Influences of Ultrafine Slag Slurry Prepared by Wet Ball Milling on the Properties of Concrete

,e application of ultrafine ground-granulated blast-furnace slag (GGBFS) in concrete becomes widely used for high performance and environmental sustainability. ,e form of ultrafine slag (UFS) used in concrete is powder for convenience of transport and store. Drying-grinding-drying processes are needed before the application for wet emission. ,is paper aims at exploring the performances of concrete blended with GGBFS in form of slurry. ,e ultrafine slag slurry (UFSS) was obtained by the process of grinding the original slag in a wet ball mill, which was mixed in concrete directly. ,e durations of grinding were 20min, 40min, and 60min which were used to replace Portland cement with different percentages, namely, 20, 35, and 50, and were designed to compare cement with original slag concrete. ,e workability was investigated in terms of fluidity. Microstructure and pore structure were evaluated by X-ray diffraction (XRD), scanning electron microscopy (SEM), and mercury intrusion porosimetry (MIP). ,e fluidity of concrete mixed with UFSS is deteriorated slightly. ,e microstructure and early strength were obviously improved with the grind duration extended.


Introduction
Cement, the main cementitious material used in the concrete, is the base material of construction.Cement manufacture is a highly energy-intensive process.
e total energy consumption of the global cement industry is estimated at 2% of global primary energy use, which accounts for approximately 7% of all global carbon dioxide emissions [1,2].e development of ecofriendly concrete in the construction industry is gaining deep concern and intensive research worldwide.
Ground-granulated blast-furnace slag (GGBFS) is a byproduct of steel making [3].GGBFS has been found to exhibit excellent cementitious properties when it was finely powdered [4].e use of GGBFS as supplementary cementitious material not only reduces the usage of cement [5] but also improves the porosity performance of OPC concrete [6].In addition, GGBFS is one of the major precursor materials used in the production of alkali-activated materials (AAMs) [7].As a kind of alternative cementitious material, GGBFS shows comparable mechanical performance to blended slag cement and similar or even lower global warming potential compared with the best available concrete technology [8].
e reactivity of GGBFS is considered an important parameter to assess the effectiveness of GGBFS in concrete composites, which varies greatly with the source of slag, types of raw material used, methods of cooling, and the duration of milling [9].Pal et al. [10] investigated the relationship between the hydraulic index (HI) of slag and the influencing factors of slag, including glass content, fineness, and chemical composition.Zhao et al. [11] studied the particle characteristics and hydration activity of GGBFS containing industrial crude glycerol-based milling aids.e result indicated that means and milling aids strongly affect the activity of GGBFS.
Wet milling is a method of producing powder slurry by milling materials with mediums together, with advantages of uniformity, high milling efficiency, and small noise contrast with dry milling.It is widely used in cement and ceramics industries [12] and rarely in the field of slag powder.Nowadays, the main milling methods of slag are dry milling processes and need to go through drying-milling-drying processes before application for wet emissions.If the dry milling process is replaced by the wet milling process, the drying process can be omitted and be applied to concrete directly.
In this paper, the feasibility of UFSS prepared by the wet ball mill process applied in concrete was investigated.e properties of concrete were tested by kinds of test methods and analysis methods.

Ground-Granulated Blast-Furnace Slag (GGBFS).
e GGBFS was from the Capital Iron and Steel Company in the state of Beijing (China).Specific gravity of GGBFS was 2.92.e particle size distribution and microstructure of slag slurry/powder for different wet milling durations and the original slag (0 min) are shown in Figure 1, Table 1, and Figure 2. e chemical composition and physical properties of slag are shown in Table 2. Compared with the original slag, the size range of UFSS was reduced and the morphology was smooth.

Cement.
Cement was from Jidong Cement Co., Ltd, the state of Hebei province (China), Portland cement 42.5, and the specific surface area is 316 m 2 /kg.e physical and mechanical properties of cements are shown in Table 2.

Other Materials.
e fine aggregates and coarse aggregates used were natural river sand and broken stones.Maximum particle size of fine aggregates and coarse aggregates was 2.36 mm and 20 mm, respectively.Fineness modulus of fine aggregates was 2.7.Table 3 shows the properties of coarse and fine aggregates of concrete.
e indicator test methods were carried out according to the Chinese national standards GB14684-2011 and GB14685-2011.

Experimental Design.
e durations of grinding were 20 min (UFSS20), 40 min (UFSS40), and 60 min (UFSS60) which were used to replace Portland cement with different percentages, namely, 20, 35, and 50, and were designed to compare portland cement with original slag concrete (from B1 to E3, Table 4).Consulting the literature [13][14][15][16], 10-60% of slag replace cement in concrete displays good performance, and the fineness of slag can also make a difference.In this study, the specimens of compressive strength and workability were concrete, and that of microstructure tests were corresponding paste.e designations of mixtures are shown in Table 4; the concrete mix proportion is cement : water : sand : stone � 1 : 0.5 : 1.57 : 2.36.e mixture codes in Table 4 are the percentage figures, which indicated the weight percentage between different raw materials.

Wet Ball Milling Details.
e ball crusher is YXQM-2L, the grinding speed is 400 r/min, the ratio of water to solid is 0.5, the ratio of ball to materials is 4, and the milling media are V8 mm agate ball and V3 mm zirconia ball.

Specimen Preparation.
GGBFS and water were mixed and ground.Firstly, different UFSS were obtained through controlled grinding duration based on the milling curve.
en, the UFSS was mixed with the remaining water during the preparation of the specimen, and the other conventional steps were carried out according to the Chinese national standard GB/T 50081-2002.

Compressive Strength.
e compressive strength tests were performed in conformity with the Chinese national standard GB/T 17671-2005, and the ages were 3 days, 7 days, 28 days, and 90 days.

Scanning Electron Microscopy (SEM).
e microstructure of specimens of 28 days was tested by scanning electron microscopy (FEI Quanta 450FEG), with the magnification of ×2000 and ×10000.

X-Ray Diffraction (XRD).
e model of laboratory X-ray diffraction used was D/MAX-RB (RIGAKU Corporation, Japan).e test angle range was 5-70 °, and the test error was controlled within 0.02 °(Δ2θ ≤ ±0.02 °). e age of specimens was 28 days.

Mercury Intrusion Porosimetry (MIP).
e microporous structure of specimens at 28 days was tested by mercury intrusion porosimetry complying ISO 15901-1:2005.e porosity, median pore diameter of area, and the average pore diameter of hydration production were analyzed using Demo windows 9400 series software.

Workability.
e workability is the ease of working with a freshly mixed concrete in the stages of handing, placing, compacting, and finishing.Slump is always regarded as an indicator of the workability of concrete [14].To explore the feasibility of UFSS replace cement in concrete, the slump was tested and is depicted in Figure 3.
e content and grinding duration of UFSS reduced slump.Mixing E3 with 50% UFSS60 showed a slump value of 169 mm as compared to 180 mm and 174 mm showed by mixtures E1 and E2 which had 20% and 35% UFSS60.

Advances in Materials Science and Engineering
Similarly discipline was observed in series A, B, C, and D. e increase of content of slag decreased the fluidity, which confirmed the trend obtained by Deb et al. [14].Under the condition of same dosage of slag, take 35% as an example, the slump of C2, D2, and E2 were reduced by 5.3%, 7.9%, and 8.4%, respectively, compared to B2. Similarly discipline was observed in 20% and 50% series.
e slump was decreased slightly with the increase of content and milling duration extended for slag.e results of this part were similar to the results of literatures [17,18].
e reasons for that were that the increases of surface of slag powder led to increased water demand.What is more, the slag was contacted with the aqueous medium directly, and the vitreous network of slag particles is more easily to be dissolved in the process of wet ball milling.e surface of the slag particles becomes rough, leading to poor workability.
is may be a further reason for the above results.

Compressive Strength.
e results of compressive strength tests of specimens at different ages are depicted in Figure 4. UFSS could accelerate the development of compressive strength at the early age of concrete.For E3 with 50% of UFSS60, the 3-day strength reached 60.1% of that of 28 days, while the values of B3, C3 and, D3 were found to be 48.1%,56%, and 58.7%, respectively.For 50%, the ratios of 7 and 28 days strength of original slag, UFSS20, UFSS40, and UFSS60 were found to be 63.7%, 65.7%, 69.3%, and 74.2%, respectively.e above results confirmed the trend obtained in dry ground slag by Yan Shi and Arash Aghaeipour [19,20].e reasons for the above results may be the disparity of activity and particle size of slag.e average diameter (d (0.5)) of UFSS20, UFSS40, and UFSS60 was 5.01 μm, 4.73 μm, and 2.32 μm, respectively, while that of original slag was 18.18 μm. e compactness of concrete was improved, and the large pores were reduced effectively (specification in Section 3.3 specifically).Sharmila and Dhinakaran [21] studied the compressive strength of commercially available ultrafine slag applied to the concrete.ey found that the performance of concrete was improved.
e study [22] showed that the activity of slag was lower than that of cement and failed to exhibit considerable reaction in the early age.Advances in Materials Science and Engineering e activity of slag disposed by the milling process was improved, which was beneficial for the improvement of compressive strength especially in early ages.
e results of compressive strength at ages 28 days and 90 days showed that the compressive strength of specimens decreased with the increase of slag content and increased with the duration of grinding extend.
e gaps of compressive strength of specimens become smaller with the extension of age.Sharmila and Dhinakaran [23] found that the compressive strength of concrete was reduced when the content of ultrafine slag exceeded 15%.e aggregation of fine particles leads to a higher porosity.However, this phenomenon was not observed with slag of 50% in this study.e wet ball mill was carried out in aqueous media, the surface of the particles formed hydrated films under the effect of aqueous media, and the surface energy of particles was relatively lower to the dry ball mill.What is more, the UFSS was mixed with water first and then mixed together with other raw materials; the particles get a good dispersion in the concrete.

Pore Structure.
e results of pore size distribution (PSD) of B2, C2, and E2 at 28 days are shown in Figure 5. UFSS refined the pores and created a distribution peak for the pore range within 100 nm, and the trend was clearly observed in the specimens with UFSS60.ree characteristic ranges of pore sizes were divided: <10 nm (Part I), 10 nm-100 nm (Part II), and >100 nm (Part III), with various peaks in each range, which represent small pores, middle capillary pores, and larger capillary pores [24].
For specimens incorporating 35% of UFSS, the pattern of PSD curves was significantly different for different grinding durations.B2 samples (original slag, 35%) present triplet  e pores consisted of small pores, middle capillary pores, and larger capillary pores.C2 samples (UFSS20, 35%) present dual peak characteristics in Part I and Part II.e pores were refined and mainly consisted of small pores and middle capillary pores.E2 samples (UFSS20, 35%) present single peak characteristics in Part I, which mainly consists of small pores.
For the range of Part I, the formation of small pores was mainly the hydration of cementitious materials [24,25].e hydration extent of B2 was limited compared to the other two groups.e values of C2 and E2 were close, indicating that the extents of hydration reaction were similar with an age of 28 days.For the range of Part II, the pores >10 nm were formed by the filling effect of particles in concrete [26].
e peak of the PSD curve of B2 was obvious; the compactness of hardened body was poor relatively.e peak of the PSD curve of C2 exits and is weaker than B2, indicating that UFSS20 could improve the compactness of concrete compared to original slag.E2 showed a smooth curve in this part, indicating that the compactness of concrete could be improved obviously.For the range of Part III, only the curves of B2 exit a peak.UFSS obtained from wet milling could improve the compactness of concrete effectively.
Figure 6 shows the cumulative pore volumes of the specimens corresponding to Figure 5.As the particle size of slag reduces, the pore volume decreased.e porosities of B2, C2, and E2 were 24.7986%, 24.0260%, and 23.7765%, respectively.e porosities decreased with the reduction of sizes of particles.e slag slurry reduced the distribution of larger pores and optimized the porosity distribution.
e compactness and compressive strength of concrete were optimized.
3.4.Microstructure Tests. Figure 7 shows the SEM images of specimens incorporating UFSS at 28 days.e larger capillary pores were easily observed in B2.From the images of D1, D2, and D3, the compactness of specimens was improved with the increasing of slag content.Ultrafine slag particles played an important role in the compactness performance of harden body.e compactness of pates was improved with the grind duration extending, which was consistent with the results of MIP tests. is further explained the increase of compressive strength of concrete with ultrafine slag.
e cement particles were wrapped by slag particles, causing delay of the reaction process for cement particles, and the hydrated products of cement particles were not easily observed.However, the activity of slag particles was lower than that of cement particles even through the milling process. is was why the compressive strength decreased with the increased content of slag, even if the porosity was improved.Advances in Materials Science and Engineering 3.5.X-Ray Diffraction Analysis.XRD analysis was carried out to examine the influences of the content and fineness of slag on hydration and phase.XRD images are shown in Figure 8. From XRD analysis, mineral phases of portlandite, calcium carbonate, larnite, and ettringite were found.
In the cement paste blended with slag, three structure reactions were involved: cement hydration, the pozzolanic reaction of slag, and hydration reaction of slag [27,28].However, slag exhibits a pozzolanic reaction in the presence of calcium hydroxide (Ca(OH) 2 ) formed upon cement hydration [20].e extent of slag involved in the reaction could be reflected by the amount of calcium hydroxide under same content conditions.It could be seen from the XRD images (Figure 8(a)) that the content of calcium hydroxide decreased with the decrease of particle size.e results illustrated that the activity slag treated through wet milling was increased, which accounted for the increase of compressive strength.With different slag dosages, the test results of various contents of slag (Figure 8(b)) complied with the above regularity: the amount of calcium hydroxide reduced with the increase in content.

Conclusion
is study investigated the influences of ultrafine slag slurry (UFSS) prepared by the wet ball mill on the properties of cement and concrete.e results obtained were summarized as follows: (i) Wet ball mill could improve the size distribution of slag particles effectively.e slag decreased the slump of concrete slightly.(ii) Use of UFSS as a substitute to cement improved the compressive strength of concrete especially at early ages.(iii) UFSS optimized the pore size distribution of the plaster.e amount of large pores (10-100 nm) were decreased notably and created distribution in the range of small pores (<10 nm).

Figure 1 :
Figure 1: Different particle size distributions of slag particles at different wet milling durations.

Figure 2 :
Figure 2: SEM images of slag powder at different wet grinding times: (a) raw slag and wet grinding for (b) 20 min, (c) 40 min, and (d) 60 min.

Figure 3 :
Figure 3: Slump of mixture with different contents and milling durations.

Figure 4 :
Figure 4: Compressive strength of specimens at different ages.

Figure 5 :
Figure 5: Pore size distribution curves of specimens with 35% of UFSS at 28 days.

Figure 6 :
Figure 6: Cumulative pore volumes of specimens with 35% of slag cured for 28 days.

Figure 8 :
Figure 8: XRD of the specimens cured for 28 days.

Table 1 :
e main integral distribution of slag powder at different wet grinding times.

Table 2 :
Chemical composition of GGBFS and cement.

Table 4 :
Designations of mixtures in this research.