Carbonized Aramid Fiber as the Adsorbent for In-Tube Solid-PhaseMicroextraction toDetectEstrogens inWaterSamples

Carbonized aramid fiber was prepared as a new type of adsorbent for in-tube solid-phase microextraction. *e surface structure, chemical composition, and graphitization degree of the resulted fiber was determined and characterized by scanning electron microscopy, X-ray photoelectron spectroscopy, and Raman spectrometry. *e prepared fiber was packed in a stainless-steel tube instead of the sample loop of a six-port and tested for the extraction of five environmental estrogen hormones coupled with highperformance liquid chromatography. Several parameters affecting the estrogens’ extraction including the sampling volume, sampling rate, NaCl content, and desorption time were investigated in detail. *e extraction tube with carbonized aramid fiber exhibited remarkable extraction performance towards five estrogen targets.*e analysis method was established, and it exhibited a wide linear range (0.5–10.0 μg/L) with good linearity (correlation coefficient ≥0.9906), low limits of detection (0.011–0.13 μg/L), and high enrichment factors (178–1335) for the five analytes. Relative standard deviations (n� 3) for intraday (≤4.8%) and interday (≤4.0%) tests indicated that the extraction material had satisfactory repeatability. Bisphenol A released from a polycarbonate (PC) bottle was quantitatively detected with a concentration of 8.3 μg/L. *e relative recoveries spiked at 5 and 10 μg/L were investigated, and the results were in the range of 74.3–121% for real water samples.


Introduction
ere is growing interest in the presence of micropollutants in the environment that can interfere with the endocrine system and affect the health, growth, and reproduction of humans and animals [1,2]. ese substances are known as endocrine-damaging chemicals (EDCs) and are related to various human diseases (such as prostate cancer, reproductive tract diseases, low sperm count, and breast cancer) [3][4][5]. As a typical endocrine disruptor, estrogen has been detected in sewage, surface water, and even drinking water in different countries [6,7]. For example, bisphenol A (BPA) as a prototypical EDC is an estrogenic high-production chemical used primarily as a monomer to produce epoxy resins and polycarbonate. It is now well known that there is ubiquitous human exposure to BPA [8]. For this reason, there is an urgent need to investigate the contamination of estrogens in the natural environment. e analytes from the complex matrices are often present at low concentrations. It requires the development of sensitive and specific methods for the determination of target analytes [9]. Solid-phase microextraction (SPME) was firstly introduced by Arthur and Pawliszyn in the early 1990s [10]. SPME is a simple and convenient sample preparation technique that has enabled automation, miniaturization, and high-throughput performance [11][12][13][14][15][16][17][18]. In-tube SPME is a novel SPME technique that is easy to operate, solvent free, and cost effective [19][20][21][22]. Coupling with high-performance liquid chromatography (HPLC), in-tube SPME can be successfully applied to separate and detect the target analytes in liquid samples online [23][24][25][26]. Nowadays, the most important task for in-tube SPME is to develop efficient extraction materials. Many reports use different materials for in-tube SPME to extract environmental organic pollutants and obtained good extraction efficiency, for example, cotton fiber, basalt fiber, polypropylene hollow fiber, and coatings based on them [27][28][29][30]. Although many materials have been developed as sorbents for the SPME, their synthesis processes are more complex, and the use of organic solvent is too much in a way. ereby, it is more meaningful to develop a cheap, simple, and green sorbent used as the support for intube SPME.
Recently, aramid fiber, one of the representatives in the high-performance engineered fibers family, has attracted wide attention due to its specific properties with soft texture, low density, high strength, and excellent thermal stability. It has been widely used in the field of aircraft, aerospace, tanks, missile, and so on [31,32]. Poly-p-phenylene terephthalamide (PPTA) fiber is the most common type of aramid fiber. It is also called para-aramid, and its main chain of the macromolecule is a linear molecular structure formed alternately by amide bonds and benzene rings. If it is chosen as a sorbent for in-tube SPME, the multiple interactions including π-π stacking, electrostatic interaction, and hydrogen bond may occur between its surfaces and the extracted target compounds of estrogenic hormones.
Based on these considerations, aramid fiber and its carbonized fiber under high temperature were initially selected as the sorbents for in-tube SPME. Both fibers were filled in the stainless-steel tubes to make the extraction tubes. e extraction tube was connected to the injection valve of HPLC, respectively, and an online analysis system was constructed. Five common estrogenic hormones were selected as the model analytes to investigate the extraction performance using two kinds of fibers. e online analytical method was established and applied to the determination of five estrogens in two real samples using the optimal extraction and desorption conditions.

Materials and Reagents.
Aramid fiber was obtained from Japan Toho Chemical Industry Co., Ltd. Methanol and acetonitrile were HPLC grade and purchased from Tianjin Damao Reagent Company (Tianjin, China). Five kinds of natural and synthetic estrogens including BPA (>99.0%), ethinylestradiol (>98.0%), diethylstilbestrol (>99.0%), hexestrol (>98.0%), and estrone (>98.0%) were purchased from Shanghai Aladdin Biochemical Co., Ltd. (Shanghai, China). eir chemical structures are shown in Figure 1. Ultrapure water (18.25 MΩ cm, 25°C) was used for the whole experiment. e polycarbonate (PC) bottle was purchased from a local supermarket. e mobile phase was filtered through a 0.2 μm organic membrane. Water/acetonitrile (53 : 47, v/v) was used as the mobile phase to elute estrogens at the detection wavelength of 202 nm.

Standard Solution and Real Samples.
e stock solution (100 mg/L) containing five estrogens was prepared with methanol and stored at 4°C. e working solution was prepared daily from by dilution of the stock solution with pure water to 10 μg/L. e boiled ultrapure water was filled into a new 1 L PC bottle and cooled to room temperature. Both the cooled water in the PC bottle and tap water taken from the laboratory were selected as real samples for the evaluation. All water samples were filtered with a 0.45 μm water membrane before chromatographic analysis.

Preparation of the Extraction Tube.
e aramid fiber was ultrasonically cleaned by acetonitrile for 20 min, repeated 3 times, and then, dried. After drying, it was placed in a hightemperature tube furnace with nitrogen protection. e carbonized temperature is investigated in the range of 500°C − 600°C for 6 h. Afterwards, 8 strands of carbonized aramid fiber with a length of 30 cm and a weight of 40 mg were filled into stainless-steel tubes (0.75 mm i.d. and 1/16 inch o.d.), respectively. Aramid fiber with the same length and weight without carbonization was also filled into the extraction tube for comparison. Figure 2, the extraction tube was connected to the loop position on the six-port valve of the Agilent 1220 HPLC system. e six-port valve was switched between load and inject states to perform the extraction and desorption processes. In the load state, the sample solution is transported through the extraction tube via the Agilent 1260 quaternary pump and the target analytes are adsorbed by the selected aramid fiber. In the injection state, the mobile phase (1.00 mL/min) flows through the extraction tube and the absorbed target compounds are desorbed and are detected consequently. e extraction and the desorption can be completed by the switching between load and inject modes.

Extraction and Analysis Procedure. As shown in
In order to calculate the enrichment factor (EF) values more accurately, a series of standard solutions were prepared in the range of 0-100 mg/L. After 20 μL standard solutions with different concentrations of 0, 0.25, 0.5, 1, 2.5, 5, 10, 25, and 100 mg/L were injected using the sample loop, respectively, the calibration curve with a slope of k 1 was then obtained according to the peak area vs. concentration. Moreover, another series of standard solutions with a constant sampling volume of 50 mL and different concentrations of 0, 0.5, 1, 2, 5, and 10 μg/L were prepared. After they are injected and detected by using an in-tube SPME-HPLC, the calibration curve was then obtained with a slope of k 2 . e final EF can be calculated according the following equation: EF � k 2 /k 1 .

Characterization.
e morphological properties of aramid fiber and carbonized aramid fiber were characterized by SEM. As can be seen from Figure 3, the aramid fiber had a smooth surface with few grooves. After carbonization at high temperature, some small holes appeared, and the increasement of roughness led to an increase of adsorption sites in extraction.
Raman characterizations were also carried out for the aramid fiber and its carbonized aramid fiber. As shown in Figure 4, there was a G-band, which corresponded to the inplane tangential vibration of graphite-like carbon about 1580 cm −1 and a D-band associated with disordered carbon around 1340 cm −1 for the carbonized aramid fiber [33]. In contrast, no obvious characteristic peak was found on the aramid fiber. e intensity ratio of D-band to G-band was around 1.17, indicating that high temperature caused its partial carbonization with more graphitized carbon atoms appeared on its surface. As shown in Figure 5, the X-ray photoelectron spectroscopy (XPS) spectrum indicated the carbonized aramid fiber mainly contained elements of carbon and oxygen.
e atomic percent of C and O was 69.4 and 17.6%, respectively. e C 1s XPS spectrum can be fitted into three components, and these peaks at 284.1, 284.5, and 287.7 eV correspond to the carbon bonds of C-C, C-OH, and C�O. e results showed that amorphous carbon was formed in situ on the surface of the carbonized aramid fiber.

Optimization of Extraction Conditions.
e treatment temperature directly affects the carbonization degree of aramid fiber, which decides its extraction performance. In our experiments, the carbonization temperature was investigated in the range of 500 − 600°C with a constant carbonization time of 6 h. Under the optimal conditions, the extraction efficiency to five estrogens was comparatively evaluated for the   Figure 6, the pristine aramid fiber and the carbonized aramid fiber at 570°C and 600°C presented the lowest extraction efficiency. When the carbonization temperature was 500°C and 550°C, the highest extraction efficiency of five estrogens was obtained. It can be seen from Table 1 that the largest peak areas of BPA, ethynylestradiol, diethylstilbestrol, and hexestrol were achieved at 500°C, but the peak area of estrone was the highest at 550°C.
It was probably attributed to that carbonization at suitable temperature promoted the structural regularity and stability of carbon atoms on the surface of aramid fiber. In this situation, more adsorption sites were created with higher extraction efficiency for the target compounds; aramid fiber carbonized at 500°C was selected as the extraction phase for next in-tube SPME-HPLC.
When the peak area tends to be constant with the increase of the sample volume, the extraction reaches equilibrium and the largest extraction efficiency will be obtained. However, excessive sampling volume may result in a waste of extraction time and affect extraction efficiency. As shown in Figure 7(a), peak areas of the analytes increased with the change of sampling volume from 20 to 80 mL, especially for diethylstilbestrol. e increase of peak areas was unremarkable for other compounds when the sampling volume was more than 50 mL. Compromising the extraction efficiency and time, 50 mL was selected as the optimal sampling volume. Sampling rate, as one of the optimized conditions, has a significant impact on extraction efficiency and extraction time. After the same sampling volume of 50 mL was loaded, the sampling rate was investigated in the range of 0.50-2.00 mL/min. It can be seen from Figure 7(b) that the peak areas of the five analytes changed little with increasing the sampling rate from 0.50 to 1.00 mL/min. While the sampling rate increases beyond 1.00 mL/min, the upward trend can be observed easily. In order to obtain better extraction efficiency and quick analysis, 2.00 mL/min was chosen as the optimal sampling rate. e addition of inorganic salts such as NaCl to the water sample can increase the ionic strength of the solution, effectively reduce the dissolution of organic compounds, and improve the extraction efficiency of SPME. On the other hand, it will increase the solution's viscosity and reduce the diffusion rate of organic matter. Herein, NaCl in the concentration range of 0-2.0% (w/w) was added in the sample solutions for the investigation. As shown in Figure 7(c), with the increase of NaCl content, each sample's peak area gradually decreased, indicating that the best extraction efficiency was obtained for the sample without NaCl.
erefore, the addition of NaCl was not considered in the subsequent experiments.
After the extraction was completed, water/acetonitrile (53 : 47, v/v) as the mobile phase flowed through the Journal of Chemistry extraction tube at 1.00 mL/min. e analytes absorbed by the support in the extraction tube were eluted, and the desorption process was carried out. Adequate desorption time ensured the full desorption of all extracted analytes and reduced the impact of residual analytes on the next extraction. e effect of desorption time was investigated in the range of 0.20-2.00 min. As shown in Figure 7(d), five estrogens' peak areas exhibited an upward trend with the increasement of desorption time; thus 2.00 min was selected as the optimal desorption time.

Method Evaluation and Application to Real Samples.
Under optimized conditions, a series of parameters including linear range, correlation coefficient (R 2 ), interday repeatability, intraday repeatability, limits of detection (LODs), and limits of quantification (LOQs) were investigated to validate the online in-tube SPME-HPLC method. As shown in Table 2, in the selected concentration range of 0.5-10.0 μg/L, all analytes exhibited satisfactory correlation coefficients (R 2 ) of 0.9915, 0.9939, 0.9962, 0.9906, and 0.9941, for bisphenol A, ethynylestradiol, diethylstilbestrol, hexestrol, and estrone, respectively. LODs (S/N � 3) and LOQs (S/N � 10) were within the ranges of 0.017-0.13 μg/L and 0.038-0.45 μg/L, respectively. ree parallel tests were performed in one day to investigate the intraday extraction repeatability, and their relative standard deviations (n � 3) were between 0.6% and 4.8%. Under the same conditions, an experiment was performed once a day for three days to get the interday extraction repeatability, and the relative standard deviation (RSDs, n � 3) of the peak area was less than 4.0%. e extraction material has good extraction repeatability. In addition, three extraction devices prepared in different batches (n � 3) were chosen to explore the reproducibility of peak areas, and the satisfactory results were obtained with their RSDs in the range of 1.1-9.2%. e EFs (BPA, ethynylestradiol, diethylstilbestrol, hexestrol, and estrone) were equal to the ratio of the slope of the standard curve before (corresponding k 1 � 0.19, 0.14, 0.13, 0.16, 0.15) and after (corresponding k 2 � 34. e developed method was compared with other reported methods for the determination for estrogens, including extraction materials, extraction time, enrichment factors, and recoveries. Relative data are presented in Table 3. Although the recoveries obtained by our developed method were close or comparable to other work [34][35][36][37][38][39], the LOD value was better than that of other methods except the    method of HPLC-FLD-UV [38]. It should be noted that the highest EF values were achieved, compared with other methods based on different extraction materials. Moreover, the extraction time could be finished within 32 min for our method, which was significantly shorter than in other methods. ese comparisons support the fact that this method is an effective analytical method for the determination of estrogen in environmental samples.
To confirm the applicability of the analytical method, two real samples were selected, including water in a PC bottle immersed in boiled water and tap water taken from our laboratory. Generally, exposure to BPA occurs mainly by consumption of contaminated foods and beverages that have contacted epoxy resins or PC plastics [8]. To test the hypothesis that bioactive BPA was released from PC bottles containing water and other beverages, the pretreatment and determination of BPA migrated from a polycarbonate bottle was attempted using the developed method. As shown in Table 4 and Figure 8, BPA was quantitatively detected in the water sample in the PC cup with a concentration of 8.3 μg/L, although no compounds were detected in the tap water. e spike recoveries of the analytes were examined by the   standard addition method. e concentration of addition in the sample was 0, 5, and 10 μg/L. e recoveries were 75.0%-121.1% for the ultrapure water in a PC bottle and 74.6%-120.7% for the tap water, respectively. e abovementioned results indicated that this method could be applied to analyze trace estrogens in real samples.

Conclusions
In this study, aramid fiber was carbonized at an optimal temperature and characterized by SEM, Raman, and XPS, respectively. It was filled in a stainless-steel tube as a novel extraction material and connected to HPLC for use in an online in-tube SPME-HPLC system to detect five estrogens in water samples. e carbonized aramid fiber exhibited good durability, chemical stability, sensitivity, and excellent extraction performance compared with the pristine aramid fiber. Compared with the reported method for estrogen determination, this method was sensitive, fast, and had a high enrichment factor. Also, it was successfully applied to separate five estrogens and detect BPA in real samples with high extraction efficiency, good repeatability, and satisfied recoveries.

Data Availability
All data included in this study are available upon request by contact with the corresponding author.