Influence of Sintering Temperature on Mechanical Properties of Glass-Ceramics Produced with Windshield Waste

Instituto Politécnico/Universidade do Estado do Rio de Janeiro (IPRJ/UERJ), Rua Bonfim, 25, IPRJ, Bloco 1, 1° andar, Sala 114, Vila Amélia, Nova Friburgo, RJ 28625-570, Brazil Centro Federal de Educação Tecnológica Celso Suckow da Fonseca (CEFET-RJ), Av. Governador Roberto Silveira, 1900, Prado, Nova Friburgo, RJ 28635-000, Brazil Instituto de Quı́mica/Universidade Federal do Rio de Janeiro (IQ/UFRJ), Av. Athos da Silveira Ramos, 149, Centro de Tecnologia, Bloco A, 6° andar, Sala 630, Ilha da Cidade Universitária, Rio de Janeiro, RJ 21941-909, Brazil Universidade Federal Fluminense Instituto de Saúde de Nova Friburgo, Faculdade de Odontologia, Rua Silvio Henrique Braune, 22 Centro, Nova Friburgo, RJ 28625-650, Brazil Instituto Politécnico/Universidade do Estado do Rio de Janeiro (IPRJ/UERJ), Rua Bonfim, 25, IPRJ, Bloco 1, 1° andar, Sala 215, Vila Amélia, Nova Friburgo, RJ 28625-570, Brazil


Introduction
Because the consumption habits of the population have generated environmental problems such as the growth of landfills and depletion of natural resources [1,2], scientific research has been much requested regarding the recycling of discarded materials, for finding new utilities and generating value from the waste [2][3][4][5].Glass, despite being recyclable, occupies large volumes in landfills [6].Considering the scope of the windshields, 40 million vehicles in the world reach the end of life every year [1] and throughout the useful life of vehicles, they may be changed and discarded.In addition, the windshields are more laborious to recycle.
is is due to the PVB (polyvinyl butyral) film, which exists between layers of glass, whose function is to protect the occupants, preventing the glass from shattering when breaking on impact [7].Several studies have proposed the use of glass for the production of glass-ceramics, adding value and targeting a discarded material [2,[8][9][10].
e silicates, which are the basis of the glasses, can be used for the production of profitable products such as glass-ceramics [2].When compared to glass, it has greater stability, durability, superior mechanical properties, resistance to thermal shock, low coefficients of thermal expansion, and fracture toughness [11,12].It features a range of applications, including the manufacture of artificial bones and teeth, heat shock-resistant transparent pans, heat-resistant windows for stoves or ovens, building walls, and cooktops [13][14][15].ere is a considerable amount of research focused on the production of glass-ceramics with industrial waste [2,10,[16][17][18][19]]. e work of Lu et al. may be highlighted, which studied the influence of sintering and crystallization on the mechanical properties of glassceramics produced by glass and fly ash from thermal power plants.
e addition of a nucleating agent to the glass powder is used to induce volumetric crystallization and reduce crystallization temperatures.e nature of crystallinity and the distribution of the crystalline phase formed during crystallization are dependent on the type and amount of the nucleating agent used.
e presence of nucleating agents, such as TiO 2 and various oxides, in the glassceramic composition favors nucleation and crystal growth.Since the surface tension decreases, the nucleation rate increases in the vitreous system [13,20,21].e addition of niobium oxide in addition to promoting crystallization also enables the formation of crystals of the perovskite group.e piezoelectric properties exhibited by perovskite glass-ceramics have been extensively studied [22].
In this work, glass-ceramics were produced from discarded glass with properties compatible with those found in the literature for this material.
e produced glassceramics were studied in terms of their flexural strength, mass density, crystallinity, microstructure formation, and biocompatibility for medical applications.In addition, this work also investigated the chemical composition and statically measured the particle sizes of the raw material produced before the sinterization procedure.

Methodology
e experimental and characterization methodologies followed in this work are presented.e production of the glass powder and the obtaining of the glass-ceramics are detailed.According to each experimental step, the procedures associated with the adopted characterization techniques are presented.

Production and Characterization of Glass Powder.
Windshield slices, glass blade, and PVB were milled and separated in a ball mill.e glass powder was passed through a 65-mesh sieve.e granulometric distribution was measured (Mastersizer Hydro 2000MU, Malver, United Kingdom), and the chemical elements of the glass powder were quantified by X-ray fluorescence (S8 Tiger Spectrometer, Bruker X-ray, United States).

Production and Characterization of the Specimens.
e glass powder was mixed with 10% water by weight, introduced in a rectangular metal matrix (28.31 mm length × 7.30 mm wide), and a 11.59 MPa load was applied with a hydraulic press for one minute (P10 ST 10 ton, Bovenau, Brazil).e specimens were extracted from the matrix and dried at 110 °C for one hour (400/3ND, Nova Ética, Brazil).ey were then heated at 5 °C/min rate and sintered for one hour at 600, 650, 700, 750 and 800 °C temperatures.Some specimens were produced with the addition of 4% of niobium oxide during the mix process under the same conditions.
Groups 1, 2, and 3 are the glass powder (GP) specimens sintered at temperatures of 650, 700, and 750 °C, respectively.Groups 4, 5, and 6 are the glass powder and niobium oxide (GPN) specimens sintered at temperatures of 650, 700, and 750 °C, respectively.Group 7 is a GPN composition specimen sintered at 600 °C, while Group 8 is a GP specimen sintered at 800 °C.
e thermodifferential and thermogravimetric analyses (Simultaneous ermal Analyzer STA 6000, PerkinElmer, United States) were carried out on specimens in an air atmosphere with a heating rate of 5 °C/min and a temperature range between 30 and 900 °C.e densities were determined by the Archimedes method, according to standard NBR 6220:2011 [23].
e flexural tests were performed at three points according to ASTM C1161-13 [24] in thirteen specimens from each group with thickness from 2.23 to 3.96 mm. e distance between the supports was 20 mm, and the loading rate was 0.2 mm/min (Shimadzu AGX-PLUS, Japan).e reliability of the flexural strength results was determined by the Weibull method [25].Scanning electron microscopy (SEM) was performed on each group on a fracture surface (UltraDry EDS JEOL JSM6510LV, ermo Fisher Scientific, United States).
X-ray diffraction (XRD) analysis was performed (Bruker-D8 Endeavor diffractometer, United States) on each group after ground on CuKa 40 kV/40 mA parameters.e scan range of diffractogram was 4-80 °with a scan speed of 0.02 °•2 °/2 s. e qualitative spectrum interpretations were performed by comparison with standards contained in the PDF02 database (ICDD, 2006) in Bruker Diffrac Plus software.
For in vitro static biofilm tests, the overnight culture of a multivirulent methicillin resistant wild-type strain (USA300) was diluted 1 : 100 in TSB supplemented with 0.5% glucose (TSB-G).Diluted bacteria were mixed with 20% pooled human plasma and used for assessment of biofilm formation on fragments of rat mandible (CEUA 740), commercial bone grafts (Aloboneporos-Osseocon 1.0 g, Clonos Dental, Lumina Bone-Criteria Biomaterials, Brazil), and Groups 1-8.
e specimens were fixed to the bottom of a 12-well polystyrene plate with Lubriseal grease ( omas Scientific, United States) and sterilized by ultraviolet irradiation.Multiwell plates were incubated at 37 °C with shaking at 100 rpm for one hour and then further incubated at 37 °C without shaking for 24 h.e wells were washed three times 2 International Journal of Chemical Engineering with phosphate buffered saline to remove nonadherent cells.Adherent biofilms were fixed with methanol, stained with crystal violet and washed three times with sterile water.Biofilm biomass formed on the mandible, bone grafts, and specimens from Groups 1-8 was determined by solubilizing crystal violet with 33% acetic acid [26] and measured at 490 nm light wavelength using a microtiter plate reader (Biorad, United States).All biofilm biomass experiments were performed in triplicates.e unpaired Student's t-test with the Tukey multiple comparison post hoc test was used to assess the statistical significance of between-group differences in bacterial count in vitro biofilm biomass with 95% confidence interval (p < 0.05).

Results and Discussion
e granulometric distribution of the glass powder resulted in a monomodal distribution with d (10) of 2.001 μm, d (50) of 14.658 μm, and d (90) 57.234 μm.Cho and Kim [11] separated three particle average sizes for the production of glass-ceramics.It was observed that the smaller particle size favors densification, especially in the lower sintering temperatures.
ese smaller particles favored the coalescence process during the sintering.In this study, the mean particle size was higher than the average particle size of Cho and Kim [11].
Table 1 shows the result of X-ray fluorescence spectroscopy of the glass powder.It is noted that the glass powder is composed primarily of silicon oxide, with about 80% by weight of the total composition.Sodium, calcium, and magnesium oxides are present in the composition at much lower levels.Aluminum oxide comprises the lowest content in the composition.
Figure 1 shows the differential thermal analysis (DTA), thermogravimetric analysis (TG), and derivative thermogravimetric analysis (DTG).A peak is observed in DTA between 700 °C and 800 °C for GP and GPN groups.is peak is not associated with mass loss, as can be seen in DTG.It indicates physical phenomena in the temperature range between 600 °C and 900 °C.Any variation was observed with the amount of niobium oxide added to the glass powder, even though it is considered a nucleating agent.In these analyses, important parameters can be obtained for the production of glass-ceramics, such as the glass transition temperature (t g ) and the crystallization temperature (t c ) of the glass powder.e nucleation of the crystals in the glass matrix will only occur in temperatures higher than the glass transition temperature.e t g is found when a slight endothermic depression begins, followed by a strong release of heat, corresponding to the crystallization peak of the differential thermal analysis (DTA).
Figure 2 shows the X-ray diffractogram of the GP and GPN specimens.In the samples with only glass powder, produced in the temperatures of 650 °C and 700 °C, the structure remains totally amorphous.At the temperature of 750 °C, some peaks began to form already, with imperfect crystalline structures, indicating the presence of crystals of albite, quartz, and diopsite.e addition of niobium oxide favored the formation of crystalline structures, confirming the production of glass-ceramics at temperatures of 650, 700, and 750 °C (Figure 2).e peak intensities of zeolite and stilbite were lower than those of isolueshite crystal structure, which is a sodium niobate, NaNbO 3 .e burning temperatures used are higher than those used for the synthesis of sodium niobate by solid reaction of niobium oxide and sodium hydroxide [26].It is important to note that all the crystalline structures have chemical elements coherent with those found in X-ray fluorescence.Given these results, two other groups were made and added to be studied.e possibility of producing glass-ceramics at different sintering temperatures according to the composition on the specimens was considered.Hence, one group consists of GPN specimens sintered at 600 °C (Group 7) and the other of GP specimens sintered at 800 °C (Group 8).Table 2 and Figure 3 show the mean density value for each group.e GP specimens showed a decrease in the mass density, with the sintering temperature increasing up to 750 °C.After this value, there is no significant change in the density of the specimens with increasing temperature, as can be observed in Figure 3, from the densities obtained through sintering at 750 °C and 800 °C.When crystallization occurs before completion of the sintering, the viscous flow viscosity increases rapidly and prevents the sintering process resulting in less dense materials [27]. is occurred at the temperatures 750 °C and 800 °C, where the crystallization of the glass powder occurred before completed sintering.
e GPN specimens showed density values between 2,115 and 2,339 g/cm 3 .Increasing the sintering temperature from 600 °C to 650 °C resulted in increased density due to coalescence of the particles.However, at 700 °C, the density decreases due to the better crystallization of the stilbite, which causes a reduction of sintering by viscous flow, making the densification difficult.After 700 °C, the density is maintained in a close value when the sintering temperature increased to 750 °C, with the formation of a new crystalline structure, albite, occurring.
At the sintering temperature of 650 °C, it can be observed that the density was higher for the GP specimens.ere was crystallization of the specimens with the addition of niobium oxide at 650 °C, rapidly increasing the viscosity, preventing the sintering, and producing less dense specimens.No crystalline phase formation occurred in the GP specimens at 650 °C, which favored sintering and densification.
e fracture surface of the GP specimens is presented in Figure 4.It is possible to observe that there is an increase in the number and size of the pores with the increasing sintering temperature, justifying the density decrease.e size of the pores seems smaller and more homogeneous in the GPN specimens (Figure 5).e mean flexural strength at different sintering temperatures is shown in Table 3 and in Figure 6.ese results showed that the niobium oxide decreases the exural strength of specimens, comparing the results of the GPN and GP groups.Despite this, the results are satisfactory since the obtained exural strengths are within the usual values for glass-ceramics [28].Cho and Kim [11] obtained an average of 84.00 MPa for the exural strength of the sintered specimens at a temperature of 900 °C, when the largest mean particle size used was 4.8 μm.In this text, glass powder particles with a wide range of granulometric distribution were used, with similar results, 77.64 MPa, in lower sintering temperatures.
e similar mechanical properties were obtained due to the use of the wide-ranged granulometric normal distribution instead of the separation in narrow bands of particle sizes.In  this case, the adopted methodology may have facilitated the compaction factor of the shaped specimens and thereby have improved the densi cation, justifying the similarity of the results.
Since crystallization in uences the densi cation of the material, it also in uences the strength of the material because both the internal and external porosity act as stress concentrators.us, the bulk crystallization promoted by     International Journal of Chemical Engineering niobium oxide increases the viscosity that prevents the exit of gases making the material porous [29].On the other hand, the presence of niobium oxide promotes the formation of isolueshite, the structure with piezoelectric properties and high dielectric constant.erefore, despite the reduction of resistance, the existence of isolueshite allows for the exploration of electrical applications of glass-ceramics [30,31].Zhang and Liu [8] also realized that crystallization increases viscosity and hinders densi cation.In addition, it was observed that, in higher temperatures, the surface densi cation is improved, because resistance of the viscous ow of the glass is smaller on the surface than in the interior part. is is a fact that favors mechanical resistance.In the glass-ceramics of this work, the improvement of the mechanical properties, provided by the surface densi cation, is not perceived since the internal porosity is increased with the increase of temperature.
e Weibull modulus (m) was determined to evaluate the reliability of the exural strength results (Table 3).Figure 7 shows the slope of the line which was used to determine the Weibull modulus, obtained from the results of exural strength of the thirteen specimens.In this case, the specimens were sintered at the temperature of 800 °C and the composition was glass powder.e acceptable range of the Weibull parameter, m, is between 3 and 15 for fragile materials [25], but Group 1 was not satisfactory.e higher the value of m, the more reliable is the results of the mechanical properties [32] (Figure 8).e correlation factors, R 2 , presented in Table 2, were higher than 0.800, which can be considered as satisfactory [33].
e in vitro bio lm formed on the mandible was reduced when compared to the biomass bio lm formed on commercial bone grafts.Glass-ceramics Groups 1-8 showed less bio lm formation ( * p 0.0477) when compared to mandible bone, indicating that these groups of glass-ceramics severely attenuated Staphylococcus aureus attachment.ese results suggest that these glass-ceramics were biocompatible and can be used as dental prostheses (Figure 9).

Conclusions
e monomodal distribution contributed to obtaining better mechanical properties at lower temperatures compatible with those in the literature, even with a larger average particle size.e recycled glass powder of windshield presented chemical composition like other glass-ceramics produced with raw material of greater cost.ermal analyses showed crystallization temperatures close to 700 °C in the two compositions.e addition of niobium oxide favored the formation of crystals at the temperatures at which sintering occurred.On the other hand, it made it di cult to densify specimens at lower temperatures.However, pure glass powder favors densi cation at lower temperatures and higher porosity at higher temperatures.e addition of niobium oxide decreased the exural strength compared to 6 International Journal of Chemical Engineering pure glass powder specimens.Even so, such results agree with the literature.e glass-ceramics produced in this work presented smaller biomass formation than the mandible and bone grafts, suggesting a possible application for dental prostheses and oral rehabilitation, after performing other tests for biocompatibility.
Data Availability e data used to support the ndings of this study are available from the corresponding author upon request.

Figure 3 :
Figure 3: Variation of the density with the sintering temperature.

Table 1 :
Composition and concentration of pure glass powder.

Table 2 :
Average density and standard deviation of the groups.

Table 3 :
Flexural strength and Weibull modulus of all groups.