Direct Synthesis of Nanocrystalline Silver from the Reaction Between Silver Carboxylates and n-Trioctylphosphine

Neat n-Trioctylphosphine (TOP) has been used for the first ever time for reduction of silver nitrate and silver carboxylates (citrate, oleate, and myristate) under mild thermal reaction conditions. UV-visible absorption measurements of re-dispersible silver particles that were obtained by reduction of silver myristrate (product-IV) and silver nitrate (product-I) showed surface plasmon resonance absorption peak at 400 nm. The powder XRD pattern of fcc zero-valent silver resulted in diameters in the range of about 25–30 nm. TEM analysis showed particle diameter similar to that was observed by the XRD. FTIR spectroscopy revealed that the organics from the carboxylate group are retained by the nano-particles in case of product-IV however, presence of TOP is observed in product-I. It is found that when silver nitrate is reduced by TOP, spherical silver nano-particles with poor re-dispersity are formed but extended heating results in formation of long silver rods of micrometer size however, the re-dispersible nano-particles are easily formed when silver carboxylates are reduced by TOP.