Abstract
The objective of the present investigation was to explore the potential of Chitosan based polymeric matrices as carrier for sustained stomach specific delivery of model drug Propranolol Hydrochloride. Briefly, single unit hydrodynamically balanced (HBS) capsule formulations were prepared by encapsulating in hard gelatin capsules, intimately mixed physical mixtures of drug, and cationic low molecular weight Chitosan (LMCH) in combination with either anionic medium viscosity sodium alginate (MSA) or sodium carboxymethylcellulose (CMCNa). The effect of incorporation of nonionic polymers, namely, tamarind seed gum (TSG) and microcrystalline cellulose (MCCP), was also investigated. It was observed that HBS formulations remained buoyant for up to 6 h in 0.1 M HCl, when LMCH : anionic/nonionic polymer ratio was at least 4 : 1. It was also observed that LMCH has formed polyelectrolyte complex (PEC) with MSA (4 : 1.5 ratio) and CMCNa (4 : 1 ratio) in situ during the gelation of HBS formulations in 0.1 M HCl. The retardation in drug release was attributed to the PEC formation between LMCH and MSA/CMCNa. Incorporation of MCCP (rapid gel formation) and TSG (Plug formation) was found to be innovative. From the data, it is suggested that Chitosan based polymeric matrices may constitute an excellent carrier for stomach specific drug delivery.
1. Introduction
It has always been difficult to engineer polymers or polymeric compositions for stomach specific drug delivery [1–3]. The engineered polymeric compositions should have attributes that are pertinent to high level of gastric retention, generally 5-6 h [4, 5], release the drug at zero-order or at a constant rate [6, 7], and degrade in vivo to smaller fragments, which can then be excreted from the body; their degradation products must be nontoxic and not create an inflammatory response; and finally, they should degrade within a reasonable period of time [1, 2]. Although polymers of various origins are available and used in drug delivery systems, natural polysaccharides find much application because of their favorable characteristics like abundant availability, inexpensive, nontoxic, noncarcinogenic, and biodegradable, and more importantly biocompatibility. Of these, Chitosan has received a great deal of attention due to its excellent biocompatibility, biodegradability, and nontoxicity. Chitosan fulfills all the polymeric attributes that are pertinent to high level of retention at applied and targeted sites via mucoadhesive bonds. The mucoadhesive property of Chitosan is due to electrostatic interaction of the protonated amino group in Chitosan with negatively charged silicic acid residues in mucin (the glycoprotein that composes the mucus). This interaction takes place very close to the mucosal surface and thus possesses potential to confer significant gastroretention to the hydrogel. Additionally, the hydroxyl and amino groups may interact with mucus via hydrogen bonding. The linearity of Chitosan molecules also ensures sufficient flexibility for interpenetration. Further, it also possesses cell-binding activity due to its polymer cationic polyelectrolyte structure and to the negative charge of the cell surface [8–11]. Although this material has already been extensively investigated in the design of different types of drug delivery systems, it is still less explored for stomach specific drug delivery systems. The objective of the present investigation is to explore the potential of this wonderful material in combination with anionic/nonionic natural polysaccharides like sodium alginate, sodium carboxymethylcellulose, microcrystalline cellulose, and tamarind seed gum in the fabrication of stomach specific single unit HBS capsule formulations using Propranolol Hydrochloride as model drug. The proposed combinations of cationic (Chitosan) and anionic polymers (sodium alginate/carboxymethylcellulose) are expected to form a low density hydrogel that remained buoyant on acidic dissolution medium (0.1 M HCl) and sustain the release of highly hydrophilic model drug by in situ polyelectrolyte complex formation.
2. Material and Methods
2.1. Materials
Propranolol Hydrochloride (PHCL) was obtained as a gift sample from Dr. Reddy’s Laboratories, India. Low molecular mass Chitosan (LMCH) [viscosity 20.00 cps of 1% in 1% acetic acid and degree of deacetylation (DD) > 80%], medium viscosity sodium alginate (MSA) [≥2,000 cps, 2% in water at 25°C], and carboxymethylcellulose sodium [CMCNa, average Mw ~90,000] were procured from Sigma Aldrich Brookfield. Tamarind seed gum (TSG) and microcrystalline cellulose (MCCP) [PH 102] were procured from the Central Drug House, India. All other chemicals used were of analytical grade.
2.2. Methods
2.2.1. Preparation of HBS Capsules Containing Propranolol HCl (PHCL)
Single unit capsules were prepared by physically blending PHCL with the required quantity of polymers as mentioned in Table 1, using double cone blender for 15 min, followed by encapsulation into hard gelatin capsules [12].
2.2.2. In Vitro Evaluation of HBS Capsule Formulations
(1) In Vitro Buoyancy Studies [12, 13]. Prepared HBS capsules were immersed in 0.1 M hydrochloric acid (pH 1.2, °C) in USP paddle type apparatus at 50 rpm. The time for which the capsules remained buoyant was observed.
(2) Determination of Drug Contents of HBS Capsules [12, 13]. PHCL contents were determined by emptying 10 HBS capsules from each formulation as completely as possible. A powder equivalent to average weight was added to 100 mL 0.1 M HCl (pH 1.2, °C), followed by stirring for one hour at 500 rpm. The solution was filtered through a 0.45 μ membrane filter and diluted suitably and the absorbance of resultant solution was measured spectrophotometrically at 290 nm.
(3) In Vitro Drug Release Studies. In vitro release of PHCL from the HBS capsule formulations was performed in USP dissolution apparatus type II at 50 rpm. Evaluation of drug release was performed by using 900 mL 0.1 M HCl (pH 1.2) at °C. At predetermined intervals, one mL aliquot was withdrawn and replenished with an equal volume of fresh dissolution medium. Withdrawn samples were analyzed spectrophotometrically at 290 nm.
2.2.3. Drug Release Mechanism
Different kinetic models such as zero-order, first-order, and square root (Higuchi) can be applied to interpretation of drug release kinetics. A zero-order release refers to a uniform or nearly uniform rate of release of a drug from the solid dosage form after coming in contact with an aqueous environment, independent of the drug concentration in the dosage form during a given time period. Dosage forms with zero-order release generally provide maximum therapeutic value with minimal side effects. For many extended release formulations, the rate of drug release initially increases rapidly followed by decreased rate of drug release. This type of drug release is categorized as the first-order release. Such dosage form may not produce uniform concentration levels of the drug in the systemic circulation for a prolonged period of time. The Higuchi release equation predicts that the drug release is caused primarily by diffusion mechanism [14]:where is the amount of the drug released in time and is the release constant from the equation. The data were also subjected to Korsmeyer-Peppas power law [15] as in (2). The Korsmeyer-Peppas model provides an insight into the type of drug release mechanism taking place from swellable polymeric matrices:where is the fraction of drug released in time , is the structural and geometric constant, and , the release exponent, is estimated from linear regression fit of the logarithmic release data. Practically, one has to use the first 60% of a release curve to determine the slope obtained from (2) regardless of the geometric shape of the delivery device. A good fit to the Korsmeyer-Peppas equation indicates the combined effect of diffusion and relaxation mechanisms for the release.
2.2.4. Statistical Analysis
The differences in average data were compared by simple analysis of variance (one-way analysis of variance) or Student’s -test (SigmaPlot 11).
3. Result and Discussion
Hydrodynamically balanced (HBS) capsule formulations are the simplest gastroretentive dosage forms. These systems are usually composed of hard gelatin capsules filled with a mixture of gel-forming polymeric substances and an active pharmaceutical ingredient. After immersion in simulated stomach fluid/acidic dissolution medium (pH 1.2) (in vitro) or swallowing (in vivo), the shell of the swollen hydrogel is formed. It controls the release rate of the drug, and it maintains appropriate integrity of the HBS and low apparent density of the systems, ensuring flotation. Such systems are best suited for drugs having a better solubility in acidic environment and for the drugs having specific site of absorption in the upper part of the small intestine [16].
3.1. In Vitro Buoyancy Studies
In vitro buoyancy studies were carried out in 0.1 M HCl (pH 1.2) maintained at °C using USP dissolution apparatus type II at 50 rpm.
For efficient buoyancy, swelling of polymer is very vital. LMCH contains –NH2– groups bound to polymer chains. In the presence of acidic gelation medium, the polymer chains in LMCH absorb dissolution medium and the binding of H+ causes the polymer to swell (). The air entrapped in the swollen polymeric network is expected to maintain the density less than unity which ultimately confers buoyancy to the hydrogel for extended period of time [17]. It was observed that the HBS capsule formulations prepared with PHCL and LMCH alone sank within h. The poor buoyancy could be attributed to the weak gel network formed due to the presence of highly soluble PHCL (225 mg/mL in 0.1 M HCl at 20°C) in LMCH based formulation that could not hold drug particles in the gel network. Therefore, to prolong the buoyancy, the auxiliary polymers (MSA, CMCNa, and TSG) were incorporated into HBS capsule formulations. These auxiliary polymers are expected to counter the rapid erosion of gel layer, thereby maintaining the integrity of the swollen hydrogel. All the formulations exhibited immediate buoyancy with no lag time (Table 2). HBS capsule formulations, J1–J6, remained buoyant up to 6 h, whereas formulations J7–J9 remained buoyant for 5 h (J7) and 4 h (J8 and J9), respectively.
It was also observed that LMCH : auxiliary polymer ratio is critical for buoyancy. The formulations remained buoyant for prolonged period when the LMCH : auxiliary polymer ratio was 4 : 1 (LMCH : MSA; LMCH : CMCNa; LMCH : MSA + TSG; LMCH : CMCNa + TSG). The addition of auxiliary polymer(s) resulted in improvement in swelling of the LMCH based formulations which in turn resulted in increase in bulk volume. The purpose of incorporating insoluble MCCP into the HBS formulation was to increase the porosity of the polymer matrix in order to improve the hydration and subsequent gel formation. It was observed that the whole polymeric matrix was hydrated within 15 min (J3 and J7) compared to 60 min in case of formulation J1. This fast hydration has resulted in rapid gelling but there was no improvement in buoyancy (J3) and in case of formulation J7, buoyancy was even decreased to 5 h. This could be attributed to the formation of a swollen hydrogel, whose density is greater than unity, due to excessive imbibition of aqueous acidic medium. Reversing the LMCH : MSA ratio (1 : 4, J8) or completely removing LMCH with MSA (J9) resulted in decreased in vitro buoyancy. The observed behavior (J8 and J9) could be attributed to the poor swelling of MSA in acidic dissolution medium coupled with the high diffusional driving force exerted by highly hydrophilic PHCL, which resulted in rapid erosion of gel layer leading to loss of gel integrity.
3.2. Determination of Drug Contents of HBS Capsule Formulations
The drug content determination test is done to ensure that each HBS capsule formulation contains equal amount of drug. For this purpose encapsulated contents of 10 HBS capsules from each formulation were emptied as completely as possible. The contents so removed were then put into 100 mL 0.1 M HCl (pH 1.2, °C) and stirred for one hour at 500 rpm. The solution was filtered through a 0.45 μ membrane filter and diluted suitably and the absorbance of resultant solution was measured spectrophotometrically at 290 nm. Drug contents of various formulations are given in Table 3. All capsule formulations were found to contain PHCL contents within limit [13].
3.3. In Vitro Drug Release Studies
In the present study, we have chosen Chitosan because of its ability to release loaded drugs slowly in the stomach, since the gel formation by cationic Chitosan is pronounced at acidic pH, which results in marked retardant effects on drug release [9, 12]. During the preliminary formulation development studies, we have investigated the feasibility of LMCH alone as a carrier for stomach specific delivery of highly hydrophilic model drug. However, polymeric matrices composed of LMCH (200 mg) and PHCL (50 mg) could not float for more than one hour and released almost 80% of PHCL (Burst release) before sinking in the acidic dissolution medium. This could be explained as, being cationic in nature, swelling of Chitosan in acidic gelation medium will be a more entropy-favored process and as the number of ions within the hydrogel structure increases, more and more osmotic and electrostatic forces will be created within the hydrogel structure [18]. This leads to increased dissolution medium (0.1 M HCl) uptake and forces a typical hydrogel to behave thermodynamically like a liquid as it occupies more space. Moreover, Propranolol is highly hydrophilic, which further reduces the strength of the aqueous gel layer due to high diffusional driving force and consequently increased erosion. As a result Chitosan hydrogel lost its integrity and became distorted leading to burst release.
Considering the above observation, in the present study, to improve the buoyancy and to address the problem of burst release, we have decided to combine LMCH with MSA or CMCNa. It is expected that such a polymeric composition not only maintains the integrity of the hydrogel and thus buoyancy, but also is expected to form in situ polyelectrolyte complex (PEC) between LMCH and MSA or CMCNa. This PEC formation is expected to retard the dilution of outer gel layer of swellable and erodible hydrogel, thereby, retarding the diffusion of PHCL. It has been reported that the PECs formed between a polycation (e.g., LMCH) and polyanion (e.g., MSA or CMCNa) exhibit a very high degree of ordering and crystal like properties and have quite compact structures and are little affected by pH variation of the dissolution medium [19]. Keeping this in view, it is expected that if these complexes are formed in situ it might be possible to overcome the initial burst release of PHCL.
From the formulation J1, about 65.2% of PHCL (Figure 1) was released within first h, after that remaining drug was released in a slower manner. This observation is opposite to our expectation, that is, retarded drug release. This could be explained as there must be sufficient polymer contents in a matrix to form a uniform barrier. This barrier protects the drug from immediately releasing into the dissolution medium. In this case, it is possible that a uniform gel layer might not have formed to retard the PHCL release.
Another reason could be the delayed gel formation. It was observed that when the formulation J1 was placed in dissolution media, due to imbibition of the acidic dissolution medium, the hard gelatin capsule shell disrupted (15 min) and a gel layer around the polymer matrix were formed (~30 min). It seems that during the first 30 min most of the PHCL particles located at the surface of the polymer matrix, dissolved and released rapidly.
Therefore, in formulation J2, it was decided to study the effect of increased concentration of MSA (LMCH : MSA ratio 4 : 1.5) in polymer matrix keeping the LMCH concentration constant. In this case significant retardation (, J1 and J2) in drug release which was observed with only 30% of PHCL (Figure 1) was released within first hour. This could be attributed to quick formation of a hydrogel in which polyelectrolyte complex (PEC) might have formed in situ. The relatively quick gel formation could be attributed to the association/dissociation/binding of various ions to the polymer chains within the hydrogel structure exposed to acidic dissolution medium [20].
To confirm PEC formation (J2) between oppositely charged polymers, Differential Scanning Calorimetric (DSC) on dried gelled polymeric compositions was carried out. Briefly formulation composition which corresponded to blank J2 was accurately weighed and put into bags made up of dialysis membrane (1000-molecular weight cutoff, Sigma Aldrich). The bags were then heat sealed on both sides and exposed to the acidic dissolution medium using USP type II dissolution apparatus. After 30 min of exposure to dissolution medium (0.1 M HCl, pH 1.2), the contents of the bags were removed and dried in an oven overnight at 60°C and DSC Thermogram (TA Instruments, USA, Model: SDT 2960) was recorded (50 to 400°C at a heating rate of 10°C/min). Nitrogen was employed as blanket gas. The characteristic peaks (endotherm and exotherm) were recorded. The DSC Thermograms of LMCH and MSA were also recorded under identical conditions for comparison and confirmation purposes.
The DSC Thermogram of LMCH (Figure 2(a)) showed a broad endothermic peak at 157°C, which indicates the glass transition temperature of polymer.
(a)
(b)
(c)
The DSC Thermogram (Figure 2(b)) of pure MSA showed a broad exothermic peak at 240°C indicating slow degradation of MSA.
The DSC Thermogram obtained from dried gel sample (blank J2) revealed an endothermic peak at 141°C and an exothermic peak 235°C (Figure 2(c)). Both these peaks were missing in the individual thermograms of polymers (LMCH and MSA). The first broad endothermic peak at 141°C could be attributed to the glass transition temperature of LMCH-MSA polyelectrolyte complex. The second exothermic peak at 235°C is very weak and could be attributed to the slow degradation of polyelectrolyte complex. The formed LMCH-MSA polyelectrolyte complex exhibited its capability of modulating the initial burst as well as the subsequent sustained release of the PHCL.
The PEC formation between LMCH and MSA was also confirmed by Fourier Transform Infrared (FTIR) Spectroscopy. To deduce PEC formation, the FTIR (Shimadzu, model 8400S) spectra of LMCH, MSA, and dried gel sample were recorded and compared. The samples were prepared in KBr disks (2 mg sample in 200 mg KBr). The scanning range was 400–4000 cm−1 and the resolution was 2 cm−1. The FTIR spectra (Figure 3(a)) of MSA showed major absorption bands at 1610 and 1402 cm−1 due to asymmetric and symmetric stretching bond of carboxyl group. The IR absorption band at 3434 cm−1 is attributed to O–H stretching.
(a)
(b)
(c)
The FTIR spectra of LMCH (Figure 3(b)) exhibited absorption band at 1635, 1421, and 1377 cm−1 due to amides I, II, and III. Absorption band at 3412.3 and 2923.9 cm−1 is due to hydroxyl stretch and C–H stretch.
The FTIR spectra of dried gel sample (Figure 3(c)) exhibited shifting in absorption bands together with appearance of a new IR absorption band. The absorption band due to amides I, II, and III in LMCH was shifted to 1654, 1454, and 1309 cm−1, indicating change in the environment and there was a new band at 1730 cm−1. Further, the FTIR spectrum also showed shifting of O–H stretching vibration to 3444.40 cm−1 from 3418 cm−1 attributed to the free –OH groups of both polymers existing in the PEC structure. All these observations could be suggestive of the PEC formation between LMCH and MSA.
From formulation J3, only 24.74% of PHCL (Figure 1) was released within first hour. Now this is interesting, as we have already showed that, below the 75 mg MSA concentration, PEC formation with LMCH was not observed and then how could the PHCL release was retarded significantly (, J1 and J3). The formulation J3 was composed of LMCH, MSA, and MCCP ( mg). The purpose of incorporating MCCP was to increase the porosity of the polymer matrix in order to improve the hydration of polymer matrix. It was observed that the whole polymeric matrix was hydrated within 15 min compared to 60 min in case of formulation J1. This fast hydration has resulted in rapid gelling and thus slow diffusion of PHCL.
In case of formulation J4, an attempt has been made to study the release of PHCL from LMCH-CMCNa PEC gel. For this purpose MSA was replaced with CMCNa in equal amount, that is, 50 mg. The PHCL release (Figure 1) was found to be significantly retarded compared (39.24% at the end of first h) to formulation J1 (, J1 and J4). Here also, in order confirm in situ PEC formation, the DSC studies on dried gelled samples [LMCH + CMCNa (4 : 1, J4 blank) prepared in the same manner as LMCH + MSA dried gel] and individual polymers were carried out.
The DSC Thermogram of pure CMCNa (Figure 4(a)) showed an endothermic peak at 144.33°C corresponding to the glass transition temperature of the polymer.
(a)
(b)
The DSC Thermogram of LMCH + CMCNa dried gel (Figure 4(b)) showed two endothermic peaks at 150°C and 219°C. Both of these peaks are missing in the individual thermogram of LMCH and CMCNa. The first broad endothermic peak at 150°C could be attributed to the glass transition temperature of LMCH-CMCNa polyelectrolyte complex. The second exothermic peak at 219°C is very weak and could be attributed to the slow degradation of polyelectrolyte complex.
The PEC formation between LMCH and CMCNa was also confirmed by FTIR spectroscopy studies. Here also the FTIR spectra of LMCH, CMCNa, and LMCH + CMCNa dried gel were recorded and compared. The FTIR spectra of CMCNa (Figure 5(a)) showed major absorption bands at 1058, 1110, 1607, and 1423 cm−1 attributed to stretching vibrations of C–OH group, C–OH group, and symmetric and asymmetric vibrations of carboxylate group.
(a)
(b)
The FTIR spectra of LMCH + CMCNa dried gel (Figure 5(b)) exhibited shifting of absorption bands. The absorption band due to symmetric and asymmetric vibrations of carboxylate group was shifted to 1654 cm−1 and 1444 cm−1. Although no new peak has appeared in the spectra, there is change in environment of carboxyl group, suggesting PEC formation.
In formulation J5, some amount of MSA was replaced with tamarind seed polysaccharide (TSG). Tamarind seed polysaccharide is a nonionic, neutral, branched polysaccharide comprising a cellulose-like backbone. It is dispersible in warm mater to form a highly viscous gel (up to 2800 cps in 3% solution) as a mucilaginous solution with a broad pH tolerance and adhesivity. It possesses properties such as mucomimetic, mucoadhesive, and pseudoplastic properties. It is a multifunctional polymer, which plays the role of release retardant, modifier, and a carrier for novel drug delivery systems for oral, buccal, colon, ocular systems and so forth [21]. It was expected that incorporation of TSG to the LMCH-MSA matrix will increase viscosity of gelled polymer matrix which in turn offer more resistance to diffusion of PHCL through the gelled polymer matrix. It was observed that addition of TSG resulted in the formation of a polymer matrix in the form of plug rather than random network of gelled mass. However, contrary to our expectation, about 51% of PHCL (Figure 1) was released within first h; this could be attributed to time period spent on plug formation. When the HBS formulations (J5) were placed in 0.1 M HCl, dissolution medium begins to penetrate into the polymer matrix through the disrupted capsule shells. Total time spent on plug formation ranged from 18 to 20 min and during this period most of the highly water soluble drug was leached out of the system. Once the plug formation was complete the PHCL release was significantly retarded with next 50%; PHCL was released in about 5 h (9, 11, 8, 11, and 9% at the end of 2, 3, 4, 5, and 6th h). In formulation J6, here also the plug formation was observed but the release retardant effect was not statistically different compared to J5 (, J5 and J6). In case of formulation J7, effect of incorporation of MCCP was again studied, this time with LMCH-CMCNa polymer matrix. As expected polymer hydration took place rapidly and about 37% of drug was released within first hour (Figure 1). It was also observed that the release profiles compared to formulation J4 were almost similar. This suggests that PEC formation could be the main mechanism of PHCL release retardation rather than fast gelling of polymer matrix. In formulation J8, the ratio of LMCH : MSA was reversed compared to formulation J1. This has resulted in significantly decreased buoyancy with no statistically different release profile (, J1 and J8). The same observation was obtained when LMCH was completely replaced with MSA. The polymer matrix could not float for more than 4 h; however, release profile was significantly ( J8 and J9) retarded.
3.4. Mechanism of Drug Release
From the data generated from kinetic analysis, HBS capsule formulations J1, J3, and J8 followed first-order release pattern as evidenced by their values (Table 4). In this case, at first there is a burst effect where the drug is rapidly dissolved and released from the surface before the gel membrane is fully formed at the surface. In the second part, the release rate decreases continuously until the end of the process. This release pattern is characteristic of first-order release kinetics. On the other hand, formulations J2 and J4–J7 followed Higuchi release kinetics as evidenced by their values. Higuchi model states that the accumulative drug release from a swollen hydrogel is diffusion controlled and is proportional to the square root of the time. This model assumes a pseudosteady state, constant diffusivity, rapid drug dissolution, and sinks conditions. The Higuchi model is applicable if the release is largely governed by diffusion through water-filled pores in the matrix [14].
A good fit to the Higuchi model together with low values determined by the Korsmeyer-Peppas equation (formulations J2 and J4–J7) suggests that the swelling of Chitosan based polymer matrices and resultant drug release in 0.1 M HCl is diffusion-controlled. Formulation code J9 followed zero-order release kinetics, a release rate that is substantially constant over time.
The values of various Chitosan based HBS formulations calculated from Korsmeyer-Peppas equation are given in Table 4. For polymeric slabs, cylinders, and spherical systems, (polymeric slab), 0.45 (cylinder), and 0.43 (sphere) indicate Fickian diffusion (diffusion controlled). Values of (slab), 0.89 (cylinder), and 0.85 (sphere) suggest case II transport (swelling controlled, purely relaxation controlled drug delivery). Occasionally the value of >1 (slab), >0.89 (cylinder), and >0.85 (sphere) has been observed, which has been regarded as the super case II kinetics. Intermediate values indicate an anomalous behavior, that is, non-Fickian kinetics corresponding to couple diffusion/polymer relaxation. In diffusion controlled systems, Fickian diffusion dominates the drug release process, whereas, in swelling controlled delivery systems, the rate of drug release depends on the swelling rate of polymer network [14, 15].
From the values, formulations J2–J7 followed Fickian diffusion; that is, drug-release is purely controlled by drug-diffusion through the gel layer. Fickian diffusional release occurs by molecular diffusion of the drug due to a chemical potential gradient, whereas formulations J1 and J9 followed anomalous non-Fickian diffusion corresponding to coupling of diffusion/polymer relaxation. This type of drug release has been used to describe diffusion of hydrophilic drug from swollen matrix. Formulation J8 followed super case II transport. This kind of release would describe a transport in which the diffusion depends on both the concentration and time and in which the rate of dissolution medium uptake into the polymer matrix is largely determined by the rate of swelling and relaxation of the polymer chains.
4. Conclusions
In this study, feasibility of low molecular weight Chitosan in combination with MSA/CMCNa/TSG as polymeric carrier for hydrodynamically balanced capsule formulations was studied using Propranolol Hydrochloride as model drug. All the combination of LMCH with MSA/CMCNa (J1–J6) in the ratio of 4 : 1 and 4 : 1.5 (LMCH : MSA/CMCNa) showed good buoyancy which last up to 6 h in 0.1 M HCl. Reversing the polymeric ratio to 1 : 4 (LMCH : MSA, J8) or completely removing the LMCH resulted in polymer matrices which remained buoyant for only 4 h in 0.1 M HCl. The drug release retardation from the formulations (J2–J7) was attributed to the in situ PEC formation between LMCH and MSA/CMCNa. Incorporation of MCCP (rapid hydration) and TSG (Plug formation) was found to be innovative. Considering the experimental data, it may be concluded that LMCH in combination with MSA/CMCNa may constitute a potential polymeric carrier for the development of sustained release stomach specific sustained delivery of hydrophilic drugs with absorption window in the upper GIT.
Conflict of Interests
The authors declare that there is no conflict of interests regarding the publication of this paper.
Acknowledgments
The authors thank Dr. R. M. Dubey, Vice Chancellor of the IFTM University; Dr. S. D. Sharma, School of Sciences, IFTM University; and Dr. Reddy’s Laboratories, India, for generosity.