Removal of iron and manganese from groundwater sources using nano-biosorbents

The presence of iron (Fe) and manganese (Mn) ions in rocky beds leads to groundwater pollution. Moreover, their excessive concentration causes bad taste and color stains of water. Tea leaves-derived char (TLC), rice straw-derived char (RSC), and nanosilica (NS) were used to adsorb Fe and Mn ions from water sources. The effects of parameters such as contact time, composition percentage, and particle size of biosorbents in a fixed-bed adsorption column were investigated. The study on the adsorption of Fe and Mn ions showed that the amount of adsorption increased significantly by decreasing the particle size. Furthermore, the combination of nano-biosorbents with nanosilica improved the adsorption. The Thomas and Adams–Bohart models adequately indicated the adsorption of Fe and Mn ions onto nano-biosorbents in the column mode. The TLC and RSC with NS are applicable for the removal of Fe and Mn ions from groundwater. According to the BET analysis results, with more crushing of biosorbents by ball mill and placing them in the furnace, specific surface area of tea leaves and rice straw increased from 0.29 to 3.45 and from 3.70 to 10.99 m2/g, respectively. The absorption of iron and manganese from the aqueous solution increased with the percentage of nano-silica. According to breakthrough curves, under best conditions (the seventh mode), nano-biosorbents could remove 98.05% and 97.92% of iron and manganese ions, respectively. The maximum equilibrium capacity of the adsorption column (mg/g) was 256.56 for iron and 244.79 for manganese.


Introduction
Iron and Manganese are two metals commonly found in wells water [1]. This is also due to the presence of a rocky bed in the groundwater, causing excessive metal taste and stains [2]. The permissible level of Mn is 0.5 mg/l. Drinking water standards set the maximum allowable amount of iron at 0.3 mg/l, because higher levels are undesirable for industrial and domestic use [3]. Due to environmental and health issues, the removal of Fe and Mn ions from water resources by surface adsorption and a low-cost adsorbent has been discussed [4]. Among various methods available for removal of metallic elements, the adsorption process is preferred owing to its flexibility, high efficiency, reproducibility and being economical [5]. Natural or modified biomaterials, by-products, or waste from industrial and agricultural operations are the most important sources of low cost adsorbents [6,7]. Most studies on the removal of metal ions in surface and groundwater are performed using a batch system, which is generally and easily applicable in laboratory studies and limited to the processing of water sources in small quantities [8][9][10]. The removal of methylene blue from water by tea waste active with H 3 PO 4 (H-AC), KOH (K-AC) and ZnCl 2 (Z-AC) agents has been studied by Toli et al. EDX, FTIR, FESEM, XRD and TGA analyses were performed on the adsorbents; the results showed that the adsorption capacity of H-AC adsorbent for removal of methylene blue is higher than the others [11]. Hameed and El-Khaiary used RSC to remove malachite green. As for their results, RSC is suitable for removing dye from aqueous solutions [12]. Tai Han Nogoyan et al. studied the application of rice straw sorbent for removal of arsenic from water sources. FTIR and SEM-EDX analyses were performed on the adsorbent. As such, by processing and converting ordinary adsorbent into RSC, the adsorption rate increased [13]. Moreover, the removal of cadmium from water using RSC was investigated by Zheng et al. RSC can be effective in removing cadmium from water [14]. The removal of methylene blue from water by Modified nano-SiO 2 by Bismuth and Iron has been studied by Salimi et al. SEM, FTIR, XRD and TEM analyses were performed on the adsorbents; the XRD results showed that Nanosilica structure is amorphous [15]. In a batch system, the equilibrium time is short, and in a continuous system, the adsorbent is always in the vicinity of the fresh solution [16,17]. The use of multi wall carbon nanotubes (MWCNTs) for Cr(VI) removal from groundwater was investigated by Mpouras et al. Batch and column experiments were conducted to examine the effect of MWCNTs, initial concentration, pH, contact time and breakthrough curves. The results showed that pH is an effective parameter in removing Cr(VI) ion from groundwater [18]. The continuous system is inexpensive, cost effective and adaptable to the ongoing process [4,19]. Himanshu Patel conducted a comprehensive study on the continuous fixed bed adsorption process in 2019, studying more than 100 titles of articles [5]. The use of tea waste for Cu and Pb removal from wastewater was investigated by Emersing et al. The experiments were performed in a fixed bed column; the effect of adsorbent dose, initial concentration, pH, particle size and breakthrough curves was assessed. As for the results, tea waste was effective in removing Cu and Pb ions from wastewater [20]. Peng Fu et al. examined the impact of pyrolysis temperature and heating rate on the production of activated carbon from rice straw; with increasing pyrolysis temperature and decreasing heating rate, the specific surface area of the adsorbent increased [21]. Vilardi et al. studied the removal of nitrate green by batch and fixed-bed columns packed method with waste biomass. The outcome was that the acidic environment was favorable for the removal of nitrate [22]. A wide variety of lignocellulosic biomasses have been investigated as biosorbents for the removal of metal ions from aqueous environments. Rice straw and tea leaves or their derivatives are two major lignocellulosic-based biosorbents, mainly composed of cellulose, hemicellulose and lignin. These compounds participate in metal ion bonding through such multiple functional groups as hydroxyl, carboxyl, carbonyl, and amine on the cell wall [23,24]. Many studies has been conducted on the removal of metal ions from drinking water sources using rice straw-derived char, tea leavesderived char and nanosilica; the superiority of modified adsorbents in the removal of disturbing ions in water has been proved [13,15,[25][26][27][28][29][30]. Various analyses such as X-ray diffractometer (XRD) [15,31,32], Fourier transforms infrared spectra (FTIR) [24,33], scanning electron microscopy (SEM), the energy dispersive X-ray (EDX) [13][14][15] and Brunauer-Emmett-Teller (BET) [34,35] were used to determine different indicators of adsorbents. In the present study, removal of Fe and Mn from aqueous solution was performed with low-cost adsorbent. The experiments were performed in a fixed bed column. The mathematical methods of Thomas and Adams-Bohart were used to describe the breakthrough curves. The biosorbents was also tested through real samples taken from Groundwater sources of drinking water located in Shaft City in Gilan province, North of Iran. The results indicate that the proposed biosorbents are a suitable alternative for removing metal ions from water sources.

Preparation of metal solutions
For preparation of synthetic water solutions, analytical grades of Iron (III) chloride (with a chemical formula FeCl 3 .6H 2 O) and Manganese (II) sulfate (with a chemical formula MnSO 4 .H 2 O) were dissolved in tap water to give a concentration of 1000 mg/l and diluting when necessary.

Preparation of nano-biosorbants and nanosilica
The raw tea leaves (TL) and rice straw (RS) were used as biosorbents. Samples were collected from tea plants and rice paddies in the North of Iran. At first, samples were several times washed with tap water for removal of such all traces as oil and dirt. The material was dried at room temperature for 3 days; for more drying, raw adsorbents were placed into oven with a temperature of 70 °C until its weight became constant. The Planetary ball mill was used to reduce adsorbent particles sizes. The adsorbents were placed in a ball mill at 600 rpm for 20 min. then; they were placed in a furnace at 400 °C for 3 h. After 24 h passed, the biosorbents char were taken out of the furnace and stored in closed containers. Biosorbents char include tea leaves-derived char (TLC) and rice strawderived char (RSC). Silicon oxide nano powder (nanosilica) with chemical formula SiO 2 , amorphous structure, and hydrophilic type were purchased from Fine-Nano Company (Made By US-NANO) with 99.5% purity.

Fixed bed column studies
The adsorption process was carried out using Fe and Mn solution with a concentration of 5 mg/l as an artificial sample as well as 0.1 g of nano-biosorbents. A feed water reservoir (with 20 L capacity) was chosen with a heat source inside, its temperature controlled by a thermo regulator. Moreover, the inlet stream was placed over the reservoir; the feed flow was pumped by a variable flow pump (WS123) at a flow rate of 10 ml/min. For the next step, the stream was conducted by a three-way pipe. One stream returned to the feed water reservoir and the other entered the flow meter. Subsequently, the stream entered the top of the column. The process was conducted in a continuous adsorption process with a fixed bed column (diameter of 1 cm and a height of 50 cm). The absorption column had an outer protective body, covered by a heating element. At the column outlet, collection of the samples was done at different times for each test. The time intervals for the process ranged from 1, 2, 5, 10, 20 to 900 (min) minutes, respectively. The process temperature was 30 ℃. In addition, the pH value was 7.9. The flow was stopped once the column was fully marked by C t =C 0 . For each test, samples were collected at a volume of 15 ml for analysis using atomic adsorption (Agilent 240-280 Series AA) as effluent Fe and Mn ions concentration (C t ). The column was washed with distilled water after each test. The schematic diagram of the fixed-bed column is presented in Fig. 1.
The breakthrough curve is usually described as the ratio of the ions concentration at the outlet to the column inlet ratio (C t /C 0 ) in the function of time for the fixedbed column. The amount of adsorbed Fe and Mn was calculated by Eq. (1): where qtotal indicates the maximum removal capacity of column in mg, Q is the volumetric flow rate circulating through the column in ml/min, A is the area under the breakthrough curve in m 2 , t total is the total flow time in min, C ad is the absorbed removal concentration in mg/l. C 0 and C t are the Fe and Mn ions concentrations (mg/l) in inlet and outlet flows, respectively. The equilibrium capacity of the column (mg/g) was obtained by Eq. (2), where m is the dry absorbent mass (g): m total is the total mass absorbed into the column in mg, which is obtained using Eq. (3): %R is the total removal percentages of iron and manganese, which is obtained using Eq. (4): In other words, (%R) is the ratio of the total removed ions in the column to the total amount of ions delivered to the column.

Mathematical description
Various simple mathematical models have been developed to describe and possibly predict the dynamic behavior of the bed in column performance. The most famous and widely applied models used in column performance theory are Thomas and Adams-Bohart [36].

Thomas model
Thomas model is one of the most common and widely used methods in expressing the theory of absorption column performance. It can predict the theoretical Breakthrough curve based on laboratory data (time and Output to input concentration ratio). The linearized form of the Thomas model can be expressed as follows: Equation (5) Here, K Th (ml/mg min) is the Thomas rate constant; q 0 (mg/g) is the equilibrium uptake of metal ions. M as the amount of adsorbent packed inside the column is denoted by (mg). C 0 (mg/l) is the influent concentration, C t (mg/l) is the outlet concentration at each time; and Q (ml/min) is the flow rate. Because the amount exp K Th q 0 M Q is much larger than one, the equation is written as follows: where q 0 and K Th amounts could be obtained through the slope and width of the origin of the linear graphs, respectively, obtained by ln C 0 −C t C t in terms of t [37].

Adams-Bohart model
Adams-Bohart provides a simple basic model for describing the initial region of absorption, often adapting to failure curves with very high accuracy. It has aided researchers to determine important and key parameters, such as adsorption rate constants and adsorption capacity. The mathematical equation of the model can be written as Eq. (7): is much larger than one, the equation is written as follows: Here, C 0 (mg/l) is the inlet concentrations. C t (mg/l) is the outlet concentration at each time. H (cm) is the bed height and U 0 (cm/min) is the superficial velocity, which is obtained through dividing the flow rate by the cross section of the column. K BA (l/mg min) is the Kinetic coefficient or constant Adams-Bohart absorption rate; and N 0 is volumetric absorption capacity (mg/l). N 0 and K BA amounts could be obtained by the slope and width of the origin of the linear graphs, respectively; they are obtained practically by ln C 0 C t − 1 in terms of t [38].

Investigating the structure of biosorbents using XRD
The X-ray powder diffraction (XRD) is an acceptable technique in the study of crystal properties.
This analysis was used to investigate the phases and structure of TLC and RSC. The results of the XRD test are presented in Fig. 2.
The information presented in Fig. 2 is associated with the TLC and RSC. The RSC chart shows a peak at 22.9º with several other small peaks in the rest of the range. The TLC chart displays a peak at 24.5º, a larger peak at 29.55º and several other peaks in other ranges.

SEM combined with EDX spectrum analyses
The surface morphology of loaded samples with Fe and Mn are displayed in Figs. 3, 4 and 5. The samples treated with Fe and Mn had a rougher surface; they were covered with small flocculent material which resembled fibers. This phenomenon is likely due to an inorganic layer formed on the surface of adsorbents by Mn and Fe ions. EDX analysis was used to prove the effective loading of iron and manganese on biosorbents.
As shown in Figs. 3, 4 and 5, the main elements existing in the TLC, RSC and NS were Fe and Mn. Such findings suggest that biosorbents could adsorb Fe and Mn ions from the aqueous solution. This also assumes that the adsorption process of Fe and Mn ions onto biosorbents may be physical in nature. In general, rough surfaces and extensively distributed pores can suggest a larger surface area and more attached metal sites.

Surface area and pore diameter (BET and BJH analyses)
BET analysis is used to study the surface of materials and their porosity. Adsorptive characterization by N 2 is one of the most widely used techniques to assess textural properties of porous solids. BJH analysis can also be employed to determine pore area and specific pore volume using adsorption and desorption techniques. The Physical characteristics of biosorbents are presented in Table 1.

Fourier transforms infrared spectra (FTIR)
The functional groups of biosorbents are analyzed using FTIR. Figures 6 and 7 show the FT-IR spectra of tea leaves and rice straw. According to Fig. 6

Analysis of experimental data
The effect of modified adsorbents and those combinations with NS in the process of fixed bed continuous adsorption were investigated. To examine the effect of adsorption percentage and particle size of adsorbents on adsorption capacity, 7 different combinations of TLC, RSC and NS adsorbents were studied. The percentages of Fe and Mn ions removal at different times by different combinations of adsorbents are shown in Table 2. By plotting the ratio of ions concentration at the output to the input column (C t /C 0 ) in terms of time, Breakthrough curves were obtained. When the ratio of the final concentration (C t ) to the initial concentration (C 0 ) is equal to 0.1, it is denoted by t 1 , and when this ratio is equal to 0.9, it is denoted by t 2 .

Breakthrough studies
The results of Table 2 are illustrated in Figs. 8 and 9.
Regarding the adsorbents, during the first 60 min of contact, the amount of Fe and Mn in solution decreased sharply. Over time, a gradual decrease in adsorption kinetics occurred. When the approximate time of 900 min was reached, the process was stopped and the final concentration was almost equal to the initial one.
To study the effect of adsorbent compound type and percentage in the fixed bed continuous adsorption process, 7 different nano-biosorbents compounds were prepared and tested. The percentage of metal adsorption rises as NS increase. The results show that the adsorbent performance of NS with RSC works more efficiently TLC; this is due to higher specific surface area of RSC.

Mathematical description of the process
Thomas and Adams-Bohart mathematical models were used to evaluate the column performance.
The fixed bed process was performed for binary systems of nano-biosorbents with iron and manganese (Nano-biosorbents-Fe|Mn). Table 3 shows the values for the models' parameters including maximum constant absorption capacity (K Th ), maximum absorption capacity (q 0 ) in Thomas model and kinetic coefficient (K BA ) and volume absorption capacity (N 0 ) in Adams-Bohart model as well as correlation coefficient (R 2 ).

Industrial application of biosorbents
To find out whether the proposed method can be used for drinking water resources, ten control samples (Table 4) were collected from groundwater in Shaft city, Guilan Province in the North of Iran. Temperature, pH, turbidity and color parameters of the collected water samples were measured before treatment. In the proposed method, the adsorbent dose was 0.1 g; the maximum contact time was 720 min; and temperature was 30 °C. The concentration of iron and manganese ions was measured by an atomic absorption spectrophotometer (Agilent 240_280 Series  Here, C 0 (mg/l) is the Initial concentration and C t (mg/l) is the final concentration of Fe and Mn ions in groundwater samples.

Discussion
As mentioned in the introduction, scientific research notes that biosorbents are very effective in removing undesirable elements from drinking water sources. The two main products in northern Iran are tea and rice.
After harvesting, they leave a lot of waste. Green tea leaf waste and rice straw were collected from farms and then processed. nanomaterials are attributed to the higher removal efficiency in adsorption. The use of biomaterials as a precursor for developing nanomaterials is a new research interest nowadays. The concept of green synthesis of nanosorbents from biological systems is environmentally friendly and stable. Present work aimed at developing a suitable nanomaterial-based adsorbent for the removal of low concentration of iron and manganese ions from Drinking water sources.
Various analyses (such as XRD, BET, SEM-EDX and FT-IR) were used to determine their characteristics. Due to XRD results (Fig. 2), the RSC has an amorphous

Table 3 Parameters of Thomas and Adams-Bohart model for iron and manganese adsorbtion by combination of TLC, RSC and NS
The results showed that the performance of NS with RSC is more efficient than other biosorbents combinations. In addition, Fe is absorbed more than Mn. The order of absorption of the systems is as follows: (2) < (4) < (5) < (1) < (6) < (3) < (7), indicating that the adsorption performance improves with increasing the ratio of NS to other adsorbents structure, because there are no peaks that would show a symmetrical structure. According to the observation of peaks in TLC, it can be concluded that its structure is crystalline. In addition, the peaks conform to calcium carbonate with chemical formula of Ca (CO3). The surface morphology of nano-biosorbents after adsorption is shown in Figs. 3, 4 and 5, respectively. Based on SEM analysis, the abundant porous and irregular structure of the nano-biosorbents could enable the easy access of Fe and Mn ions into it. In addition, in the sample sent to the laboratory for EDX analysis, only the amount of iron and manganese in the sample was given in the results. It should be noted that the raw sample of the adsorbent contains Silica, carbon and oxygen. In the final sample, the highest amount of ions was related to iron and manganese and other elements were ignored. BET and BJH analysis (Table 1) was used to measure the specific surface area and pore size of the adsorbents. With converting ordinary biosorbent (TL and RS) to char (TLC and RSC) and based on BET analysis, the specific surface area (m 2 /g) of tea leaves increased from 0.29 (TL) to 3.45 (TLC); and rice straw increased from 3.70 (RS) to 10.99 (RSC) as well. The results of FTIR analysis (Figs. 6 and 7) pinpoint to the strong interaction between functional groups and adsorbate. The results of the analysis of adsorbents showed that they can be used to reduce undesirable elements such as iron and manganese from drinking water sources.
The column operation provides more proficient utilization of the adsorbent's capacity compared to the batch process. Due to the high rate of drinking water consumption, continuous methods should be used to purify drinking water resources.
In the present study, nano-biosorbents include TLC, RSC and NS are packed in the column, and iron with manganese solution of initial concentration 5 mg/l is passed through it. A polyester membrane filter was used to hold the adsorbent. According to the pre-tests performed, the amount of adsorbent was considered 0.1 g. If the amount of adsorbent used is high, the saturation time of the adsorption column will be very long. The maximum height of the adsorbent in the adsorption column was 2 cm and the solution containing iron and manganese entered from the top of the adsorption column and left the end of the column after contact with the adsorbent. To keep the solution in the upper part of the adsorbent, the height of the adsorption column was considered to be 50 cm. The flow rate was maintained at 10 ml/min, and the pH of the stock solution was 7.9. A flowmeter was used to show the flow rate. Several control valves were used to control and regulate the flow in the process path. The flow was transferred from the source to the top of the column by a pump. A reciprocating flow was also used in the flow path after the pump. The process temperature was controlled by a heat source installed in the system. Both the source and the absorption column had a heat source. A heating element was used inside the source and its temperature was controlled using a thermostat. A filament heating element was used to control the temperature of the column. The element was immersed in water. The temperature of the element was controlled using a thermostat. The temperature was 30 ℃. This was achieved due to the many pre-tests that were performed.
The composition percentage of nano-biosorbents is one of the critical parameters in evaluating the adsorption   Figures 8 and 9 represent the breakthrough curves at different composition percentage of nano-biosorbents. The plot clearly shows that the amount of Fe and Mn ions adsorbed increased with an increase in NS. The slightly different shape and gradient of the breakthrough curve could be seen with the variation of composition percentage of nano-biosorbents. As the NS of the column was increased, the breakthrough curve shifted from left to right. The breakthrough occurred slowly for the Sample number 7 than for 3, 6, 1, 5, 4 and Sample number 2. The increase in Fe and Mn ions uptake capacities with higher NS in the column is due to the increase in specific surface area of the adsorbent. Therefore, more Fe and Mn ions can be fixed on the active sites of the nanobiosorbents film. The exhaustion time of adsorbent was increased for higher NS. The delayed exhaustion time shows that the bed is able to operate for a longer period without changing the nano-biosorbents packing. The higher Fe and Mn ions sorption capacity at higher NS can also be attributed to the sufficient residence time of the cation in the adsorption column. This provides ample time for diffusion or interaction of the Fe and Mn ions with nano-biosorbents films. The total removal percentage of Fe and Mn column was seen to increase with NS ( time and the nanofilm bed performance. The data obtained from the column adsorption experiment were applied into mathematical theories to get information on the influencing parameters. This gives us a more comprehensive, complete and clear view of the effect of independent variables in the absorption process. The correlation between experimental and theoretical data of column operation was compared with two models (Table 3). Correlation coefficients for samples 1 to 7 for Thomas and Adams-Bohart model are above 0.83. The calculated R 2 values for the experimental conditions Sample number 7 and 2 shows close agreement (R 2 = 0.95 and 0.98 for Thomas model and R 2 = 0.94 and 0.98 for Adams-Bohart model). From the values of the correlation coefficient, the Thomas model was found to fit well to the experimental data. Adam Bohart correlation was proved best for the initial part of the adsorption process.
Also in this research, real samples were collected from groundwater and their iron and manganese levels were measured using an atomic absorption device. Then, the samples were placed in the vicinity of plant adsorbents (TLC and RSC) using a fixed bed column, and the amount of iron and manganese in the final samples was measured again, and the results indicate the good performance of the adsorbents.
Overall, the experimental results, breakthrough curves, and Thomas and Adams-Bohart models showed that the adsorption capacity of RSC is greater than that of TLC, and RSC with NS absorbs more Fe than Mn.

Conclusions
The results of the present study proved the ability of RSC, TLC, and NS in removing Fe and Mn ions. The XRD, FTIR, SEM-EDX, and BET analyses were applied to characterize the used adsorbents. The experimental results revealed that the char made of tea leaves and rice straw with nanosilica were applicable to remove Fe and Mn ions from groundwater. The higher percentages of nanosilica resulted in higher absorption of iron and manganese from the aqueous solution. Thomas and Adams-Bohart models sufficiently explained the adsorption of Fe and Mn ions onto nanobiosorbents in the column mode. The constants for Thomas and Adams-Bohart mathematical models were calculated. The q 0 values of iron and manganese ions removal by the best combination of TLC, RSC, and NS (the seventh mode) were 222.56 and 158.56 mg/g, respectively. Meanwhile, the corresponding N 0 values were 9.45 and 6.41 mg/l, respectively. In real systems, biosorbents can be used with good efficiency to remove undesirable elements from groundwater sources. The results indicated that the impact of rice straw char was more significant than tea leaves char, and nano-biosorbents had more iron than manganese ions.