membranes[J]. Nature Communications, 2017, 8(1): 825. doi: 10.1038/s41467-017-00990-x
    [68] FATHIZADE M, TIEN H N, KHIVANTSEV K, et al. Printing ultrathin graphene oxide nanofiltration membranes for water purification[J]. Journal of Materials Chemistry A, 2017,5(39): 20860-20866.
    [69] KIM H W, YOON H W, YOON S M, et al. Selective gas transport through few-layered graphene and graphene oxide membranes[J]. Science, 2013, 342(6154): 91-95. doi: 10.1126/science.1236098
    [70] LI H, SONG Z, ZHANG X, et al. Ultrathin, molecular-sieving graphene oxide membranes for selective hydrogen separation[J]. Science, 2013, 342(6154): 95-98. doi: 10.1126/science.1236686
    [71] LIU R, ARABALE G, KIM J, et al. Graphene oxide membrane for liquid phase organic molecular separation[J]. Carbon, 2014, 77: 933-938. doi: 10.1016/j.carbon.2014.06.007
    [72] LIU G P, JIN W Q. Graphene oxide membrane for molecular separation: challenges and opportunities[J]. Science China Materials, 2018, 61(8): 1021-1026. doi: 10.1007/s40843-018-9276-8
    [73] NAIR R R, WU H A, JAYARAM P N, et al. Unimpeded permeation of water through helium-leak-tight graphene-based membranes[J]. Science, 2012, 335(6067): 442-444. doi: 10.1126/science.1211694
    [74] DREYER D R, PARK S, BIELAWSKI C W, et al. The chemistry of graphene oxide[J]. Chemical Society Reviews, 2010, 39(1): 228-240. doi: 10.1039/B917103G
    [75] HUANG L, ZHANG M, LI C, et al. Graphene-based membranes for molecular separation[J]. The Journal of Physical Chemistry Letters, 2015, 6(14): 2806-2815. doi: 10.1021/acs.jpclett.5b00914
    [76] ROMANOS G, PASTRANA M, TSOUFIS T, et al. A facile approach for the development of fine-tuned self-standing graphene oxide membranes and their gas and vapor separation performance[J]. Journal of Membrane Science, 2015, 493: 734-747. doi: 10.1016/j.memsci.2015.07.034
    [77] ZHANG M C, MAO Y Y, LIU G Z, et al. Molecular bridges stabilize graphene oxide membranes in Water[J]. Angewandte Chemie, 2019, 58: 2-9. doi: 10.1002/anie.201813331
    [78] MI B. Graphene oxide membranes for ionic and molecular sieving[J]. Science, 2014, 343(6172): 740-742. doi: 10.1126/science.1250247
    [79] AN Z, COMPTON O C, PUTZ K W, et al. Bio-inspired borate cross-linking in ultra-stiff graphene oxide thin films[J]. Advanced Materials, 2011, 23(33): 3842-3846.
    [80] LEE H, DELLATORE S M, MILLER W M, et al. Mussel-inspired surface chemistry for multifunctional coatings[J]. Science, 2007, 318(5849): 426-430.
    [81] XU K, FENG B, ZHOU C, et al. Synthesis of highly stable graphene oxide membranes on polydopamine functionalized supports for seawater desalination[J]. Chemical Engineering Science, 2016, 146: 159-165.
    [82] VEPIKA K, ANA M P, ACEVEDO B, et al. Enhanced covalent p-phenylenediamine crosslinked graphene oxide membranes: Towards superior contaminant removal from wastewaters and improved membrane reusability[J]. Journal of Hazardous Materials, 2019, 380: 120840. doi: 10.1016/j.jhazmat.2019.120840
    [83] LI B, CUI Y, JAPIP S, et al. Graphene oxide (GO) laminar membranes for concentrating pharmaceuticals and food additives in organic solvents[J]. Carbon, 2018, 130: 503-514. doi: 10.1016/j.carbon.2018.01.040
    [84] MAHALINGAM D K, WANG S F, NUNES S P. Stable graphene oxide cross-linked membranes for organic solvent nnanofiltration[J]. Industrial & Engineering Chemistry Research, 2019, 58(51): 23106-23113.
    [85] ZHANG Y Z, SU K M, LI Z H. Graphene oxide composite membranes cross-linked with urea for enhanced desalting properties[J]. Journal of Membrane Science, 2018, 563: 718-725. doi: 10.1016/j.memsci.2018.06.037
    [86] JIA Z, WANG Y. Covalently crosslinked graphene oxide membranes by esterification reactions for ions separation[J]. Journal of Materials Chemistry A, 2015, 3(4405): 4405-4412.
    [87] JIA Z, SHI W, WANG Y, et al. Dicarboxylic acids crosslinked graphene oxide membranes for salt solution permeation[J]. Colloids and Surfaces A:Physicochemical and Engineering Aspects, 2016, 494: 101-107.
    [88] YI R, YANG R, YU R, et al. Ultrahigh permeance of a chemical cross-linked graphene oxide nanofiltration membrane enhanced by cation–π interaction[J]. RCS Advances, 2019, 9: 40397-40403.
    [89] YU W, YU T, GRAHAM N. Development of a stable cation modified graphene oxide membrane for water treatment[J]. 2D Materials, 2017, 4(4): 045006. doi: 10.1088/2053-1583/aa814c
    [90] LIU T, YANG B, GRAHAM N, et al. Trivalent metal cation cross-linked graphene oxide membranes for NOM removal in water treatment[J]. Journal of Membrane Science, 2017, 542: 31-40. doi: 10.1016/j.memsci.2017.07.061
    [91] CHEN L, SHI G, SHEN J, et al. Ion sieving in graphene oxide membranes via cationic control of interlayer spacing[J]. Nature, 2017, 550: 380-383. doi: 10.1038/nature24044
    [92] HAN J L, HAIDER M R, LIU M J, et al. Borate inorganic crosslinked durable graphene oxide membrane preparation and membrane fouling control[J]. Environmental Science & Technology, 2019, 53(3): 1501-1508.
    [93] HAN J L, ZHANG D P, JIANG W R, et al. Tuning the functional groups of a graphene oxide membrane by ·OH contributes to the nearly complete prevention of membrane fouling[J]. Journal of Membrane Science, 2019, 576: 190-197.
    [94] RAN J, CHU C Q, PAN T, et al. Non-covalent cross-linking to boost the stability and permeability of graphene-oxide-based membrane[J]. Jouranl of Materials Chemistry, 2019, 7(14): 8085-8091. doi: 10.1039/C9TA00952C
    [95] XU X L, LIN F W, DU Y, et al. Graphene oxide nanofiltration membranes stabilized by cationic porphyrin for high salt rejection[J]. ACS Applied Materials & Interfaces, 2016, 8(20): 12588-12593.
    [96] WANG L, WANG N X, LI J, et al. Layer-by-layer self-assembly of polycation/GO nanofiltration membrane with enhanced stability and fouling resistance[J]. Separation and Purification Technology, 2016, 160: 123-131. doi: 10.1016/j.seppur.2016.01.024
    [97] LIU Y, ZHNEG S X, GU P, et al. Graphene-polyelectrolyte multilayer membranes with tunable structure and internal charge[J]. Carbon, 2020, 160: 219-227. doi: 10.1016/j.carbon.2019.12.092
    [98] LIU T, TIAN L, GRAHAM N, et al. Regulating the interlayer spacing of graphene oxide membranes and enhancing their stability by use of PACl[J]. Environmental Science & Technology, 2019, 53(20): 11949-11959.
    [99] MENG N, ZHAO W, SHAMSAEI E, et al. A low-pressure GO nanofiltration membrane crosslinked via ethylenediamine[J]. Journal of Membrane Science, 2018, 548: 363-371. doi: 10.1016/j.memsci.2017.11.044
    [100] HU M, MI B. Enabling graphene oxide nanosheets as water separation membranes[J]. Environmental Science & Technology, 2013, 47(8): 3715-3723.
    [101] HU M, MI B. Layer-by-layer assembly of graphene oxide membranes via electrostatic interaction[J]. Journal of Membrane Science, 2014, 469: 80-87. doi: 10.1016/j.memsci.2014.06.036
    [102] YUAN Y, GAO X, WEI Y, et al. Enhanced desalination performance of carboxyl functionalized graphene oxide nanofiltration membranes[J]. Desalination, 2017, 405: 29-39. doi: 10.1016/j.desal.2016.11.024
    [103] LIM M Y, CHOI Y S, KIM J, et al. Cross-linked graphene oxide membrane having high ion selectivity and antibacterial activity prepared using tannic acid-functionalized graphene oxide and polyethyleneimine[J]. Journal of Membrane Science, 2017, 521: 1-9. doi: 10.1016/j.memsci.2016.08.067
    [104] CHEN Z H, LIU Z, HU J Q, et al. β-cyclodextrin-modified graphene oxide membranes with large adsorption capacity and high flux for efficient removal of bisphenol A from water[J]. Journal of Membrane Science, 2019, 595: 117510.
    [105] RENTERIA J D, RAMIREZ S, MALEKPOUR H, et al. Strongly anisotropic thermalconductivity of free-standing reduced graphene oxide films annealed at high temperature[J]. Advanced Functional Materials, 2015, 25(29): 4664-4672. doi: 10.1002/adfm.201501429
    [106] HUANG H, JOSHI R K, DE SILVA K, et al. Fabrication of reduced graphene oxide membranes for water desalination[J]. Journal of Membrane Science, 2019, 572: 12-19. doi: 10.1016/j.memsci.2018.10.085
    [107] XI Y H, HU J Q, LIU Z, et al. Graphene oxide membranes with strong stabilityin aqueous solutions and controllable lamellar spacing[J]. ACS Applied Materials & Interfaces, 2016, 8(24): 15557-15566.
    [108] HAN Y, XU Z, GAO C. Ultrathin graphene nanofiltration membrane for water purification[J]. Advanced Functional Materials, 2013, 23(29): 3693-3700. doi: 10.1002/adfm.201202601
    [109] LI G, WANG X, TAO L, et al. Cross-linked graphene membrane for high-performance organics separation of emulsions[J]. Journal of Membrane Science, 2015, 495: 439-444. doi: 10.1016/j.memsci.2015.08.042
    [110] JANG J H, WOO J J, LEE J, et al. Ambivalent effect of thermal reduction in mass rejection through graphene oxide membrane[J]. Environmental Science & Technology, 2016, 50(18): 10024-10030.
    [111] LI Y, YUAN S, XIA Y, et al. Mild annealing reduced graphene oxide membrane for nanofiltration[J]. Journal of Membrane Science, 2020, 601: 117900. doi: 10.1016/j.memsci.2020.117900
    [112] ZHAO Z, NI S, SU X, et al. Thermally reduced graphene oxide membrane with ultrahigh rejection of metal ions’separation from water[J]. ACS Sustainable Chemistry & Engineering, 2019, 7(17): 14874-14882.
    [113] YU H, HE Y, XIAO G Q, et al. Weak-reduction graphene oxide membrane for improving water purification performance[J]. Jouranl of Materials Science& Technology, 2020, 39: 106-112.
    [114] LI Y, ZHAO W, WEYLAND M, et al. Thermally reduced nanoporous graphene oxide oembrane for desalination[J]. Environmental Science & Technology, 2019, 53(14): 8314-8323.
    [115] CHEN X Y, FENG Z H, GOHIL J, et al. Reduced holey graphene oxide membranes for desalination with improved water permeance[J]. ACS Applied Materials & Interfaces, 2020, 12: 1387-1394.
    [116] SONG X X, ZAMBARE R S, QI S, et al. Charge gated ion transport through polyelectrolyte intercalated amine reduced graphene oxide membranes[J]. ACS Applied Materials & Interfaces, 2017, 9(47): 41482-41495.
    [117] ZHANG Z S, LI N, SUN Y G, et al. Interfacial force assisted in situ fabrication of graphene oxide membrane for desalination.[J]. ACS Applied Materials & Interfaces, 2018, 10(32): 27205-27214.
    [118] CHEN X, QIU M, DING H, et al. A reduced graphene oxide nanofiltration membrane intercalated by well-dispersed carbon nanotubes for drinking water purification[J]. Nanoscale, 2016, 8(10): 5696-5705. doi: 10.1039/C5NR08697C
    [119] HAN Y, JIANG Y, GAO C. High-flux graphene oxide nanofiltration membrane intercalated by carbon nanotubes[J]. ACS Applied Materials & Interfaces, 2015, 7(15): 8147-8155.
  • 加载中
图( 15) 表( 2)
计量
  • 文章访问数:  5436
  • HTML全文浏览数:  5436
  • PDF下载数:  125
  • 施引文献:  0
出版历程
  • 收稿日期:  2021-08-30
  • 录用日期:  2021-09-02
  • 刊出日期:  2021-12-10

氧化石墨烯高压膜的制备及其在水处理中的应用研究进展

    通讯作者: 孔繁鑫, E-mail: kfx11@cup.edu.cn
    作者简介: 孔繁鑫(1985—),男,博士,副教授。研究方向:膜法水处理技术。E-mail:kfx11@cup.edu.cn
  • 中国石油大学(北京)化学工程与环境学院,重质油国家重点实验室,油气污染防治北京市重点实验室, 北京 102249
基金项目:
国家自然科学基金资助项目 (51708556);北京市优秀人才青年骨干个人项目(2017000020124G102);中国石油大学青年拔尖人才项目(2462019BJR004);环境模拟与污染控制国家重点联合实验室开放课题(K03ESPCT);污染控制与资源化研究国家重点实验室开放课题(PCRRF17011)

摘要: 氧化石墨烯(GO)是一种理想的二维结构分离膜材料。从GO结构性质入手,探讨了GO混合基质膜和GO层压膜(GO膜)的制备及其在水处理中的研究现状与前景。分析了GO的添加方式对混合基质膜性能的影响,未来需要进一步对GO表面的活性基团进行改性以提高其分散性和与聚合物的相容性,并加强GO及改性GO的添加方式对膜性能影响的研究。GO混合基质膜在一定程度上可克服传统聚合物膜的Trade-off 效应,技术成熟度较高、应用前景较好。GO膜在水溶液中的不稳定性是其在水处理中应用中的瓶颈,在系统分析提高GO膜稳定性的方法的基础上,进一步指出需要探讨采用新型交联剂或多种稳定方法同步强化其稳定性的可行性,同时其在实际应用中的稳定性及长期运行效果需要进一步研究和验证,以利于开拓其应用。

English Abstract

  • 膜分离技术具有无二次污染、占用空间小、分离效率高、操作简单等优点,因而在水处理过程中应用广泛[1-2]。以纳滤(nanofiltration,NF)和反渗透(reverse osmosis,RO)膜为代表的高压膜技术可高效去除无机盐和微量有机物等溶解性污染物[3-4],已逐渐发展成为脱盐、除硬、污水再生利用和高品质饮用水处理领域的关键技术[5-6]。膜材料是膜技术的核心[7],其主要性能指标为分离膜的渗透性和选择性[8-10]。高分子聚合物因种类多、易加工、价格低等优点被广泛用于的分离膜制备,然而高分子聚合物分离膜普遍存在渗透性和选择性相互制约、此升彼降的矛盾关系(Trade-off效应)。因此,进一步提高分离膜的水通量和选择性,寻找新材料或改变传统的膜制备方法(如在传统基质膜中加入纳米材料等)来改善膜渗透性和选择性成为膜技术发展的迫切需求[11-12]

    二维材料因厚度超薄,具有纳米尺寸的孔洞和通道,以及易于成膜、亲水性良好、易改性等特点被认为是理想的膜材料[12-14]。其中,氧化石墨烯(graphene oxide,GO)因表面富含大量含氧官能团,且亲水性和化学修饰性较好,制备方法简单,化学性质稳定,比表面积巨大[15-16],成本低廉等优点被广泛应用于膜制备中[17-18]

    本文以GO的结构性质为切入点,梳理了GO混合基质膜和GO层压膜(以下简称“GO膜”)的制备方法及其膜性能,分析GO在膜分离技术中尚存在的不足,并对未来的研究和应用前景进行了展望。

    • GO是石墨烯的衍生物,具有超大比表面积和单层碳原子的二维结构(见图1),含有大量的含氧官能团。根据Lerf-Klinowski模型[19],羟基和环氧基存在于GO纳米片的上下面,羧基在GO纳米片的边缘位置。这些含氧官能团表现出极强的亲水性,使GO能均匀地分散在水溶液和部分有机溶液中[20]。此外,超大表面积和官能团为GO改性提供了大量活性位点,使其易于接入特定功能的官能团调控其物理和化学性质,进而提高膜的稳定性、选择性和亲水性等[21]

      GO在膜制备中的应用主要有两种方式。一是将GO纳米材料原位引入聚合物膜内形成GO混合基质膜[22](见图2),GO混合基质膜的制备和应用已成为膜技术领域的研究热点,GO的加入可有效提高膜的亲水性并改变膜结构,进而提高其水通量,在一定程度上克服Trade-off效应[23]。二是通过GO纳米片的有序组装制备层状GO膜[24],GO膜的制备方法简单易操作,其高渗透性和截留率依赖于GO本身的结构性质和传质特性[25]。通过在GO片层中插入不同的离子或有机化合物等手段,调控其层间距,进而实现目标污染物的精准分离(见图2)。

    • GO混合基质膜结构包含支撑层(常称为基膜)和分离层,其常见制备方式有4种[27](见图3):1)将GO添加至基膜中;2)将GO添加至界面聚合水相或有机相中;3)将GO添加至中间层;4)以表面沉积的方式添加GO。

    • GO作为无机二维纳米材料加入基膜后,能有效增强膜的亲水性及抗污染性能(见图4)。ZINADINI等[28]将GO纳米片添加到聚醚砜(polyether sulfone,PES)超滤膜中制备GO/PES膜,制得的GO/PES膜接触角明显降低,亲水性增加,对直接红的截留率为96%~99%, GO/PSE膜的通量为PES膜的2倍。ZHAO等[29]在聚偏氟乙烯(Polyvinylidene fluoride,PVDF)中加入GO制备了GO/PVDF膜,制得的膜材料孔隙率和平均孔径随着GO添加而增加,加入质量分数为2%的GO后通量恢复率为88.56%,蛋白质吸附仅为PVDF膜的21.5%。以上报道表明,GO的加入不仅提升了膜通量,而且有效解决了膜污染问题。基膜除了决定复合膜的机械性能外,还会影响水相单体的赋存和扩散,进而影响界面聚合过程聚酰胺(Polyamide,PA)活性层的形成。LAI等[30]将GO纳米片掺入PSF基膜中,以此为基底进行界面聚合形成PA层,结果表明,添加GO质量分数为0.3%后的PA膜亲水性有所增加,通量增加了30%,且盐的截留率没有明显降低,说明研究制得的膜材料克服了Trade-off效应。NASSERI等[31]使用相转化法制备了用于去除水中双酚A的GO/PSF膜,与PSF膜相比,GO/PSF膜的孔隙率更高,孔径变小,纯水通量增加了50%~56%,对双酚A的去除率高达93%。GO加入基膜后通过影响基膜孔径、孔隙率及亲水性等改善PA膜的性能。

      若加入过多GO会形成孔隙率和孔径均较小的海绵状支撑膜,但较高的表面能使其在基膜中团聚,从而影响基膜的结构,导致复合膜性能降低,而改性后的GO能有效减弱GO纳米颗粒间的相互作用力来抑制团聚。 ZHAO等[32]在PSF超滤膜中加入了异氰酸酯改性的GO,提高了膜表面亲水性,进而改善了PSF膜的耐污染性能。XIE等[33]使用磺化GO制备PSF超滤膜时发现,随着磺化GO的增加,膜亲水性和孔隙率逐渐增加,粗糙度逐渐减小,添加质量分数为0.2%的磺化GO后超滤膜的通量高达600 L·(m2·h)−1。以上报道表明,通过加入GO来改变基膜的孔径、孔隙率和亲水性,可改善基膜的亲水性、表面粗糙度等,进而可影响PA层的形成。

    • 将GO、改性GO与界面聚合过程水相单体溶液或有机相单体溶液混合,制备GO混合基质膜(见图5),可有效增强膜的耐氯性,从而提升抗污染性能。改性GO则可缓解GO在单体溶液中的团聚,提高其在单体溶液中的分散性。

    • 将GO分散到有机相溶液是GO加入PA层的方法之一,由于GO在有机相中分散性较差,故这方面研究相对较少。YIN等[34]将GO加入均苯三甲酰氯(trimesoyl chloride,TMC)中与间苯二胺(m-phenylenediamine,MPD)进行界面聚合,当GO加入量为0.015%(质量分数)时,制得膜材料在2 MPa下水通量为59.4 L·(m2·h)−1,Na2SO4截留率为97.3%,通量比不加GO时增加了50%。陈贤鸿等[35]通过在二次界面聚合的有机相中加入GO对商业RO膜进行改性,评价了 GO 掺杂后膜的分离性能和耐氯性能,结果表明:添加GO可提高膜的分离性能、耐氯性能和亲水性能;当 GO 添加量为 30 mg·L−1时,膜通量为(77.7±0.9)L· (m2·h)−1,截留率为97.6%±0.5%,相比商业膜分别提高了 38.4%和4.5%。GO在有机溶剂中的分散性较差,故更多研究者将GO分散在水相溶液中制备GO混合基质膜。

    • 把GO加入水相溶液(如哌嗪(piperazine,PIP)和MPD等)是制备GO混合基质膜最常用的方法。HU等[36]将GO添加至PIP,通过界面聚合制备GO/PIP膜,结果表明,GO的加入提高了膜的亲水性,水通量比原始膜提高了近4倍,且截留效果未受太大影响。ZHAO等[37]将GO加入PIP中制膜,在最佳GO剂量为0.01%(质量分数)时,在0.1 MPa下水通量为15.63 L· (m2·h) −1,Na2SO4去除率为96.56%,MgSO4去除率为90.5%。上述报道表明,GO/PIP 膜在盐截留率略微降低的情况下,有效改善了水通量且表现出更高耐氯性。不同单体界面聚合形成的膜略有不同,PIP分子链较柔软易形成孔径大的分离层,故GO加入后水通量增大的同时截留率略有下降。

      与分子链柔软的PIP相比,MPD因含有苯环更易形成结构紧密的分离层。GO的加入对膜截留效果的影响较小。芦瑛等[38]以MPD为水相单体、TMC为油相单体,GO作为水相添加物,采用界面聚合法制备的GO/PA膜分离性能优于PA膜,且具有较好的耐氯性。该项研究表明,膜通量随着GO含量的增加而增大,当添加量为0.005%时,膜具有最大通量(63 L· (m2·h)−1)。BANO等[39]在界面聚合过程中将GO加入MPD水溶液中制备了GO/PA膜,结果表明,当GO添加量为0.2%(质量分数)时,所制备GO/PA膜在截留率不变的情况下通量比原始膜高出约12倍。AIL等[40]以含有GO的MPD与TMC为反应单体制备分离膜,结果表明,GO的加入有效改善了膜的水通量、机械稳定性和抗污染性,在1.5 MPa的条件下水通量为29.6 L·(m2·h)−1,脱盐率高于97%。XIA等[41]将 GO加入MPD中制备GO/PA膜,并研究其对天然水体中有机物的去除效果,结果表明,质量分数为0.012%的GO/PA膜对有机物中的紫外吸收(UV254)和溶解有机碳(DOC)的去除率为空白PA膜的2倍。此外,WANG等[42]使用水滑石处理的GO加入聚乙烯亚胺(polyethyleneimine,PEI)与TMC反应形成GO/PA膜,结果表明,膜通量在0.8 MPa下达到26 L·(m2·h)−1,对MgCl2的截留率为97%,对Na2SO4的截留率为32.5%。

    • 改性后的GO能有效减弱GO纳米颗粒间的相互作用力来抑制团聚,从而有效地提高其在膜材料中的分散性及其与膜材料的相容性[43]。ZHANG等[44]将羧基化的GO(CFGO)和GO分别加入PIP制备了CFGO/PA膜和GO/PA膜,发现CFGO比GO分散得更均匀,CFGO的最佳投加质量分数为0.07%,而GO最佳投加质量分数仅为0.05%,其水通量高达110.4 L·(m2·h)−1,比GO/PA膜提高约17%,使用PA膜、0.05%GO/PA膜和0.05%CFGO/PA膜对染料进行处理,发现CFGO/PA膜的染料去除效果最好(对新胭脂红去除率为95%),表明CFGO/PA膜在染料脱色和脱盐中具有巨大的应用潜力。KANG等[45]将磺化GO加入PIP中制备改性GO混合基质膜,在盐截留率保持不变的情况下,0.3%磺化GO膜具有更高的渗透性,水通量从6.3 L·(m2·h)−1增至11.8 L·(m2·h)−1。为进一步增加膜的亲水性及对无机盐的截留效果,WEN等[46]使用酰氯GO(GO-COCl)加入PIP和TMC界面聚合制备了GO-COCl/PA膜,在0.6 MPa下膜通量由11.6增加到22.6 L·(m2·h)−1,Na2SO4的截留率由95.0%增加到97.1%。ZHANG等[47]将对氨基苯酚改性的GO(mGO)加入MPD制备mGO/PA膜,mGO/PA膜接触角降低了21.4$ ° $水通量增加了24.5%(23.6 L·(m2·h)−1),对NaCl具有超高的截留率(99.97%),对大肠杆菌和金黄色葡萄球菌杀菌率(96.78%、95.26%)也远高于PA膜(4.95%、2.48%)。

      使用无机材料改性GO也是常见方法。ALI等[48]使用Ag+改性的GO加入PA层,对其防污和抗菌性能做了评估,结果表明,Ag-GO/PA膜具有高负电性、亲水性和光滑的膜表面,优化制备的 Ag/GO膜具有89%的水通量恢复率和良好的抗微生物污染特性。LIU等[49]将SiO2修饰的GO加入PIP制备SiO2-GO/PA膜,膜通量明显增加,对NaCl、Na2SO4、MgSO4的截留率分别为40.7%、90.2%、82.4%,且具有更好的防污性能。ABADIKHAH等[50]使用TiO2和Ag+修饰还原GO(rGO),并将其加入MPD中制备Ag-TiO2-GO/PA膜,发现Ag-TiO2-GO/PA的膜通量高达52 L·(m2·h)−1,对Na2SO4的截留为96%,对玫瑰红染料截留率为98%,杀菌率约为90%。以上报道表明,将改性GO加入混合基质膜已成为目前的研究热点,改性GO有效改善了GO与聚合物膜相容性差的问题,提高了其在膜中的分散性。在水通量增加的同时,盐截留率有所上升,抗污染性能也得到有效提升。

    • GO 中间层通常以过滤的方式形成。过滤会使GO在膜上分布得更加均匀,形成的多孔选择层降低了水的输送阻力,因此比GO直接分散在单体溶液制备膜的渗透性更好。LAI等[51]将GO过滤到基膜表面,然后用PIP和TMC在GO层上进行界面聚合,研究GO及加入方式对膜通量的影响,结果表明,膜通量在GO加入后增加了129.4%,对Na2SO4和MgSO4的截留均在95%以上。 SHI等[52]将GO过滤至混合纤维素膜上,之后用MPD和TMC在GO层上形成PA层(见图6),发现含80$ \mathrm{\mu }\mathrm{g} $GO的GO/PA膜通量为30 L·(m2·h)−1,对NaCl的截留率高达99.7%,具有优异的脱盐性能。过滤法形成的GO中间层与基底及表层之间没有化学相互作用,导致GO层易脱落,因此,LI等[53]将乙二胺(ethylenediamine,EDA)交联的GO沉积在基膜上,之后在GO层上制备GO/PA膜,结果表明,膜对乙醇的渗透量远高于PA膜(20.74 L·(m2·h)−1),对罗丹明B的截留率为99.3%。该研究还发现,所制备的GO/PA膜在二甲基甲酰胺溶液中浸泡166 d后,对罗丹明B的截留率仍保持在98% 以上,表明其具有良好的溶剂稳定性。

      上述报道表明,混合基质膜中的GO中间层减小了水的输送阻力并有效降低了膜表面粗糙度。平滑的GO层有效抑制了水相溶液向基膜的扩散,并为水相和油相的界面聚合反应提供了稳定的反应界面,更有利于超薄PA层的合成[53]

    • 通过层层自组装(Layer-by-Layer,LBL)等方式将GO以表面沉积的方式加入混合基质膜(见图7),在利用GO性质增强膜性能的同时,能更有效地发挥其二维结构和独特层间传质的优势。CHOI等[54]用LBL法在MPD和TMC合成的PA层上沉积GO层以制备新型GO/PA膜,结果表明,GO/PA膜的接触角降低了60%,对NaCl具有相似截留效果的情况下,GO/PA通量为14 L·(m2·h)−1比PA膜高出了12%。该结果说明,膜表面的GO层不仅降低了膜表面粗糙度,增强了膜的防污性能,而且在氯稳定测试中充当了PA膜的保护层。FRANCOIS等[55]利用羧基之间的偶联反应将GO连接到PA膜表面,制备了具有抑菌性能的RO膜,结果表明,GO的加入使得膜亲水性增加了1倍,且膜在与大肠杆菌接触1 h后,细胞数量减少了64.5%。WANG等[56]通过GO环氧基与O-(羧甲基)-壳聚糖(O-carboxymethyl chitosan,OCMC)活性层氨基之间的开环聚合作用,将GO添加到OCMC膜的表面形成GO/OCMC膜,GO表层的加入使膜具有更高的渗透性和选择性,1.5 MPa下膜通量是原始膜的2倍(26.8 L·(m2·h)−1),对NaCl的截留率由56%增加到了69.10%。上述报道表明,混合基质膜上的GO表层明显增加了膜的亲水性,在与水中污染物质接触时充当了PA层的耐氯保护层,有效增强了膜的耐氯性和抗污染性能。

    • GO膜因其亲水性和独特的层压结构表现出高水通量和对污染物质的高截留率[57]。目前,主流观点认为分离机制主要是尺寸排阻的筛分和静电作用[58](见图8)。GO膜以层层堆叠的的形式组合在一起[59],层与层之间通过大量氢键和π-π作用相连,形成具有一定层间距的通道,二维平面以共价键相连形成二维的纳米通道[60]。层间通道和二维通道是GO膜尺寸筛分的关键。当大于GO通道尺寸的物质从GO纳米片的边缘扩散到GO膜的层间空间时,它们会被层间通道和平面通道拦截。GO膜表面的电荷与污染物之间的静电作用也是实现截留的重要机制。GO膜因表面官能团在水环境中的水解电离带负电,故对带负电的污染物截留效果会更好。通过层间通道和含氧官能团实现的尺寸排阻和静电作用是GO膜截留的主要机理,其独特的层间传质特性使得GO分离膜在水处理方面得到更广泛的研究。

    • GO膜常用的制备方法有真空过滤、LBL法和旋涂等(见表1)。真空过滤是用过滤装置将GO均匀地分布在基膜上,方法简单、易操作。ZHANG等[62]通过将GO分散液分别过滤到无机陶瓷管、聚丙烯腈(polyacrylonitrile,PAN)膜、聚碳酸酯(polycarbonate,PC)膜上,研究不同基材对GO膜性能的影响时发现,GO/陶瓷膜的机械强度更大,GO/PAN膜的界面粘附性更强、稳定性更高, GO/PC膜因PC膜直通孔而具有最大的渗透性。LBL法指通过静电作用将GO与聚电解质分别多次沉积在基膜上形成稳定的GO层[63]。NAN等[64]以预处理PAN膜为基底,将GO和PEI用LBL技术制备了带正电荷的NF膜,探究了GO浓度对水通量和盐截留率的影响。旋涂法是将基膜置于匀速旋转的平板上,将GO溶液匀速滴落使其均匀附着在膜表面。ZHU等[65]通过旋涂法制备了无支撑层的GO膜,成功控制了层间距并用于盐类及有机物的处理。

      随着GO膜研究的深入,电场辅助和喷墨打印等新型制备方法被应用到GO膜的制备当中(见图9)。WANG等[66]在LBL的基础上增加电场辅助,成功地在PAN膜上合成了GO/PEI膜,发现在外加电压5 V,沉积时间3 min下制备的双层膜的水通量(压力0.1 MPa下)高达16.4 L·(m2·h)−1,对MgCl2的去除率为80.9%,且比静态LBL形成的膜稳定性更高。QI等[67]使用电泳沉积在多孔不锈钢中空纤维(porous stainless steel hollow fiber,PSSHF)上实现了超薄无缺陷GO层的快速沉积,得到的产物对KCl、NaCl、Na2SO4、CaCl2、MgCl2的截留效果均达到99%以上,实现了对各类型的混合物进行精准分离。FATHIZADE等[68]采用喷墨打印的方法在改性PAN基底上通过调节GO溶液浓度和打印时间制备了超薄(7.5~60 nm)GO膜,该膜具有较高的水通量且对小分子有机物也有较高的截留率(95%)。

      GO膜在气体、溶液分离渗透中表现出了良好的适用性。早在2013年,KIM等[69]报道了相对湿度较大且层间衔接较好的GO膜对CO2/N2有很好的选择分离效果。GO膜在气体分离中的研究证实了GO膜是一种理想的压力驱动膜[70],且具有高亲水性和低水分子摩擦阻力等优势[71]。这些研究成果使学者们开始关注和研究GO膜在水处理中的应用,但GO良好的亲水性使其在水溶液中极不稳定[72]。NAIR等[73]发现,干燥状态下的GO膜结构紧凑层间距不超过0.3 nm,当GO膜浸入离子溶液中时,水合作用使得间距扩大到0.9 nm。如图10所示,随着在水中浸泡冲洗时间的增加,GO的强亲水性导致表面含氧官能团与水形成氢键,产生的水合排斥作用会破坏原有结构中的氢键和π-π键[74],最终导致层间距的增加并发生溶胀剥离的现象[75-76]。除了GO层间易剥离不稳定外,GO层与基膜之间较弱的非共价相互作用也可能导致GO膜在过滤期间从基膜上脱离[22]。因此,稳定性是GO膜的研究和应用中亟需解决的问题。

    • GO膜一般由两部分组成,即GO选择层和具有机械强度的多孔材料支撑层。因此,制备稳定的GO膜需要考虑两个方面的稳定性:一是GO片层和基底的结合力;二是GO片层与片层之间的结合力。如金万勤教授课题组[77]采用多巴胺长链的交联作用提高GO片层和膜基底之间的结合力,通过含胺基的小分子提高片层之间的稳定性,调控层间距。

      GO膜在水中的溶胀会造成选择层的层间距增大,进而降低溶质截留率。目前,常通过添加交联剂、制备改性GO或rGO的方法来增强膜稳定性,相关机理如图11所示。交联剂与GO基团之间反应生成共价键或基团增强GO膜之间的结合力[78],改性GO通过改性基团之间相互连接来增强GO膜的稳定性; rGO通过减少官能团的数量来减弱水合作用、缩小了层间距,增强片层间的π-π作用来提升GO稳定性。根据上述思路,常用稳定的GO膜制备方法主要有4种:1)交联剂插层GO膜;2)改性GO制备稳定膜;3)rGO膜;4)复合方法制膜。

    • 交联反应是制备稳定GO膜的重要方法。通常在GO溶液中加入交联剂来提高GO膜与基底、GO层与层之间的结合力[79]。目前,常使用的交联剂主要有多胺类化合物,有机酸、无机物等。通过交联剂与GO上的含氧官能团发生作用,在层与层之间形成共价键或强化非共价相互作用增强层间的结合力,从而增强GO膜的稳定性(表2)。

      1)多胺类化学交联。多胺类化合物是常用的交联剂,有研究表明,聚多巴胺中的儿茶酚基团能通过共价反应增强膜与基底之间的结合力[80]。ZHANG等[77]使用多巴胺交联GO制备稳定的GO膜,XRD结果显示,交联膜在水中的层间距变化仅为0.06 nm,多巴胺有效抑制了GO膜在水中的溶胀度,在1 MPa压力下通量高达45 L·(m2·h)−1对染料的截留在98%以上,且在长期运行中依然保持稳定。XU等[81]使用多巴胺作为GO和多孔α-Al2O3基膜之间的连接体,成功制备了高度稳定的GO膜并应用于海水脱盐,结果表明,在30 ℃条件下负载量为1.966 g·m−2的GO膜通量为8.5 kg·(m2·h)−1,离子截留率超过99.7%且在运行336 h后依然稳定。多胺类化合物与GO层间的交联主要是通过胺类上的氨基与GO的环氧基反应形成—C—N—键来增强层间作用力[81]。KIM等[22]使用N-异丙基丙烯酰胺和N,N'-亚甲基双丙烯酰胺等聚合物交联GO纳米片,测得制备的GO膜稳定性良好时纯水通量为33.5 L·(m2·h)−1,NaCl的截留率为98.5%;通过测量2 MPa时2 000~15 000 mg·L−1的NaCl溶液的通量和截留来模拟并评价膜对海水脱盐的效果,结果表明,膜通量随着NaCl浓度的增加而减少,最大通量为52.3 L·(m2·h)−1,膜对NaCl的截留率稳定保持在98.3%左右。VEPIKA等[82]通过浸涂辅助LBL法将对苯二胺引入膜中,在GO层为5层时交联膜的截留率比未交联时提高了12.4%,在0.1 MPa压力下连续操作120 h膜性能也没有明显降低。

      使用最简单的二胺物质对GO进行交联,能有效制层间距抑制膜的溶胀。LI等[83]将EDA交联的GO过滤到多巴胺涂覆的基底上制备GO/EDA膜,在1.5 MPa的条件下水通量高达115.5 L·(m2·h)−1,运行168 h后仍能保持完整的形态及膜性能。MAHALINGAM等[84]使用EDA交联GO,GO/EDA膜水通量提升了50%左右(14 L·(m2·h)−1),丙酮和N-甲基吡咯烷酮的通量为30和5 L·(m2·h)−1,且对有机物和染料有很好的截留效果。然而,有研究发现,EDA的会使GO还原,导致部分氧官能团丧失,且在EDA的插入扩大了GO层的自由间距,导致GO与EDA的交联反应,引起水通量下降和离子截留效能的降低。 ZHANG等[85]分别用尿素(UR)和EDA制备GO/UR膜和GO/EDA膜,结果表明,在80 kPa下GO膜和2种交联膜通量分别为17.5、12和15.2 L·(m2·h)−1,GO/UR膜对盐类物质截留效果最好比GO膜高了1.6~2.4倍(即NaCl:26.8%,CaCl2:63.2%,MgSO4:63.2%和CuSO4:81.9%)。

      2)以小分子羧酸类和醇类作为交联剂。JIA等[86]以二羧酸、二醇和多元醇为交联剂,以盐酸为催化剂在80 $ \mathrm{℃} $的条件下制备了交联的GO膜,结果表明,随着羧酸类物质分子链的增长,GO层间距从0.699 nm增加到了0.754 nm;除辛二酸外,膜弹性模量随着羧酸分子长度增加,其中,己二酸交联膜弹性模量最高(4.69 GPa)约为原始膜的15.6倍,机械强度大幅增加。对与醇类物质而言,膜的弹性模量随着烷基链长的增加而增加,最大的为3.49 GPa。为进一步探究此类交联剂对GO膜性能的影响,JIA等[87]使用羧酸类物质(草酸、丙二酸、琥珀酸、己二酸、辛二酸等)与GO交联反应,结果表明,交联膜的水和盐溶液中的渗透性更好,膜在水中的溶胀度下降了约66%。其中,己二酸交联的GO膜在水中的溶胀度最低(39.8%),辛二酸因其疏水性和低亲和力显示出较低的热解温度。这说明不同类物质交联的GO膜在交联机理及机械性能等方面均有较大差异,而同类物质交联的GO膜也会在热解、溶胀、渗透性和机械性能等方面表现出明显的差异性。

      3)以金属离子作为交联剂。金属离子通过阳离子- π相互作用和配位键作用与GO交联,能调控GO膜的层间距,抑制膜在水中的溶胀,改善膜稳定性。YI等[88]使用Mg2+交联GO膜,通过阳离子- π相互作用增强GO膜的稳定性,渗透和截留实验的结果表明,GO/Mg2+膜的水通量高达143.2 L·(m2·h)−1,对罗丹明B截留为66.54%,对硝基苯胺的截留为97.90%,对甲基蓝的截留为99.42%。YU等[89]加入Al3+、Ca2+、 Mg2+和Na+交联GO,发现GO的层间距随着阳离子量的增加而增加,且与低价态离子相比高价阳离子交联的GO膜的稳定性更强。LIU等[90]使用Al3+和Fe3+作为交联剂,交联膜的完整性能保持30 d以上,相应层间距由0.8 nm分别增加到了0.86 nm和0.95 nm,结果表明,当GO/Fe3+膜和GO/Al3+膜分离效果相似时前者通量约为后者的1.1~2.3倍。此外,GO/Fe3+膜对有机物中的UV254和总有机碳(TOC)的去除率均高于GO/Al3+膜。因此,GO/Fe3+膜的性能更优于GO/Al3+膜。为进一步研究阳离子对GO层间距的控制机理,CHEN等[91]使用K+、Na+、Ca2+、Li+和Mg2+交联的GO膜层间距分别为1.14、1.21、1.29、1.35和1.36 nm,而K+与其他阳离子混合后对GO进行交联,层间距稳定保持在1.12~1.14 nm(见图12)。另外,密度泛涵理论计算和紫外吸收光谱发现,最稳定的阳离子吸附位置是氧化物基团和芳环存在的地方。上述研究表明,金属离子与GO交联能有效提高膜稳定性、调控其层间距,其交联程度取决于离子的静电力和配位键的强弱,阳离子价态越高膜的稳定性越好。

      4)用其他交联剂制备GO膜。虽然有机交联剂交联的GO膜具有良好的稳定性,但有机交联层很有可能在处理或清洗过程中被氧化剂氧化而崩解,这也限制了GO膜的应用范围[92]。HAN等[92]利用四硼酸钠与GO交联制备出无机交联的GO膜,交联膜的临界载荷从8 nN增加到了80 nN,在破坏性实验中GO膜的形态、通量和截留效果都表现出良好的稳定性。另一方面,在无机交联GO膜的基础上通过加入H2O2和FeCl2,引入羟基自由基(·OH)来增强膜抗污染性,发现四硼酸钠和·OH的引入提高了GO膜的稳定性、抗氧化性和抗污染性能,有效解决了有机交联剂不耐氧化的问题[93]。在上述GO共价交联的过程中,大量的氧位点被其他基团取代或支配,不利于GO溶剂化,而通道尺寸和溶剂化水平的降低可能会不利于后续的溶质的传质。因此,RAN等[94]利用咪唑官能化的溴化聚(2,6-二甲基-1,4-苯撑氧)对GO进行非共价交联制备溶剂化的GO交联膜,浸泡90 d的GO交联膜外形完整,具有良好的稳定性,其膜通量比GO膜增加了1.5倍,对罗丹明B和NaCl的截留率均在95%以上。XU等[95]采用阳离子的卟啉制备交联的GO膜,卟啉与GO片层未氧化区域通过π−π作用和静电作用相连接,该膜对Na2SO4的截留率为87.7%,水通量为 9.3 L·(m2·h)−1

      5) 聚电解质层层组装。聚电解质与GO通过LBL法静电作用组装的膜具有良好的稳定性。WANG等[96]采用聚阳离子(聚二烯丙基二甲基氯化铵、聚丙烯酸、PEI、聚丙烯胺盐酸盐)和LBL方法在PAN基膜表面制备了GO膜(见图13),水通量、截留率和稳定性均都有大幅提升。其中,在0.5 MPa条件下,通量达到64.2 kg·(m2·h·MPa)−1,对甲基蓝的截留率为99.2%。LIU等[97]通过调节GO和PEI溶液离子强度和pH制备了内部带负电荷、正电荷和电中性的GO膜,其中,电中性膜对MgCl2的截留率最高为86%,而带正电的膜在保持水通量的同时,可进一步提高阳离子截留率。聚氧化铝(PACl)是一种预水解的铝基阳离子聚合物,PACl的阳离子性质使其可通过静电力与GO交联。LIU等[98]用PACl交联GO来制造具有可调节的层间距和水溶液中高稳定性的GO膜。结果表明,膜的层间距稳定在0.8~1.09 nm,对有机物有很好的处理效果。其中,对腐殖酸截留率高达99.6%,对水中TOC的去除率在90%~95%。

    • 对GO表面的含氧官能团进行改性则为GO在膜制备的研究和应用提供了更多可能。YUAN等[102]使用甘氨酸对GO进行改性制备亲水性好的GO—COOH膜,结果表明,改性膜在1.5 MPa压力下水通量增加了20%,对Na2SO4的截留高达91.3%,与GO膜相比,改性膜水通量更高、截留效果更佳。LIM等[103]通过单宁酸(tannin acid,TA)官能化的GO与PEI交联制备TA/GO膜,通过离子渗透实验来评估改性膜的水净化和选择性离子渗透性能,结果表明,GO膜和TA/GO膜对K+/Mg2+的选择值为2.12和18.89;膜渗透实验结果则显示,TA/GO膜的膜通量为15.4 L·(m2·h)−1,对MgSO4的截留率为82.3%,对牛血清蛋白的截留率高达99.9%。此外,TA/GO膜对细菌的抑制率高达99.4%,抗菌性也明显优于GO膜。CHEN等[104]用β-环糊精(β-CD)对GO进行改性制备CDGO纳米片,之后将CDGO过滤到纤维素酯膜上制备CD/GO膜, β-CD独特的空腔结构使CD/GO膜的通量明显增大,在0.2 MPa压力下通量高达199 L·(m2·h)−1 CD/GO膜对双酚A的吸附容量高达18 mg·g−1,对水中双酚A的去除效果几乎能达到100%。因此,高通量和高吸附容量的分离膜在水处理领域应用前景广阔。GO表面的含氧官能团为GO改性提供了大量活性位点,改性后的GO在一定程度上具有了改性基团或物质的优点,因此可根据特定处理要求对GO进行改性。

    • rGO通过减少含氧官能团缩小层间距,使得片层间的π-π相互作用增强,水合作用的斥力减弱,从而增强GO片层之间的稳定性[105]。HUANG等[106]用水热还原法合成了rGO,通过改变rGO的负载量和反应时间来控制膜厚度和还原程度,发现rGO膜通量增加、层间距缩小,对Na+的截留也有所增加;在160℃下rGO具有最好的Na+/Cl离子渗透率,具有良好的海水脱盐潜力。XI等[107]利用水合肼和氨溶液对GO进行还原,结果表明:官能团的减少导致rGO减弱了与水分子之间的水合作用,增强了片层间的π-π作用,使膜在水和酸碱溶液中都表现出良好的稳定性;实现了单价/多价离子的精准筛分,并表现出良好的重复性和稳定性。水合肼还原和水热处理法制备的GO容易形成较多的皱纹和波纹,从而影响rGO膜的性能。而碱回流则易形成更均匀更小的rGO纳米材料。HAN等[108]利用碱回流还原GO,制备得到的rGO膜的最大水通量为218.3 L·MPa−1,在0.5 MPa压力下对甲基蓝和直接红81截留率分别为99.8%和99.9%,对带正电的罗丹明B截留率为78%。LI等[109]将EDA与GO交联后用氢碘酸溶液制备成rGO膜,结果表明,rGO膜的通量为225 L·(m2·h)−1,且对甲苯、汽油、豆油和石油醚等有机物的分离效率在99.9%以上。

      空气、真空进行热还原或紫外辐射等方法能降低GO的纳米褶皱和缺陷的产生,还能精准控制还原程度[110]。LI等[111]将GO膜分别在80 ℃和150 ℃进行热制备中温还原GO(MrGO)膜和高温还原GO(HrGO)膜。2种膜的间距都为0.95 nm,但MrGO膜通量HrGO高70%(39.9 L·(m2·h·MPa)−1),对Na2SO4的截留为90.90%,中温还原提供了一个温和的还原过程,易形成更有序的层状结构,从而实现膜性能的调控。ZHAO等[112]用热处理还原制备rGO膜,通过调节还原时间和温度等来调节膜的性能,结果表明,厚度为795 nm的rGO膜性能最佳,膜通量为0.42 L·(m2·h)−1,对NaCl的截留高达99.56%,具有良好的热稳定性和机械稳定性。YU等[113]通过控制紫外辐射时间来控制GO膜的还原程度,发现rGO膜的通量增加了近270%(38.27 L·(m2·h)−1),对铬黑T、结晶紫、罗丹明B和亚甲基蓝4种染料截留率均在96%以上。以上结果说明,弱还原的GO膜能有效克服Trade-off效应,故可在实际废水的处理领域有很好的应用。

      rGO亲水性的降低和层间距的减小导致rGO膜通量的降低,在GO纳米片上制造纳米孔能有效提高rGO膜的水通量。LI等[114]首先采用H2O2氧化在GO纳米片上产生高密度的(2.89 × 1015 m–2)纳米孔径(平均孔径为3 nm),之后用真空抽滤制备GO膜,最后用热还原法对真空抽滤的GO膜进行还原制备rGO膜,其水通量增加了26倍,且截留率没有受到明显的影响。CHEN等[115]通过H2O2化学蚀刻法在GO表面形成纳米孔(见图14),之后,通过抽滤到基膜表面上用氢碘酸溶液制备rGO膜。结果表明,产生的纳米孔使水通量从0.4 L·(m2·h)−1增加到6.6 L·(m2·h)−1,并且 Na2SO4的截留率高于 98.5%,长时间在错流装置研究表明其具有较好的抗污染性和稳定性。

    • 单一稳定方法制备的膜会存在一些不足和缺陷,而将不同的稳定方法结合制备的GO膜能进一步提升膜性能。SONG等[116]使用聚电解质(PE)和改性的PE(mPE)分别插层rGO制备了PE/rGO膜和mPE/rGO膜,经对比不同带电性膜对盐类的截留性能,发现带正电的PE/rGO膜的盐截留顺序为MgCl2(93.0%)>NaCl(88.2%)≈MgSO4(88.1%)>Na2SO4(65.1%),带负电的mPE/rGO膜的盐截留顺序为Na2SO4(90.3%)> NaCl(85.4%)> MgSO4(68.3%)> MgCl2(42.9%)。ZHANG等[117]通过制备氨基接枝的PrGO调控GO膜表面性质以及层间距,制备的GO膜具有较高的水通量 (17.2~86.5 L·(m2·h·MPa)−1),较好的盐截留率 (NaCl:27.7%~62.6%;Na2SO4:68.4%~86.1% )和较高的甲基橙截留率(92.3%~96.8%)。在二维GO纳米片中插入碳纳米管(CNT)能形成均匀的网络,为分子传输提供更多的传质通道,使膜具有高渗透性和分离性能(图15)。CHEN等[118]将CNT插层的rGO真空抽滤制备了NF膜,用于饮用水中纳米粒子、染料、蛋白质、有机磷类物质、糖类和腐殖酸的去除,其对甲基橙的截留率为97.3% (327 Da),其他物质截留率均高于 99%,水通量高达200~300 L·(m2·h·MPa)−1,具有良好的渗透性、抗污染性和截留性能。HAN等[119]采用rGO 和酸处理的多壁碳纳米管(MWNTs)插层组装制备高通量的NF膜(G-CNTm),通量是rGO膜的2倍( 113 L·(m2·h·MPa)−1),具有优异的染料截留率(直接黄>99% ,甲基橙>96%)和盐截留率 (如 Na2SO4:83.5%和NaCl∶51.4%)。因此,将交联和还原法结合制备的GO膜,比单一法制备的膜稳定性更好,膜性能也得到进一步提升。

    • 1)需要进一步研究混合基质膜中GO的添加方式对高压膜性能的影响。目前主要通过铸膜液、界面聚合水相溶液或油相溶液中添加GO制备混合基质膜,但GO易在水相中团聚使膜产生非选择性缺陷,降低膜性能,故可将改性GO加入水相或与聚合物共混来制备性能优异的GO混合基质膜。

      2)需要进一步深入开展GO中间层或表面沉积在混合基质膜上的研究。随着GO混合基质膜研究的深入,不少学者将GO以中间层或表面沉积的方式加入PA膜。通过过滤形成的中间层不仅为界面聚合反应提供了稳定的平台,而且有效降低了膜表面粗糙度。表面沉积的GO顶层则明显增加了膜亲水性并充当了PA层的耐氯保护层。

      3)应加强对GO膜孔道精准控制和提高稳定性的研究。GO膜的渗透性和对离子/分子的选择性主要取决于层间孔道的大小。对层间距进行调控不仅能有效增强GO膜稳定性,还能实现溶液中不同离子/分子的精准筛分,同时污染物在膜中的传质和截留机理仍需进一步的研究和探索。。

      4)积极开展实际水处理过程中膜性能和长期稳定性的研究。GO混合基质膜和GO膜对实际废水处理效果及稳定性还有待深入研究。