Preparation of Pore-Size Controllable Activated Carbon from Rice Husk Using Dual Activating Agent and Its Application in Supercapacitor

Activated carbons prepared from rice husk by chemical activation with dual activation agents, KOH and NaOH, have been studied and characterized by BET, SEM, EDX, FTIR, Boehm titration, Raman, and TGA. It was found that the KOH/NaOH impregnation ratio plays an important role on textural properties of AC. At the same amount of total alkali hydroxide, the KOH/NaOH ratio higher than 1.33 resulted in larger specific surface area (2990∼3043m·g), microporous surface area (2747∼2831m·g), and higher micropore volume (1.4250∼1.4316 cm·g). -e as-prepared samples exist in the form of spherical-shaped particles with the size ranging from 20 to 60 nm and contain numerous surface functional groups. -e asprepared activated carbons were then assessed as an electrode material of supercapacitor operating in the 0.5MK2SO4 electrolyte in potential windows of −1.0∼0.0 V. -e highest capacitance obtained was 205 F·g at the scan rate of 2mV·s and 225 F·g at a current density of 0.2 A·g. At the scan rate as high as 50mV·s, all the as-prepared activated carbons in this study have the specific capacitance greater than 100 F·g.


Introduction
It is well known that activated carbon (AC) is a material with a porous structure and high specific surface area and is widely used as an adsorbent in water/air treatment, catalyst supporter, or electrical energy/gas storage material.By utilizing agricultural wastes, the synthesis of AC becomes more cost-effective which helps us to speed up the commercialization process measurably.
e preparation of AC consists of two stages: the carbonization stage at lower temperature and the activation stage at elevated temperature.Due to the advantage of lower temperature, shorter time, and developed porous structure, chemical activation is usually chosen over physical activation.In the chemical activation process, the chars (carbonized materials) are impregnated in activation agents such as potassium hydroxide (KOH), sodium hydroxide (NaOH), zinc chloride (ZnCl 2 ), and phosphoric acid (H 3 PO 4 ) followed by activation at temperature in the range between 600 and 900 °C under nitrogen flow.e characteristics of the resulting AC are very sensitive to preparing conditions, especially types of activating agents.e activated carbons prepared from lapsi seed (Nepal) are highly porous when activated by KOH or CaCl 2 than nonactivating agent pyrolyzed char; on the other hand, the activated carbons impregnated with MgCl 2 , FeCl 3 , and H 2 SO 4 do not show porous structure [1].Activated carbons prepared from macadamia nutshells have more microporous structure when activated by KOH while have more mesoporous structure when activated by ZnCl 2 [2].With agricultural waste precursors, the alkali hydroxide activating agent produces more developed surface area than other salts, oxides, or acids.For example, Enteromorpha prolifera (China) based activated carbon activated by KOH resulted in higher surface area and larger total pore volume than that activated by H 4 P 2 O 7 [3]; tomato paste processing industry waste (Turkey) established highest surface area that was activated by KOH, much larger than by K 2 CO 3 or HCl [4].
Furthermore, for rice husk, because of its high silica content, alkali hydroxide leaching is a preferable method for AC preparation.Comparative researches between KOH and NaOH have been conducted and showed that NaOH activation can satisfactorily control the mesopore volume of the activated carbons [5].e KOH ACs had higher micropore volumes, whereas NaOH ACs had relatively higher densities [6].Another difference between the activation process by KOH and NaOH is that KOH can be used effectively with any types of materials while NaOH only with disorder materials.
is is ascribed to the intercalating ability of metallic K compared to metallic Na produced during the redox reactions.Metallic Na can only intercalate into the highly disorganized materials [7].Nevertheless, no study has been conducted to use both KOH and NaOH as well as the effect of the KOH/NaOH ratio on the properties of activated carbon.
e main objective of this work is to prepare AC from rice husk with high porosity and large specific surface area using dual activating agent (KOH and NaOH) and investigate the effect of the NaOH/KOH ratio on the specific surface area, pore structure, morphology, and thermal stability of the AC samples.Moreover, the obtained materials were characterized and evaluated for potential application as supercapacitor electrode materials.

Materials and Chemicals. Rice husk was collected from
Vinh Phuc Province, Vietnam.
e raw precursor was washed, oven-dried at 110 °C for 12 h, grounded, and then sieved to obtain uniform particle with a diameter of 1.0 mm.All chemicals used were of analytical reagent grade, and distilled water was used to prepare all solutions.

Preparation of Activated Carbon.
e prepared husks were first carbonized at 500 °C for 90 min in nitrogen atmosphere.e resulting chars were then impregnated with KOH and NaOH under various impregnation weight ratios as indicated in Table 1.For comparison, the chars were also impregnated with only KOH or NaOH (with the same molar ratio).e activation process was carried out in a tube furnace under nitrogen flow of 300 mL•min −1 and at heating rate of 10 °C•min −1 .e samples were heated to 400 °C and left for 20 min, and then afterwards, the temperature was raised to 850 °C and maintained for 90 min (following our previous research [8] and other literatures [9]).e activated products were washed sequentially with 0.1 M HCl solution and hot distilled water to the neutral pH range (6.6-7.0).Finally, the activated carbon samples were dried at 120 °C for 24 h and stored for use.e as-prepared samples were labeled as presented in Table 1.

Characterization of Activated Carbons.
Textural properties of the ACs were measured from N 2 adsorption/ desorption isotherms at 77 K (Micromeritics, TriStar 3020).
e specific surface area (S BET ) was calculated by the Brunauer-Emmet-Teller (BET) equation [10]; the microporous surface area (S mic ), external surface area (S ext ), and micropore volume (V mic ) were evaluated by the t-plot method [11]; and the mesopore volume (V mes ) was obtained by the Barrett-Joyner-Halenda (BJH) method [12].e total pore volume (V tot ) was evaluated by the sum of microporous and mesoporous volumes.e pore-size distribution of AC samples was calculated using density functional theory (DFT) [13] with the assumption that the pores of the sample have slit shape.e morphology of the activated carbons was observed using a field-emission scanning electron microscope S4800 (Hitachi).e element analysis was determined using SM-6510LV (Jeol).
e surface chemistry characteristics were identified by Fourier-transform infrared spectroscopy (Nicolet, Nexus 670) operating in a wave number range of 500-4000 cm −1 and employing the potassium bromide pellet method.
e concentrations of surface acidic/basic functional groups were determined by following the Boehm titration method [14] and were calculated under the assumption that NaOH neutralizes carboxylic, phenolic, and lactonic groups; Na 2 CO 3 neutralizes both carboxylic and lactonic groups; and NaHCO 3 neutralizes only carboxylic groups.e amount of basic groups was calculated from the amount of hydrochloric acid consumed by the ACs.
Raman spectra were obtained with the Renishaw Raman microscope using an excitation wavelength at 250 nm.
e thermal behavior was performed with the thermogravimetric analyzer (DTG-60H, Shimazu).Before measurement, the AC samples were dried in air at 120 °C in 2 h to remove adsorbed water.en, the AC samples were heated from 120 to 650 °C in pure air (flow rate 50 mL•min −1 ) at a ramping rate of 10 °C min −1 .Measurements were made using calcined alumina as reference material.

Electrode Preparation and Electrochemical Measurement.
A mixture of activated carbon, conductive additive (carbon black), and binder (polytetrafluoroethylene) with weight ratio 8 : 1 : 1 was dispersed in ethanol.e slurry was laminated on each side of the current collector (nickel foam) and dried in oven at 120 °C for 15 h.e resulting electrode was then pressed under 20 MPa and cut into 1 cm × 1 cm geometry shape.Electrochemical measurements were conducted in a three-electrode cell using an Autolab 302N instrument.e as-prepared activated carbon electrode was used as the working electrode, with saturated calomel Specific capacitance based on CV measurements was calculated by the following equation: while the gravimetric specific capacitance based on charge/ discharge curves was evaluated by the following equation: where  |I|Δt is the area of the current (A) against the time (s) curve, m is the mass of the active material in the electrode (g), I d is the discharge current (A), Δt d is the discharge time (s), and ΔV is the potential interval (V).

Activated Carbon Characterization
3.1.1.Porous Texture.Nitrogen adsorption/desorption isotherms at 77K of AC samples prepared at different KOH/ NaOH impregnation ratios are shown in Figure 1.All the isotherms are a combination of type I at low relative pressures (p/p °) and type IV at intermediate and high relative pressures according to IUPAC classification [15] with hysteresis loops, indicating the coexistence of micropores and mesopores.Physical properties of AC samples obtained from N 2 adsorption isotherms are summarized in Table 2.It can be observed that the samples activated with single activation agent, RH-K4N0 and RH-K0N3, have different pore structures despite having the same amount of alkaline molecules.RH-K4N0 has higher specific surface area (2696 m 2 •g −1 ) consisting mainly of micropores while RH-K0N3 is detected with about 20% percent of mesopores (0.4396 cm 3 •g −1 ). is result is in good agreement with other research studies [16].Nevertheless, the BET surface of single agent activated samples is smaller than that of all the samples activated with dual activation agents (S BET is in the range of 2365∼3043 m 2 •g −1 ).
erefore, it could be deduced that using dual activation agents enhances the development of the surface area of the activated carbon.
e effect of employing the dual activation agent KOH and NaOH on porous characteristic of the obtained activated carbon can also be seen from Table 2. e specific surface areas and the total pore volume were lowest when the alkali hydroxide/char impregnation ratio is 3.0 (2365 m 2 •g −1 and 1.2002 cm 3 •g −1 for RH-K1N2; 2829 m 2 •g −1 and 1.3636 cm 3 •g −1 for RH-K2N1).When the alkali hydroxide/char impregnation ratio is higher than 3.0, specific surface area and total pore volume increased to a certain degree (2945∼3043 m 2 •g −1 and 1.7212∼1.8084cm 3 •g −1 , respectively), which indicate that surface pyrolysis and interior etching processes happened concurrently.
While the amount of impregnated alkali hydroxide tends to affect the pore texture of the AC samples, the KOH/NaOH ratio however seems to have more influence.e S BET was significantly increased from 2365 to 3043 m 2 •g −1 at KOH/ NaOH ratios from 0.50 to 1.33.Nevertheless, as the KOH/ NaOH ratio further increased to 2.00, S BET decreased to 2990 m 2 •g −1 .Additionally, the following points were observed from Table 2: (i) At the same amount of alkali hydroxide, higher KOH content gave larger specific surface area, microporous surface area, and higher micropore volume.RH-K1N2 has  g −1 , and 1.4250 cm 3 •g −1 ).(ii) At the same amount of the KOH/char ratio, as the NaOH/char ratio increased from 1.0 to 1.5 (RH-K2N1 and RH-K2N1.5),specific surface area and micropore surface area increased from 2829 and 2736 m 2 •g −1 to 3043 and 2831 m 2 •g −1 .When the NaOH ratio further increased to 2.0 (RH-K2N2), specific surface area and micropore surface area decreased slightly to 2990 and 2747 m 2 •g −1 .However, external surface area, mesopore volume, and total pore volume increased with the increase of the NaOH ratio from 1 to 2 (S ext, V mes , and V tot increase from 93 m 2 •g −1 , 0.1369, and 1.3636 cm 3 •g −1 to 243 m 2 •g −1 , 0.3768, and 1.8084 cm 3 •g −1 , respectively).(iii) At the same amount of the NaOH/char ratio, when the KOH/char ratio increased gradually from 1 (RH-K1N2) to 1.5 (RH-K2N1.5)and 2 (RH-K2N2), specific surface area as well as total pore volume increased, reaching the highest value of 2990 m 2 •g −1 and 1.8084 cm 3 •g −1 . is raise is resulted from the increase of micropore and mesopore, which were from 2258 and 107 m 2 •g −1 to 2747 and 243 m 2 •g −1 .
e change in specific surface area and pore characteristic of AC samples with KOH/char and NaOH/char ratios might be explained by the formation of alkali metal through the reaction of hydroxide and carbon in the process of preparation of AC [17,18] and by the lower boiling point of KOH (758 °C) than NaOH (883 °C [19]).It is easier for potassium to diffuse into the layer of carbon, causing the enhancement of pores (especially micropore), which in turn increases the specific and microporous surface area as well as the microporous volume of AC samples.As a result, the variation of Na content only causes the change in external site and mesopore of AC samples.
Figure 2 shows the pore-size distributions (PSDs) calculated from the N 2 adsorption isotherm by applying the DFT method.It can be noticed that a considerable amount of pores is distributed in the range from 0.8 to 1.8 nm, and from 1.8 to 5 nm, further indicating the concurrence of micropores and mesopores, which corresponds well with the observation from N 2 adsorption/desorption at 77K in Figure 1.Combined with the summarized data in Table 1, it 4 Journal of Chemistry can be seen that the total volume is increasing with the increase of alkali hydroxide/char ratios and V tot is highest with alkali hydroxide/char � 4.0 (RH-K2N2).At the same amount of alkali hydroxide/char, the higher KOH content resulted in the development of microporosity.V mi /V tot of RH-K2N1.5 and RH-K2N1 (82.8% and 90.0%) are higher than those of RH-K1.5N2 and RH-K1N2 (84.6% and 76.7%).According to Alcaniz-Monge and Illan-Gomez [20], the development of microporosity is due to carbon gasification and the metal intercalation, and only KOH generates supermicroporosity.
With the significantly improvement of porous characteristic of activated carbons by employing dual activation agents and by varying the KOH/NaOH ratio, we focus on dual activation agents in further studies.

SEM Analysis.
e SEM micrographs of AC samples are shown in Figure 3.All samples exist in the form of spherical-shaped particles with the size ranging from 20 to 60 nm.e impregnation ratios only have slight effect on the compact of the samples.ere are more cracks and crevices as the KOH/NaOH ratios increase, and the samples with higher amount of impregnated KOH are more porous than the other.

Element Analysis.
e element analysis of AC samples was determined by EDX measurement and is given in Table 3.All the samples have relatively high carbon content (94.38∼95.23%)and no or less than 0.09% silica content.
is is due to the use of the alkali hydroxide activation agent which reacts with silica (relatively rich in rice husk) to form alkali silicate and be removed in the washing process [21].
e presence of oxygen (4.54∼5.35%) is owing to the adsorbed water and surface functional groups.e existence of Cl, Cr, and Fe might be caused by the reactor container during the activation process and by HCl washing thereafter.Neither K nor Na has been detected, which demonstrates the effectiveness of the washing process.

FTIR Analysis.
e FTIR spectra of all the AC samples are shown in Figure 4, which have similar shapes with most of the peaks located at the same wave number.e wide bands located at 3450 cm −1 can be attributed to the presence of -OH vibration [22].e band at 2920 and 2860 cm −1 may be assigned to the presence of aliphatic C-H vibration [23].
e strong band at 1630 nm represents the C�O vibration [24].e peak at 1384 cm −1 is ascribed to CH 2 and CH 3 groups [23].ere is no SiO 2 absorption peaks (at 1101, 944, and 789 cm −1 [25]), indicating that silica has been successfully removed from the samples.e obtained result is consistent with earlier EDX studies, in which Si content of all AC samples is less than 0.1%.

Boehm Titration.
e acid/base properties of the AC samples are evaluated by Boehm titration and shown in Table 4. From the results in Table 4, it can be observed that the acidic sites are dominant over basic sites.Total amount of acidic groups is in the range of 1.387∼1.771mmol•g −1 whereas the amount of basic groups is only from 0.346 to 0.704 mmol•g −1 .e smallest amount of total acidic groups is found at the RH-K1.5N2sample (1.387 mmol•g −1 ) and the highest at the RH-K2N1.5 sample (1.771 mmol•g −1 ). is result is in good agreement with the EDX measurement that oxygen content is lowest and highest in RH-K1.5N2(4.54%) and   in RH-K2N1.5 (5.35%), respectively.It can also be noticed from Table 4 that the numbers of carboxylic, phenolic, and lactonic groups as well as total basic groups are almost unrelated to the amount of alkali hydroxide used or the KOH/NaOH impregnation ratio.

Raman Analysis.
e degree of surface disorder and defect of the as-prepared AC samples were evaluated by Raman spectra and are illustrated in Figure 5 and Table 5.
ere are graphite (G) peak at 1580 cm −1 and the defectdisorder (D) peak at 1350 cm −1 .e G-peak is associated with E 2g , and the D-peak is corresponded to A 1g .e ratio of the integrated intensities of D-band and G-band (I D /I G ) is consistent with the degree of graphitization of carbonaceous materials, and I D /I G increases with the decreasing in crystallinity [26].e results from Table 5 reveal that RH-K2N1.5 has the highest I D /I G value which indicates the highest surface disorder degree of this sample.e I D /I G values of RH-K1.5N2 and RH-K2N2 are 1.361 and 1.291, suggesting that these two samples have higher degree of graphite organization.is outcome confirms the Boehm titration results, since the surface disorder degree is resulting from high amount of surface functional groups.
e crystalline size along the basal plane (L a ) in Table 5 was calculated by the following equation [27]: L a (nm) � (4.35 × I G )/I D (3).RH-K1.5N2 and RH-K2N2 have low value of I D / I G ; consequently, their calculated crystallite sizes are towering over other samples.Table 6.e weight loss of all the samples in this range is lower than 5.09% and is due to the decomposition of some oxygen containing groups (carboxylic 100-250 °C and lactonic 200-400 °C [28]).Hence, for the convenience of comparison, the amount of carboxylic and lactonic groups evaluated from Boehm titration is also presented in Table 6.Table 6 shows that there is a consistency between the weight loss and the total amount of carboxylic and lactonic groups, which further confirms the Boehm titration results above.

TGA Analysis.
It also has to be pointed out that the main difference between TGA-DTA curves is only shown in the exothermic peaks of the second weight loss range.At the same impregnated alkali hydroxide amount, the exothermic peak temperature is lower for higher KOH content (between RH-K2N1.5 and RH-K1.5N2 or between RH-K2N1 and RH-K1N2) confirming that KOH is a more reactive agent, in comparison with NaOH [29].

Electrochemical Features.
e electrochemical performance of electrodes made of the as-prepared AC samples was evaluated using cyclic voltammetry and galvanostatic charge/discharge.Figure 7 depicts cyclic voltammograms of AC electrodes in 0.5 M K 2 SO 4 electrolyte at four typical scan rates 2, 10, 30, and 50 m•V s −1 in the potential windows of −1.0∼0.0V vs. SCE.At 2 mV•s −1 , CV curves exhibit a symmetric rectangular shape with a slight distortion, indicating an ideal electrochemical double-layer capacitor behavior.
e little hump appeared in CV curves of AC electrodes can be accounted for the reaction of surface functional groups [30].
In detail, as the scan was initiated at 0.0 V in negative direction to −1.0 V, the K + ions immigrated to the activated carbon surface, diffused into the pores, and adsorbed onto the surface as well as inside the pores to form an electrical double layer.e specific capacitance of activated carbon is caused by the double-layer capacitance of the adsorbed K + ions (positive charge) and the electrons accumulated on the carbon surface (negative charge) as well as the pseudocapacitance provided by the reduction of surface functional    Journal of Chemistry groups.By reverse scan from −1.0 to 0.0 V, the K + ions are desorbed and diffused out of the pores.Simultaneously with this process, there exists the oxidation of surface functional groups.According to Frackowiak and Béguin [31], the redox reaction can be described as follows: As the scan rate increases from 2 to 10, 30, and further to 50 mV•s −1 , the CV curves are deformed.e deviations from the rectangular shape are more pronounced with increasing scan rate and in the order RH-K2N2 < RH-K2N1.5 < RH-K1.5N2< RH-K1N2 < RH-K2N1. is is due to the kinetic limitation of the adsorption/desorption rate of K + ions which is directly affected by the diffusion of K + ions into and out of the micropores of AC electrodes.is, in turn, will increase the resistance of AC materials, leading to a deformed rectangle [32].RH-K2N2 has the largest external surface (243 m 2 •g −1 ); thus, it is the least affected by the scan rate.By contrast, as the external surface of RH-K2N1 (93 m 2 •g −1 ) is smallest, its CV curve is the most deviated from the ideal shape.
e specific capacitances calculated from CV curves at different scan rates are summarized in Table 7.All the calculated C CV are in the range of 160∼205 F•g −1 at the scan rate of 2 mV•s −1 .ese values are about 1.6∼2 times of the  PICATIF activated carbon in the same testing conditions [33]. is is owing to the high specific surface area of the asprepared activated carbons.RH-K2N1.5 and RH-K1N2 has the highest and lowest specific surface area (3043 vs. 2365 m 2 •g −1 ); for that reason, the C cv of RH-K2N1.5 is the highest (205 F•g −1 ) and of RH-K1N2 is the lowest (160 F•g −1 ).Besides, the contribution of surface functional groups should be taken into account, especially at the low scan rate.e highest amount of acidic and basic groups of RH-K2N1.5 (2.475 mmol•g −1 ) also help raising its specific capacitance.
As the scan rate increases, the specific capacitance of the sample decreases.However, at the scan rate heighten up to 50 mV•s −1 , specific capacitances of all samples are still greater than 100 F•g −1 , which implies the good capacitance of the as-prepared activated carbon in the K 2 SO 4 electrolyte.With the increasing scan rate, the specific capacitance decreases gradually, which could be due to the limited diffusion of K + ions.At the scan rate as high as 100 mV•s −1 , the highest specific capacitance of 90 F•g −1 was observed with the RH-K2N2 sample while the lowest of 69 F•g −1 was seen in the RH-K2N1 sample.
is result might be explained by the effect of the external area of the samples as described above.
Figure 8 displays the charge/discharge curves of AC electrodes at two typical current densities 0.5 and 3.0 A•g −1 in 0.5 M K 2 SO 4 electrolyte.A good linear variation of potential vs. time is observed for all curves, and the charge curves are symmetric to the corresponding discharge counterparts.
ere are only small Ohmic drops at high current density, implying the small resistivity of the cell.e Ohmic drops increase with but not proportional to the increasing of current density.At current density of 0.5 A•g −1 , the Ohmic drops increase in the order RH-K2N2 RH-K1.5N2< RH-K2N1 RH-K1N2 < RH-K2N1.5.At current density of 3.0 A•g −1 , however, the order changes to RH-K2N2 < RH-K2N1.5 < RH-K1.5N2< RH-K1N2 < RH-K2N1.
e difference in the Ohmic drop is owing to the internal resistance of materials, and the less mesopores (lower external surface), the higher the internal resistance.However, the surface disorder of the material also adds up to the increase of internal resistance.e Raman results in Table 5 show that the surface disorder increase in the following order: RH-K2N2 < RH-K1.5N2< RH-K2N1 < RH-K1N2 < RH-K2N1. 5. is means that the surface conductivity of the samples decreases in order RH-K2N2 > RH-K1.5N2> RH-K2N1 > RH-K1N2 > RH-K2N1.5, which is consistent with the magnitude of Ohmic drops at low current density (0.5 A•g −1 ).At high current density, the Ohmic drop strongly depends on the mesopores amount.RH-K2N2 has the highest mesopores amount (BET result in Table 2); therefore, it has the smallest Ohmic drop.In contrast, the Ohmic drop of RH-K2N1 is highest owing to its low mesopores amount.
e gravimetric specific capacitances at different current densities calculated from equation ( 2) are illustrated in Figure 9.It can be seen from Figure 9 that the specific capacitance decreases with the increasing of current density.As current density increases from 0.2 to 3.0 A•g −1 , the specific capacitance of RH-K2N1.5 decreases from 225 to 154 F•g −1 .It also can be seen from Figure 9 that the change in the specific capacitance of AC samples with current density is similar to the change with the scan rate (described above).is result confirms the CV result and can also be explained due to Raman as well as BET result.

Conclusions
High surface area activated carbons from rice husk have been prepared by chemical activation with dual activation agents, KOH and NaOH.e activation condition, namely, total alkali hydroxide/char and KOH/NaOH ratio can affect the pore structure of the activated carbons.e as-prepared activated carbon samples have a porous structure with developed specific surface area (2365∼3043 m 2 •g −1 ) and high pore volume (1.2002∼1.8084cm 3 •g −1 ).e alkali hydroxide/ char and KOH/NaOH ratio have a significant effect on the pore texture of AC samples.e AC sample prepared with alkali hydroxide/char � 3.0 and KOH/NaOH � 0.5 has specific surface area and pore volume as 2365 m 2 •g −1 and 1.2002 cm 3 •g −1 , respectively.Alkali hydroxide/char � 3.5 and KOH/NaOH � 1.33 give the highest specific surface area of 3043 m 2 •g −1 and pore volume of 1.7212 cm 3 •g −1 .
e asprepared AC samples have particle size in the range of 20∼60 nm and were estimated to have more than 94% carbon, about 5% oxygen, and a trace amount of other elements (Si, Cl, Cr, and Fe). e presence of oxygen is due to the adsorbed water and surface functional groups (1.931∼2.475mmol•g −1 ).All the AC samples exhibit a good capacitive behavior when used as an electrode material of supercapacitors.In the 0.5 M K 2 SO 4 electrolyte, the highest capacitance obtained is 205 F•g −1 at the scan rate of 2 mV•s −1 and is 225 F•g −1 at the current density of 0.2 A•g −1 . is result shows the potential for valorization of rice husk waste by Journal of Chemistry controlling the specific surface area and pore structure of the prepared activated carbon toward the application as a supercapacitor electrode.

Figure 1 :
Figure 1: Adsorption-desorption isotherms of N 2 at 77K for AC samples (the same scale on the quantity adsorbed axes was maintained to enable better comparison between graphs).

Figure 3 :
Figure 3: SEM images of AC samples.

Table 1 :
AC samples prepared under various impregnation ratios.

Table 2 :
Physical properties deduced from N 2 adsorption at 77K of AC samples.

Table 3 :
EDX analysis of AC samples.

Table 4 :
Functional groups on the surface of AC samples by Boehm titration.

Table 5 :
I D , I G , I D /I G , and L a .

Table 6 :
Weight loss of AC samples and total carboxylic and lactonic groups.