Fabrication of ECM Mimicking Bioactive Scaffold: A Regenerative Approach for MSC Mediated Applications

Biomaterials are feasible resources that aids to replace damaged structures in our bodies. The most biologically active flora is Aloe vera which has many bioactive compounds that are anti-inflammatory, antimicrobial, and have ECM mimicking protein content which helps in the healing of wounds and also acts as an ECM factor for stem cell homing and differentiation. The Aloe vera containing 10 w/v of gelatin was lyophilized. Scaffolds had sharper morphology, greater hydrophilic properties, and a Young's modulus of 6.28 MPa and 15.9 MPa of higher tensile strength are desirable. In tissue engineering and regenerative medicine, biologically active scaffolds have been producing hopeful outcomes in both restoration and replacement, respectively. The objective of the present investigation is to test the idea that incorporating gelatin to Aloe vera scaffolds might enhance their structure, good biocompatibility, and possibly even bioactivity. The SEM picture of the composite scaffold revealed pore walls. The scaffolds had linked pores with diameters ranging from 93 to 296 μm. Aloe vera and the matrix interact well, according to the FTIR study, which could lead to a reduction in the amount of water-binding sites and a reduction in the material's ability to absorb water. Aloe vera with 10% gelatin (AV/G) scaffold was investigated for different biological reactions of human gingival tissue mesenchymal stem cells (MSCs) in terms of cell proliferation, morphology, and cell migration. The results demonstrated the potential of the AV/G scaffold as a biomaterial that offers new insight in the field of tissue engineering.


Introduction
The field of regenerative medicine encompasses tissue engineering and stem cell technology. Organ regeneration is significantly impacted by the biomedical-related research areas of tissue engineering and regenerative medicine (TERM). It incorporates clinical research along with concepts from fields like biotechnology, mechanics, cell biology, and materials science. By constructing an environment that promotes cell growth and proliferation, tissue engineering is aimed at replacing and repairing damaged tissues [1] and generation of new tissue or organ which stimulation of the extracellular matrix [1,2]. Scaffolds are made to encourage cellbiomaterial interaction, cell attachment, proliferation, and motility; and also make it easier to transfer mass, nutrition, and regulatory factors so that cells can survive, proliferate, and differentiate; further, allow for controlled degradation that simulates the pace of tissue regeneration under the culture conditions of interest; and have acceptable mechanical characteristics like tensile strength, porosity, and elasticity which are required to provide temporary structural strength and better spatial reorganization of the tissue until the formation of complete tissue to provoke a low level of toxicity or inflammation in the animal model [3]. Unlike simple injection of cells, scaffolds have the benefit of limiting cell loss and enabling cell transfer into a defective spot [4]. Natural biomaterials can be fabricated to offer a similar biological environment mimicking extracellular matrix (ECM) to provide better interaction with cells and for replacement of normal tissue without inducing inflammation. Scaffolds made with natural biomaterials have bioactive compounds which also help in efficient treatment and bioengineering for organ replacement. Biomaterials replicate physicochemical and biological properties and provide native ECM tissue replacement [5].
According to the World Health Organization (WHO), the most physiologically active flora is Aloe vera from the Liliaceae family [6]. There are 75 components that are bioactive in it. The glycoproteins accelerate cell proliferation to aid in the healing of wounds. It also has aloe-emodin which has antiviral, antibacterial, and anticancer properties [7]. Monosaccharides found in it are said to have excellent anti-inflammatory, anticancer, antiallergic, antimicrobial, and antitumor capabilities. Vital minerals like calcium, chromium, copper, iron, selenium, magnesium, manganese, phosphorus, chlorine, potassium, sodium, and zinc are required for metabolism and are crucial for the enzymes' proper operation [7]. There are sixteen different enzymes found in Aloe vera, which are frequently used as antibacterial, antifungal, antiviral, anti-inflammatory, and analgesic agents (bradykinase) for purposes [7]. Topographically, it has been observed that characteristics including holes, ridges, groves, fibres, nodes, or a mix of these can affect how cells behave [8]. Gelatin is a hydrolyzed version of collagen. Bovine and porcine skin serves as the primary source of collagen and gelatin [9]. Gelatin may form polyion complexes and is a biodegradable and biocompatible polymer. Gelatin is frequently utilised for medication and cell delivery in tissue engineering applications to target many tissues, including bone, cartilage, and skin, as a result of these qualities [10,11].
The ability to self-renew, proliferate, and differentiate into multiple cell lineages are all characteristics of stem cells. Mesenchymal stem cells (MSCs) have demonstrated considerable potential in numerous animal studies and clinical trials as regenerative medicine. Signaling molecules, cell-to-cell contact, and stem cells' interactions with their surrounding cells to form an extracellular matrix (ECM) make up a niche [12]. Biomaterials, which act as artificial ECM, mimic the biological and mechanical properties of the native ECM found in tissues throughout the body [13]. Scaffolds with bioactive compounds can home a microenvironment that defines the fate of the cells. Stem cells can be appropriately differentiated depending on the niche when implanted with scaffold at a specific site for the reconstruction of specific tissues. In our current study, we have fabricated Aloe vera/gelatin (AV/10% gel) scaffold. The scaffold was further characterized for its physicochemical properties. Ethical clearance was obtained from the Department of Periodontology at Saveetha Dental College (SRB/SDMS15PER1). Stem cells from the patient's human gingival tissue were collected, isolated, and characterized using flow cytometry and confocal studies. Alkaline phosphatase and oil red O staining were used to confirm the osteogenic and adipogenic differentiation of HG Stem cells. We have employed Stem cells on a scaffold to check biocompatability. However, reconstruction in combination with stem cell and tissue engineering approaches will be a new insight to be used for tissue repair and restoration, and the ultimate outcomes will be patient safety and satisfaction.
2.1. Scaffold Preparation. The Aloe vera leaf was cleaned and wiped with isopropyl alcohol. Then, the spines and outer layer of the Aloe vera leaf were removed. The Aloe vera gel was extracted from the Aloe vera leaf. Then, the aloe gel was blended with ethanol (for 20 ml of Aloe vera gel, 2 ml of ethanol). Then, a 10% w/v of gelatin was added to Aloe vera to make the gel. The gelatin and Aloe vera gel were mixed using a magnetic stirrer at 40°C. The gel was poured into Petri plates and stored at -80°C.

Lyophilization (Freeze Drying).
The Aloe vera/gelatin in Petri plates were placed at -80°C overnight before freezedrying. Then, the Petri plates were placed in the lyophilizer at -143°C for 4 hours. After freeze-drying scaffolds, were obtained.

Mesenchymal Stem Cell Isolation from Human Gingival
Tissue. Gingival tissue was obtained either during the crown lengthening procedure or an operculectomy in patients who fall in the age group of 15-35 years old of either gender. The site where sampling was obtained was assessed before sampling to check for any clinical signs of inflammation. Any 2 Stem Cells International supragingival plaque which was present was removed by thorough scaling. Local anaesthesia containing 2% lidocaine with 1: 80,000 concentration of adrenaline was given to the site from where the sample was obtained. Using a scalpel number 12 or 15 was used to excise the tissue from the operculectomy site and for crown lengthening, respectively. The obtained tissue was rinsed with saline to remove any blood clots present in the tissue. Any loose fibrin tags were removed with either a scalpel or scissors. The tissue was then immediately placed in a solution containing phosphate buffer saline (PBS) and an antibiotic containing 100 U ml −1 penicillin, 100 μg/ml, streptomycin, 100 μg/ml amphotericin B, with a ratio of 1 : 1. The medium is then transported to the laboratory for further culturing. After obtaining the tissue, the tissue was placed in a Petri plate with sterile PBS solution (without Ca and Mg) along with an antibiotic and antimycotic solution containing 100 U/ml penicillin, 100 μg/ml, streptomycin, 100 μg/ml, and amphotericin B. The tissue was washed thrice with 1X PBS to remove any debris or blood clots present on the tissue surface. It was then gently scraped off with a surgical blade to remove any dead cells and minced into 1 mm pieces with the help of a surgical blade and forceps. Tissues were re-suspended and incubated in 0.3 U of collagenase type IV enzyme for 40 minutes in a CO 2 incubator at 5% CO 2 , 95% humidity, and 37°C. After the incubation period, it was centrifuged at 1000 rpm at 4°C for 10 minutes. The supernatant was discarded, and the pellet was resuspended with 1 ml of 20% serum DMEM: F12 media.

Characterization of Mesenchymal Stem Cells
(a) Adipogenic differentiation: cells were grown in DMEM/F12 media with 10% serum along with the following reagents for adipogenic differentiation: 1 μM dexamethasone, 500 μM 3-isobutyl-1-methylxanthine (IBMX), insulin-transferrin-selenium (ITS), 60 μM indomethacin, and 5 g/ml insulin as a supplemental factor. On the day 14 . Electron microscopy is a precise tool that can precisely photograph bionanostructures, monitor biomaterials within nanomaterials, assess physical attributes, and even ascertain composition. SEM micrographs are helpful for analysing the structure of the surface because they produce three-dimensional images of a composite scaffold when they photograph a surface with an electron beam. Porosity-containing pore networks tying scaffold interiors to surface holes were observed using SEM images.

Fourier Transform-Infrared Spectroscopy (FTIR).
FTIR is a method of analysis used to distinguish between organic and, in certain situations, inorganic materials. This method plots the wavelength vs. the amount of infrared radiation that the sample material absorbs. Molecular parts and structures are recognized through infrared absorption bands. Plots of intensity vs. wavenumber are typically used to illustrate FTIR spectra (in cm -1 ). The wavelength's reciprocal, wavenumber, is the wavelength. Plotting the intensity as a percentage of light transmittance or absorption at each wavenumber is possible.

Differential Scanning Calorimeter (DSC).
A thermal analysis tool called a DSC measures temperature and heat flow in relation to material transitions as a function of temperature and time. It is used to measure a number of the composite scaffold's distinguishing characteristics. This method allows for the observation of fusion, crystallisation, and glass transition temperatures (Tg). It utilised to examine the chemical reactions and stability of oxidation in the samples and utilised for researching liquid crystals. The modest energy changes that take place as matter transforms from a solid to liquid crystals and from a liquid crystal to an isotropic liquid can be seen via DSC.

X-Ray Diffraction (XRD).
Using an X-ray diffractometer (Rigaku, model Mini flex600, Japan), with a step angle of 3 Stem Cells International 2°C/min, X-ray patterns of the gelatin-based scaffold were recorded over a range of 5-60°.

Contact
Angle. The contact angle is the angle traditionally measured through the liquid when a liquid-vapour contact meets a solid surface. There is a specific equilibrium contact angle for every system comprising a given solid, liquid, and vapour at a given temperature and pressure. It measures the wettability of a solid surface area.
2.5.6. Tensile Strength. The tensile test is one of the easiest and most commonly performed mechanical tests. Material characteristics can be ascertained by measuring the amount of force needed to stretch a specimen to its breaking point. The maximum stress that a composite structure can bear while being stretched or pulled before breaking is how ultimate tensile strength is calculated.
2.5.7. Confocal Microscopy. Confocal microscopy has shown advantages for visualization of the external and internal surfaces of scaffold. Pore size and shape varied between random and aligned scaffolds. Fiber packing density, fiber alignment, and the three-dimensional view can also be analyzed. Aloe vera has an autofluorescence (green).

Biological Characterization of Scaffold
2.6.1. MTT Assay. 5 × 10 3 cells/well were plated on the scaffold in a 96-well plate. After 24 hours, a MTT assay was performed. Another plate was also seeded and incubated for 72 hours. On the day of the MTT assay, media was removed and 100 μl of 1X PBS and 10 μl of MTT were added to each well. Incubate it for 3 hours in the dark at 37°C incubator. After the incubation, MTT and PBS were removed, and 100 μl of DMSO was provided with each well, followed by a 15-minute dark incubation. This was read at 492 nm and 650 nm in the Tecan Spark multimode reader, and the graph was plotted.
2.6.2. Swelling Ratio. The swelling capacity of a scaffold is determined by the amount of liquid that can be absorbed. Swelling ratio formula Wt is the weight of the wet scaffold; Wo is the weight of the initial scaffold.
The absorption capacity of the scaffold was determined using distilled water, Dulbecco's modified Eagle's medium, and phosphate buffer saline at 37°C, pH 7.4.

Analysis of Amino Acids Using Reverse-Phase HPLC.
A reverse-phase liquid chromatographic method for the separation and relative quantification of PITC-derivatized amino acids was carried out based on the method described by Hariharan et al. [14]. Briefly, 100 μL of Aloe vera gel was deproteinized by mixing with acetonitrile (lysate:acetonitrile (60 : 40)), vortexed, and centrifuged for 1 min at 9000 rpm. After vacuum centrifugal drying of the 100 μl of the supernatant, 10 μl of methanol were added. Vacuum drying is followed by combining a solution of water : triethylamine (2 : 1 : 1 v/v). The samples that had been vacuum evaporated were treated with 20 μl of ethanol, water, triethylamine, and PITC (7 : 1 : 1:1 v/v), mixed, and incubated for 10 minutes before being vacuum dried. Prior to HPLC injection, the samples were mixed in 750 μl of sodium acetate (pH 7.5)acetonitrile (98 : 2 v/v) solution and filtered with 0.2 μm filter. An Agilent 1200 infinite HPLC system with autosample injection was used for HPLC analysis. A C18 column (150 × 4:6 mm I.D., 3 m) (Inertsil-ODS-2) thermostated at 41°C and a straightforward multistep linear gradient of two solvents were used for the HPLC separation. Wateracetonitrile (40 : 60 v/v) was solvent B; 0.05 M sodium acetate (pH 5.1)-acetonitrile (98 : 2 v/v) served as solvent A. A UV detector set to 254 nm was used to detect the separated PITC amino acid derivatives using a 20 μl injection volume. To verify the process, a standard run using the amino acid standard (Sigma) was carried out. The relative quantification analysis was performed utilising the known quantity of norleucine and the area under curve (AUC) values of the corresponding amino acid peaks.
2.6.4. Confocal Studies. 2 × 10 4 MSCs were seeded onto the Aloe vera/10% gelatin scaffold in a 12-well plate and incubated for 24 hours. The cells were washed three times with 1X PBS after the medium was removed. For 20 minutes at 4°C, 4% paraformaldehyde was used to fix the cells to the scaffold. Paraformaldehyde was removed, and the cells were rinsed thrice with 1X PBS. DAPI and F-actin-conjugated phalloidin (red) were used to stain the cells (blue). The cells on the scaffold were viewed under confocal microscopy with muted green fluorescence to avoid background disturbance.
2.6.5. Scratch Assay. A scratch assay was performed to analyze the wound healing property. 2 × 10 5 cells/well of human gingival stem cell-like cells were seeded onto six-well culture plates in a CO 2 incubator at 5% CO 2 and 95% humidity at 37°C. Cells were left for 80% confluency. The monolayer of MSCs was scratched using a 200 μl tip to create a wound. The detached cells were removed by washing with 1X PBS and 20% serum DMEM: F12 media with AV/G for 48 h, along with a control group for 48 h. After incubation, the wells were washed and fixed in 4% paraformaldehyde. Photographs were taken using an inverted microscope (Euromex, The Netherlands).

Statistical Analysis.
All the results were shown as the mean ± SD. A statistically significant difference was determined by the student's t test. A p value < 0.05 was regarded as statistically significant.

Results
Reconnoitering cutting-edge technology solutions to enhance healthcare for a diseased population, still remains to be a global challenge. One innovative idea among several that have been developed into a promising strategy to fulfill patients' future requirements is tissue engineering and regenerative medicine (TERM). It is now possible thanks to the development of tissue engineering and 4 Stem Cells International regenerative medicine (TERM). By combining cells, scaffolds, and growth factors, tissue engineering can restore or replace damaged tissues. Although regenerative medicine integrates immunomodulation, gene therapy, and cell-based therapy to promote in vivo organ regeneration, TERM is aimed at establishing three-dimensional (3D) cells or organoids in a biomaterial scaffold structure, which mimics a structural and functionality of a live tissue or organ that can be used to regenerate and repair damaged tissue or organs. The bioscaffold must be able to sustain gaseous exchange, the movement of nutrients and waste, and cell growth as a minimum need.

Scaffold Fabrication and Isolation and Differentiation of
Human Gingival Tissue Stem Cells. Aloe vera gelatin scaffold was fabricated at a 10% concentration of gelatin and further characterized physicochemically. Figure 1 shows fabricated AV/G (Aloe vera/10% gelatin) scaffold. Human gingival tissue (Figure 1(b)) from patient dental samples is collected from Saveetha Dental College. Gingival tissue was processed, and stem cell-like cells were obtained from 14-21 days of culture in DMEM: F12 with 20% FBS. Spindle-shaped, elongated stem cell-like cells outgrow from the Human gingival tissue was observed in Figures 1(a) and 1(b)). Further, to characterize these cells to be stem cells, differentiation ability of the cells was analyzed. Figure 1(d) shows the differentiation of human gingival stem cells to adipocytes and analyzed using oil red O staining. Figure 1

Physical
Characterization of Scaffold. SEM images of the AV/G scaffold revealed that the AV/G scaffold was found to have a porous surface with random orientation. The SEM images (Figure 3(a)) of the freeze-dried AV/G scaffold showed minimal porosity at 1500 × , 4500 × , and 5000 × magnifications. FTIR (Fourier transform infrared spectroscopy) has been used to validate and define the components in a biological composite system containing two or more components of the biomaterials Aloe vera and gelatin. Figure 3(b) reveals typical band assignments for gelatin where amide A (N-H stretching vibration) was observed at 3300 cm -1 , and the band absorbed by Aloe vera was 3314 cm −1 . Further, amide I was expressed at the range of 1633-1639 cm -1 , amide II was observed at the range of 1546-1551 cm -1 , and amide III was observed in the range of 1239-1241 cm -1 . The absorption peak observed around 1450 cm -1 for carboxyl -COOH stretch bands and C-O stretching of polysaccharides of Aloe vera was observed at 1079 cm -1 .
Observations of DSC patterns reveal the characteristic endothermic peaks representing the temperature of dehydration (T D ) and enthalpy of dehydration (ΔH D ) of components of biomaterial. Figure 3(b) shows the AV/G scaffold with T D value of 139.75°C and ΔH D of -26.40 W/g. CHNS was also estimated in (Figure 4(a)) and AV/G was found to have C% = 29:983, H% = 11:732, N% = 10:582, S% = 60:730 , and O 2 % = 0. In Figure 4(b), graph represents X-ray diffraction of the AV/G scaffold. A huge amorphous peak was observed in the range of 2θ = 20°−40°, exhibiting compatibility. Figure 5(a) shows the representation of functional groups CH 3 , CH 2 , Amide I (CO), Amide II δ(NH)+V(C-N), Amide III δ(NH) + V(C-N), Amide A (NH), and Amide B (CH 2 ). The contact angle of Aloe vera with gelatin scaffold was found to be 37.31°, which shows wettability ( Figure 5(b)), representing a good characteristic scaffold. The AV/G scaffold's tensile strength (MPa) was found to be 23.2, and an elongation break at 8.58 shows better tensile stress. Confocal images of the AV/G scaffold were observed due to the autofluorescence of Aloe vera. The 3D image and thickness of the scaffold were viewed under a confocal microscope (Figures 6(a) and 6(b)) at 40 × magnification and were found to be about 60-80 μm.

Biological Characterization of Scaffold.
The biological characterization of the scaffold determines its compatibility and degradability. A MTT assay was performed to study (Figure 7(a)) the biocompatibility of AV/G and analyzed its viability and proliferation for 3 consecutive days. The proliferation rate of MSCs increases from days 1 to 3 which also shows the biocompatibility and viability of the scaffold. The swelling ratio of the freeze-dried AV/G scaffolds prepared showed a high degree of swelling (Figure 7(b)) upon placement in DMEM media at 37°C. It was also seen that the scaffold increases in ratio with 1X PBS, DMEM, and distilled water, respectively. The hydrophilicity of a scaffold is favorable for cell adhesion and growth. HPLC studies reveal amino acids in the protein content of 100 μL of AV/G scaffold. This was deproteinized using 60% acetonitrile and PITC-derivatized for amino acid analysis using RP-HPLC. The AUC values (Figures 8(a) and 8(b)) of each analyte were converted to concentration (ng/μL) using norleucine as a control. MSCs were cultured on the AV/G scaffold and treated with F-actin-conjugated phalloidin (red), and the nucleus was stained with DAPI (blue). HPLC results ( Figure 9) showed amino acid concentrations in the Aloe vera with 10% gelatin gel. Figure 10(a) shows MSCs at 24 hours, and Figure 10(b) shows MSCs at 72 hours that shows viability and proliferation. A wound healing assay was performed by creating a scratch, in which Figure 11 images show cell migration and gradual closure of the wound in MSCs with scaffold compared to control (MSCs without scaffold) was observed after 48 h at 10 × magnification.

Discussion
Tissue engineering involves the principles of life sciences and engineering biomaterials for scaffold construction towards the development of biological substitutes which 5 Stem Cells International mimic, restore, maintain, and improve the function of an organ. It combines cells, materials, and appropriate biochemical elements to enhance or replace biological function. Fabrication of biologically active scaffolds has been generating promising results in tissue engineering and regenerative medicine. In 3D organ regeneration, a scaffold's topography and porosity are crucial factors [15]. In this study, human gingival MSCs were employed to design a tissue construct employing a three-dimensional AV/G scaffold for cellular adhesion, growth, and multiplication. Prior to this, Aloe vera gel with various concentrations of gelatin was lyophilized, and Aloe vera with 10% gelatin was optimized  Stem Cells International (Figure 1(a)). Lyophilization of Aloe vera with a gelatin (biopolymer) blend was studied for its functional benefits such as tensile properties, stability, porosity, and microstructural characteristics. Scanning electron microscopic (SEM) evaluation revealed that the AV/G scaffold was found to have a porous surface with random orientation. The SEM images of freeze-dried AV/G scaffold showed minimal porosity at 1500×, 4500×, and 5000× magnification (Figure 3(a)). These porous scaffolds have desirable characteristics for the purpose of cell integration which was similar to the one observed by Hassan and Peppas [16,17]. The curve indicates a variation in the swelling of the scaffolds. Mesenchymal stem cells were isolated from human gingival tissue gives similar yield to any adult tissue stem cells. Isolation of mesenchymal stem cells derived from human gingival tissue (Figure 1(b) (Figure 1(c)). MSCs were also characterized by differentiating them to osteocytes and adipocytes. Differentiated adipocyte and osteocyte from human gingival-derived mesenchymal stem cells were analyzed by alkaline phosphatase staining to determine osteocyte with the deposition of pink colour due to phosphate  (Figures 1(d) and 1(e)). The images were viewed and imaged at 10× magnification under phase contrast microscopy. These cells were characterized in a flow cytometer, and 96.04% of cells were shown CD73 positive, 97.54% showed CD90 positive, and CD105 showed 96.77% of positive cells (Figure 2). Our results corre-late with Zuk et al.'s [18] research, which described the separation and description of adipose-derived human stem cells. The differentiation of these cells into the adipogenic and osteogenic lineages was seen. The analysis of the cell surface markers CD73, CD90, and CD105 showed that the cell population expresses the known immnophenotype of MSC as reported by Lozito et al. [19]. The differentiation of MSCs into  adipocyte (fat-containing cells) and osteocyte (bone cells) was analyzed by alkaline phosphatase staining that stains calcium and the phosphate deposited in the nucleus and oil red O staining that stains the oil drops inside the cells, respectively. So as to evaluate the property of MSCs, we characterized it with markers and subjected them to differentiation studies, and our result was similar to Vazin et al. [20]. Fourier transform infrared spectroscopy ( Figure 5(b)) could be used as an effective method to define each component in a biomaterial containing Aloe vera and gelatin material. The position of the peaks, width, and intensity of the spectral band are sensitive to chemical conformational changes in molecules. The typical band reported in the literature assigned for gelatin is amide A(N-H stretching vibration) observed at around 3300 cm -1 which is similar to the results of the band absorbed by Aloe vera at 3314 cm −1 from the study conducted by Jithendran et al. [21]. Amide I was observed in the range of 1633-1639 cm -1 , amide II was found at 1546-1551 cm -1 , and amide III was in the range of 1239-1241 cm -1 . Additional bands seen at 1450 cm -1 are attributed to identical -COO groups identified in the literature. The C-O stretching of Aloe vera polysaccharides is what causes the absorption peak to be noticed at 1079 cm -1 . The carboxyl -COOH stretching bands are represented by the peaks in the spectra that are seen at approximately 1450 cm -1 . Functional groups and FTIR were used to estimate CHNS (Figure 5(a)). The presence of a -helix with -turns and a distinctive absorption band indicating the peptide bonds (-CONH-) for amides I, II, and III are confirmed by observation of the spectral band. The N-H bonds' stretching vibration is what causes the peak of amide A. The stretching vibration of the C-O bonds is what gives amide I its peak. The amide II band is caused by N-H bending and C-H stretching vibration, and the amide III peak is caused by C-N stretching vibration. The spectral results exhibit aloe and gelatin's distinctive peaks, indicating that these ingredients were successfully incorporated into the scaffold's polymeric framework.
DSC exhibits small energy shifts that occur as matter transitions from a solid phase to a liquid crystalline phase and from a liquid crystal phase to an isotropic liquid phase. The DSC pattern (Figure 3(c)) depicts a shift in the energy of the AV/G scaffold on the basis of a T D value of 139.75°C and ΔH D -26.40 W/g.  Amino acid concentration analyzed in HPLC Figure 9: Amino acid concentration of AV/G analysed by HPLC.

12
Stem Cells International weight-to-volume ratio to Aloe vera does not impact the pyrolytic property but stabilises the supercoil structure as seen by the higher solid-state H D values of the sample (lyophilized condition). The XRD graph was plotted with intensity along the y-axis and 2θ along the x-axis. XRD was used to analyse the composite scaffold's phase. The enormous amorphous peak seen in the region between 2θ = 20°−40°reduced the characteristic diffraction peaks for both AV/G (Figure 4(b)). The XRD data indicated that the gelatin and Aloe vera molecules in the scaffold had good compatibility and interaction. The broad peaks provided evidence that the synthesised scaffold was primarily amorphous. At the point where a liquid-vapor interface and a solid surface come together, the contact angle is a routinely measured angle through the liquid on the scaffold. The contact angle ( Figure 5(b)) of Aloe vera with the gelatin scaffold was found to be 37.31°. It quantifies the wettability of a solid surface by a liquid through the Young equation. There is a specific equilibrium contact angle for every system comprising a given solid, liquid, and vapour at a given temperature and pressure. This implies that the hydrophilic characteristic has decreased with cross-linking. This may be due to the involvement of the chains in hydrogen bonding through hydroxyl groups. The stress-strain relationship of a material is dependent on the flexibility of the polymer chains, and the strength of the material determines its tensile strength (MPa). The stress-strain curve for the prepared Aloe vera with gelatin scaffold's tensile strength (MPa) was found to be 23.2, and an elongation break at 8.58 shows a better tensile stress of the AV/G scaffold. Very high tensile strength may result in the scaffold staying with the wound bed longer until it regenerates, as reported by Suganya et al. [22]. AV/G scaffold being autofluorescent, the 3D image of the scaffold was viewed under a confocal microscope (Figures 6(a) and 6(b)), and the thickness of the scaffold was found to be about 60-80 μm. However, the Z-stack of the AV/G scaffold shows minimal porosity. MSCs were cultured on the AV/G scaffold, and cell viability, compatibility, and proliferation were   Figure 11: In vitro scratch wound healing assay. Human MSCs were injured, and cell migration assay with and without scaffold was viewed after 48 h. Images was obtained using an inverted phase contrast microscope at 10× magnification.
13 Stem Cells International studied for 3 consecutive days through the MTT assay. For proliferative and viability studies, 1 × 10 4 MSCs were seeded onto the AV/G scaffold. An increase in the proliferation rate from day 1 to day 3 was observed using the MTT assay (Figure 7(a)). The biocompatibility of AV/G was analyzed for viability and proliferation. The proliferation rate of MSCs increases from days 1 to 3 which also shows the biocompatibility and viability of the scaffold.
The swelling ratio of the freeze-dried Aloe vera with gelatin scaffolds prepared showed a high degree of swelling upon placement in water at 37°C. It was also seen that the scaffold increases in ratio with 1X PBS, DMEM, and distilled water, respectively (Figure 7(b)). It has been described that a higher degree of crosslinking results in lower water uptake, as proposed by Gupta et al. [23]. From the results, we can see that this point holds true for this study too. The swelling ratio aids in rigidity and polymer stability. The reduced swelling ratio could be attributed to a more rigid network formed by the interpolymer reactions, making the scaffold more stable. The scaffold's hydrophilicity promotes cell attachment and proliferation. Also, the water-holding ability would make it simpler for nutrients to diffuse from the scaffold to the cells in the culture system. In wound healing, this would balance the fluid loss from the body at the wound site [21]. Protein estimation (Figure 7(c)) of AV/G was done by the Bradford method which shows the presence of bioactive components in the AV/G scaffold and also an ECMmimicking niche.
HPLC results from Figures 8(a), 8(b), and 9 showed amino acid concentrations in the Aloe vera with 10% gelatin gel which were similar to the results of Hariharan et al. [14]. 100 μL of AV/G was deproteinized using 60% acetonitrile and PITC-derivatized for amino acid analysis using RP-HPLC. The AUC values of each analyte were converted to concentration (ng/μL) using norleucine as a control. The presence of amino acids shows the AV/G scaffold to be biologically active. For the adherence study, 10 4 stem cells were seeded onto the AV/G scaffold. Images show that the lyophilized scaffold did not contain many pores, as seen using SEM analysis, and that both stem cells adhered to the surface. The cells were treated with F-actin-conjugated phalloidin (red), and the nucleus was stained with DAPI (blue). As Aloe vera autofluorescence green filter was muted to avoid background colouration. Images were taken after loading the cells onto the scaffolds. This was viewed at 40 × magnification in confocal microscopy. Figure 10(a) shows MSCs at 24 hours, and Figure 10(b) shows MSCs at 72 hours. The images of freeze-dried AV/G scaffold show pores and that the cells are embedded into the scaffold, and the MSCs are adhered and viable. Wound healing capacity of MSCs loaded AV/G in Figure 11. Images show strong wound-healing potential in terms of increasing MSC efficacy and wound closure in MSC-loaded AV/G scaffold to that of control (MSCs).
Regenerative medicine allows the human body to repair by producing new, useful tissue to replace damaged or missing ones. The endogenous system for repair and regeneration in the human body uses stem cells. Because stem cells serve as a backup in practically all of the essential organs, the idea of TERM is that the restoration of function of the stem cells is best accomplished in a bioscaffold. Regenerative medicine goes hand-in-hand with tissue engineering and stem cell technology. Tissue engineering has attracted much attention as a therapeutic tool which aids in providing 3dimensional dynamic scaffold structure with biomaterial to mimic the lost organ. A cascade of signaling molecules is used in the dynamic and complex process of wound healing in order to rebuild tissue layers and cellular structures. Aloe vera gel has been investigated for decades and proven to be potentially useful in tissue matrix engineering. Ayurveda has established Aloe vera gel as a natural healing agent for ages. Aloe vera gel is used as a cosmetic and has been shown to hasten wound healing, protect, and soothe skin tissues. The anti-inflammatory property and increased collagen expression promote wound healing and antiaging. Stem cells are known to be unspecialized cells with high proliferative and differentiating properties. Stem cells are highly potent and relatively easy to isolate and expand with valuable properties for regenerative medicine. Signaling molecules, cell-tocell contact, and interactions between stem cells and the extracellular matrix (ECM) around them make up a niche. Due to its distinct and appealing physicochemical and biological characteristics, Aloe vera has a bright future in tissue engineering applications. Aloe vera has been demonstrated to be helpful for tissue engineering as a material for scaffolds, drug-eluding implants, and wound dressings. Due to its characteristics, such as the effectiveness of bioactive compounds, biodegradability, biocompatibility, hydrophilicity, and synthesis of ECM, Aloe vera-based biomaterials have a new insight into the field of regenerative medicine. This study shows that an AV/G scaffold embedded with MSCs can be effectively used for wound healing and has been shown to be a promising candidate for tissue engineering applications.

Data Availability
All of the data used to support the findings of this study are included within the article.