Synthesis and Characterization of Hydroxyapatite- (HAP-) Clay Composites and Adsorption Studies on Methylene Blue for Water Treatment

Dyes used by the textile, tannery, and food industries tend to pollute water bodies and must be removed to get clean water. Hydroxyapatite (HAP) was synthesized from eggshells using the wet precipitation process. 'e as-synthesized HAP was characterized using Fourier Transform Infrared (FTIR) and X-ray powder diffraction (XRD). 'e synthesized HAP was mixed with three different clays: halloysite (HNT), kaolinite (KAO), and bentonite (BENT). 'e removal efficiency values of methylene blue (MB) from the data showed that HAP-BENT adsorbents had higher values, followed by HAP-HNT and then HAP-KAO adsorbents. 'e combined masses of 24mg, 34.5mg, and 33mg (representing 20%, 15%, and 10% of HAP-BENT mass) had average adsorption capacity values of 20.7mg/g, 17.2mg/g, and 17.9mg/g, respectively. For each mass percentage, the adsorption capacity values were found to decrease with adsorbent dosage. 'e HAP-BENTcomposites had removal efficiency values of 98.4, 91.9%, and 91.9%, respectively. Adsorption data for the HAP-BENTadsorbents were found to be well described by the Langmuir isotherm model and pseudo-second-order kinetic model. 'e effect of temperature on adsorption capacity was evaluated and thermodynamical modeling was undertaken. 'e thermodynamical modeling predicts that based on the value of the change in enthalpy and Gibbs free energy the process was exothermic and spontaneous. 'is work confirms the potential of HAP-clay composites in removing MB from water.


Introduction
e textile, tannery, and food industries utilize dyes in most of their production processes. e majority of these dyes tend to generate toxins and carcinogens when they are not treated before being discharged into the environment [1]. Since most dyes do not degrade biologically, measures have to be put in place in order to contain and control them to prevent pollution problems [2]. Dyes and other pollutants found in water sources do not only pose a threat to aquatic life but also endanger human health when found in drinking water sources [3,4]. For most people, the water quality is greatly affected by how the water looks, as such color is the first contaminant to be observed in wastewater. Even a very small quantity of dyes (less than 1 ppm) in water is easily visible, undesirable, and harmful [5][6][7]. Methylene blue (MB) is a commonly used dye for dying textiles such as cotton, wool, and silk. It can cause eye burns leading to a permanent eye injury in humans and animals. Besides eye burns, when inhaled, it can cause short rapid breaths or even difficulty in breathing [8].
Researchers have shown that several conventional methods and remediation methods to treat these polluted water sources are often not effective in dye removal [9]. e use of adsorbents to remove pollutants from water has been proven to be efficient and reliable especially when the adsorbent is abundant and economical [10]. Activated carbon is an adsorbent frequently used despite its relatively high price. Activated carbon has a well-developed pore structure, large surface area, and high degree of surface reactivity and so is mostly used to remove water pollutants [11].
In recent years, clay minerals have been used for their potential to adsorb both inorganic ions and organic molecules. Studies have been carried out on interactions between MB and clay particles [12][13][14], and it has been established that clay minerals show a strong affinity for MB. Bagane and Guiza [15] showed that clay is able to remove MB due to its high surface area as it showed an adsorption capacity of 300 mg/g. Almeida et al. [16] used montmorillonite to remove MB from synthetic wastewater. It was reported that as an effective adsorbent, equilibrium was attained in less than 30 minutes. Kaolin as a dye adsorbent was also studied by Ghosh and Bhattacharyya [14] who showed that NaOH was able to improve its adsorption capacity through purification and treatment.
Also, hydroxyapatite (HAP; Ca 10 (PO 4 ) 6 (OH)) is explored in the removal of MB from aqueous suspension [17]. HAP is classified as a bioceramic that has a chemical resemblance to the inorganic mineral composition of hard tissues like teeth and bones in mammals. HAP can be synthesized using methods such as hydrolysis, hydrothermal, or precipitation methods, dry process, and sol-gel technique.
e wet precipitation method is preferred because only water is produced as a by-product. Also, the risk of contamination during processing is low, leading to the formation of high purity crystals, and it is cheap [18]. is research adopts the wet precipitation method for the HAP synthesis (considering the advantages: affordability, high chemical and thermal stability, ionic exchange capacity, and adsorption affinity) and, consequently, forms composites with clay minerals for the MB removal from water [19][20][21].
Recently, the use of HAP composites for some environmental pollutant removal has also been reported [22][23][24], but the efficacy of HAP-clay adsorption of dyes has been rarely reported [21,25,26]. In this research, HAP powder is synthesized from chicken eggshells, mixed with clay minerals, and then used to explore their removal efficiencies in the removal of MB dye from water.

Materials and Methods
Analytical grade chemicals used were obtained from Sigma-Aldrich, United Kingdom. e clays were acquired from Sigma-Aldrich and used in their form without any modification except where stated. ese clays are halloysite (particle size 1-3 µm), bentonite clay (particle size ≤25 µm), and kaolinite (particle size ≤25 µm). HAP was synthesized from chicken eggshells which were collected from the Madina market in Accra, Ghana.

Preparation of Hydroxyapatite.
Distilled water was used to wash the eggshells which ensured the removal of all fecal matter and other foreign materials were removed. e cuticle layer inside each eggshell was then removed and washed again with distilled water. e eggshells were mechanically crushed by hand into smaller fragments to facilitate sun-drying for a week. e sun-dried eggshells were further dried in an oven for one hour at a temperature of 105°C to ensure thorough removal of water and then pulverized into a fine powder using a mortar and pestle after which sieving was done with a 180 μm sieve. e eggshell powder was then calcined in a muffle furnace for two hours at a temperature of 900°C. is process converted the primary constituent in the eggshell powder which was CaCO 3 into CaO. Figure 1 shows the main steps in the preparation of the eggshells to calcined egg powder. 0.5 M Ca(OH) 2 solution was measured into a 250 ml beaker and stirred intensely at 600 rpm on a hot plate for an hour at 90°C, after which 100 ml of 0.3 M H 3 PO 4 solution was added dropwise to the Ca(OH) 2 solution at 90°C. e stirring continued for another one hour, after which the resulting mixture was allowed to cool. e pH of the mixture was adjusted to 10 by adding few drops of 1 M ammonium hydroxide (NH 4 OH). e mixture was covered with aluminum foil and allowed to age for 48 hours. e pH was checked periodically to ensure it remained at 10. After the aging process, the precipitate was filtered using a conical flask, funnel, and filter paper. e precipitate was then ovendried at 110°C for an hour and then calcined at 900°C for two hours to produce the HAP powder. Figure 2 shows the processes described.

Preparation of Adsorbents.
e adsorbents were in powdered form. e synthesized HAP was mixed with various clay types-halloysite, kaolin. and bentonite. e masses of the clay types were 20%, 15%. and 10% of the weight of the HAP in the respective experiments. e HAPclay mineral was mixed thoroughly and further heated to 110°C in an oven to remove all moisture prior to the adsorption experiment. Table 1 presents details of the batches undertaken for HAP-clay mineral composites.

Characterization of Adsorbents.
Fourier Transform Infrared (FTIR) and X-ray powder diffraction (XRD) were used to characterize the synthesized HAP sample. FTIR analysis was performed with Bruker (PerkinElmer, Frontier, Perkin Elmer, Ohio, USA), and the XRD was carried out using a PANalytical Empyrean (Series 2) powder diffractometer (PANalytical B.V., Lelyweg 1, 7602 EA, Almelo, e Netherlands). e XRD was equipped with a copper-target tube and was operated at 45 kV and 40 mA to give the Cu-Kα line at a wavelength of 15.406 nm. e K β line was removed with a nickel filter. e analysis of the XRD patterns was carried out on the Panalytical HighScore Plus software (v. 4.8) and with the ICDD PDF-4/Organics 2020 database.

Batch Adsorption Experiments.
e adsorption experiment was performed in a beaker using a 5 mg/L MB dye solution. Initially, the experiment was undertaken using mixtures of HAP and HNT (mass is equivalent to 20% of HAP). is was followed by other mixtures (for HAP-BENT and HAP-KAO) as given in Table 1. e beaker containing the solution and adsorbent was placed on a magnetic stirrer plate to ensure continuous mixing for the allowed time stated in Figure 1. After that, Whatman 1 filter paper with a pore size of 11 µm was used to filter the solution. e absorbance of the resulting solution was analyzed using a UV-VIS spectrophotometer ( ermoScientific Genesys) at 668 nm wavelength to determine the absorbance of the MB dye in the filtrate. e concentration of the remaining MB  was calculated from the measured absorbance. e experiment was repeated with HNT with masses equivalent to 15% and 10% of HAP in combination with HAP (Table 1). e different adsorption dosages (20%, 15%, and 10% of the HAP-given masses for clay masses) were repeated for KAO and BENT.
To further investigate kinetics and isotherm models, the repetition of the adsorption experiments was done for different adsorption times, every 30 minutes for the mass combinations that resulted in the highest adsorption capacity. HAP:BENT composite mass combinations were further investigated ((20 mg : 4 mg) and (30 mg : 4.5 mg) and (30 mg : 3 mg)). Each combined mass of adsorbent was to remove MB (5 mg/L concentration solution) allowing 30 minutes of contact time.
is was undertaken every 30 minutes till the 300 minutes ((5th) hour) of contact time for adsorbent and measured MB solution. e adsorption data was analyzed to understand the mechanisms via fitting to the two main isotherm models: Freundlich and Langmuir isotherm models. e initial pH in the range 5.5-7.5 was used for the experiments and at a constant temperature of (25 ± 1)°C. e basic Freundlich and Langmuir isotherms model fittings were done, and the key parameters were computed. e adsorption capacity, q, which was the amount of dye adsorbed was calculated using where q is the dye adsorbed (mg/g), C 0 is the initial concentration of dye (mg/L), C t is the concentration of dye in solution at a given time (mg/L), V is the solution volume (L), and m is the adsorbent dosage (g). e percentage removal is given by where A% is the percentage of MB dye removed, and the remaining parameters are defined.

Isotherm and Kinetic
Modeling of Adsorption Data. e two widely used models to describe isotherm processes in adsorption are Freundlich and Langmuir models. e Langmuir equation assumes that the maximum adsorption takes place when the surface is covered by adsorbate in a monolayer while the Freundlich model is empirical [11,27]. Again, the Langmuir model assumes that the point of valance exists on the surface of the adsorbent and that each of these sites is capable of adsorbing one molecule. Furthermore, it is assumed that the adsorption sites have equal affinities for molecules of adsorbate and that the presence of adsorbed molecules at one site will not affect the adsorption of molecules at an adjacent site [28,29]. e original and linear forms of the Langmuir and Freundlich equations are given in equations (3) and (4), respectively.
linear form : original form : q e � K F * C e 1/n , where K L and q m are Langmuir constant and maximum adsorption capacity (mg/g), respectively, q e is the equilibrium adsorption capacity (mg/g), K F and (1/n) are the Freundlich constant, respectively, and C e is the equilibrium concentration (mg/L). e process kinetics described the solute uptake rate thereby allowing the estimated residence time required to achieve a definite extent of MB removal [29,30]. e adsorption kinetic models used in this work are the pseudofirst-order (PFO) and the pseudo-second-order (PSO) rate equations and were both fitted to the experimental data. e pseudo-first-order equation assumes that the rate of change in solute adsorption over time is directly proportional to the difference in saturation concentration and the amount of adsorptive solid uptake over time [31]. e two models as used in this work are found in where q e and q t are the amount of MB adsorbed (mg/g) at equilibrium and any time t, respectively, and k 1 (min −1 ) and k 2 (min −1 ) are rate constants of adsorption for PFO and PSO,  (3), a plot of log (q e −q t ) versus time, t, results in a negative slope with gradient being (k 1 )/ 2.303 and log (q e ) intercept on the vertical axis. Also, to deduce the parameters of adsorption in equation (4), t/q t is plotted against t with slope (1/q e ) and intercept (1/k 2 q 2 e ) on the vertical (t) axis.

ermodynamical Modeling.
ermodynamic parameters, including Gibbs free energy change (ΔG°), enthalpy change (ΔH°), and entropy change (ΔS°), serve to evaluate the effect of temperature on the adsorption of MB onto adsorbents and provide in-depth information regarding the inherent energy changes associated with the adsorption process [32]. ese parameters are calculated from equations (7)- (9): where R is the universal gas constant (8.314 J/mol·K), T the temperature (K), and K L°t he (dimensionless) 'thermodynamic' Langmuir constant for the adsorption process.

Characterization of Adsorbents.
e results of the FTIR analysis of synthesized HAP samples are plotted in Figure 3(a) for the calcined hydroxyapatite (cHAP) and crushed or powdered eggshell (EggS) samples. e carbonate functional group showed up within the range 1395-1600 cm −1 (]3; asymmetric stretch vibration) and 873-889 cm −1 (]2; out-of-plane bend vibration). e crushed eggshell showed this carbonate functional group at 1026 cm −1 . In the cHAP spectrum, there was a peak of the PO 4 3− functional group at 1065 cm −1 vibrational frequency [33]. e spectrum also showed the presence of CO 3 2− peaks at 895 cm −1 and 1361 cm −1 for cHAP, and the respective carbonate functional groups for the EggS were observed at 874 cm −1 and 1065 cm −1 [34]. ere was a clear reduction in intensity for the carbonate functional group after calcination, and an increase in intensity for the phosphate functional group (at 1026 cm −1 ) was observed. e presence of the OHfunctional group observed at 3642 cm −1 for EggS disappeared after calcination. e FTIR spectra for the clays are plotted in Figure 3(b). e bands 3550 to 4000 cm −1 were the structural hydroxyl groups in addition to the water molecules in the interlayer space of the raw bentonite. e FTIR spectrum in the lower region showed bands at 1631, 1002, 900, 817, 720, and 538 cm −1 , and these bands were due to the vibrational modes of the SiO 4 tetrahedron of bentonite. e O-H stretching band was at 3622 cm −1 , and the intralayer H-bonded and O-H stretching was seen at broadband centered at 3381 cm −1 .
e 1631 cm −1 band was the H-O-H bending vibration of water, while the 1416 cm −1 band could be attributed to the siloxane (-Si-O-Si-) group stretching. is indicated the possibility of the hydroxyl linkage between octahedral and tetrahedral layers. Another sharp and intense 1631 cm −1 band observed was due to ]2 asymmetric OH stretch (deformation mode) of water and was a structural part of the mineral.
Furthermore, the FTIR spectrum for kaolinites is shown in Figure 3 e 3622 cm −1 band observed can be attributed to the inner hydroxyls (crystalline hydroxyl), and the bands observed around the other three characteristic bands were generally ascribed to vibrations of the external hydroxyls. e three 3693 cm −1 , 3645 cm −1 , and 3622 cm −1 bands were the kaolinite. e 1000 cm −1 to 500 cm −1 bands were dominated by the functional groups of Si-O and Al-OH. e bands at 817 cm −1 and 720 cm −1 were said to be Siquartz whereas 1002 cm −1 and 900 cm −1 were the OH vibrations usually linked to 2Al 3+ . e main bands of the HNT were 3622 cm −1 , 1631 cm −1 , 1002 cm −1 , and 900 cm −1 . e 3622 cm −1 is for the O-H stretching of inner hydroxyl groups, 1631 cm −1 shows O-H deformation of water, and 900 cm −1 was interpreted as the O-H bending of inner hydroxyl groups 1002 cm −1 for Si-O stretching [35]. Figure 4 shows the XRD pattern obtained for the assynthesized HAP for the (a) crushed eggshells and (b) calcined samples. Most XRD patterns showed HAP diffraction peaks observed in standards and literature. e major phase in the calcined sample, as expected, was HAP, when compared with the data obtained from the ICDD reference code 01-074-4172 using the search and match protocol in HighScore Plus. From Figure 4(b), the peaks with high intensities at 2Ө equaling to 31.7681°, 32.1784°, 32.906°, and 25.8571°were confirmed as HAP. e respective Miller indices (hkl) values for these peaks were (211), (112), (300), and (002) [34,36]. ere were also peaks corresponding to calcium phosphate, Ca 3 (PO 4 ) 2 (ICDD reference code 00-009-0169), indicating the presence of this compound as well.
e ICDD reference codes 01-089-5969, 98-015-4315, 00-011-0293, and 01-009-0169 showed that these patterns corresponded to calcium hydrogen phosphate, apatite, calcium phosphate hydroxide hydrate, and calcium phosphate [36]. e effect of the calcination could be seen in the removal of some of these compounds resulting in the main hydroxyapatite phase.

Adsorbent Dose Effect.
e adsorbent dose effect on the efficient removal of the MB dye by the HAP-clay was studied. Figures 5(b), 5(d), and 5(f ) show the outcome of the effect of dosage on MB dye removal for HAP-HNT, HAP-KAO, and HAP-BENT. e maximum removal efficiency of MB dye for HAP-HNT mixtures was found to be 95% for a combined mass of 120 mg. It was seen that the efficient removal for combined masses of 84 mg and or more was at least 80%. Also, the average removal efficiency for 20% mass of HAP used as HNT mass was found to be higher values than the 15 and 10 percentages. e maximum removal efficiencies obtained for 15% and 10% masses (for HNT mass) used were 80.7% and 52.7%, respectively. e HAP-KAO mixtures were found to have low removal efficiency Two main trends were noted in the removal efficiency data.
e first was that, for all mixtures, the increase in adsorbent dosage increases the value of the removal efficiency and that the incremental changes are not significant after the third hour of contact time. is is because, at the initial stage of adsorption, the surface of the adsorbent is   bare resulting in faster sorption kinetics of the adsorbate onto the surface of the adsorbent (usually through diffusion kinetics). At the later stage of the adsorption process, the main kinetics changes from a diffusion process to more of an attachment-controlled process [37]. e second trend observed was that the removal efficiency values for HAP-BENT adsorbents were higher than HAP-KAO and HAP-HNT composites in adsorption processes. Also, the adsorption capacity values were found to be the highest with the HAP-BENT combinations. e combined adsorbent masses of 24 mg, 23 mg, and 22 mg (which represents 20%, 15%, and 10% of HAP mass) had adsorption capacity values of 20.2 mg/g, 17.2 mg/g, and 17.9 mg/g, respectively. For each percentage, the adsorption capacity values were found to be decreasing with adsorbent dosage.
Considering the values of the removal efficiency and the adsorption capacities, the best adsorbent for each category of adsorbent HAP: BENT was selected. e adsorption capacity values 20.17 mg/g, 13.32 mg/g, and 13.92 mg/g for 20%, 15%, and 10% (of HAP mass used as bentonite mass), respectively, were found to be associated with removal efficiency values 97%, 92%, and 92% for the respective percentages. is proposes that the best performance in terms of the adsorptive capacity and removal efficiency was 24 mg combined mass (HAP mass � 20 mg and BENT mass � 4 mg) which was associated with 20% HAP-BENT adsorbent composite. e combined masses of 34.5 mg (HAP mass � 30 mg and BENT mass � 4.5 mg) and 33 mg (HAP mass � 30 mg and BENT mass � 3 mg) representing 15% and 10% HAP -BENT composites were the best performers in their respective adsorption processes. e adsorption capacity values for all combinations are also plotted in Figures 5(a), 5(c), and 5(e). A similar trend was observed for all combinations. ere is a decrease in adsorption capacity values as the adsorbent dosage increases.
is observation which was the decrease in adsorption capacity values could be described by two reasons. ese were as follows: (1) the available active sites are utilized at low adsorbent dose compared to high adsorbent dose in which too many sites are available for a limited quantity of adsorbate, and (2) high adsorbent dose causes low equilibrium MB concentration as a reduced driving force for adsorption occurs. e same trends were reported by Salvestrini et al. [32] for laterite and Wu et al. [33] for pyrophyllite [38,39]. Wu et al. [33] said the possible aggregation, overlapping, and overcrowding of adsorbent contributed to the reduction to a decrease in adsorption capacity due to the decreased available surface area [39].

Effect of Contact Time.
e effect of contact time is crucial to understand the binding processes of MB dye and the equilibrium time which strongly depends on factors like pore structure of adsorbent, adsorbent particle size or surface area, and adsorbent concentration. e efficient removal of MB results obtained as a function of contact time for 24 mg combined adsorbent mass (20 mg HAP : 4 mg BENT) is presented in Figure 6. e average removal efficiency for the 24 mg combined adsorbent mass (20 mg HAP : 4 mg BENT) was 98.1% with a maximum value of 99.4% (at the 5th hour of contact time). e minimum removal efficiency value for the 24 mg combined mass HAP-BENT was 96.2% (at 30 minutes of contact time).
Generally, for all adsorbents of HAP-BENT, removal efficiency values increased with increasing contact time with marginal increases from the third hour of contact time. e best performer in terms of both removal efficiency and adsorptive capacity for HAP-BENT adsorbents with combined masses of 24 mg, 34.5 mg, and 33 mg was 98.7% (at 90 minutes of contact time), 98.7% (at 210 minutes of contact time), and 99.2% (at 90 minutes of contact time), respectively. e minimum removal efficiency values for HAP-BENT adsorbents with 24 mg, 34.5 mg, and 33 mg were 96.2% (at 20 minutes of contact time), 96.5.0% (at 180 minutes of contact time), and 84.6% (at 300 minutes of contact time). is observation suggests that the adsorption of MB dye under this study is time-dependent and that the significant increase from 20 minutes of contact time to 150 minutes for all adsorbents could be due to the initial vacant absorbent sites and the concentration gradient of the solute was high [40].
Ion-exchange processes dominate the adsorption of MB on clay minerals. us, the sorption capacity can vary strongly with pH [41]. Al-Ghouti et al. [41] showed that the mechanism of adsorption of dye onto diatomite was due to physiosorption (depending on the particle size) and electrostatic interactions (depending on the pH used) [41]. e adsorption of dyes unto HAP adsorbent was also noted to be highly dependent on ion exchanges and strongly dependent on pH. According to Allam et al. [20], the adsorption of MB as a cationic dye on the adsorbent microwave-HAP could be explained as follows: the electrostatic attraction between the negatively charged surface of the microwave-HAP and the positively charged group of the dye was more important at pH above 7.2 [20]. On the contrary, electrostatic repulsions in an acidic medium occurred between positively charged surface sites on microwave-HAP and MB cations, and this does not favor the adsorption of MB. Indeed, there was a competition between excess protons (H + ) and MB cations for active adsorption sites in microwave-HAP when the solution was acidic and resulted in lower adsorption [20]. A similar observation has been reported elsewhere [42]. e adsorption capacity of microwave-HAP was reported as 33.3 mg/g while raw HAP was 0.7 mg/g [20]. Table 2 shows the summary of related adsorbents and their respective adsorption capacity. e effect of time on adsorption capacity and removal efficiency for a combined optimum mass of the composites varied is shown in Figure 6. In this investigation, the pH of the composite was not altered and stayed within 5.5-7.0. It is, therefore, proposed that the mechanism for the composite adsorbent will be dominated by clay adsorption of MB.

Adsorption Isotherm and Kinetic Models.
e best performers in the three sets of weight percentages have their data fitted to the Langmuir model in Figures 7(a)-7(c) and the Freundlich in Figures 8(a)-8(c). e key parameters of the two models were computed and presented in Table 3. e R-square values for HAP-BENT composites 24 mg, 34.5 mg, and 33 mg were found to be 0.99, 1.00, and 0.99, respectively, for the Langmuir model fit. ese values were greater than the R-square values from the Freundlich isotherm model fitting. is implies that the adsorption data for the HAP-BENT-24 mg, 34.5 mg, and 33 mg combined masses can be described with the Langmuir isotherm model. e values obtained for the separation factor, R L , confirm this deduction. e expression for the dimensionless quantity, separation factor, R L , is defined as where C 0°r efers to the initial concentration of the adsorbate in (mg/L) and K L is the Langmuir constant which is related to the adsorption capacity in (mg/g). It is worthy to note that a variation of the suitable area and the porosity of the adsorbent can be correlated with K L , implying the fact that higher adsorption capacity can be because of large surface area and pore volume. e R L values for all HAP-BENT adsorbents (24 mg, 34.5 mg, and 33 mg combined masses) were found to be 0.264, 0.356, and 0.801 (which were all        Journal of Chemistry 11 between 0 and 1). According to Tchomgui-Kamga et al. [40], the adsorption nature can be described using the separation factor and that it can be indicated to be either linear (R L � 1), irreversible (R L � 0), unfavorable (R L >1), or favorable (0 < R L < 1) [44]. e values from this current research support the conclusion that the adsorption favors the Langmuir isotherm model and is supported by other researchers [45,46]. e kinetics of the adsorption process which is critical to process efficiency was also investigated and the understanding of mechanism(s) was involved. is was done by fitting adsorption data to equations (5) and (6) for PFO and PSO, respectively. e PFO and PSO key parameters for best adsorbent masses of 24.0 mg, 33.0 mg, and 34.5 mg are presented in Table 4. e R-square values from fitting as indicated in Table 4 and Figure 9 show that the kinetic process is best described by PSO. In addition, the adsorption capacity values for the PSO in all cases can be found to be comparable to the experimental value to the PFO adsorption capacity values.
is research output with regard to the kinetics being best described with PSO was supported by other studies [45][46][47][48].

Effect of Temperature and ermodynamical Modeling.
e effect of temperature studies for HAP:BENT composites on MB adsorption was explored on the best adsorbent mass, 24.00 mg HAP:BENT composite only. e temperatures at which the adsorption was undertaken were 308.15 K, 318.15 K, and 328.15 K. e adsorption capacities of the HAP: BENT (24 mg mass) for MB decrease slightly with an increase in temperature (Figure 10(a)). e decrease of adsorption capacity with increasing temperature indicates that the adsorption is an exothermic process [48]. e increasing temperature may decrease the adsorptive forces between the dye species and the active sites on the adsorbent surface as a result of decreasing adsorption capacity [49]. e enthalpy (ΔH°) and entropy (ΔS°) parameters were estimated from the classical equations (8) and (9). e plot of LnK L°v ersus 1/T from equation (8) yielded a straight line (Figure 10(b)), and the values of ΔH°(kJ/mol) and ΔS°(J/mol K) were calculated from the intercept and slope of the plots, respectively. e values of ΔG°(kJ/mol) were calculated from ΔH°and ΔS°( Table 5) using equation (9). e Van't Hoff (equation (9)) plot indicates an exothermic adsorption process. e negative ΔG°values confirmed the feasibility and spontaneity of the adsorption process.

Proposed Mechanism of MB Removal.
e adsorption mechanism channels are known to depend on the compositions of the composite and their subsequent availability of suitable sites. HAP adsorption potency for MB as well as clay minerals has been documented to be dependent on pH. Regarding MB adsorption on HAP, lower adsorption has been reported at lower pH compared to adsorption between high values pH of 8-12. e most identified mechanisms involve hydrogen bonding, electrostatic attraction, and acid interaction.
Clays are hydrous aluminum phyllosilicate generally made up of an octahedral arrangement of silicate sheets sandwiched between two tetrahedral aluminas with various cations. Hydroxyl groups located on the lateral cleavages of clay crystallites are capable of protonation-deprotonation reactions depending on the pH of the surrounding solution [41]. e presence of the 'hidden' OH and water molecules is confirmed by the FTIR plots presented in Figure 3(b). e broken bonds and M(cations)-OH bonds along the surfaces of the clay crystals result in hydrolysis [27]. Figure 11 is a schematic representation of the adsorption of MB by the HAP-clay composite. is was drawn after considering the mechanism of MB adsorption by HAP and clay separately via literature by Vezentsev et al. [50] and others [45][46][47]50]  charge which promotes adsorption of MB cations. As a result, the positively charged surface cannot absorb MB cations effectively because of electrostatic repulsion [50]. Despite low pH, electrostatic repulsion, and competitive adsorption of O + ions, a reasonable amount of MB is absorbed. e high removal efficiency also associated with HAP:BENT is mainly due to the presence of the bentonite which is smectite clay (three-layer type) as compared to kaolin and halloysite which are two layers. Bentonites are noted for a high degree of chemical substitution within their smectite structure, the nature of the exchangeable cations present, and the type and amount of impurities present [51,52].

Conclusion
HAP was successfully synthesized from chicken eggshells and characterized. e FTIR characterization compares well with scholarly literature. is was confirmed via XRD analysis. e adsorption capacity of the class of HAP-BENT adsorbents was found to have higher values, followed by HAP-HNT and then HAP-KAO adsorbents. Similar trends were observed for the removal efficiency parameter for the composites. e combined mass of 24 mg of HAP-BENT resulted in 20.2 mg/g and was the highest in all composite adsorptions. e combined masses of 24 mg, 23 mg, and 22 mg (representing 20, 15, and 10 percentages of HAP mass used as a mass of bentonite) had adsorption capacity values of 20.7 mg/g, 17.2 mg/g, and 17.9 mg/g, respectively. e HAP-BENT adsorbents with combined masses of 24 mg, 34.5 mg, and 33 mg were found to show the best performances in terms of removal efficiency and adsorptive capacity. Generally, for all adsorbents HAP-BENT, removal efficiency values increased with increasing contact time with marginal increases from the third hour of contact time. e adsorption capacity values were found to decrease as the adsorbent dosage increases. e adsorption process for the HAP-BENT can be described with the Langmuir isotherm adsorption model and PSO kinetic modeling. Regarding the thermodynamical modeling, the negative values of the enthalpy change and Gibbs free energy indicate the exothermic and spontaneous process. is research confirms the use of natural materials for water treatment and the ease of use.

Data Availability
e "Data supporting work" file used to support the findings of this study is included within the supplementary information file.

Conflicts of Interest
ere are no conflicts of interest.

Acknowledgments
is project was partly funded by Cambridge-Africa Partnership for Research Excellence (CAPREx) project and the  Journal of Chemistry 13