Study on the Photodegradation Stability of Poly ( butylene Succinate-co-butylene Adipate ) / TiO 2 Nanocomposites

A poly(butylene succinate-co-butylene adipate)/TiO2 (PBSA/TiO2) nanocomposite was prepared by a melt-blending process. )e effect of TiO2 nanoparticles on the photodegradation behaviors of the nanocomposite was investigated by transmission electron microscopy (TEM), differential scanning calorimetry (DSC), Fourier-transform infrared spectroscopy (FT-IR), field-emission scanning electron microscopy (FE-SEM), rheological measurements, and mechanical tests. TEM images of the PBSA/TiO2 revealed that the TiO2 nanoparticles were well dispersed in the matrix without obvious aggregation. )e FT-IR results indicated that the TiO2 nanoparticles can block high-energy ultraviolet (UV) light and reduce the degradation of the PBSA matrix. )e viscosity analysis results indicated that the TiO2 nanoparticles inhibited the chain scission of PBSA matrix under irradiation. In addition, the surface of the PBSA/TiO2 films and their mechanical properties change less than that of untreated PBSA films during the photoaging process. )e obtained results imply that the TiO2 nanoparticles can be considered as an efficient photodegradation-resistant additive to PBSA for reducing photodegradation.


Introduction
Biodegradable polymers have gained significant attention because of their potential to alleviate certain environmental problems [1,2].Specifically, poly(butylene succinate) (PBS) and copolymer poly(butylene succinate-co-butylene adipate) (PBSA) are very attractive for their mechanical properties and service temperatures, which are even comparable with current polyolefin materials [2].At present, these chemicals can find applications in packaging materials, biodegradable fibers, injection-molded products, mulch films, and other areas [3,4].Unfortunately, an insufficient service life limits this material's further applications, as it is easy to become fragile during storage, transportation, and outdoor use by exposure to heat, oxygen, and ultraviolet (UV) light [5].As reported by Konstantinou and Albanis [6], the service environment is the cause of oxidation and loss or breakage of small molecular components, which eventually leads to the poor physical properties of PBSA.
As the stability of the mechanical properties during the aging process is important for extending service life, many researchers have attempted to reduce any change in the physical properties of PBS over time, such as chemical copolymerization, physical blending, and nanocompounding [2,[7][8][9].However, there is little research on improving the stability of PBSA's mechanical properties during the photoaging process.
Yang et al. [10] used SiO 2 , Al 2 O 3 , and ZnO nanoparticles as inhibitors on linear low-density polyethylene (LLDPE) and compared three kinds of composites to the pure LLDPE after irradiation.e results showed that all three types of nanoparticles improved the photodegradation stability of the resulting nanocomposites.Huang et al. [11] prepared PBS/TiO 2 nanocomposites via a vane extruder and found that the introduction of TiO 2 improved the thermal stability and mechanical properties stability of the nanocomposites.Yang et al. [12] studied the UV-blocking property of TiO 2 powders with different-sized additives for films and fabrics, showing that TiO 2 is a good UV-barrier-additive for polymer matrices due to their properties of UV absorption, scattering, and reflection.
In the studies mentioned [10][11][12][13][14][15][16][17][18][19], the TiO 2 nanoadditives have attracted a high degree of attention, mainly because they are not only UV-screening agents but also performance-enhancing additives.Furthermore, as TiO 2 is more refractive than that of most light-colored inorganic additives, such as SiO 2 , Al 2 O 3 , ZnO, and others, the ability of shielding UV radiation is stronger than that of other additives [20].e purpose of this paper was to improve the photodegradation stability and prolong the service life of PBSA by adding nano-TiO 2 additives based on their UVscreening characteristics.
e different TiO 2 loadings of PBSA/TiO 2 nanocomposites were prepared by a meltblending process.
e effect of the TiO 2 nanoparticles on the photodegradation behaviors of the nanocomposite was investigated by transmission electron microscopy (TEM), differential scanning calorimetry (DSC), Fouriertransform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), rheological measurements, and mechanical tests.

Materials.
e PBSA pellets were supplied by Blue Ridge Tunhe Polyester Co., Ltd.(China).e comonomer content of the adipic acid used for PBSA was set at 5 mol%.e index of the melt flow was 16.1 g per 10 min.e melting temperature was 111.9 °C.Rutile TiO 2 nanoparticles coated with silicon-aluminum composite compounds were supplied by Hangzhou Wanjing New Material Co., Ltd.(China).
e speed of the rotary was 40-60 rpm, and the mixing temperature was 140 °C.When preparing the PBSA/TiO 2 nanocomposite with 0.1 wt.% TiO 2 , 49.95 g of PBSA pellets was first fed into a mixing chamber and blended for 2 min at 140 °C.en, 0.05 g of TiO 2 nanoparticles were added to the chamber and blended for another 10 min.PBSA/TiO 2 nanocomposites containing 0.5, 1.0, and 1.5 wt.% TiO 2 were prepared according to the proportional relation.e pure PBSA pellets were also blended in the mixing chamber for 2 min at 140 °C.e films and plates of the pure PBSA and PBSA/TiO 2 nanocomposites were molded by hot-pressing.
e thicknesses of the film samples and plate samples were about 100 μm and 2 mm, respectively.

Photoaging Test.
e film and plate samples with different TiO 2 contents were exposed to the aging chamber for accelerated photoaging tests.e aging test of the samples was carried out at 38 ± 2 °C in a Q-SUN xenon test chamber (Xe-3-HS, Q-Lab Co., USA) for different times.e energy distribution in the test chamber simulated that of the solar spectrum, and the relative humidity in the chamber was 30 ± 5%.

Morphology Characterization.
e surface morphology of film samples was observed by SEM (JSM-7401, Japan).e SEM samples were plated with platinum before observation at a scan voltage of 3 kV.e dispersion of TiO 2 nanoparticles in the PBSA matrix was observed by TEM (JEOL JEM-2000) at a voltage of 120 kV. e TEM samples were prepared with a microtome (Leica EMUC 6, Germany) at −80 °C, and the samples were placed on copper grids.

Carbonyl Index Determination.
e FT-IR spectra of the film samples were analyzed by an FT-IR spectrometer (Nicolet-6700, USA) with a Ge-attenuated total reflection detector.e wavenumber range was from 400 to 4000 cm −1 by signal averaging 32 scans at a resolution of 4 cm −1 .e carbonyl index (A C�O /A C-H ) was defined as the area ratio of carbonyl absorbance to the reference peak [21][22][23], and the changes in the carbonyl absorbance are represented in detail in the region of 1600-1800 cm −1 .e 2856 cm −1 peak was attributed to the C-H stretching according to the previous literature [24].

Viscosity Aging Index Determination.
e dynamic rheology of the plate samples was measured by a stress-/ strain-controlled rheometer (Anton Paar MCR301) [25,26].
e diameter of the rheometer parallel plate was 25 mm, and the testing gap was 1 mm.e oscillatory shear model was used in the rheological tests with parameters set at a temperature of 140 °C, a deformation strain of 1%, and a sweep frequency range from 0.01 to 100 Hz.In order to compare the decrease of the zero-shear viscosity of samples after irritation, the viscosity aging index (VAI) was introduced according to the following formula: where |η * 0 | is the initial viscosity value, with the data read from the curves of complex viscosity at 0.01 Hz of samples, and |η * t | is the aged viscosity value.

ermal Analysis.
e thermal behavior of the film samples was tested by a differential thermal analyzer (Shimadzu DSC-60, Japan) at an N 2 flow of 50 mL/min.e samples (3-5 mg) were sealed in aluminum crucibles with an empty aluminum seal crucible as a reference.During the test, the sample was heated from 30 to 160 °C then held for 5 min in order to eliminate the thermal history in the aging test; then the sample was cooled to 30 °C. e rate of the heating and cooling operations was both 10 °C/min.e crystallinity of PBSA/TiO 2 and pure PBSA nanocomposites was calculated with the following formula: where ΔH m is the melting enthalpy of the sample, ΔH 0 m is the melting enthalpy of PBS that is 100% crystalline (ΔH 0 m �110.3J/g [27]), and ω is the content of TiO 2 in the PBSA matrix by weight percentage.

2
Journal of Chemistry

Mechanical Tests.
e mechanical properties of the film samples were measured at 25 ± 2 °C by a TS-2000 tester (Gotech Inc., Taiwan), including tensile strength and elongation at break.e sample was conditioned in 30% relative humidity for 48 h at 25 ± 2 °C before testing.e rising speed of the crosshead was 10 mm/min.e final test results were calculated from the mean value of five measurements for each sample.

Dispersion of Nanoparticles in Polymer Matrix.
Figure 1 shows a TEM image of PBSA/TiO 2 nanocomposites containing 1.5 wt.% TiO 2 , from which it can be seen that the TiO 2 nanoparticles are dispersed evenly in the PBSA matrix without obvious aggregation, and the size of nanoparticles is from 30 to 50 nm.e good dispersion of TiO 2 in PBSA can be attributed to the surface modification by the coated compound [28] and the high sheer forces during extrusion, which reduced the aggregation of the nanoparticles.

FT-IR Characterization.
e FT-IR spectra of pure PBSA was acquired; the peak in the 1046 cm −1 region is due to the stretching of the carbon-oxygen bond [29].e 1157 cm −1 peak was assigned to the stretching of the carbonoxygen-carbon group in the ester bond of PBSA [30].e band region from 1650 to 1750 cm −1 results from C�O stretching of the ester group [29] and the degradation fragments [31].e 2856 and 2946 cm −1 peaks were assigned to C-H stretching, and the peak at 2856 cm −1 peak was used as the reference in calculating the value of the carbonyl index [24].
Carroccio [32] investigated the photo-oxidation of poly(butylene succinate) by mass spectrometry and ascertained three photo-oxidation processes of aliphatic polyesters, including α-hydrogen abstraction, the Norrish I of chain cleavage, and the hydroxyl end groups oxidation.During the processes of photo-oxidation, many aldehyde and carboxyl groups were produced, and the content of carboxyl groups changed dynamically at different oxidation times (Scheme 1), which corresponds with the increase and broadening of C�O peaks with increasing irradiation, as seen in Figure 2.After further comparisons of the FT-IR curves for the PBSA/TiO 2 nanocomposite with pure PBSA under the same irradiation time in Figure 2, the increase of the C�O peak intensity for the PBSA/TiO 2 nanocomposite is less than that of pure PBSA, which indicates that the TiO 2 nanoparticles can significantly prevent the PBSA photodegradation process.
Normally, the carboxyl groups can be used as a signature to reveal the degree of photodegradation of PBSA [31].Figure 3 shows the changes in the carbonyl index of the PBSA/TiO 2 nanocomposites and pure PBSA at different irradiation times.It can be seen that the photodegradation process starts immediately as the irradiation process starts [27].e carbonyl index of the pure PBSA is higher than that of any PBSA/TiO 2 nanocomposite.With the increase of the TiO 2 content, the value of the carbonyl index decreases gradually at the same irradiation time. is means that TiO 2 is an effective stabilizer for PBSA under irradiation.e improvement in the photostability of PBSA with the nano-TiO 2 results from the fact that the rutile-type TiO 2 nanoparticles have strong absorbability within the UV band by the quantum size effect [11,12], which can block highenergy UV light effectively and reduce photodegradation of the PBSA matrix.

Rheological Properties.
e changes of molecular weight and the degradation degree of the polymer can be characterized by the change of viscosity [25,26].Figure 4 presents the complex viscosity of the PBSA/TiO 2 nanocomposites and pure PBSA both before and after 360 h of irradiation.All samples exhibit a non-Newtonian behavior in the entire frequency range of the rheological test and show the characteristic of shear thinning.e zero-shear viscosities of all nanocomposites are higher than that of pure PBSA, while the complex viscosity (|η * |) of all nanocomposites decreases more rapidly than that of pure PBSA with the increase of frequency, demonstrating a much stronger shear thinning behavior [24].
Figure 4(a) shows the complex viscosity, (|η * |), measured at 140 °C as a function of the frequency before irradiation.e addition of nanoparticles leads to a significant increase in the viscosity at low shear rates.Similar behaviors have been previously observed for other nanocomposites [33,34], with the reason behind the behavior being that TiO 2 can act as a physical entanglement point and improve the complex viscosity of PBSA at low frequencies.e formation of physical entanglement points in polymers results in the stress transfer between matrix and filler, which is beneficial to the improvement of mechanical properties, such as the tensile modulus and yield strength [34,35].
After irradiation, it can be seen that there was an obvious reduction of the zero-shear viscosity in the samples after 360 h of irradiation when compared to the initial samples (Figure 4(b)).As reported previously [36,37], there is a power law relationship between the molecular weight and the zero-shear viscosity of linear polymers.Corresponding to the Norrish I reaction of the photo-oxidation processes in Scheme 1, the decrease of the zero-shear viscosity indicates that the photodegradation of PBSA provokes chain scission; then the low-molecular-weight products have been formed by degradation [38].Table 1 lists the VAI values of pure PBSA and the PBSA/TiO 2 nanocomposites after 360 h of irradiation.e VAI value of pure PBSA is as large as 89.3%, and the value decreases with the increase of TiO 2 in the matrix of the PBSA/TiO 2 nanocomposites, which results from the positive effect of TiO 2 during the photoaging process.

3.4.
ermal Properties.e thermal properties of the samples for different irradiation times were detected by DSC.
e crystallization temperature (T c ) and melting temperature (T m ) were obtained by reading the peak values of cooling curves and heating curves, respectively.e crystallinity was calculated from the DSC curves.

Journal of Chemistry
Figure 5 shows the change of T c and crystallinity of the PBSA/TiO 2 nanocomposites and pure PBSA both before irradiation and after being irradiated for 72, 120, 240, and 360 h.For the unaged samples, it can be seen that the T c and crystallinity of pure PBSA are the smallest.With the increase of TiO 2 content in the PBSA/TiO 2 nanocomposites, the T c and crystallinity increase gradually.
e relationship between both the test parameters of the samples and the TiO 2 content shows that TiO 2 is beneficial for promoting the nucleation and crystallization of PBSA, which was also reported by Zhou et al. [39].
From the data in Table 2, the T m of all samples show few differences after 360 h of irradiation.However, the T c decreases, and the crystallinity increases significantly after 360 h of irradiation.Furthermore, the pure PBSA showed the largest decrease in T c and the maximum increase in crystallinity.e decrease in T c can be attributed to some long chains of PBSA breaking during UV irradiation with the broken short chains having stronger mobility, which is helpful for ordering shorter chains at lower temperature and reducing the crystallization temperature [23].In addition, the higher mobility of the broken molecules in the Norrish I H Scheme 1: Overall photo-oxidation processes in PBS and its copolymers [32].4 Journal of Chemistry amorphous regions can cause them to rearrange and recrystallize, which promotes the increase of crystallinity [40].
As the TiO 2 content increases in pure PBSA, the degradation of the PBSA chains decreases gradually, and the effect of the degraded shorter chains on reducing the crystallization temperature and promoting crystallization is weakened accordingly.

Surface Morphology.
e morphological changes caused by irradiation were analyzed by SEM to reveal the effect of surface changes on the photodegradation.Figure 6 shows the surface changes of PBSA/TiO 2 nanocomposites and pure PBSA film both before and after 360 h of irradiation at a magnification of 3 kX.Before irradiation, both the PBSA/ TiO 2 nanocomposites and pure PBSA film exhibit a relatively smooth surface.
e surface of the pure PBSA film becomes rough with randomly distributed pores appearing after 360 h of  irradiation, which is consistent with the observations by Zhang et al. [23].e formation of the pores is due to the degradation of the PBSA, beginning from the film surface, and then deteriorating in the depth dimension with irradiation time.In contrast, the surface of the PBSA/TiO 2 film changes little under the same irradiation conditions, which shows that the TiO 2 nanoparticles can effectively delay the aging of the PBSA matrix.
3.6.Mechanical Properties. Figure 7 shows the mechanical properties of film samples for different irradiation times.For the pure PBSA film, the tensile strength is 16.6 MPa, the elongation at break is 431%, and both mechanical parameters obviously decreased with the increase of irradiation time.For the unaged samples containing TiO 2 nanoparticles, the tensile strength increased, and the elongation decreased compared to pure PBSA (Figure 7(a)).As the irradiation time increased, the elongation of PBSA/TiO 2 nanocomposites decreased gradually, and the strength changed slowly.As can be seen from Figure 7(b), as the aging time increases, the elongation at break of the pure PBSA decreases from 420% to 250%, while that of nanocomposites containing 1.5% TiO 2 decreases from 337% to 302%.e changing trend of elongation at break after irradiation is similar to that of VAI in the rheological test in Table 1, which indicates that nano-TiO 2 can effectively prevent the breaking of molecular chains as the elongation at break has correlation with molecular weight, and it has a positive effect on maintaining the mechanical properties during irradiation.

Conclusion
In this study, rutile TiO 2 nanoparticles were mixed with PBSA, and the PBSA/TiO 2 nanocomposites were successfully prepared by melt-blending.
e effect of the TiO 2 nanoparticles on the photodegradation behaviors of the nanocomposites was investigated.e changes in the carbonyl index analysis, thermal properties, and rheological properties of the pure PBSA were caused by chain cleavage and group oxidation under the photoaging process, which spurred the surface of the sample until it was rough and worsened its mechanical properties.e rutile-type TiO 2 nanoparticles, well dispersed in the matrix, can retard the chain scission of

Data Availability
e compressed data named DATA.rarused to support the findings of this study have been deposited in the Figshare

2 Figure 3 :Figure 4 :
Figure 3: Changes in the carbonyl index of PBSA/TiO 2 nanocomposites and pure PBSA at different irradiation times.

Figure 5 :
Figure 5: (a) Crystallization temperature and (b) crystallinity of PBSA/TiO 2 nanocomposites and pure PBSA as a function of irradiation time.

Figure 6 :Figure 7 :
Figure 6: SEM images of surface changes before UV irradiation of (a) pure PBSA and (b) PBSA containing 1.5 wt.% TiO 2 and after 360 h UV irradiation of (c) pure PBSA and (d) PBSA containing 1.5 wt.% TiO 2 at a magnification of 3 kX.

Table 1 :
VAI values of PBSA/TiO 2 nanocomposites before and after 360 h of UV irradiation.

Table 2 :
ermal parameters of PBSA/TiO 2 nanocomposites with and without irradiation time.effectively improves the surface integrity and mechanical properties of the nanocomposites under irradiation.is study may promote the application of PBSA in the industry and improve its service life.