Synthesis of Wollastonite Powders by Combustion Method : Role of Amount of Fuel

.e objective of this work has been the synthesis of wollastonite by solution combustionmethod..e novelty of this work has been obtaining the crystalline phase without the need of thermal treatments after the synthesis. For this purpose, urea was used as fuel. Calcium nitrate was selected as a source of calcium and colloidal silica served as a source of silicon..e effect of the amount of fuel on the combustion process was investigated. Temperature of the combustion reaction was followed by digital pyrometry. .e obtained products were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), and specific surface area. .e results showed that the combustion synthesis provides nanostructured powders characterized by a high surface area. When excess of urea was used, wollastonite-2M was obtained with a submicronic structure.


Introduction
e materials which are used to replace or supplement the functions of living tissues are known as biomaterials.To meet the requirement of an ideal biomaterial, it must be biocompatible, biodegradable, and bioactive, among others.One of the areas where biomaterials are used is in bone substitute or regeneration, which most often uses scaffolds.In this case, in addition to the intrinsic properties of the biomaterials, these must be osteoconductors and osteoinducers.Also, they must present an interconnected network of open porosity that is essential for cell nutrition, proliferation, and migration for tissue vascularization and providing mechanical support until formation of new tissues [1].
A variety of materials such as metals [2], ceramics [3], natural and synthetic polymers [4], and their combinations [5] have been explored for replacement and repair of damaged bone tissues.An extensive attention has been paid on the development of bioactive materials, including calcium phosphates, silicates, glasses, etc. which were used in the tissue regeneration applications [5,6].More attention has been paid on the calcium silicate ceramic materials, particularly wollastonite (CaSiO 3 ), used as a biomaterial for bone regeneration because of its excellent in vitro bioactivity.A lot of authors have studied their ability to induce formation of the hydroxyapatite layer on their surface in vitro conditions when immersed in simulated body fluid (SBF) with ion concentrations, pH, and temperature almost equal to those of human blood plasma [7][8][9][10][11][12][13].
It was demonstrated by De Aza and Luklinska [14], De Aza, Guitian, and De Aza [15,16], and Wu et al. [17] that materials which contain Ca and Si atoms in their composition and which are free of P atoms can also produce HA layer on their surface.Fiocco et al. [9] proposes that the Mg atoms can further enhance the bioactivity of calcium-silicate materials.
Generally, calcium silicates are synthesized at high temperatures, between 900 and 1100 °C.Wollastonite can be synthesized by the solid state route [18], sol gel [19], or coprecipitation method [20] but these methods require high energy and a long time for the formation of products.
Solution combustion synthesis (SCS) is widely used to synthesize submicronic oxide ceramic powders. is synthesis consists in an exothermic redox reaction, associated with the decomposition of nitrates (oxidants) and the oxidation of the fuel.e heat evolved is larger than that needed to maintain the combustion process; thus, the system becomes self-sustained.
e SCS has become an excellent technique for synthesis because of their inherent superior qualities, which include the better homogeneity, composition control, lower processing temperature, and single step operation, which result in high reactive powders [20,[23][24][25].
e final product is usually a crystalline material with nanometric size clusters and has a large specific surface area as a consequence of the large amount of gases produced during the synthesis process. is high volume of gases produces high porous agglomerates.e ignition temperature (T ig ) is significantly lower than the combustion temperature (T c ) which results in the final solid phase formation [23].
Chakradhar et al. [26] prepared macroporous nanocrystalline wollastonite (CaSiO 3 ) ceramic powders by a simple, low-temperature initiated, self-propagating, and solution combustion process.e phases of β-CaSiO 3 and α-CaSiO 3 were obtained only after heating at 950 °C and 1200 °C, respectively.Huang and Chang [22] synthesized wollastonite (α-CaSiO 3 ) by a citrate-nitrate gel combustion method using citric acid as a fuel and nitrate as an oxidant.
e formation of α-CaSiO 3 was observed only after calcining powders at 650 °C for 2 h.e objective of this work was obtaining β-CaSiO 3 by combustion synthesis without the need of using further heating treatment.For this, Ca(NO 3 ) 2 and colloidal SiO 2 were employed as precursors and urea was used as fuel.e effect of the amount of fuel on the combustion process and characteristics of the products were studied as well.
e solution was dried and homogenized by stirring at 80 °C to remove excess water.e beaker containing the solution was introduced into a muffle furnace preheated to 600 °C.When placed in the furnace, the mixed solution soon started to boil, underwent dehydration, and the mass swelled to yield foam. e entire process required less than 15 min with flame duration of nearly one minute.
e as-synthesized products were typically voluminous, fluffy foam-like mass that occupied a large volume.
e resulting soft agglomerate was readily ground manually in an agate mortar/pestle into fine powder and was characterized.

Characterization.
e phase composition of the prepared powders was determined by X-ray diffraction (XRD; Bruker D8) using nickel-filtered CuK α radiation.Intensities were collected by step-scanning from 10 °to 60 °(2θ) with a step size of 0.02 °and counting time of 1 s for each step.Fourier-transform infrared spectroscopy was obtained using a SPECTRUM 400 FTIR spectrometer.e samples were prepared at potassium bromide (KBr) pellets (ca.2% by mass in KBr).e infrared spectra of prepared samples between 400 and 4000 cm −1 were recorded.e specific surface area (S BET ) of the powders was determined by nitrogen absorption (ASAP 2020M Analyzer, Micromeritics).e equivalent diameter (d BET ) of particle was calculated from the measured surface area (S BET ) values by using the following relationship: where ρ is the theoretical density of the powder (2.8 g/cm 3 for the wollastonite).Field emission scanning electron microscopy (FESEM S-4700, Hitachi, Japan) was used to characterize the microstructure and morphology of the combustion product, which beforehand was coated with gold, by sputtering.Temperature profiles of the powder mixture were measured by a two-color pyrometer (IMPAC model IGAR 12-LO) that can measure temperature in the range 500 °C-2200 °C.e pyrometer was placed near the open door of the reactor furnace.e optics (with a glass fiber guide) was focused on the sample.Maximum flame temperatures were theoretically calculated for the combustion reactions with urea as fuel and for different ratios of fuel/oxidant.is was calculated from enthalpy of combustion reaction (ΔH °) and the heat capacity of products (C p ) at constant pressure.

Results and Discussion
e synthesis of wollastonite by combustion reaction can be represented by the (2): where n is a coefficient that defines the total amount of fuel. is is related to the total released energy during the synthesis.e values of the coefficient n were 1, 2, and 3 for samples: n � 1 implies that the amount of urea required is the stoichiometric ratio of fuel to oxidant, considering aluminium nitrate as the only oxidant.n � 2 or 3 implies that the amount of fuel is twice and thrice, respectively, the stoichiometric one; in this case of fuel excess, corresponding amount of HNO 3 was added to balance the rest of fuel.
Available thermodynamic data in literature [27] of various reactants and products are listed in Table 1.Under adiabatic condition, the flame temperature (T f ) of 2 International Journal of Chemical Engineering combustion systems for different contents of fuel was calculated by Equation (3): where ΔH is given by reactants , ΔH 298 °is the standard enthalpy of formation, C p is the heat capacity of reaction products at constant pressure, and T ad is the adiabatic flame temperature, in Kelvin scale (K).
e typical temperature-time profile for the solution combustion synthesis of CaSiO 3 is shown in Figure 1.Initially, it is observed that a short constant temperature region is the referred region where the temperature of the sample is lower than the minimum temperature range of the pyrometer.During this time, water is partially evaporated.Later, a sudden increase in temperature takes place up to a maximum value (T max ), and the synthesis is terminated with slow cooling.
e measured (T c ) and calculated flame temperatures (T f ) of this reaction and those with different fuel to oxidizer ratios are shown in Table 2.In all the profiles, it is observed that in the initial instants, the temperature verified by the pyrometer is of 500 °C, although the furnace was at 600 °C, and this difference of temperature is related to the fact that, initially, the sample was in a temperature lower than the minimum temperature measured by the pyrometer, which is 500 °C. is period is also characterized by the evaporation of still remaining free water in the sample.When the material has not yet reached the furnace temperature, combustion begins.
is increases rapidly from temperatures below 500 °C to the maximum of combustion.International Journal of Chemical Engineering e measured temperatures are much lower than the corresponding calculated temperature.e main reason is that, in addition, the pyrometer used for measurement has area of measure approximately 2 mm in diameter, which means that it measures not only the combustion front temperature but also areas of preheating and cooling.In conclusion, the temperature measured corresponds to the average of the area of measurement.e maximum combustion temperature was observed when an excess (n � 3) of fuel was used.e sharp increase in temperature indicates the ignition of the combustion reaction.
e maximum temperature is referred to as combustion temperature, and after reaching the maximum temperature, the sample cools down rapidly.It can be observed that a dependence of the measured combustion temperature on the varying ratio, increasing the amount of fuel provides an increase in combustion temperature of the sample.
X-ray diffraction analysis of the combustion products obtained with different amounts of urea is shown in Figure 2. It can be observed that when n � 1, the powder showed poor crystallinity and the formed phases were α′-Ca 2 SiO 4 (JCPDS file no.00-036-0642), c-Ca 2 SiO 4 (JCPDS file no.00-049-1672), CaO (JCPDS file no.01-075-0264), and SiO 2 (JCPDS file no.01-082-1564); probably, the starting materials used did not react as expected and therefore did not form a desired phase, thus causing the formation of the SiO 2 phase.
When the amount of urea was increased (n � 2), fully crystalline phase of wollastonite-2M was observed (JCPDS file no.00-027-0088), indicating that the temperature achieved was sufficient to obtain the desired phase without subsequent calcination.
Further increase of amount urea (n � 3) provides the disappearance of wollastonite-2M phase and the appearance phases α′-Ca 2 SiO 4 (JCPDS file no.00-036-0642), c-Ca 2 SiO 4 (JCPDS file no.00-049-1672), CaO (JCPDS file no.01-075-0264), and SiO 2 (JCPDS file no.01-082-1564).ese phases have high crystallinity due to the high temperature of the synthesis, confirmed by the temperature measurements using the pyrometer (Figure 1).e higher combustion temperature provided by the large amount of fuel probably exceeded the melting temperature of wollastonite (as the calculated temperature predicts) and arrives directly to the liquid phase.As can be seen in the phase diagram (Figure 3), at a given temperature (T �1544 °C), this phase has a congruent melting point.e direct passage to the liquid phase may have led to precipitation of the coexistent crystalline phases at the reached temperature during cooling.
Figure 4 shows infrared spectrum of all samples.e IR spectroscopic analysis data confirm that the IR peaks in the range of 480-1110 cm −1 are due to CaSiO 3 [9,28] .e peaks in ∼480 cm −1 can be attributed to the bending vibration Si-O-Si bond.ose bands within the range 900-1110 cm −1 were assigned to Si-O-Si asymmetric stretching vibration and the O-Si-O stretching vibration absorption band [29,30].
e peak around 1370 cm −1 is attributed to the vibrations of ionic (NO 3 ), indicating the presence of trace amounts of nitrate from the starting material calcium nitrate in the sample; this peak decreases with the increase of the  Huang (1995) [28]. 4 International Journal of Chemical Engineering amount of fuel [31].e bands in the range 1470 cm −1 , when a sample was formed, show the presence of CaO in the sample, with the increase amount of fuel, and these bands progressively decreased [32,33].e band around 1644 cm −1 can be ascribed to be the bending vibration of the H-O-H bond in molecule water.A broad band around 3400-3600 cm −1 is caused by the stretching vibration of different kinds of hydroxyls and the remaining adsorbed water.With the increase in the amount of urea and consequently at the combustion temperature, these peaks disappear.e decrease could be attributed to the release of water molecules trapped inside the solid matrix [26,34,35].
Table 3 shows the specific surface area (SSA) and particle sizes (estimated from specific surface area (d BET ) of the powders obtained by combustion as a function of n.It is a well-established fact that, in combustion synthesis, the higher the combustion temperature, the longer the flame duration, leading to coarsening of the particles.Within the framework of this study, when n � 1, low flame temperature and high gas volume inhibited the particles growth and generated powder with higher surface area.As the amount of fuel increases, n � 2, the higher temperature during combustion reaction decreases the surface area due to grain growth.On the contrary, when n � 3, a possible melting and precipitation of new phases, caused by the high combustion temperature, provided a small particle size and high specific surface.International Journal of Chemical Engineering FESEM observation of the product (Figure 4) shows that all samples exhibit particle nanostructures with nodular morphology which are quite agglomerated.At higher magnification (Figures 4(b), 4(d), and 4(f)), it is possible to observe that powders are structured submicronically and presented smaller particles were sintered together and form larger particles, which can be due to the high combustion temperature.e heterogeneity can be confirmed from the analysis of the X-ray results (Figure 2) of these samples that evidence the formation of distinct phases.In the case of samples obtained with n � 3, where the phases found are crystalline, this can be explained due to the fact that the high combustion temperature was obtained that favoured the dissociation and decomposition of the wollastonite obtained when n � 2.

Conclusions
Crystalline CaSiO 3 has been synthesized by the solution combustion method without any thermal treatment after the synthesis.International Journal of Chemical Engineering It was observed that the amount of fuel significantly influences the composition of the phase.
When an excess of urea (n � 2) was used the wollastonite-2M was the only phase obtained.e use of a stoichiometric amount of fuel (n � 1) did not favour the synthesis by combustion and consequently it was not possible to obtain crystalline phases of the material.While a higher amount of fuel (n � 3) provided the formation of calcium silicate phases, but it was not possible to obtain the wollastonite.
e combustion synthesis method for obtaining submicronic structured wollastonite, using urea as fuel, is an efficient method for obtaining powders without needing additional heat treatment.

Figure 1 :
Figure 1: Time-temperature profile of aqueous solution combustion synthesis of wollastonite (initial furnace temperature of 600 °C).

Figure 2 :
Figure 2: XRD patterns of combustion synthesis powders obtained from systems containing different amounts of urea.

Figure 4 :
Figure 4: FTIR spectra of powders obtained from systems containing different amounts of urea.

Figure 5 (
d) shows a greater presence of pores, when compared to samples shown in Figures 5(b) and 5(f ), which is a microstructural characteristic of the products of combustion due to the escape of a large number of gases during the combustion; the increase of the amount of fuel (Figures 5(e) and 5(f )) provides a decrease in the presence of these pores, indicating a greater sintering of the particles.In Figures 6(a) and 6(b), it is possible to observe another type of morphology of the samples obtained with n � 1 and n � 3, respectively, and a heterogeneous morphology is formed by a crystalline phase (clear part) surrounded by an amorphous phase (dark part).

e
thermodynamic data used to support the findings of this study have been deposited in the Lange's Handbook of Chemistry, Dean, 1999 repository 10.1080/10426919008953291.(b)

Table 2 :
Influence of n ratio on the maximum combustion temperature.

Table 3 :
Influence of n ratio on the specific surface area and particle size of as-synthesized powders.