Structural Behaviour of Polystyrene Foam Lightweight Concrete Beams Strengthened with FRP Laminates

Lightweight concrete (LWC) is one of the most important building materials nowadays. Many research studies were focused on LWC produced using lightweight aggregates. However, limited work was cited for LWC produced using polystyrene beads. In this study, LWC beams strengthened with carbon fibre reinforced polymer (CFRP) and glass fibre reinforced polymer (GFRP) were experimentally tested to investigate the improvement in their flexural and shear behaviours. LWC in this investigation was achieved by partial replacement of normal aggregate by polystyrene beads and resulted in approximately 30% less weight compared to Normal weight concrete. Fourteen Reinforced Concrete (RC) LWC beams of 100 mm by 300 mm cross section having an overall length of 3250 mm were tested under fourpoint bending. These beams were designed, detailed, and tested to obtain flexural and shear mode of failure. These beams were divided into two groups based on the intended failure mode. In each group, six beams were strengthened using CFRP and GFRP laminates, while the remaining one beam was used as control. The tested parameters were the type of FRP, the width of the laminates used in shear strengthening, and the number of layers used in flexural strengthening. It was found that strengthening of LWC beams using CFRP and GFRP layers resulted in increasing the loading capacity and decreasing deflection as compared to control. The strengthening with CFRP and GFRP is also suitable in reducing the crack width and crack propagation which is more significant in LWC beams. The experimental results were also compared with the expressions in codes for forecasting the strength of LWC beams and it was that these expressions are compatible with the experimental results.


Introduction
Deterioration of concrete structures and/or changing the function of structures and buildings needs retrofitting and repair of such buildings. Other factors that contribute to the deterioration of civil engineering infrastructure include ageing, poor construction, a lack of maintenance, a change in use, more stringent design criteria, and natural disasters, such as earthquakes. Strengthening is a promising approach to improve or regain the load-carrying capacity of structures to extend their serviceability (Shaaban & Seoud, 2018). There are many strengthening techniques, such as guniting (Ramesh et al., 2021), jacketing (Maraq et al., 2021), external prestressing (Kim et al., 2021) and fibre reinforced polymer (FRP) (Alhaddad et al., 2021). FRP gained wide acceptance as a promising technique for retrofitting structural members for its high strength to weight ratio, its damping capabilities, its high resistance to corrosion, its fatigue resistance, and the short time scale for repair (Panahi et al., 2021). Glass fibre reinforced polymer (GFRP) and Carbon fibre reinforced polymer (CFRP) are the widely explored types of FRP which have been discussed in the subsequent para.
GFRP inclined strips were used in the shear deficient Normal weight concrete (NWC) beams and they were found effective in arresting the cracks on higher load as compared to control beam (Sundarraja & Rajamohan, 2009). Flexural strengthening of NWC beams using GFRP, CFRP and hybrid FRP sheets was studied (Attari et al., 2012). This research concluded that the use of a two-layer GFRP for strengthening was very efficient as it enhanced the strength capacity by 114%. In another study, NWC beams were strengthened using wrapping of the shear edges of the beams twice at 45 ∘ in opposite directions by either CFRP or GFRP and found that the strength increase of the beams strengthened with CFRP was 84% and the displacement reduction was found to be 39.5%. The increase in strength of the beams strengthened with GFRP was 45%, and the deflection reduction was found to be 53.6% (Önal, 2014). Strengthening of NWC beams using FRP was also found to improve the fatigue performance of retrofitted beams by extending the strength and lifetime of the beams (Danraka et al., 2017).
In the last decade, there has been more interest in using lightweight concrete (LWC) in structural members for its reduction of the structural weight while providing suitable thermal insulation (Agrawal et al., 2021). It has many applications including multi-storey buildings, frames, floors, bridges, and prestressed elements of all types. To boost the flexural strength of under-reinforced beams, a series of 40 LWC reinforced beams were strengthened with CFRP. Parameters investigated were reinforcement ratio, CFRP sheet length, CFRP sheet width, beam and half-beam width. The reinforced beams demonstrated a small gain in ultimate load-carrying capacity, as well as a reduction in mid-span deflection. Jacketing was the most successful strengthening strategy in terms of strength augmentation (approximately 41%) when compared to control beam, but it dramatically affected ductility (Shannag et al., 2014).
Flexural behavior of concrete strengthened with PU matrix adhesive laminates using small-scale single lap shear specimens, unreinforced flexural specimens, and large-scale RC girders were studied. Experimental results show that although the normal and shear strengths of PU-based adhesives are low, PU-strengthened beams show increased strength and deformability, owing to the load redistribution ability within the bond line (Al-Jelawy & Mackie, 2020).
Bond durability under accelerated environmental conditioning of two FRP systems commonly employed in civil infrastructure strengthening were investigated: epoxy and polyurethane systems. Five environments were considered under three different conditioning durations (3 months, 6 months, and 1 year).
Results indicate that both epoxy and polyurethane FRP systems do not degrade significantly under environmental exposure. However, flexural tests on the FRP strengthened concrete beams indicate that bond between FRP and concrete shows significant degradation, especially for aqueous exposure (Al-Jelawy, 2013).
Number of different rehabilitation and retrofitting techniques for RC columns reviewed and evaluated. The outcomes can be drawn from the review as follows:  (Naji et al., 2021).
Al-Jelawy et al. (Al-Jelawy Haider & Mackie Kevin, 2021) investigated the effect of different environments on the durability and failure modes of two different wet lay-up CFRP systems applied to flexural reinforcement of concrete were investigated: a two-part epoxy and a preimpregnated, water catalyzed polyurethane with aromatic chemistry as a matrix. Durability of concrete, CFRP laminates, and small-scale CFRP-strengthened concrete flexural beams was investigated for each duration (125, 250, and 365 days) and accelerated conditioning environment. Inverse analysis with a numerical model was used to develop conditioned bond-slip models for each composite system. Results and failure modes of control and conditioned specimens showed that degradation of CFRP-strengthened beams was controlled by the conditioned concrete tensile strength and bond cohesive energy in the epoxy and polyurethane systems, respectively.
Aljaafreh (Aljaafreh, 2016) tested eight LWC beams strengthened using CFRP. It was found that the LWC beams strengthened with the CFRP layer exhibited an appreciable increment in flexural strength compared to the control beam. Similarly, experimental, and analytical results of LWC beams strengthened with GFRP Strips was compared. The results showed that strengthening of Reinforced Concrete (RC) beams by GFRP strips is an effective technique (Kotwal et al., 2017). In 2021, an experimental study was conducted to evaluate the use of FRP-based strengthening procedures to extend the service life of damaged LWC members that had been exposed to intense fires. The heated LWC reinforced beams regained a considerable amount of their load capacity after strengthening and exhibited typical flexural fractures in the bending zone, as well as flexure-shear cracks in the shear span. In addition, it was found that using a single layer and U shaped jacket of FRP sheets at sides and bottom of the beams, was the most effective technique among the others used in their research for regaining their full flexural capacity (Alshannag & Alshenawy, 2021).
LWC and NWC beams were experimentally and numerically tested with U-shaped and closed shape of epoxy-bonded CFRP reinforcement to compare shearresisting mechanisms between the two beams types. It was found that CFRP can successfully be used in strengthening of LWC beams and the shear strength gained for LWC is less than NWC samples, while modes of failures were almost the same. On the other hand, diagonal shear cracks propagated through the LWC aggregates, while the cracks in NWC were around the aggregates. The numerical results showed that the current design guidelines to estimate the CFRP contribution do not differentiate between concrete types (Al-Allaf et al., 2019).
Partial replacement of normal aggregate by polystyrene beads results in LWC with the benefits of maintaining a reasonable strength, reduced the overall weight of the LWC test beams by approximately 30% compared to their counterparts of NWC beams, low price, and good insulation of polystyrene [Shaaban et al., 2020;Vishakh and Vasudev, 2018 ]. This is necessary as the use of LWC is increasing day-by-day and the weaker aggregates and interfacial zone of LWC is susceptible for crack propagation and widening (Newman & Owens, 2003). However, we did not cite published work for the LWC beams containing polystyrene beads and strengthened by FRP. Thus, this study is focusing on the LWC beams containing polystyrene beads and their flexural and shear strengthening using GFRP and CFRP. The parameters of the study are the width of wrapping for shear strengthening and the number of layers for flexure strengthening. The design equations in the codes which were formulated for NWC beams are applied and validated in this investigation for LWC beams containing polystyrene beads and strengthened using FRP laminates.

Research Significance
Lightweight concrete is one of the most important building materials that can help to the development of sustainable materials; yet, because of the weaker particles and interfacial zone, crack propagation in LWC beams is relatively faster than in standard concrete beams. As a result, the importance of strengthening LWC beams became apparent. The current study aims to investigate the flexural and shear strengthening using GFRP and CFRP laminates of LWC beams containing polystyrene beads. The existing codes and their design equations for the strengthening of beams using FRP were applied on LWC studied beams containing polystyrene beads. The Comparisons between experimentally obtained loading capacities and those predicted using design codes were carried out.

Experimental Program
Total 14 LWC RC beams having dimensions 100 × 300 × 3250 mm were tested under four-point bending. These beams were divided into control, shear and flexure groups, as shown in Table 1. All beams were detailed according to Egyptian Code of Design and Construction of Reinforced Concrete Structures, ECP 203-2018(ECP, 2018. The dimension, reinforcements and strengthening details of these groups are also mentioned in Table 1. Seven beams (Including one control and Beams in Flexure groups) were detailed in such a manner that intended failure mode was flexure. Beams in Flexure groups were then strengthened for flexure by GFRP and CFRP, as shown in Table 1. On the other hand, the remaining seven beams (Including one control and Beams in shear groups) were detailed in such a manner that the intended failure mode was shear. Fig. 1a, b shows a schematic of reinforcement details of the beams tested for flexure and shear mode of failure, respectively. Two steel types were used, main steel for longitudinal bars of yield tensile strength ( f y = 360N /mm 2 ) and ultimate tensile strength ( f ult = 520N /mm 2 ) and mild steel for stirrups of yield strength ( f y = 240N /mm 2 ) and ultimate tensile strength ( f ult = 370N /mm 2 ).

LWC Mixes Containing Polystyrene Beads
LWC was obtained by replacing 50% of coarse aggregate with polystyrene beads and adding silica fume to the mix to compensate the weakness of polystyrene (Shaaban et al., 2020). Polystyrene is a petroleum-based plastic made from the styrene monomer and it is known as Styrofoam, which is the trade name of a polystyrene foam product used for housing insulation. Polystyrene is a light-weight material (95% air) and rigid cellular foam. Polystyrene has an excellent resistance to moisture, imperiousness to rot, mildew, and corrosion. In addition, it is a very good electrical insulator, has excellent optical clarity due to the lack of crystallinity, and has good chemical resistance to diluted acids and bases. However, polystyrene brittle and it has poor impact strength due to the stiffness of the polymer backbone. Despite this weakness, styrene polymers are very attractive large-volume commodity plastics. The polystyrene beads are shown in Fig. 2 and their physical properties are reported in Table 2. The mix proportion required by weight for one cubic meter of fresh concrete for the LWC specimens are given in Table 3. Characteristic compressive cube strength, f cu , of the LWC mix was 32 N/mm 2 is the average strength obtained by testing six cube specimens of 150 × 150 × 150 mm. Six cylindrical Specimens of 150 diameter × 300 mm height, were tested under compression to obtain the stress-strain response. The average cylindrical compressive strength was f ′ c = 27N /mm 2 . The average density of LWC was 1740 kg/m 3 .

Beam Fabrication
The formwork made of wood was used for the casting of Beam specimens. The steel reinforcement used in the specimens was prepared and placed in the formwork and the thickness of concrete cover was 2.5 cm (refer to Fig. 3). The beams were cast and compacted for 3 min after casting using an electrical vibrator. The beam surface was levelled to obtain a smooth surface. Samples were cured for 28 days and the curing was carried out by covering the samples with burlap and spraying them with water daily. Strain gauges were embedded in the concrete and mounted on main reinforcement, stirrup reinforcement and longitudinal reinforcement, as shown in Fig. 1a, b.

Steps for Beam Strengthening
GFRP and CFRP layers were attached to the beams after 28 days of casting. The main steps for preparing the surface of beam are as follows: 1. Cleaning the concrete surface using an electrical hand blower to remove the debris on the concrete cover.  additional epoxy resin. The fibres orientation of the layer was parallel to the span of the beam (refer to Fig. 4). 6. For shear specimens, wrapping the concrete beam with one layer of U-shaped GFRP or CFRP layers using epoxy resin (refer to Fig. 5). 7. Rolling the FRP layers using a special laminating roller to ensure that the FRP is saturated in epoxy resin and there are no air voids exist between the fibres and concrete surface.

Testing Setup
Beam Specimens were tested in load control mode using a 1000 kN capacity hydraulic jack with a loading rate of 0.33 kN/s till failure. The load controlled mode was used with slow loading rate as it is suitable for LWC beams as the elastic response is largely governed in LWC due to its matrix. Above the elastic limit, cracks propagate, which reduces the stiffness of the LWC specimen. This results achieving the peak load and displacement almost at the end of elastic limit with bent-up load-deflection response. The testing setup is shown in Fig. 6. Specimens were instrumented to measure deflection, strain in concrete, strain in transverse reinforcement (stirrups), longitudinal reinforcement strains and crack width synchronised with the applied load. The crack width and deflection were measured using two linear variable displacement transducers (LVDT) 100 mm capacity and 0.001 mm accuracy, as shown in Figs. 7 and 8. The deflections were recorded using three LVDTs which were arranged to measure the deflection distribution. The steel reinforcement strains were measured using five strain gauges.   Table 3 Mix proportion of concrete.   Table 4 presents the failure load and cracking load for shear and flexural cracks. As expected, all the beams detailed as shear deficient were failed in shear before the flexural capacity was reached. While beams in Flexural group were failed in flexure after attaining their capacity. There was no slippage of flexural reinforcement during the testing. As shown in Table 4, the failure load is higher in Shear group and its corresponding control as compared to the failure load in Flexure group and in its control. This is due to the shear span to depth ratio which is smaller in shear deficient beams. It can also be noticed from Table 4 that strengthening for shear using CFRP resulted in higher loads compared to those of GFRP laminates. In addition, increasing the width of FRP strips for GFRP laminates is more significant than that for CFRP in increasing the failure loads. This is due to the better bonding of GFRP which plays an important role when sufficient width of laminate is provided.

Response of Shear Dominant Specimens
For Group 1, as mentioned in Table 4, the failure load, first shear cracking, and flexural cracking loads for beam BGS1 having 30 mm width of GFRP strip, were higher than those of the control specimen CBS by 13.7%, 57.1%, and 90%, respectively. Increasing the strip width to 50 mm (BGS2), resulted in raising the failure load, first shear cracking, and flexural cracking loads over those of the control specimen CBS by 25.7%, 100%, and 110%, respectively. Similarly, Beam BGS3 having 100 mm width of GFRP strip, increased these loads by 37%, 136%, and 140% as compared to control. For Group 2, as mentioned in Table 4, the failure load, first shear cracking, and flexural cracking loads for beam BCS1 having 30 mm width of CFRP strip, were higher than those of the control specimen CBS by 20%, 81.4%, and 120%, respectively. Increasing strips' widths to 50 mm (BCS2), resulted in raising the failure load, first shear cracking, and flexural cracking loads over those of the control specimen CBS by 29%, 128.6%, and 150%, respectively. Similarly, Beam BCS3 having 100 mm width of CFRP strip, increased these loads by 50%, 171.4%, and 200%, respectively. The increase in the width of strip of GFRP and CFRP played a dominant role in improving the loading capacity. Shear causes diagonal tension perpendicular to the direction of diagonal crack and increase in the width with fixed length enhanced the tensile capacity of GFRP and CFRP. Therefore, the results are incoherent with the response and propagation of diagonal crack.

Response of Flexural Dominant Specimens
For Group 3, as mentioned in Table 4, the failure load, first shear, and first flexural cracking loads for beam BGF1 having one-layer of GFRP, were higher than those of control specimen CBF by 11.5%, 5.3%, and 0.7%, respectively. Increasing the number of GFRP layers to two (BGF2), resulted in raising the failure load, first shear cracking, and flexural cracking loads over those of the control specimen CBF by 27%, 26.3%, and 19.3%, respectively. Similarly, Beam BGF3 having three layers of GFRP, increased these loads by 50%, 63.2%, and 48%, as compared to control.
For Group 4, as mentioned in Table 4, the failure load, first shear, and first flexural cracking loads for  beam BCF1 having one-layer of CFRP, were higher than those of control specimen CBF by 26.2%, 10.5%, and 6.9%, respectively. Increasing the number of CFRP layers to two (BCF2), resulted in raising the failure load, first shear cracking, and flexural cracking loads over those of the control specimen CBF by 50.5%, 36.8%, and 34.5%, respectively. A further increase of CFRP layers to three (BCF3), increased these loads by 71.5%, 105.3, and 86.2%, as compared to control. The gain in load carrying capacity after cracking is evident from the above discussion and at the same time there is a deflection-hardening response. Thus, loading capacity along with ductility is enhanced by the strengthening of LWC beam through GFRP and CFRP.

Crack Pattern
The crack pattern was marked to provide the necessary information for defining the failure mechanism of each specimen, as shown in Fig. 9. For beams strengthened for shear, the first diagonal crack suddenly developed at the mid-depth within the shear span. Diagonal cracks were observed parallel to the compression strut, and they propagated toward the loading region and supports (see Fig. 9). For all flexural specimens, the flexural cracks initiated on the tension side in the mid span of the beam, and the cracks propagated upward with increasing load. All beams strengthened for flexure exhibited flexural failure with pealing out of bottom FRP layers in the specimens BGF1, BGF2, and BCF2, as shown in Fig. 9. This is similar to the study conducted in which pealing out of layers of CFRP in some of their NWC concrete specimens strengthened with CFRP laminates for flexure was observed (Valivonis & Skuturna, 2007). However, the loading capacity and deflection-hardening response was observed in all beams strengthened for flexural failure. This infers that the peeling out of FRP layers do not hinder in attaining the ductile response of LWC beam strengthened through FRP.

Load-Deflection Response
The load-deflection curves for all the beams are shown in Fig. 10. The load-deflection was approximately linear from zero-load to crack initiation in all the beams. The  large reduction in stiffness caused by excessive cracking resulted in a relatively large increase in the deflection values. Closing to the failure load, the deflection continued to increase, even when the applied load was constant. Fig. 10 shows that the stiffness and load carrying capacity was increased by increasing the width of FRP strips for shear strengthening or increasing the number of FRP layers for flexural strengthening. Beam specimens BGS1, BGS2 and BGS3 were strengthened via surface attachment of U-shaped GFRP laminates with widths of 30, 50, and 100 mm, respectively. Fig. 10a shows that the load carrying capacity of specimens BGS1, BGS2 and BGS3 were higher than that of CBS control specimen; however, the deflection was lesser at the same load level for beams BGS1, BGS2 and BGS3 by approximately 11%, 18% and 28%, respectively. Beam specimens BCS1, BCS2 and BCS3 were strengthened via surface attachment of U-shaped CFRP laminates with widths of 30, 50, and 100 mm, respectively. Fig. 10a shows that the load carrying capacity of specimens BGS1, BGS2 and BGS3 were higher than that of CBS control specimen; however, the deflection was lesser at the same load level for beams BCS1, BCS2 and BCS3 by approximately 18%, 35% and 40%, respectively. It can be observed that there is an improvement in stiffness as a result of increasing the FRP strip width from 30 to 100 mm regardless the type of  FRP. However, the effect of increasing the width of CFRP strengthening strips on the stiffness of the studied beams is slightly higher than that for GFRP strips. To take maximum advantage of FRP strengthening, it is recommended to employ the maximum width of FRP for strengthening LWC beams for shear. Fig. 10b shows that beam specimens BGF1, BGF2, and BGF3 were strengthened by attaching one, two and three layers of GFRP laminates to the bottom surface of each specimen. The load carrying capacity of specimens of BGF1, BGF2 and BGF3 specimens were higher than that of CBF control specimen; however, the deflection was lesser at the same load level for beams BGF1, BGF2 and BGF3 by approximately 18%, 33% and 48%, respectively. Beam specimens BCF1, BCF2 and BCF3 were strengthened by attaching one, two and three layers of CFRP laminates to the bottom surface of each specimen. The load carrying capacity of specimens of BCF1, BCF2 and BCF3 specimens were higher than that of CBF control specimen; however, the deflection was lesser at the same load level for beams BCF1, BCF2 and BCF3 by approximately 30%, 40% and 52%, respectively. Based on these results, it is inferred that there is an improvement in stiffness as a result of increasing the FRP strengthening layers. However, the effect of increasing the number of CFRP layers on the stiffness is more significant than that for GFRP layers. As a result, this strengthening technique reduces or eliminates the rate of crack formation, delays initial cracking, reduces stiffness degradation with residual deflection, and extends the fatigue life of LWC beams. CFRP is the greatest alternative for strengthening LWC beams.

Crack Width
The crack width was measured using LVDTs, as shown in Fig. 11. By comparing the crack widths of the tested beams at the same load level, it was observed that the crack width was decreased with increasing the width of strips or the number of strengthening layers.
For Shear strengthened beams, the crack widths of beam specimens BGS1, BGS2 and BGS3 were less than that of CBS control specimen at the same load by approximately 26%, 38% and 45%, respectively. Similarly, the crack widths of BCS1, BCS2 and BCS3 specimens were less than that of CBS control specimen at the same load level by approximately 32%, 51% and 58%, respectively. For Flexural strengthened beams, the crack widths of BGF1, BGF2 and BGF3 specimens were less than that of CBF control specimen at the same load level by approximately 9%, 18% and 37%, respectively. Similarly, the crack widths of BCF1, BCF2 and BCF3 specimens were less than that of CBF control specimen at the same load level by approximately 24%, 35% and 48%, respectively.  et al. Int J Concr Struct Mater (2022) 16:59 These results also show that the crack width was decreased due to the increase in the overall beam stiffness as a result of increasing the width of FRP strips or increasing the number of FRP strengthening layers. It can also be observed that Shear strengthened beams with CFRP laminates generally had less crack width as compared to the beams strengthened using GFRP laminates. The crack width was almost zero in the elastic range of LWC beams strengthened through FRP, as shown in Fig. 11, this is important as reducing the crack width also limit the exposure of reinforcement to the deleterious substances, such as chloride and sulphates. The reduction in crack width is also depending on the steel strain which is directly proportional with the crack width. The effect on the steel strain through FRP a is discussed as under: Fig. 12 shows the strain at steel level measured through electrical strain gauges mounted on the beam longitudinal reinforcement and stirrups. Fig. 12a shows the load vs strain at longitudinal steel level for shear strengthened beams. It is evident that the strain was increased after strengthening and it depends upon the widths of strengthening strips. The strains at failure were below the strain at yielding point of steel. This shows that the shear strengthened beams were failed on the higher load, but the mode of failure was compression rather than yielding. Strengthening with CFRP has a higher effect on the steel strains compared Page 13 of 20 Montaser et al. Int J Concr Struct Mater (2022) 16:59 with strengthening with GFRP. In addition, the effect of increasing the widths of CFRP strengthening strips on the longitudinal steel strains was more significant than for GFRP strips. Fig. 12b shows the load vs strain at longitudinal steel level for flexural strengthened beams. It is evident that the strain was increased after strengthening and it depends upon the number of layers of laminates. The strains at failure were higher than the strain at yielding point of steel. This shows that the flexural strengthened beams were failed on the higher load with the mode of failure was tension. Strengthening with CFRP has a higher effect on the steel strains compared with strengthening with GFRP. In addition, the effect of increasing the number of CFRP layers on the longitudinal steel strains was more significant than for GFRP layers.

Strain at Longitudinal Reinforcement Level
Based on the preceding discussion, it is clear that FRP strengthening does not change the mode of failure; rather, the increased strain, number of fractures, and loading capacity indicate that LWC beams are exhibiting symptoms prior to failure. This is especially crucial for shear deficient LWC beams to show signs of failure before approaching the brittle failure phase. Page 14 of 20 Montaser et al. Int J Concr Struct Mater (2022) 16:59 that of CBS control specimens at the same load level by approximately 7%, 11%, and 18%, respectively, for beams strengthened for shear. Furthermore, at the same load level, the steel strains of BCS1, BCS2, and BCS3 specimens were roughly 46%, 65%, and 71% lower than the CBS control specimen. It's worth noting that the reduction in stirrup strain caused by CFRP strip stiffening is nearly 7 times more than that caused by GFRP strip stiffening. For GFRP laminates; however, increasing the strip width from 30 to 100 mm had a greater impact. Fig. 13b shows that the steel strains of the stirrups of BGF1, BGF2, and BGF3 specimens were lower than those of the CBF control specimen at the same load level by about 16%, 25%, and 43%, respectively, for beams strengthened for flexure. The steel strains of the BCF1, BCF2, and BCF3 stirrups, on the other hand, were roughly 36%, 65%, and 84% lower than the CBF control specimen at the same load level. The difference between the two FRP types on the stirrup's strains is less than the difference between the other examined parameters in the preceding sections, as can be seen from the above values. It may conclude that the number of layers is more effective for GFRP laminates as compared to CFRP. However, all beams strengthened through GFRP and CFRP demonstrate deflection-hardening, reduction in crack width, and longitudinal steel strains.

Comparison of Experimental and Analytical Results
In the following sections, the predictive equations specified in design codes were used and compared with the ultimate load capacity of beams strengthened with FRP laminates. These equations are primarily developed for normal weight concrete and comparison of the predictive loads with the lightweight concrete beams was performed in this study. The idea is to highlights the shortcomings in  Page 15 of 20 Montaser et al. Int J Concr Struct Mater (2022) 16:59 the existing equations and check whether these can serve for designing LWC beams retrofitted by GFRP and CFRP materials.

Specimens Strengthened for Shear
To conveniently investigate the performance of LWC beams shear-strengthened with FRP composites, the following simple superposition approach is adopted to evaluate shear capacity V u of the shear-strengthened beams: where shear resistance of the concrete and longitudinal steel reinforcements V c and shear capacity of transverse steel reinforcements V s can be obtained from the test results of control beams or calculated via various existing design equations for RC structures. The accurate prediction of FRP shear contribution V f is a key issue for the development of design guidelines. (1) Three design codes for NWC, namely, ACI 440. 2R-17 (ACI, 2017), the Egyptian Code of Practice (ECP, 2005), and International Federation for Structural Concrete fIB- TG9.3 (FIB, 2001) were used to determine the shear capacity to calibrate the design equations in these resources with the experimental results in this study.
In (ECP, 2005), the nominal shear strength of the FRP shear reinforcement is given by Spacing S f is less than either d/4 or 200 mm, whichever is smaller; this stipulation is also true for the width of the (2) Page 16 of 20 Montaser et al. Int J Concr Struct Mater (2022) 16:59 FRP composites measured in the direction of the member axis.
In (ACI, 2017), the shear contribution of the FRP shear reinforcement is given by where The tensile stress in the FRP shear reinforcement at nominal strength is directly proportional to the level of strain that can develop in the FRP shear reinforcement at nominal strength: The effective strain in the FRP reinforcement is given by where bond-reduction coefficient k v is given by The bond-reduction coefficient relies on two modification factors, k 1 and k 2 , which account for the concrete strength and wrapping scheme, respectively. These modification factors are given by where f ′ c is the compressive strength of lightweight concrete, and where active bond length Le is the length over which most of the bond stresses is maintained; this length is given by In fib-TG9.3 (Fib, 2001), 2001, the shear capacity of a strengthened element is calculated according to the EC2 format as follows: where FRP contribution to the shear capacity V fd is given by 14a shows a comparison between the experimental results and the three analytical models described above. Equations (2-5) (ECP, 2005) were used to compute q fu , Eqs. (6-10) (ACI, 2017)) were used to compute V f , and Eqs. 11, 12a, 12b (FIB, 2001) were used to compute V fd . The failure loads of each test beam specimen were predicted using the above design codes and compared with the measured experimental values. Since, these codes are not calibrated for the LWC beam, there will be a deviation of analytical models from experiment. This evident in Fig. 14. It can be seen from Fig. 14a that all the analytical models underestimate the prediction of failure loads compared to their counterparts obtained experimentally to different degrees. Fig. 14b presents the effect of the width of the GFRP and CFRP strips on the analytical results. It was noticed that the ACI 440.2R-17 (ACI, 2017) code is more compatible with the experimental results, while the ECP 208-2005 (ECP, 2005), fIB-TG9.3 (FIB, 2001) codes are more conservative.

Specimens Strengthened for Flexure
In ECP 208-2005208- (ECP, 2005, determining the strain level in the FRP reinforcement at the ultimate moment of the cross section is important. The value of the strain permitted in FRP laminates at section failure ( ε fe ) is governed by the strain level developed in the FRP at the point at which concrete crushes, the FRP ruptures, or the FRP debonds from the substrate. The value of this strain is calculated by where And CE equals to 0.95.
The calculation procedure used to determine the ultimate flexural strength of the cross sections strengthened with externally bonded FRPs should satisfy the compatibility and equilibrium conditions and consider the governing failure mode. Such a procedure requires a trial-and-error method to ensure the compatibility and equilibrium requirements are satisfied. The values of the strains and stresses that develop in the reinforcing steel (12b) are calculated by the following equations using a trialand-error method: The depth of the equivalent rectangular stress block of the compressed concrete is calculated by The ultimate flexural moment is calculated by The ultimate load Pu for two-point loading is calculated by where X is the distance between the supports and the loading point in mm.In ACI 440.2R-17 (ACI, 2017), according to the strain distribution, for any assumed depth to the neutral axis c, strain level in the FRP ε f can be computed using the following: Stress level in the FRP f f can be calculated from the strain level in the FRP, assuming elastic behaviour: and strain level in steel under tension ε s can be calculated by  Page 18 of 20 Montaser et al. Int J Concr Struct Mater (2022) 16:59 In addition, for steel under compression, the strain level can be calculated by Stress level in steel f s is calculated from the strain level in steel, assuming elastic-plastic behaviour: Internal force equilibrium may be checked using where β 1 = 0.8 for concrete with a compressive strength of 35 MPa. Actual neutral axis depth c is found by simultaneously satisfying Eqs. 21, 24 and 26, thereby establishing the internal force equilibrium and strain compatibility. The nominal flexural strength of the section with FRP external reinforcement Mu can be computed using where = 0.85. Ultimate load Pu for two-point loading is calculated by In fib-TG9.3 (FIB, 2001), according to the steel yielding/ concrete crushing failure mode, which is the most desirable mode, failure of the critical cross section occurs by the tensile steel reinforcement yielding followed by concrete crushing, while the FRP remains intact. The design bending moment of the strengthened cross section is calculated based on RC design principles. First, neutral axis depth x is calculated from the strain compatibility and internal force equilibrium, and then the design moment is determined based on the moment equilibrium. The analysis should consider that the RC element may not be fully unloaded when strengthening occurs, and hence, initial strain ε• in the extreme tensile fibre should be considered. The design bending moment capacity can be calculated using the following approach.
Mu where δ G = 0.4.Ultimate load Pu for two-point loading is calculated by Fig. 14c shows a comparison between the experimental results and the three analytical models obtained from the design codes. Equations (13-20) (ECP 208-2005) (ECP, 2005), Eqs. 21-28 ACI 440.2R-17 (ACI, 2017), and Eqs. 29-33 (fIB-TG 9.3) (FIB, 2001) were used to compute the flexural moment and failure loads of the strengthened specimens. The failure loads of the test beam specimens were predicted by the design codes for NWC and compared with the measured values for LWC. While Fig. 14d shows the accuracy of the analytical models when taking the number of layers into consideration for GFRP and CFRP vs the experimental results. It can be noticed from Fig. 14c, d that the ACI 440.2R-17 (ACI, 2017), FIB-TG9.3 (FIB, 2001) codes are more compatible with the experimental results, while the ECP 208-2005 code (ECP, 2005) is more conservative in predicting the ultimate load and it is not accurate in predicting the failure load when taking the number of FRP layers into account.

Conclusions
The effect of strengthening of LWC beams containing polystyrene beads using GFRP and CFRP laminates on the flexural and shear behaviour of studied beams was evaluated experimentally. The studied parameters were varying width of FRP wrapping for shear and number of FRP layers for flexure. In addition, the equations (29) 0.85ψf cd bx + A s2 E s ε s2 = A s1 f yd + A f E fu ε f ,