Improving SERS Sensing Efficiency and Catalytic Reduction Activity in Multifunctional Ternary Ag-TiO2-GO Nanostructures: Roles of Electron Transfer Process on Performance Enhancement

Multifunctional nanocomposites have received great attention for years; electron transfer (ET) is considered as an explanatory mechanism for enhancement of performance of these nanostructures. The existence of this ET process has been proved in many studies using either experimental or computational approaches. In this study, a ternary nanocomposite system of Ag/TiO2/GO was prepared to evaluate the performance enhancement in two experimental models: a physical model (i.e., surface-enhanced Raman scattering (SERS) sensor) and a chemical one (i.e., catalytic reduction reaction). The metal/semiconductor heterojunction between Ag and TiO2, as well as Ti-O-C bonds, has allowed plasmonic hot electrons to be transferred in the internal structure of the material. An investigation on the role of Ag content on the SERS sensing and catalytic reduction efficiency of Ag/TiO2/GO was performed in both models. Interestingly, they all resulted in the same optimal Ag content of 50 wt%. It was then further discussed to provide a convincing evidence for the plasmon-induced electron transfer phenomena in the Ag/TiO2/GO nanostructure. These findings also suggest a pathway to design and develop high-performance, cost-effective, facile-preparation, and eco-friendly multifunctional nanostructures for detecting and removing contaminants in environment.


Introduction
It is now widely accepted that electron-transfer (ET) mechanism in metal-semiconductor (MS) nanocomposites/nanohybrids must be involved to explain the enhancement of their contaminant detection/degradation performance, in comparison to single metals or semiconductors [1][2][3][4][5].ET naturally occurs in connection with the transduction of energy.In MS materials, ET process takes place in a dualmode pathway.It means electrons can be transferred from metals to semiconductors or from semiconductors to metals, which depends directly on the wavelengths of excitation sources [2][3][4]6].When a metal nanostructure contacts with a semiconductor, a specific space-charge region is created in MS interface, which leads to the band bending in the semiconductor and gives rise to a Schottky transition [2,6].Due to the light-matter interaction between ultraviolet (UV) light and the semiconductor, electrons are excited and then, they can be injected into the metal via the Schottky transition, causing the increase of the electron lifetime [6].Meanwhile, localized surface plasmon resonance (LSPR) of the metal plays a central role in the generation of hot electrons when interacting with a visible or infrared light, followed by injection of the hot electrons into the semiconductor [1,3,5].As a result, a large number of active electrons were created, leading to the improvements in the efficiency of various applications such as sensing devices [4], photocatalysis [2], solar cells [3], photovoltaics [1], and photothermal therapies [5].
For several decades, many reports on ET process in MS structures, including both experimental and computational ones, have been published to clarify the importance of ET in the enhancement mechanisms of various technological applications [7][8][9][10].For instance, Furube et al. utilized femtosecond transient absorption spectroscopy on Au/TiO 2 to observe plasmon-induced ET from Au nanodots to TiO 2 nanoparticles (NPs) [8].Iida et al. proposed a directly transferred pathway of electrons from Ag nanoclusters to TiO 2 layers without passing through the conduction band of the Ag nanoclusters, using a computational approach [9].Filippin et al. reported on another approach, in which they employed surface-enhanced Raman scattering (SERS) platform as an experimental model to investigate the enhanced Raman signals of R6G using TiO 2 nanotubes decorated with Ag NPs, resulting in 9 × 10 7 of Raman enhancement factor (EF) [7].Yazid et al. investigated the enhanced catalytic reduction of 4-nitrophenol (4-NP) using AuNPs immobilized on the TiO 2 support; Au/TiO 2 exhibited superior catalytic activity in reduction of 4-NP, compared to AuNPs only [10].Those reports have clarified the ET process in MS interfaces.However, each of those reports only focused on one kind of material for one specific application while ET process in MS materials may have led to the enhancement of the performance of various applications.Therefore, using different experimental models to investigate the enhancement of the performance efficiency of different applications with one material structure may answer the question if ET process in MS structures would exhibit the same effects on those distinct applications.Furthermore, it would provide more convincing evidence for the ET process in internal MS structures.
However, one of the main drawbacks of MS structures is their low adsorption capacity due to the poor adsorption capacity of their components (i.e., metals and semiconductors) [11].Unfortunately, many popular applications including SERS sensors [12], photodegradation [13], and catalytic reaction [14] require an intimate interaction between the target molecules and the surface of the MS structures.Because of the poor adsorption capacity, only few target molecules can be adsorbed on MS surfaces to interact with active electrons, leading to the low performance of the applications using MS materials [12,13].Therefore, it is necessary to improve the adsorption capacity of MS materials to enhance their performance in those applications.
In the effort to find out an effective solution to improve the adsorption capacity of the MS structures, the introduction of graphene oxide (GO) to the nanocomposite structures has been regarded as a promising approach [15,16].GO is a two-dimensional carbon-based nanostructure which exhibits excellent adsorption capacity due to the presence of abundant oxygen functional groups such as hydroxyl, epoxy, and carboxyl groups on its surface [16].Wang et al. claimed that the photodegradation activity of TiO 2 /GO composites was remarkably superior to that of TiO 2 due to the strong absorption capacity of GO [17].In addition, GO can serve as an electron transporter.Gillespie et al. employed hybrid density functional theory calculations to propose that reduced-GO (rGO) in TiO 2 /rGO had acted as a photoelectron trap (electron acceptor) via Ti-O-C bonds, leading to extended lifetimes of photoexcited charge carriers in TiO 2 /rGO composites and improved photocatalytic efficiency [18].Electrons should have continued to be transferred from TiO 2 to the GO sheets, leading to a stronger enhancement in the performance of TiO 2 /rGO nanocomposites, in comparison to bare TiO 2 NPs.This study suggested an idea to fabricate other MS/GO nanocomposites, in which electrons can be transferred from metals to semiconductors and then GO sheets and improve the overall performance of their applications.
In this work, we prepared a set of Ag/TiO 2 /GO nanocomposites (as MS/GO nanocomposites) to investigate their ET process.However, instead of focusing on specific measurements, such as femtosecond transient absorption spectroscopy [8], we stressed on the enhancement of the performance of the MS/GO structures and the repeat of this phenomenon in different experimental models.Thus, we aimed to discuss in detail about the correlation between the ET process and the performance of these empirical models.In more detail, we employed two experimental models including a physical model (i.e., SERS sensor) and a chemical model (i.e., catalytic reduction).Using a set of MS nanostructures that differed in Ag ratios, we further clarified the effects of Ag content in the composite structure on the performance of Ag/TiO 2 /GO in each model.Moreover, the roles of TiO 2 , GO in the performance enhancement were also discussed.The similar optimal Ag content in two models provided a convincing evidence for the ET process in multifunctional Ag/TiO 2 /GO nanostructures.were purchased from Shanghai Chemical Reagent and used directly without further purification.Graphene oxide (GO) was prepared using a modified Hummers method.Double distilled water was used throughout the experiments.

Experimental Procedures
2.2.Synthesis of Ag/TiO 2 /GO Nanocomposites.Ag/TiO 2 /GO nanocomposites (ATG Nces) were synthesized through a facile wet chemistry approach as described in Scheme 1. First, pure TiO 2 NPs were fabricated via a modified sol-gel method based on TiCl 4 precursors [19].Gel solution was obtained by aging for 12 h at room temperature, followed by the annealing process at 400 °C for 4 h, which induced the crystallization of TiO 2 NPs.The crystalline TiO 2 (0.After 2 hours of reduction, the as-synthesized Ag/TiO 2 NPs were purified by three washing cycles (1000 rpm) using deionized water and were dried at 60 °C for 4 h.Then, GO nanosheets were synthesized using the modified Hummers' method reported by Paulchamy in 2015 [20].A simple self-assembly approach was employed to decorate GO nanosheets with functional Ag/TiO 2 NPs.A homogeneous solution containing Ag/TiO 2 NPs was prepared by an ultrasonic homogenizer for 20 min.Then, the self-assembly of Ag/TiO 2 on the GO (3 ml, 2 mg/ml) surface occurred under constant stirring at 200 rpm for 2 h.Finally, we obtained a set of ATG Nces with varied ratios of Ag including 25, 33, 50, and 75 wt%, named as A1TG, A2TG, A3TG, and A4TG, respectively.GO content is fixed to be 6 wt% in every kind of ATG Nces investigated in this study.
2.3.Characterizations.The crystal phase and composition of Ag/TiO 2 /GO were investigated by X-ray diffraction (Bruker D5005 X-ray diffractometer, Cu K α , λ = 1:5406 Å) under a voltage of 40 kV and a current of 30 mA.The morphologies of Ag/TiO 2 /GO were analyzed using scanning electron microscopy (SEM Hitachi S-4800) operating under an acceleration voltage of 5 kV and transmission electron microscopy (TEM JEOL JEM-1010) at an accelerating voltage of 80 kV.Chemical analyses of the nanocomposite were performed by Fourier-transform infrared spectroscopy (FTIR HL ReactIR 45P), Raman spectroscopy (Horiba Macro-RAM™) with 785 nm laser excitation, and Energy Dispersive X-ray Spectroscopy (EDS).Optical analyses were carried out using a UV-Vis spectrophotometer (JENWAY 6850), and 10 mm path length quartz cuvettes were used for the measurements of absorption ranges.
2.4.Investigated Experimental Models: SERS Sensor, Catalytic Reduction.To investigate the enhanced electron transfer in ATG Nces, two experimental models with different electronic excitation/providing sources were undertaken.
The first model was a SERS sensor based on the electronic excitation of a high-energy laser beam on Ag nanoparticles.
To evaluate the SERS activity of ATG Nces, methylene blue (MB) was selected as a reporter molecule.Solutions at various concentrations of MB (10 -4 to 10 -9 M) were prepared in water.The substrates were fabricated through a few facile steps, in which square aluminum (Al) substrates were prepared with the dimension of 1 × 1 cm 2 and surface-active circular area with a diameter of 0.2 cm.ATG Nces with different contents of Ag was dispersed in water, then coated on the surface-active of Al substrate by a drop-casting method, and dried naturally at room temperature.MB reporter with various concentrations was dropped directly onto the ATG Nces-Al substrate, followed by the natural evaporation of water.SERS measurements were acquired via Raman spectroscopy under an excitation wavelength of 785 nm by means of a 100x objective lens with a 0.90 numerical aperture.The laser power was set to be 45 mW at 45 °of contacting angle, with a diffraction-limited laser spot diameter of 1.1 μm (1.22 λ/NA, where λ is the wavelength of the laser, and NA is the numerical aperture of the microscope objective) and focal length of 115 nm.The expose time for each measurement was 10 seconds with 2 accumulations.A baseline calibration was conducted to obtain the final spectrum.Scheme 1: Schematic illustration of the synthesis steps for Ag/TiO 2 /GO ternary nanocomposite.

Adsorption Science & Technology
The second experimental model was based on the catalytic reduction property of ATG Nces with BH 4 -ions as an electron donor.The reduction of 4-nitrophenol (4-NP) to 4-aminophenol (4-AP) by NaBH 4 was selected as a model reaction for evaluating the catalytic reduction performance of our ATG Nces.First, 5 ml of 4-NP (2 × 10 −4 M in water) was mixed with 5 ml NaBH 4 (0.01 M in water); the solution turned from light yellow to bright yellow rapidly.Subsequently, 0.8 mg of ATG Nces with different contents of Ag was added to the solution.Time-dependent absorption spectra were recorded by UV-Vis spectroscopy.The degradation rate catalytic reduction model was calculated by using the following equation: where C 0 and C t represent, respectively, the initial 4-NP concentration and that at time t of degradation.

Results and Discussion
3.1.Characterizations of Ag/TiO 2 /GO.Scheme 1 demonstrates the formation of ATG nanostructures.Firstly, the Ag/TiO 2 NPs were fabricated due to the reduction of Ag + ions adsorbed onto TiO 2 crystal matrix.Then, the assynthesized Ag/TiO 2 NPs were self-assembled onto the surface of the GO sheets via electrostatic interactions.The morphology of ATG has been revealed in TEM and SEM images (Figure 1).01-086-1175).These results suggest successful formation of both Ag NPs and TiO 2 NPs in our as-synthesized composite nanomaterials.Furthermore, the diffraction peaks of ATG Nces are well-matched with those of Ag/TiO 2 (ICDD file No. 98-005-8369), which provides an evidence for the presence of Ag NPs in the TiO 2 crystal matrix.Besides, the Scherrer formula was employed to calculate the average crystal grain size of Ag NPs and TiO 2 NPs via their diffraction peaks [21].The obtained results of 43 nm for Ag NPs and 125 nm for TiO 2 NPs have confirmed the assumptions about their sizes that we have provided from TEM and SEM analysis.
FTIR, Raman, and EDX spectra were recorded to analyze the chemical properties of ATG Nces.In the FTIR spectrum of ATG Nces (Figure 2(b)), the characteristic peaks of O-H stretching vibrations (3651 cm -1 , 3078 cm -1 ) and C=O stretching vibrations (1715 cm -1 ) are in agreement with the peaks observed in the FTIR of GO, including a broad band appeared at 3580 cm -1 and a sharp peak at 1640 cm -1 , respectively [22].It can be ascribed to GO-containing ATG Nces.In addition, the characteristic peaks at 800 cm -1 and 467 cm -1 indicate to Ti-O-C bonding, which demonstrates the direct binding of TiO 2 onto the surface of GO sheets [23,24].Figure 2(d) shows Raman spectrum of ATG Nces, in comparison to those of GO and TiO 2 .The Raman spectrum of the nanocomposite reveals two prominent peaks corresponding to D-band (1300 cm -1 ) and G-band (1600 cm -1 ) of GO, between which D-band is broad and higher in intensity compared to G-band.The ratio of intensities between D-band and G-band (I D /I G ) of ATG Nces (1.6) is larger than that of GO-pristine (1.4).It has been reported that a broad D-band with higher relative intensity compared to that of G-band can be the result of high disorder in graphite [25].The disorder of graphite in our materials may be due to the deposition of Ag/TiO 2 on the surface of GO sheets [25].In addition, the two bands at 156 cm -1 and 635 cm -1 are also observed in the spectrum of TiO 2 , which are assigned to the E g modes of TiO 2 anatase phase.These Raman spectra have reconfirmed the presence of TiO 2 in the nanocomposite materials [26].The chemical composition of the ATG Nces surface was studied by EDX spectroscopy.The EDX spectrum (Scheme 1) indicates the presence of Ag, Ti, O, and C and proves the high level of purity of ATG Nces.To analyze the optical properties of ATG Nces, UV-Vis absorption spectra were recorded (Figure 2(c)).The spectra of both TiO 2 and ATG Nces exhibit a significant absorption band in the UV region.However, the absorption spectrum of ATG Nces shows higher band intensity and a red-shift in the absorption edge.To clarify this difference in absorption edge, the optical bandgap of TiO 2 and ATG Nces were determined via Tauc plot (Figure 2(c), inset) using Kubelka-Munk function [27].Tauc plot results indicate that the absorption edges in the spectra of TiO 2 and ATG Nces correspond to optical bandgaps of 3.15 eV and 2.83 eV, respectively.The difference in optical bandgap values between ATG Nces and TiO 2 can be explained by the interactions of TiO 2 and Ag (via attachment) and GO (via Ti-O-C bonding), which has been 4 Adsorption Science & Technology confirmed by XRD and FTIR spectra, respectively.The formation of Ag/TiO 2 and Ti-O-C bonds has fulfilled all the requirements for the nanocomposite materials to be employed to study the electronic transfer process in their internal structures.
3.2.SERS Sensor Model.SERS sensor was the first model that we employed to investigate the enhanced electron transfer in ATG Nces, taking advantages of the unique plasmonic properties of Ag and enhanced Raman scattering caused by chemical enhancement of the nanocomposite materials [4,12,28].As the plasmonic properties of Ag are the key to fabricate SERS sensors based on ATG Nces, a set of samples with distinct contents of Ag has been employed for SERS measurements as mentioned in Section 2, including A1TG, A2TG, A3TG, and A4TG. Figure 3(a) exhibits the SERS signals of MB in the presence of 4 kinds of nanomaterials as active substrates.On the substrate with 25 wt% of Ag (A1TG), the SERS spectrum reveals two characteristic peaks of GO (1300 cm -1 and 1600 cm -1 ) at high intensity.In contrast, the intensity of the characteristic peak of MB at 450 cm -1 is much lower.In the increase of Ag contents, the SERS spectra of MB on A2TG and A3TG do not show such significant peaks of GO but the characteristic peaks of MB at 450, 505, 1396, and 1620 cm -1 , which corresponds to vibrations of C-N-C skeletal deformation, C-S-C skeletal deformation, C-H in-plane ring deformation, and C-C stretching ring, respectively [29].Unexpectedly, when the Ag content increases up to 75 wt%, the intensity of the characteristic peaks of MB suffered a great loss, compared to A3TG.It has to be stressed that the concentration of MB solution for every measurement was the same; thus, it is undeniable that the Ag content has a great effect on SERS activity of the nanocomposite material.In this case, the highest intensity of the MB characteristic bands allows A3TG to be the most SERS-effective substrate, compared to A1TG, A2TG, and A4TG.Enhancement factor (EF) of ATG Nces with varied contents of Ag was calculated to further testify the SERS performance (Figure 3(a)).The SERS EF was observed in agreement with the previous report following the equation below [30]: The EF values of A1TG, A2TG, A3TG, and A4TG were calculated to be 9:7 × 10 4 , 2:1 × 10 5 , 3:6 × 10 5 , and 1:3 × 10 5 , respectively.This calculation reconfirms that A3TG Nces is the highest SERS-effective substrate.In addition to the impressive enhancement factor of A3TG, the limit of detection for MB deposited on this SERS substrate was down to 0.93 nM with a linear range from 10 -9 M to 10 -4 M (Figure 3(b)).It is obvious that Ag content has a great effect on the performance of SERS sensor using ATG Nc substrates.In this case, the optimal Ag content is 50 wt%.Similar results have been reported in previous studies on other composites such as ternary Au@Cu 2 O-Ag nanocomposite and Ag-TiO 2 composite [31,32].In Section 3.1, we have pointed out that the formation of Ag/TiO 2 structures and Ti-O-C bonds, which might be convenient chargeseparation pathways to increase the hot-electron age.Due to the local surface plasmon resonance (LSPRs) phenomenon, in which coherent electrons oscillate around the Ag NP surface formed hot electrons, it is reasonable that higher Raman intensity of MB was achieved when Ag content in ATG Nces increased (A1TG, A2TG, and A3TG).However, the unexpected decrease in the Raman signal of MB in the presence of A4TG might be explained by the surplus of Ag, which led to the decrease of TiO 2 and GO contents, as well as the formation of Ag/TiO 2 structures and Ti-O-C bonds.As a result, the electron transfer rate in the chargeseparation pathway in the internal structure of ATG Nces might have been reduced.In addition, the EF value of A3TG is no more than 5 times higher than that of A1TG, A2TG, and A4TG.These small differences cannot be due to electromagnetic mechanism as it is usually related to large 6 Adsorption Science & Technology enhancement (10 6 -10 10 or even more) [30].Instead, it can be explained by chemical mechanism, of which EFs are in the range of 10 1 -10 3 [33].It is worth mentioning that CM is directly related to electron transfer.Thus, in addition to the presence of Ag, the electron transfer through Ag/TiO 2 contacts and Ti-O-C bonds may be another factor causing the differences in the enhancement of Raman signal of MB on the ATG Nces containing varied Ag content.The important role of TiO 2 and GO in the improvement of the SERS sensitivity of ATG Nces was confirmed by a comparison among the SERS spectra of MB (10 -6 M) in the presence of only Ag NPs, Ag/TiO 2 , Ag/GO, and Ag/TiO 2 /GO (A3TG) (Figure 3(b)).Instead of 4 characteristic bands as mentioned previously, MB only exhibits 2 weak peaks at 450 cm -1 1620 cm -1 in the presence of only Ag NPs.The use of Ag/TiO 2 (50 : 50 wt%) obviously improves the sensitivity of the SERS sensing due to the presence of all characteristics.However, the intensity and the sharpness of the peaks are relatively lower than those using Ag/TiO 2 /GO as SERS substrate.The utilization of Ag/GO also results in high intensity of SERS signal.However, Dband and G-band of GO overlap the peaks at 1393 cm -1 and 1620 cm -1 of MB while two other ones at 450 cm -1 and 505 cm -1 are not as clear as those in the use Ag/TiO 2 /GO.This comparison has emphasized the role of TiO 2 and GO to enhance the SERS performance in the nanocomposite materials.Moreover, the materials achieved the highest efficiency in the presence of both TiO 2 and GO.It would confirm the hypothesis above about the impacts of the electron transfer through Ag/TiO 2 contacts and Ti-O-C bonds of ATG Nces in their SERS performance improvement.

Catalytic Reduction Model.
In addition to the physical model, we also generated a chemical one to answer the question of whether the electron transfer in the ATG Nces has any influences on other applications and how it affects their performance.A model of catalytic reduction was selected as its performance is directly related to electron transfer phenomena.The catalytic reduction model was studied through the reduction of 4-NP to 4-AP using NaBH 4 as an electronic providing source from BH 4 -to investigate the catalytic reduction properties of ATG Nces [34].To clarify the role of TiO 2 and GO on the catalytic reduction performance of ATG Nces, we prepared two sets of samples.One set included Ag, Ag/TiO 2 , Ag/GO, and Ag/TiO 2 /GO.The other one consisted of ATG Nces containing varied Ag contents.The materials from each set were employed as catalysts for the reduction of 4-NP to 4-AP in the same experimental conditions as mentioned in Section 2.4.For each comparison, we used the same experimental conditions as the mass of catalyst material (0.8 mg), the concentration of 4-NP (2 × 10 −4 M), NaBH 4 (0.01 M), and catalytic reduction reaction time (30 s).The absorption spectra of the reaction solutions in the presence of different catalysts were then recorded using UV-Vis spectroscopy.The peak at 400 nm in UV-Vis spectra, which is ascribed to 4-nitrophenolate ions, would be decreased gradually with time in the presence of catalytic materials, signifying the degradation of 4-NP.Contemporaneously, the appearance of a new band at 300 nm represents the formation of 4-AP [34].Figure 4 demonstrates the absorption spectra of the reaction samples using different catalytic materials in the two experimental sets.
Concerning the first set including Ag, Ag/TiO 2 , Ag/GO, and Ag/TiO 2 /GO, the 4-NP degradation efficiency of these four materials can be calculated based on the intensity of the absorption band at 400 nm (Figure 4(a)).Using Ag as the catalysts, the obtained absorption spectrum only exhibits a small decrease in the band at 400 nm, which represents the degradation efficiency of about 10% which is much lower than those of Ag/GO (~28%) and Ag/TiO 2 (~80%).Meanwhile, under the same reaction conditions, in the presence of Ag/TiO 2 /GO, 4-NP was nearly completely degraded with the disappearance of the 400 nm band.The reduction of 4-NP to 4-AM is also confirmed by the increase in intensity of the 300 nm band.As expected, the absorption spectrum of reaction solution in the presence of Ag/TiO 2 /GO shows the highest intensity at 300 nm, in comparison to the others.The differences in catalytic degradation efficiencies of the reaction using four distinct catalytic materials demonstrate the great effect of TiO 2 and GO on catalytic reduction performance of ATG Nces.In addition, Ag content also influences the performance of this application (Figure 4(b)).Thanks to the presence of Ag, TiO 2 , and GO in the composite structures, it is not surprising that the 4-NP degradation efficiencies of A1TG, A2TG, A3TG, and A4TG are relatively high.However, the differences appear in the 300 nm band as the reaction solution using A3TG results in the highest intensity compared to the other one.Therefore, in the catalytic reduction model, 50% wt is still the optimal content of Ag in ATG Nces.
As negatively charged 4-nitrophenolate and BH 4 -preferably interact with the metallic catalyst and facilitate the hydrogenation process on the 4-nitrophenolate, it is obvious that Ag is the key component in ATG Nces, which has the highest effect on catalytic performance.However, the presence of TiO 2 in Ag/TiO 2 has also enhanced catalytic performance.Moreover, the addition of GO has continued improving this performance.When discussing about the characterization of ATG Nces and the SERS sensor model, we have demonstrated the formation of Ag/TiO 2 nanostructures and Ti-O-C bonds as well as their effects on SERS sensing efficiency.Once again, TiO 2 and GO have exhibited their importance in the performance of another application using the ATG Nces.Furthermore, the same optimal Ag content in ATG Nces in both SERS and catalytic reduction models suggests a similarity in the mechanism of performance enhancement in both models.As mentioned in the previous section, this mechanism is based on the separation pathway in the internal structure of ATG Nces through Ag/TiO 2 nanostructures and Ti-O-C bonds.It has been claimed in previous studies that when a metal oxide contacted with a metal intimately, a Schottky junction would be formed and Fermi level alignment would lead to charge redistribution, which was also known as the electron transfer process [2,34].Besides, other reports stated that an additional band edge and a bandgap tuning were created due to the formation of Ti-O-C bonds and provided a conductive pathway for electron transfer from TiO 2 to GO [18,35].

Relationship of SERS Sensor Model and Catalytic
Reduction Model: Effects of Electron Transfer on Their Performance.The interesting similarity in optimal Ag content in both models has triggered us to further analyze the relationship between their performances and clarify the effect of electron transfer process on their performance.The comparisons of EFs in the SERS model and degradation efficiencies in the catalytic reduction model using ATG Nces with varied Ag contents are shown in Figures 5(a) and 5(b), respectively.A similar trend can be observed in the two graphs as EFs and degradation efficiencies both increase in the increase of Ag content and reach the highest peak at the content of 50 wt% (A3TG).Then, both of them decrease dramatically when the content of Ag rises to 75% (A4TG).Moreover, the similarity in impacts of TiO 2 and GO in the improvement of ATG Nces performance in both models is also worth mentioning.It may be an evidence for the ET pathway that will be further discussed in this section.
Concerning the SERS sensor model, according to quantum theory, when an incident laser light interacts with Ag NPs surface, Ag NPs serve as a light absorber, where hot electrons are generated due to by LSPR phenomenon [2].Previous reports have stated that the specific interaction of the adsorbed MB molecule and the surface of Ag might lead to electron transfer from Ag to MB molecule, named metal to molecular transfer [12].The superposition of energy levels should have been formed between Ag and adsorbed MB molecule [36].The Fermi level of Ag was reported to be -4.26eV [37], while the absolute energy of the lowest unoccupied molecular orbital (LUMO) of MB is -3.328 eV [38].Thus, the plasmon-induced hot electrons can be transferred from Ag into the LUMO level of MB, then decay with the SERS signal of MB.However, the adsorbed surface area of Ag is relatively small and MB ions are positively charged, so the absorption of MB on the Ag surface can be prevented.Therefore, that ET process should not have been completely responsible for the obtained SERS signal enhancement of our materials.This hypothesis has been confirmed by a significant loss of SERS signal when using the ATG Nces with surplus Ag content.Another ET pathway in the internal structure of ATG Nces, the metal-semiconductor transition, might have taken the lead in this case.Wu et al. proposed the ET pathway in a study about a system of CdSe-Au hetero-nanostructures and named this hot-electron transfer pathway a plasmon-induced interfacial charge-transfer transition (PICTT) to discriminate against the common plasmon-induced hot-electron transfer (PHET) or direct metal-to-semiconductor interfacial charge-transfer transition (DICTT) [39].In PICTT, the metal serves as a light absorber, but strong interdomain coupling and mixing of the metal and semiconductor levels lead to a new plasmon decay pathway.Besides, PICTT also exhibits the quantum efficiency to be higher than 24%.In addition, Iida and Noda reported on the photoinduced silver-TiO 2 electronic interaction that allowed the excited electrons to be directly transferred from the silver nanocluster to the TiO 2 layer without passing through the conduction band of the silver nanocluster.Nevertheless, it might potentially occur due to the formation of Ag-O bonds between the silver-TiO 2 layers [9] while in our nanocomposites, Ag and TiO 2 only form a weak interaction due to natural deposition.Thus, the PHET pathway might be the more suitable mechanism that has occurred in our materials.In PHET, the metal decays into a hot electron-hole pair through Landau damping, followed by injection of the hot electrons into the conduction band (CB) of the semiconductor [40].Here, electrons might have been transferred through Ag/TiO 2 interaction (Schottky junction).Moreover, TiO 2 is an excellent electron acceptor via d-orbital [41].In addition, plasmon-induced hot electrons can inject into CB of TiO 2 with conduction band minimum energy of -4.0 eV [42].Therefore, the transferred electrons have more opportunities to interact with MB molecule.Nevertheless, electron transfer process in CB of TiO 2 competes with electron relaxation through rapid electronelectron scattering.Then again, Ti-O-C might have been allowed electrons to be transferred from TiO 2 to GO sheets, whose Fermi level is -5.02 eV [25].Since GO is an excellent adsorber [16], the GO sheets might have increased the direct interaction between hot electrons to MB molecular.As a result, many active electrons have interacted with MB reporters via the charge-separation pathways in ATG Nces; thus, the Raman signal of MB has been enhanced by the chemical mechanism.
Concerning the catalytic reduction model, the potential charge-separation pathway in ATG Nces should have been an important factor to lead to the enhancement of 4-NP degradation efficiency.Due to the adsorption of negatively charged BH 4 -on the surface of Ag NPs, BH 4 -ions acted as electron donors that provided active electrons to Ag.In the same electron transfer pathway as in the SERS sensor model, electrons would have escaped from Ag and  In summary, the Ag content has a great effect on the electron transfer process in the internal nanostructure of  ATG Nces; therefore, it also influences the performance of SERS and catalytic reduction of ATG Nces.The same optimal Ag content, as well as the similar trend of performance changing observed in the presence of ATG Nces containing varied Ag content in those two models, has demonstrated the important role of electron transfer in the enhancement of their performance.Through the SERS sensor model and the catalytic reduction model, we propose a potential electron transfer pathway in ATG Nces via Ag/TiO 2 interaction and Ti-O-C bonds, which is exhibited in Figure 6.Thanks to the ET process, the performance of ATG Nces materials in different applications has been enhanced.With a low LOD of 0.93 nM, our ATG Nces-based SERS sensor for MB detection is capable to determine MB at extremely low levels.Table 1 presents the comparison in SERS sensibility among ATG Nces and several reported materials, in which ATG Nces-based sensor results in the lowest LOD.It suggests the development of high-performance SERS sensors using this nanocomposite material as the substrate for detection of other contaminants.Moreover, ATG Nces also exhibit excellent 4-NP removal efficiency via catalytic reduction reaction with 100% of 4-NP degraded after 20 s, which is competitive in comparison to several reported catalytic materials (Table 2).Similarly, the performance of other applications related to the electron transfer pathway, such as photocatalysis, electrocatalysts, and solar cells, might be also enhanced with the utilization of ATG Nces.Thus, with a few facile steps of preparation as mentioned in Section 2, we can fabricate a multifunctional material that consists of nontoxic components (i.e., Ag, TiO 2 , and GO).Furthermore, the synthesis can be scaled up to increase the mass production and reduce the cost of the fabrication.It suggests a direction to fabricate multifunctional, high-performance, cost-effective, facile-preparation, and nontoxic materials for detecting and removing contaminants.

Conclusions
In this work, Ag/TiO 2 /GO Nces were successfully synthesized.The SEM, TEM, XRD, FTIR, Raman, UV-Vis, and EDX results confirmed the formation of Ag/TiO 2 structure and the deposition of Ag/TiO 2 on GO nanosheets via Ti-O-C bonds.We investigated the electron transfer process in Ag/TiO 2 /GO Nces using two experimental models including SERS sensor and catalytic reduction, in which the Ag/TiO 2 /GO Nces acted as SERS substrates and catalysts.The optimal Ag content of 50 wt% was appropriate in both models.From these results, we proposed a chargeseparation pathway in the internal structure of ATG Nces that is suitable for both models.This study provides a clear explanation for the electron transfer process in composite nanostructures which leads to the enhancement of application efficiencies.
was added into 50 ml of C 2 H 5 OH.Subsequently, to arrive at different Ag contents in the nanocomposites, 10 ml of AgNO 3 solution at different concentrations of AgNO 3 (62 mM, 91 mM, 185 mM, and 555 mM) was added to the solutions.The mixture was subjected to vigorous stirring at room temperature for 1 h, allowing the adsorption of Ag + ions onto the TiO 2 NP's surface.A required 10 ml volume of NaBH 4 (62 mM, 91 mM, 185 mM, and 555 mM) was added to reduce ions Ag + to Ag 0 metals in each solution.

Figure 1 (
a) shows the TEM image of ATG Nces with the presence of three types of materials with distinct shapes and sizes marked as Type 1, Type 2, and Type 3.Both Type 1 and Type 2 are spherical nanostructures but differed in size.The distribution histograms of SEM result shown in Figure1(c) reveals the average diameters of Type 1 and Type 2 nanoparticles to be 50 nm and 100 nm with frequencies of 35% and 65%, respectively.Besides, Figure1(b)shows the presence of Type 1 on the surface of Type 2. Thus, it can be assumed that Type 1 nanostructures represent Ag nanoparticles while Type 2 ones represent TiO 2 nanoparticles.In addition, Figure1(c) and its magnified image (Figure1(e)) also exhibit a sheet-like structure which reminds of the two-dimensional structure of GO-pristine (Figure1(d)).The presence of Ag and TiO 2 nanoparticles on the surface of this sheet-like structure reveals the structure of Ag/TiO 2 /GO, in which the Ag/TiO 2 nanostructures have been situated on the surface of GO sheets.The presence of GO in the nanocomposite can be also observed in the TEM image (Figure1(a)) as large and plane nanostructures (Type 3).The XRD pattern of ATG Nces is shown in Figure2(a), in comparison with the reference patterns of TiO 2 , Ag, and Ag/TiO 2 .The position of the diffraction peaks at 2θ = 38:010, 44.09 °, and 64.03 °can be assigned to the (111), (200), and (220) planes of Ag NPs (ICDD file No. 01-087-0597), respectively.In addition, the XRD pattern also shows the diffractions of the crystal planes (101), (200), (211), (105), and (022) at 2θ = 25:410, 47.830, 54.990, 53.800, and 62.660, which correspond to anatase TiO 2 (ICDD file No.

Figure 1 :
Figure 1: TEM image of (a) Ag/TiO 2 /GO, (b, c, e) SEM images with different magnification and particle size distribution histograms of Ag/TiO 2 /GO, and (d) GO-pristine.

Figure 4 :
Figure 4: UV-Vis spectra of the catalytic reduction of 4-nitrophenolate (400 nm) to 4-aminophenol (300 nm) in the water and comparison of catalytic efficiency of Ag, Ag/TiO 2 , Ag/GO, and Ag/TiO 2 /GO (a); comparison of catalytic efficiency of varied contents of Ag in ATG Nces (b).

Figure 5 :
Figure 5: Comparison of enhancement factor (at 10 -6 M) (a) and degradation efficiency (b) of Ag/TiO 2 /GO with different Ag contents.

Figure 6 :
Figure 6: Potential electron transfer process in ATG Nces for both SERS sensor model (a) and catalytic reduction model (b) through Ag/TiO 2 contact and Ti-O-C bonds.