Calculation and Estimation of Surface Roughness and Energy Consumption in Milling of 6061 Alloy

,e best surface quality that can be achieved in manufactured products has become the main goal of industrial enterprises in recent years. Due to the subsequent increase in energy consumption costs from rising energy efficiency rates, manufacturers are contributing to this issue by applying advanced design functions for their machines. In line with the same objective, this study investigated the machinability of 6061 aluminum alloy, which has a high throughput rate and low machinability featuring built up edge. ,e aim of the research was to optimize the cutting parameters for minimum surface roughness (Ra) and energy consumption (EC) using a CNCmilling machine. At the same time, measurements of power indices (A) of both the spindle and theXaxis motors were carried out with the goal of improved chip removal as compared to literature studies. ,e experiment was designed according to the Taguchi L16 (2 × 4) orthogonal index. Four different cutting speeds (60, 120, 180, and 240m/min), feed rates (0.10, 0.15, 0.20, and 0.25mm/rev), and cutting depths (0.5, 0.10, 0.15, and 0.20mm) and two different cooling methods (coolant fluid and dry cutting) were selected as cutting parameters.


Introduction
Today, energy saving has become a significant consideration in the manufacture of both consumer products and industrial equipment. Studies on energy saving, especially recently, have focused on the required energy consumed in the production sector [1][2][3] for the manufacture of semi-and fully finished products. e industrial machining process forms an essential part of the global economy. e determination of the optimal criteria for this process can contribute to a maximum number of quality parts being produced at a minimum of energy consumption [4,5]. Roughness is an important factor in the assessment of mechanical components and can affect their performance. A low roughness value is desirable, but manufacturing costs and difficulties in processing make this a challenging goal. Production costs generally rise in parallel with reduced surface roughness [6]. Energy consumption in the machining process has previously been the subject of many studies. Cutting condition effects on power consumption in the drilling and end milling of S45C carbon steel were determined by Mori et al. using a vertical machining center [7]. In the milling of ASSAB 760 steel performed under dry cutting conditions, Liu et al. measured the forces via a dynamometer and the power consumption by a power meter. As a result, a new machining energy consumption model was introduced [8]. In the turning of AISI 6061 T6, Camposeco-Negrete reported the determination of optimal cutting parameters for minimal surface roughness, cutting force, cutting energy, and energy consumption [9]. Oda et al. experimentally determined the optimal inclined angle for lowering the consumption of energy [10]. In the turning of AISI 1045 steel, Shokoohi et al. determined the impact of the heat generated in the cutting zone on power consumption and workpiece quality [11]. e effects of tool features on power consumption during the processes of drilling and turning were examined by Neugebauer et al. [12]. In addition, Muñoz-Escalona et al. measured the energy consumption and surface roughness in the end milling of austenitic stainless steel under cryogenic, fluid coolant and dry cutting conditions [13]. Nas and Ozturk applied face milling to a spheroidal graphite cast iron workpiece, measured the increase in the consumed power index (PI) with an ammeter device, and optimized the machining process with two different cutting tools [14].
A model was presented for the establishment of the energy consumption allowance (ECA) according to the movement of the workpiece within the machining system [15]. In the slot milling of Al-7075, a model was proposed for estimating surface roughness. e hybrid technique used to develop the model was a combination of the analytically calculated specific cutting energy consumption (SCEC) and the experimentally characterized correlation of the SCEC and the surface roughness [16].
An examination of the literature studies showed that varying amounts of electrical energy are expended by machine tools depending upon their work loads and environments. During operation, the energy consumption is greater than the energy required to meet the demands of the machine. Consequently, the focus of this study was on the energy consumption throughout the duration of operation [17]. e surface quality of this material is lower than other alloys due to this BUE property. For this reason, it is very important, especially for the automotive and aerospace sectors, for the 6061 series aluminum alloys, which have low processability, to be at their best regarding the surface quality.
e energy consumption during cutting (P cutting ) gives information about the workability of the material. In this study, the aim was to optimize the cutting parameters to yield minimum surface roughness with minimum energy consumption during the manufacturing process by using the Taguchi method. Energy consumption surveys in the literature do not include measurements for the X-axis servo motors, where the cutting force occurs. In this study, the energy consumption values of both the spindle and X-axis servo motors during chip removal were examined along with the amount of surface roughness. In addition, the slot milling operation was investigated for the first time under both dry and wet (coolant fluid) cutting conditions.

Taguchi Design.
In order to achieve a successful outcome when conducting experimental studies, it is essential that the experiments be designed correctly. us, the experiments were designed and analyzed via the method of Genichi Taguchi. In this method, results are analyzed using the signal to noise (S/N) ratio to statistically measure the performance. e evaluation of the experimental results is carried out using the signal factor (S) as the actual value from the system and the noise factor (N) not as an element of the experimental design, but as an influencing factor on the result. All variables resulting in deviations from the target values for performance characteristics constitute sources of the noise. Dependent upon the quality characteristic, three cases are used when calculating the S/N ratio: "the nominal is the best," "the largest is the best," and "the smallest is the best" [18,19]. In the present study, as the lowest values for Ra and EC were desired for achieving machining efficiency, the S/N values were calculated according to "the smallest is best" formula, as expressed in the following equation: where y i represents the surface roughness and energy consumption values and n represents the number of experiments carried out. e machining parameters were selected as cutting speed (V), feed rate (f ), depth of cut (DOC), and cooling method (Cm). Table 1 presents the control factors and levels applied in the slot milling of the Al T6061 alloy. Table 2 shows the L 16 orthogonal array utilized in conducting the experiments. In order to determine the variable effect levels on Ra, analysis of variance (ANOVA) was applied on the experimental results (CI 95%). Minitab 16 software was used to carry out the experimental design and statistical analysis in accordance with the Taguchi method.
In general, due to their complexity, conventional experimental design approaches are challenging. Moreover, as the number of process parameters is increased, more experimental trials need to be conducted, thus requiring identification and control, under laboratory conditions, of the factors responsible for variations. By using the orthogonal arrays of the Taguchi design technique, the number of experiments can be reduced significantly, and better quality is ensured when the uncontrollable effects of those factors are reduced. erefore, the Taguchi experimental design and L 16 orthogonal index given in Table 2 were used for the study.

Workpiece, Cutting Tools, and Machining
Center. In this experimental study, SCC APKT 11T 308-PM series carbide tools, manufactured from TiNN PVD-coated tungsten-cobalt alloy, were used for the processing of the aluminum alloy. Chip removal was carried out by mounting a single insert to the 16 mm diameter APKT 11 R390 holder. e CNC milling machine used in the experiments was the Microcut CNC 1000 model with a 15 KW drive motor (Figure 1(a)). e Microcut vertical machining center has Fanuc spindle drivers. In this study, current transformers were connected to power cables having three phases in the power consumption drive inputs, and the experiments were performed by displaying the measured power index PI (A) from these current transformers using an Entes ammeter (Figure 1(b)).

Measurement of Energy Consumption and Surface
Roughness. Studies in the literature have generally measured changes in spindle servo motor energy consumption during the metal cutting process. Other studies did not consider the fact that energy was consumed with the table axis motor running in the direction of chip removal, whereas this study measured the energy consumed by both the X-axis and the spindle axis servo motors simultaneously. By using this 2 Advances in Materials Science and Engineering ammeter, it was possible to measure the energy index with ± 1% accuracy. e existence of a relationship between the machining power and the electrical current in three-phase motors was suggested by Shokoohi et al. [11]. Equation (2) was used to calculate Ptotal. While two-phase motors work with 220 V, that is, a phase voltage, three-phase motors work with 380 V, that is, three-phase network voltage (in Turkey Network). In the calculation of electrical power equation, besides the power coefficient and voltage, it is the third determining electrical current. In this paper, since other variables are taken as constant, the effect of current change on power change is discussed.
In this equation, when the ammeter's current value (I) was measured, the processing voltage value (V) of the CNC vertical machine was 0.38, while the value of the servo motors (Cos σ) was listed in the catalog as 0.6. When calculating the P total value in the chip removal process, the value of the machine during the period when chip is not being removed is defined by different names in the literature, such as (P idle ) and (P air ). e total power consumption can be used to calculate this value. Equation (3) can be used to calculate the cutting power (P cutting ) value, which is the main parameter effective on the surface roughness, tool wear, shear calculation, and chip formation during metal cutting [9,13,16].
Spindle and servo motor energy consumption stems from two sources. e first is the movement of the spindle shaft and workbench and acceleration/deceleration under the influence of inertia, friction resistance, and gravity. e second is the cutting force expended in overcoming cutting resistance [7]. Equation (4) presents the energy consumption model P (Wh) representing the machine tool operating mode (positioning and acceleration of the spindle after a tool change/machining/returning of the spindle to tool exchange position after machining/stopping of the spindle).
In equation (4),  [16,20] e energy consumption type in machining processes is defined as total energy consumption (SEC) and specific cutting energy consumption (SCEC) required for removing 1 cubic meter of the chip. Equations (5) and (6) give the specific energy consumption (SEC) and shear energy consumption (SCEC) required for chip removal [16,20].
Surface roughness values of the aluminum alloy workpiece after machining were determined using the Mitutoyo Surftest SJ-210 measurement device. Surface roughness (Ra and Rz) measurements were carried out in accordance with the ISO 4287 standard. After the experiments, the surface was measured at the beginning, in the middle, and at the end of each sample and the arithmetic average was taken as the surface roughness value.

Experimental Results.
e flow indices were measured and then the energy power conversion equations (equations (2)- (6) and the total energy consumption of the 6061 aluminum alloy during metal cutting were calculated (Tables 3 and 4). ese values were calculated for both the spindle servo motor and the X-axis servo motor. e low SEC and P cutting (kW) levels held great significance for electricity consumption in the tables.  Information about the workability of the product was also revealed by these data as the quality of the machining was directly affected by changes in the surface roughness. Examination of the graphs in Figure 2 shows that the surface roughness values reached the highest levels in the first four experiments, especially in the 3rd and 4th experiments. In these two experiments, maximum surface roughness values were achieved under dry cutting conditions with increases in depth of cut and feed rate. Depending on different materials and processing parameters, other     [13]. e SEC of both servo motors can be seen to occur in very high amounts at low revolutions. Similar results have been obtained in other studies [9,13,16]. A correlation can be seen between P cutting change and surface roughness values. Such a result had not previously been included in the literature. In order to express this relationship in graphic form, Figure 3 presents the effects of P cutting values of both spindle (S) and Xaxis (X) servo motors on the surface roughness (Table 5). When this figure is examined in detail, it has been determined that there may be a relationship between the P cutting S value measured from the spindle engine and the amount of surface roughness. It can be said that this cutting power is generally high for low surface roughness. On the other hand, when the surface roughness was greater than 4, this P cutting S value shows the lowest results for the spindle axis. Also, with an increase in the P cutting X values of the Xaxis servo motor, the amount of surface roughness stepped up in direct proportion. According to the results in this graph, the power of the X-axis servo motor has increased due to the probable ascend in the cutting force. At the same time, it is thought that the increase of these forces has stepped up the amount of surface roughness. e most likely reason for this situation was the BUE property of the 6061 alloy [21][22][23][24], which caused a reduction in its workability. Although a low surface roughness value was obtained during the ideal stock removal process, the stock removal energy consumption of the X-axis servo motor increased. e increase in X-axis motor energy consumption and reduction in the spindle servo motor energy consumption led to a general increase in the surface roughness value. ese results demonstrated that the forces directly affected electricity consumption and surface roughness.

Optimization of Surface Roughness (Ra and Rz) and
Energy Consumption (SEC S, P cutting S, SEC X, and P cutting X) Outputs. In the studies in the literature, different types of   4 5 6 7 8 9 10 11 12 13 14 15 16 Pcutting S (W) Test no.  4 5 6 7 8 9 10 11 12 13 14 15 16 Pcutting X (W) Test no.    Advances in Materials Science and Engineering coolants and machining processes, variable cutting parameters, the Taguchi experimental design, and ANOVA analyses have been used to investigate surface roughness. Previous studies have accounted for the spindle motor energy consumed during the cutting process dependent on the cutting speed. In this study, the energy consumption values of both spindle servo motor and X-axis servo motor were calculated and compared with the surface roughness results. In this way, energy expenditure on the X-axis motor, which determines the feed rate, was measured and the effects on surface roughness were investigated. In the slot milling operation, the influence of the BUE of the A6061 was determined under dry and coolant fluid cutting conditions. e Taguchi L 16 orthogonal array was used to carry out machining tests on Al T6061 alloy. e optimum levels of cutting speed, feed rate, and depth of cut were determined for energy consumption and surface roughness, and these values were used in the calculation of the S/N ratios (Tables 3-5).
e Taguchi method was used to generate the S/N responses which were used in the determination of the control factors most effective on the optimal levels of surface roughness and energy consumption. In this table, the highest S/N values represent the optimal levels of each control factor. Table 6 gives the effect of each control factor on surface roughness and energy consumption as shown by the S/N responses. e values in this table are obtained as a result of Taguchi optimization. We can determine the most effective input parameters on the output parameters and values in this table. However, the order of effects between the parameters is also determined. e response table is similar to analysis of variance. But rarely, it may differ. ANOVA results showed a parallel with the S/N response table in this study. e cutting speed, feed rate, depth of cut, and cooling method, respectively, were found to be the most effective factors on the surface roughness and energy consumption. e ANOVA results confirmed these findings. e main effect graph in Figure 4 shows the optimum values for the control factors (machining parameters). As in the S/N response table, the optimum level is indicated by the highest S/N value for each parameter in this graph. e optimal cutting speed, feed rate, depth of cut, and cooling method values determined for Ra were, respectively, 180 m/ min, 0.10 mm/rev, 0.5 mm, and wet machining, and for Rz, they were, respectively, 180 m/min, 0.15 mm/rev, 0.5 mm, and wet machining.

Confirmation Tests.
e experimental study obtained optimum surface roughness and energy consumption results via application of the Taguchi optimization method.
e ANOVA results revealed the effective percentage distributions of the parameters. As a final step, the validity of the optimization process was assessed by confirmation experiments. e Taguchi method was used to determine and calculate surface roughness and energy consumption values by applying equations (7)-(18) [25][26][27]. Using these equations under optimal milling conditions, Ra, Rz, P cutting S, P cutting X, SEC S, and SEC X were calculated, respectively, as 0.968 μm, 5.853 μm, 7.306 W, 20.133 W, 6.447 J, and 1.039 J.
Rz cal � 10 − η G /20 , Advances in Materials Science and Engineering In equations (7) where F α, 1, f e : F ratio at 95% CI, α: level of significance, f e : degrees of freedom of error, V e : error variance, n eff : effective number of replications, and R: number of confirmation experiment replications.
By using equations (19) and (20) Table 8. e predicted values and the experimental values can be seen to be very close. In order for statistical analyses to be considered reliable, error values must be below 20% [28,29]. Many important studies have been carried out on energy consumption during the machining process [30][31][32][33]. e comparison of surface roughness and energy consumption values (Table 8) underscores the fact that the level of difference between the results of the confirmation test and those obtained via the Taguchi method was insignificant. Consequently, the successful optimization was reflected in the results of the confirmation tests.

Conclusions
For this study, in the slot milling of Al T6061 alloy, a number of milling experiments were performed and experimental and statistical analyses on energy consumption and surface roughness were carried out. e experiments were designed according to the Taguchi L 16 orthogonal array and reached optimal surface roughness (Ra and Rz) and energy consumption (P cutting S, P cutting X, SEC S, and SEC X) values in a shorter time with 16 experiments instead of 128, resulting in savings of time and cost. is study determined the energy consumption of both servo motors used in the processing of the 6061 alloy, which is widely used in industry but has low workability due to BUE. Furthermore, the effects of these energy consumption values on the surface roughness values were also determined. e cutting parameters effective on energy consumption and surface roughness were determined via ANOVA. Confirmation experiments were conducted to assess the validity of the optimization. In conclusion, the following results were obtained from the study: (i) e surface roughness decreased as the energy consumption value increased for the spindle axis motor during cutting. (ii) On the contrary, as energy consumption values of the X-axis servo motor increased during cutting, the amount of surface roughness increased in direct proportion. (iii) e optimal Ra values for the cutting speed, feed rate, depth of cut, and cooling method were determined as 180 m/min, 0.10 mm/rev, 0.5 mm, and wet machining, respectively, whereas the optimal values for Rz were 180 m/min, 0.15 mm/rev, 0.5 mm, and wet machining. (iv) e optimal P cutting S values for the cutting speed, feed rate, depth of cut, and cooling method were determined as 60 m/min, 0.15 mm/rev, 0.5 mm, and wet machining, respectively, whereas the optimal values for P cutting X were 180 m/min, 0.10 mm/rev, 0.5 mm, and wet machining. (v) e optimal SEC S values for the cutting speed, feed rate, depth of cut, and cooling method were determined as 240 m/min, 0.25 mm/rev, 2.0 mm, and dry machining, respectively, while the optimum values for SEC X were 240 m/min, 0.25 mm/ rev, 2.0 mm, and wet machining. (vi) e ANOVA results determined the most important parameter effective on Ra and Rz to be the cutting speed, at 36.18% and 39.07%, respectively. (vii) e parameter most effective on P cutting S was determined as the cutting speed (70.20%), whereas for P cutting X, it was depth of cut (35.73%). (viii) e most effective parameter on SEC S and SEC X was the cutting speed, at 37.34% and 51.40%, respectively. (ix) According to the confirmation test, the values measured were found to be within the 95% confidence interval (CI).
As demonstrated by the optimization results, the Taguchi experimental design method was shown to have been successfully applied in the determination of the optimal values for surface roughness and energy consumption in the slot milling of the Al T6061 alloy.

A:
Power indices ANOVA: Analysis of variance BU: Built up edge CI: Confidence interval Cm: Cooling method CNC: Computer numerical control DOC: Depth of cut DF: Degree of freedom EC: Energy consumption Noise factor n eff : Effective number of replications PCR: Percentage contribution ratio PI: Power index (A) PVD: Physical vapor deposition P air : Energy consumption when the machine does not remove chips P idle : Energy consumption when the machine does not remove chips P total : Total power consumption P cutting : e energy consumption during cutting P cutting S: Power consumption in the S-axis P cutting X: Power consumption in the X-axis R: Number of confirmation experiment replications Ra: Surface roughness S: Signal factor SS: Sum of squares SEC: Specific energy consumption SCEC: Specific cutting energy consumption SEC S: Specific energy consumption in the S-axis SEC X: Specific energy consumption in the X-axis T dof : Total main factor degrees of freedom V: Cutting speed v: Voltage V e : Error variance.

Data Availability
e data used to support the findings of this study are available from the corresponding author upon request.

Conflicts of Interest
e authors declare that they have no conflicts of interest.