Feasibility Assessment of Incorporating Copper Slag as a Sand Substitute to Attain Sustainable Production Perspective in Concrete

Motivated by the sustainable production perspective, a laboratory testing program is exercised to ascertain the feasibility of utilizing copper slag in place of the natural fine aggregate in concrete. Totally, fifteen concrete mixtures were prepared to incorporate copper slag in place of the fine aggregate in concrete.*e attributes of concrete specimensmadewith varying proportions of copper slag were compared (ranging from 0% to 100% substitution) at a w/c ratio of 0.44, and the optimum percentage of copper slag was decided.*e w/c ratio in the mix containing optimum copper slag percentage was then varied (from 0.42 to 0.36) to examine the influence of the change in the quantity of available water on the strength attributes of concrete. Concrete specimens were assessed for workability, density, compressive strength, flexural strength, and split tensile strength. SEM images and X-ray diffractograms of concrete specimens were also studied.*e results obtained indicated a significant increase in workability and a small rise in the bulk density of concrete.*e study concludes that substituting 60% sand with copper slag results in better compressive strength compared to control concrete and can be improved further by reducing the w/c ratio in the mix.


Introduction
e remarkable versatility, the ease of construction, and certain durability properties of concrete have made it an essential constituent of construction for decades. e primary challenge before today's construction industry is to meet the demand of efficient and economically viable construction material posed by the huge infrastructural need. e natural ingredients, fine aggregate, and coarse aggregate constitute more than 70% volume of concrete. e availability of these natural resources is decreasing at a very high pace. In fact, due to the severe problem with natural sand, the construction industry is faced with a pressing need to consider available options to lessen the reliance on natural fine aggregate. On the other front, due to rapid urbanization and industrialization, waste generation has increased tremendously. Traditionally, industries manage their wastes by dumping them into the environment, most of the time without any prior treatment.
Discharging the industrial waste materials into the environment which have significant potential to cause environmental hazards can also become a serious threat to human health. Researchers have conducted many investigations to find practical and environment-friendly ways of disposing off industrial waste in recent years.
Disposal of this enormous volume of industrial waste in concrete appears to be the call of the hour. Sustainable development means wisely using existing resources so that the future demands can be satisfied with ease. Utilization of the industrial waste in concrete can not only provide a cheap and abundant source of the fine aggregate in the concrete but also reduce the environmental pollution resulting in the improved sustainability credentials of the concrete. However, this is possible only if the substitute raw material either improves or at least maintains the attributes of the concrete.
Researchers in the past have successfully produced concrete utilizing industrial waste materials as a substitute for natural fine aggregate. Onprom et al. [1], Ghafoori and Bucholc [2], Aggarwal et al. [3], Andrade et al. [4], and Bai et al. [5] experimentally tested the influence of bottom ash as a substitute for natural sand in concrete. Zhu et al. [6] experimentally determined the influence of iron ore tailings as fine aggregate on the concrete. Tripathi and Chaudhary [7] tested the feasibility of utilizing imperial smelting furnace slag in concrete. Al-Bawi et al. [8] have investigated the strength attributes of the concrete comprising recycled glass as a sand substitute.
Copper slag is one of the materials that have a tremendous potential to be adopted in place of the natural fine aggregate in concrete. Around 2.2 ton of copper slag is generated for each ton of copper extracted [9]. Disposal of such vast quantity of waste is a big headache. Motivated by the sustainable production perspective, the present study is intended to explore the viability of incorporating copper slag in place of the natural fine aggregate in concrete. Excellent mechanical and physical attributes of copper slag make it a potential source of fine aggregate. A variety of research work has been performed on the utilization of waste copper slag as the raw material in concrete. Zain et al. [10] used copper slag in the making of cement mortar. e findings of this investigation showed optimum strength performance up to 5% substitution. Khanzadi and Behnood [11] studied the influence of copper slag together with different silica fume content on the properties of concrete. Results showed better strength with use of copper slag. Al-Jabri et al. [9] conducted an experimental study to examine the impact of copper slag as a sand replacement on the properties of high-performance concrete. e experimental findings indicated a slight increase in density and rapid rise in workability of concrete mixes. Substitution of the 50% fine aggregate by copper slag showed strength comparable with the strength of conventional concrete. Furthermore, Al-Jabri et al. [12] researched the use of copper slag to produce high-strength concrete. ey reported a decline in water demand with the rise in the quantity of copper slag. e study also indicated an enhancement in the properties of concrete comprising copper slag. e experimental work by Wu et al. [13] on the utilization of copper slag in place of fine aggregate in concrete indicated that when less than 40% copper slag was used, the compressive strength of concrete was observed to be equivalent or superior to the strength of conventional concrete. Wu et al. [14] also studied the attributes of concrete comprising copper slag under dynamic compression. Results indicated improvement in the dynamic compressive strength up to 20% substitution and a fall in strength beyond 40% substitution. Brindha and Nagan [15] focused on the utilization of copper slag as a substitute for sand and cement. e result showed that up to 40% replacement as sand and up to 15% replacement as cement improves the strength of concrete.
Although a number of experimental studies have been conducted on the attributes of concrete incorporating copper slag as sand substitution, a review of available literature has not produced a single reference on the utilization of copper slag as a sand substitute on the volume basis. is presents an opportunity to examine the influence of substitution of natural fine aggregate with an equivalent volume of copper slag on the concrete properties.

Experimental Investigation
e primary aim of this experimental investigation is to substitute the natural sand with industrial waste and copper slag so that the attributes of the concrete should remain least affected.
e experiments were carried out using 15 different concrete mixes. e mix CC (control concrete) was made with 100% natural sand, whereas the Type A mixes were prepared with different proportions (10% to 100%) of copper slag (namely, CS10 to CS100) as a substitute for natural sand at a w/c ratio of 0.44. Optimum copper slag content was then found from the Type A mixes and Type B mixes (CW1 to CW4) prepared with 60% copper slag at a varying water-cement ratio (w/c) (ranging from 0.42 to 0.36) with a decrement of 0.02 at each stage. e quantity of copper slag in all mixes was decided on the volume basis so that the total volume of the fine aggregate in all the fourteen mixes was maintained identical to that of natural sand in control concrete. e slump of fresh concrete and 28 days' density of concrete specimens cast were measured. Specimens were tested for compressive, flexural, and split tensile strengths at the age of 7, 28, 56, and 112 days. SEM (scanning electron microscope) images and X-ray diffractograms were also studied.

Materials and Equipment.
Ordinary Portland cement (OPC) of 53 grade conforming to BIS:12269-2013 [16] was utilized for the preparation of all the concrete mixes. Natural river sand brought from Tapi River, India, and copper slag procured from Birla Copper Hindalco Industries (Dahej, Gujarat, India) were used in this experimental study. Natural sand, as well as copper slag, was passed through 4.75 mm IS sieve. e specific gravity of natural sand and copper slag was experimentally determined to be 2.62 and 3.43, respectively, by using pycnometer as per BIS:2386 part III-1963, R 2002 [17]. Coarse aggregates (basalt) of size 10 mm and 20 mm having a specific gravity of 2.77 and 2.82, respectively, were used. e specific gravity of course aggregates was determined by density bucket method as per BIS:2386 part III-1963, R 2002 [17]. Water absorption for natural sand, copper slag, and course aggregate were determined by the conventional method described in BIS:2386 part III-1963, R 2002 [17] and were found to 2 Advances in Materials Science and Engineering be 1.02%, 0.02%, and 0.6% respectively. roughout the experimental work, drinking water was used for blending the concrete. e chemical composition of copper slag was determined using energy dispersive X-ray fluorescence (EDXRF) spectrometer at the Exova metallurgical services, Mumbai, India, and is shown in Table 1. Scanning electron microscope at the SVNIT (Surat, India) was used to analyse the aggregate-matrix interface of the concrete specimens, and X-ray powder diffractometer at the Savitribai Phule Pune University (Pune, India) was used to identify any crystalline phases formed in the matrix.

Mix Preparation.
e mix proportion of the M40 mix with a target strength of 48.25 MPa was obtained for the concrete mix CC by referring BIS:10262-2009 [18] recommendations. e proportions of cement, fine aggregate, and coarse aggregate were taken as 1 : 1.49 : 2.53 at a w/c ratio of 0.44. e Type A mixes were made by replacing the natural fine aggregate by copper slag in the proportion of 10% to 100% volume of natural sand.
e Type B mixes were prepared by reducing the water content in the mix CS60 which was an optimum percentage for sand substitution. e mix proportion of candidate mixes is given in Table 2.

Chemical and Physical
Properties. e chemical constitution of copper slag is given in Table 1. 90.09% of copper slag is composed of SiO 2 , Al 2 O 3 , and Fe 2 O 3 together. e high concentration of the Fe 2 O 3 present in the copper slag is the reason for its high specific gravity. e lime content of the copper slag utilized in this study is very low. is indicated that copper slag cannot act as a cementitious material if used in concrete as the quantity of lime available is insufficient to attain the necessary hydration rate.

Workability and Density of Concrete.
e influence of using copper slag in place of natural sand on the workability and the bulk density of candidate concrete specimen are illustrated in Figure 1. For the Type A mixes, a notable rise in the workability of concrete compared to the mix CC can be seen with a rise in the quantity of copper slag in concrete. Also, the Type B mixes show improvement in the workability of the copper slag concrete with a rise in the w/c ratio for obvious reasons. At all substitution percentages, slump of concrete was higher than that of the mix CC. e glossy surface texture and the quality of very low water absorption Advances in Materials Science and Engineering of the copper slag are responsible for the substantial increase in the slump. e increased workability due to the presence of copper slag can be used beneficially to manufacture concrete with high workability at low w/c ratio. e density of the Type A concrete specimen raised with the rise in the copper slag content almost linearly. e Type B mixtures showed a decrease in the bulk density of concrete with the rise in the w/c ratio. e bulk density of the Type A concrete increased owing to the high specific gravity of the copper slag compared to that of natural sand. Due to the difference in the specific gravity, larger quantity of copper slag is required to occupy the same volume as occupied by the natural sand.

Compressive Strength.
e influence of copper slag substitution and varying w/c ratio on the compressive strength gained over 7, 28, 56, and 112 days of curing age is depicted in Figure 2. e results for the Type A mixes show that, as the quantity of copper slag present in the mix increased, the compressive strength of concrete increased almost linearly up to 60% substitution of natural sand by copper slag. Beyond 60% substitution, a notable reduction in the compressive strength was seen. A significant improvement of 4.14%, 5.24%, 4.62%, 6.9%, 7.18%, and 10.04% compared to that of the mix CC in compressive strength at the age of 28 days can be seen in the Type A concrete mixes CS10, CS20, CS30, CS40, CS50, and CS60, respectively. A decrease of 14.41% in 28 days' compressive strength compared to the mix CC was observed in the compressive strength of the mix CS100 which gained the least compressive strength among all concrete mixes.
From the results obtained for the slump values of concrete and the results of the previous research work [12], it can be inferred that the available water in concrete mix rises with rising quantity of copper slag in the mix. e glossy surface texture and the very low water absorption quality of copper slag particles are the likely causes for this increase.
is increased water in the mix which is in excess of the water required for the proper compaction and hydration of the cement paste results in the increased porosity of candidate mixes due to the separation of the concrete ingredients. is results in the reduced performance of the concrete mixes with more than 60% content of copper slag.
Motivated by these results, the Type B mixes were cast by changing the w/c ratio in the concrete mix CS60 which yielded highest compressive strength among the Type A mixes to 0.42, 0.40, 0.38, and 0.36. From Figure 2, it is clearly evident that the mix CW2 yielded the highest compressive strength among the Type B mixes. However, all Type B mixes showed improved compressive strength compared to the compressive strength of the mixes CC and CS60 at all w/c ratios. e mixes CW1, CW2, CW3, and CW4 showed an increase in compressive strength of 16.69%, 26.79%, 22.03%, and 13.56%, respectively, compared to the mix CC at 28 days of curing. Also, the Type B mixes CW1, CW2, CW3, and CW4 achieved an increase in compressive strength of 6.04%, 15.22%, 10.90%, and 3.20% over that of the mix CS60 at the curing age of 28 days. As the Type B mixes achieved greater strength compared to the mix CC and Type A mixes, variation of the compressive strength of the Type B mixes compared to the mixes CC and CS60 at 28 days of curing is presented in Figure 3. e reduction in the water content of the Type B mixes might have reduced free water available in the concrete mix which results in less porosity and improved compressive strength.
Because of the abrasion properties associated with its rough surface texture, natural sand can enhance the cohesion between coarse aggregates and cement paste. Despite this, the abrasion property of sand weakens over time because of years of weathering [22]. On the contrary, the improved cohesion due to sharp, angular edges and the better compressibility of the copper slag particles [13,14] compensates the adverse effect of sand to some extent and results in improved compressive strength.

Split Tensile Strength.
e in uence of copper slag substitution on tensile strength of concrete is illustrated in Figure 4. For the Type A mixes, the split tensile strength of concrete improved with the rise in the quantity of copper slag present in the mix till 60% substitution of natural sand by copper slag. At 70% substitution, the copper slag concrete gained split tensile strength similar to that of control concrete. On further increase in substitution, a considerable reduction in the split tensile strength was observed. A substantial improvement of 4.24%, 4.98%, 5.43%, 6.87%, 9.16%, and 11.83% in split tensile strength compared to that of the mix CC can be seen in the concrete mixes CS10, CS20, CS30, CS40, CS50, and CS60, respectively, at the curing age of 28 days. e Mix CS100 gained least split tensile strength among all the concrete mixes which were 12.74% less than that of the mix CC at the curing age of 28 days.
It is apparent from Figure 4 that the split tensile strength of all Type B concrete mixes is more than that of the mix CC.
An improvement of 8.10%, 20.65%, 13.54%, and 9.56% can be seen in the split tensile strength of the mixes CW1, CW2, CW3, and CW4, respectively, compared to the mix CC. e mixes CW2 and CW3 also showed an improvement in the split tensile strength of 7.88% and 1.52% over that of the mix CS60. However, the split tensile strength of the mixes CW1 and CW4 was 3.34% and 2.02% less than that of the mix CS60. A comparison of the split tensile strength of the Type B mixes with the mixes CC and CS60 at 28 days of curing is presented in Figure 5. e declined split tensile strength of the specimens with more than 60% substitution can also be because of increased porosity of concrete due to excess free water remaining in the mix [13]. e relation of the split tensile strength and compressive strength of the Type A and Type B concrete mixes is shown in Figure 6. For all the concrete mixes, the split tensile strength was greater than the value given by formula 0.45 f ck . Advances in Materials Science and Engineering

Flexural Strength.
e variation in the exural strength of candidate mixes with di erent copper slag substitution is depicted in Figure 7. Similar to the split tensile strength, the exural strength also increased up to 60% substitution of natural sand by copper slag. A drop in exural strength is noted as the percentage substitution increased over 60%. A negligible improvement in the exural strength of the mix CS10 is observed over the exural strength of the mix CC after curing time of 28 days. At the curing age of 28 days, the concrete mixes CS30, CS40, CS50, and CS60 achieved exural strength which was 0.56%, 1.17%, 2.13%, and 4.28% greater than that of the mix CC. e mixes CS20, CS70, CS80, CS90, and CS100 showed an decrease of 1.05%, 1.84%, 7.55%, 10.63%, and 12.76%, respectively, compared to the exural strength of the mix CC at 28 days' curing age. Percentage variation in the exural strength of the Type B mixes compared to that of the mix CC, and the mix CS60 is illustrated in Figure 8. It is visible from Figure 8 that the mixes CW1, CW2, CW3, and CW4 gained 2.12%, 9.37%, 7.86%, and 3.32% higher strength respectively compared to the mix CC at 28 days of curing. e mixes CW1 and CW4 showed a decrease of 2.07% and 0.91%, respectively, in exural strength compared to the exural strength of the mix CS60. e 28 days' exural strength of the mixes CW2 and CW3 improved by 4.88% and 3.43% over that of the mix CS60. e relationship of exural strength and compressive strength of the Type A and Type B mixes is depicted in Figure 9. e exural strength of all the concrete mixes was recorded to be greater than 0.7 f ck [23].
3.6. SEM. Scanning electron microscope (SEM) images of concrete specimens CC, CS60, CS100, and CW2 at 28 days are shown in Figure 10. Small micropores can be seen in Figure 10(a) which shows the microstructure of the mix CC. Figure 10(b) shows microstructure of the mix CS60. e better compressibility of copper slag and reduced pores due to increase in cohesion by the presence of copper slag are the probable reasons for the improvement of the strength. It is evident from Figure 10(c) that micropores are formed in the mix CS100. e interconnectivity of these micropores could have resulted in the reduced exural strength of the mix CS100. ese micropores become the weakest link. e micropores present in concrete quicken the progression of microcracks in concrete and form interconnected fractures which cause the failure of concrete. e decrease in the strength is predominant beyond 60% substitution because of the rise in the available free water in the mix. Also, more amount of copper slag is required to occupy the volume occupied by natural sand which results in increased surface area of copper slag compared to the surface area of concrete. e increased surface area demands high cement paste in case of high copper slag substitution.
e poor binding of copper slag ends in a lowering the strength of concrete. e reduced water content in the mix CW2 could have reduced the free water available in the mix due to the presence of copper slag.
is could be the probable cause for an enhancement in the strength of the mix CW2. e dense microstructure of the mix CW2 is visible in Figure 10(d).
3.7. X-Ray Di ractograms. X-ray di raction method was used to recognise di erent phases existing in hardened concrete at the curing age of 28 days. e XRD investigation was performed for di raction angle 2 theta between 5°and 80°on the cement paste isolated from the test specimen and screened through 90-micron sieve. e presence of phases such as alite, gehlenite, calcium silicate, calcium aluminum silicate hydrate, ettringite, silica, calcium hydroxide (portlandite), and calcium

Conclusion
For the continuing development, the construction of buildings and infrastructure is unavoidable. e environmental impact of construction activities is becoming a bigger and bigger concern with increasing global interest in sustainable development. e use of industrial wastes in concrete is a key driver towards the sustainable construction.
e ndings of the present experimental work undertaken to ascertain the feasibility of utilizing      copper slag as a substitute for natural sand infer that copper slag possesses a great potential to be utilized as fine aggregate in concrete. e following are the outcomes of the present experimental study: (1) ere is a significant drop in water demand when copper slag is used as a substitute for fine aggregate in concrete, which results in the improved workability of concrete. (2) e density of the copper slag concrete is greater than that of control concrete for the obvious reason that the specific gravity of the natural sand is about three-fourths of that of copper slag. (3) Partial substitution of sand by copper slag effectively improves compressive strength of concrete up to 60% substitution level, whereas the strength of concrete at 70% substitution remains similar to that of control concrete. (4) e split tensile and flexural strength of concrete also improved up to 60% copper slag substitution for natural sand. However, these values lowered for a further increase in substitution percentage. (5) Presence of high CaCO 3 in the mixes CS60 and CS100 could have hindered the crystallization of the portlandite and might have resulted in the reduction of the strength in these mixes. (6) e strength of the concrete containing copper slag significantly improves when the water content is reduced because of the reduction in free water available in the mix. (7) Reduction in the w/c ratio enhances the strength due to decline in free water available as long as enough water is available for proper hydration reaction. (8) It is recommended to use copper slag as fine aggregate in concrete up to 70% substitution level.

Conflicts of Interest
e authors declare that they have no conflicts of interest.