Highly Stable Fe 3 O 4 /C Composite: A Candidate Material for All Solid-State Lithium-Ion Batteries

Fe 3 O 4 nanoparticles synthesized by a base catalyzed method are tested in an All-Solid-State (ASLB) battery using a sul ﬁ de electrolyte. The pristine nanoparticles were morphologically characterized showing an average size of 12 nm. The evaluation of the electrochemical properties shows high speci ﬁ c capacity values of 506 mAhg − 1 after 350 cycles at a speci ﬁ c current of 250 mAg − 1 , with very high stability and coulombic ef ﬁ ciency. 2020. This paper is part of the JES Focus Issue on Challenges in Novel Electrolytes, Organic Materials, and Innovative Chemistries for Batteries in Honor of Michel Armand. micrographs carried a Tecnai kV TEM In simulated electron diffraction patterns have been reconstructed by performing a Fast-Fourier Transform (FFT) analysis of selected areas of the micrographs using the in the code. TEM the powders in acetone the grids Thermogravimetric analysis (TGA) ramp

The large development of Li-ion technology allows for a massive spreading of portable electronics, as well as for a progressive diffusion of electrical vehicles (EV). However, the increasing demand for battery systems with higher energy density requests a breakthrough in finding new materials. 1 In the last decade, the industry standard has been represented by insertion materials for both anode and cathode, while recently alloy-forming materials with Li x Z (Z = Si, Sn, Sb, Bi) formula 2 have emerged as viable, alternative anodes materials. In addition, recently a new chemistry has surfaced, allowing to store more Li + by the so-called conversion mechanism. [3][4][5] In this process the active material is reversibly reduced into metallic nanoclusters embedded in a Li 2 O matrix, 6,7 following the general Eq. 1: Among the others, several transition metal oxides, 8 sulfides, 9 nitrides, 10 phosphides 11 and fluorides 12 have been explored and tested as conversion anodes. Considering 3d-transition metal oxides, among iron oxides α-Fe 2 O 3 and Fe 3 O 4 have received great attention. 13 Fe 3 O 4 , also known as magnetite, is a low cost, environmentally benign metal oxide that can undertake a reversible conversion reaction with Li + ions, 14  Despite these premises, transition metal oxides associated with the conversion mechanism usually suffer from a series of issues intimately connected with the conversion reaction itself. In fact, remarkable structural changes and volume expansion are associated with this mechanism, 6 eventually leading to pulverization and loss of contact between active material particles and the current collector, which result in poor electron and ion transport limiting the overall cycle-life.
In order to improve the electrochemical performance, different approaches have been proposed: firstly, the use of composite nanoarchitectures with optimized morphologies, such as nanorods, 15 hollow 16 or nano-spheres 17 and carbon coating strategies [18][19][20] ; lastly the use of graphene to form composites [21][22][23] showed remarkable improvements in terms of cycle-life.
Here, we report the synthesis, characterization and evaluation of the electrochemical properties of pristine Fe 3  heating rate of 10°C min −1 to 400°C and then 5°C min −1 to 700°C with a final plateau of 3 h. The Fe 3 O 4 /C composite was then prepared by directly ball-milling iron oxide particles and the PAN derived carbon nanofibers at 250 rpm for 1 h, using ZrO 2 spheres and a Retsch PM100 instrument. The Fe 3 O 4 :C ratio was 80:20.
The Fe 3 O 4 /C powder was characterized by means of X-ray diffraction (XRD) using a Rigaku Ultima diffractometer (Cu Kα = 1.540 Å). X-ray photoelectron spectroscopy (XPS) data were acquired using a PHI 5800, Physical Electronics instrument, under Ar atmosphere, using Al Kα radiation (200 W, 13 kV), at a pressure of 10 −9 Torr. The diameter of the analyzed surface was 800 μm. The spectra were calibrated by the binding energy of the C 1s peak (BE = 284.5 eV). All spectra were fitted by the deconvolution software Casa XPS (Casa Software). Gaussian-Lorentzian (30% Gaussian) functions and a Shirley-type background were employed in all fitting spectra. SEM micrographs were recorded on a ZEISS LEO 1550 instrument, equipped with a X-MAXN EDX detector by Oxford Instruments. Transmission electron microscopy experiments have been carried out using a FEI Tecnai 200 kV cryo-TEM instrument. TEM pictures have been analyzed using the ImageJ software. 25 In particular simulated electron diffraction patterns have been reconstructed by performing a Fast-Fourier Transform (FFT) analysis of selected areas of the micrographs using the routines embedded in the ImageJ code. TEM samples have been prepared by suspending the powders in acetone by sonication: the suspension has been dropped on holey carbon grids and directly transferred into the microscope. Thermogravimetric analysis (TGA) has been performed with a Mettler-Toledo TGA/SDTA 851 instrument, in air atmosphere, in a temperature range of 25°C-900°C with a heating ramp of 10°C min −1 .
Cell assembly and electrochemical tests.-The electrode powder was prepared by ball milling the active material, the solid-state electrolyte and carbon nanofibers (CNF) as conductive additive, in the 35 (Nanocomposite): 60 (Solid Electrolyte): 5 (CNF) proportion, respectively, at 250 rpm for 10 min. Solid state torque cells were assembled in Ar-filled glovebox (MBraun): 200 mg of a LiI:Li 2 S-P 2 S 5 solid state electrolyte were weighed and cold-pressed at 1 ton to prepare a pellet, then 5 mg of electrode powder (1.75 mg in Fe 3 O 4 /C content and 1.4 mg in pure Fe 3 O 4 ) were weighed and put, with a Li-In counter electrode, into the respective side of the solid state cell and pressed at 4 ton. The cell was tightened using a torque wrench. Active material mass loading was 1.33 mg·cm −2 . Cyclic voltammetry, galvanostatic cycling tests and impedance experiments were performed using a VMP2/Z potentiostat/ galvanostat (Bio-Logic) in the potential ranges 0.100 V-3.000 V. Impedance spectra were recorded with bias potential of E = 3.000 V, in the frequency range of 100 KHz-100 mHz with an oscillation amplitude of ±5 mV. Potential values were reported vs Li + /Li couple. The electrochemical experiments were conducted at 40°C in a Tenney TJR environmental chamber. Specific capacity values given in this paper are referred to the total Fe 3 O 4 /C content in the electrode powder mix.

Results and Discussion
Structural and morphological characterization.-The Fe 3 O 4 /C composite was characterized using different techniques. Figure 1 reports the thermogravimetric analysis (TGA) and the X-ray Diffraction (XRD) spectra. Thermogravimetric analysis, Fig. 1a, shows a small weight loss, around 5%, up to 100°C, due to volatile species and moisture residues in the sample. The progressive weight decrease, leading to a sharp loss at 400°C, due to the conversion of carbon materials to CO 2 , accounts for a total of 25% weight loss, which excluding moisture at the beginning, is in line with the Fe 3 O 4 /C proportions of the prepared composite. It is worth noting that the composite powders were always dried at 120°C for 12 h under vacuum before moving them into the glovebox to assemble the torque cells.
The XRD pattern of the pristine magnetite powder, Fig. 1b, shows a series of peaks related to Fe 3 O 4 diffraction (Crystallography Open Database (COD), card no. 00-152-8612). The small size of each crystallite is estimated as ∼12.60 nm using Rietveld refinement (Maud software suite). 26 Rietveld data is shown in Table SI. Figures 2a-2d reports the SEM images of pristine powder. The morphology of Fe 3 O 4 is characterized by spherical shaped nanosized crystallites, aggregated in bigger secondary particles, without any peculiar feature. The electrospun polyacrylonitrile (PAN) derived carbon nanofibers are shorter than usual, due to the mechanical milling step during the preparation of the composite material. Fe 3 O 4 nanoparticles result to be in close contact with the electrospun carbon fibers, thus the overall electronic conductivity is expected to be improved. Additional micrographs of the PAN-derived carbon nanofibers are reported in Fig. S1 (available online at stacks.iop.org/ JES/167/070556/mmedia), detailing the difference in the pristine state, and after the ball milling.
The nanomorphology of the composite material has been investigated by TEM (see Figs. S2-S3) and conforms the observation by SEM. Despite the formation of aggregates, probably due to magnetic stirring during the synthetic procedure, the nanoparticles have a spherical shape with the boundaries of each single crystallite still visible, as can be seen in Fig. S1, reporting the HR-TEM micrographs. The large carbon matrixes are surrounded and decorated by dark nanoparticles, partially agglomerated. The FFT analysis of a selected area shown in the Fig. S3c is presented in the Fig. S3d. The simulated electron diffraction image confirms the identification of randomly oriented nanocrystals of magnetite Fe 3 O 4 , with cF56 structure. 27,28 The crystallite size is evaluated in the range of 6 nm-13 nm (Fig. 1b), consistent with the value calculated by applying the Scherrer's equation.
X-ray photoelectron spectroscopy (XPS) analysis is performed to better understand the composition of the iron-based composite. The survey spectrum reported in Fig. 3a   (e.g. O-H etc…) which, in turn, could induce a small shift in the Fe 2+ and Fe 3+ related doublets. 29,30,31 The C1s core level, Fig. 3d, shows three peaks at 284.7, 286.2 and 289 eV related to C-C and C-O species as residual products from the synthesis of the electrode powder. 26,27 Electrochemical characterization.-Electrochemical characterization using solid state electrolyte is performed by means of several techniques to have a wider picture on the cycling behavior and electrochemical performance. Cyclic voltammetry, Fig. 4, in the potential range 0.100 V-3.000 V at 0.050 mVs −1 scan rate, evidences several electrochemical signals: during the first cathodic sweep, three peaks, at 1.66 V, 1.10 V and 0.70 V respectively, are visible. The peak at 1.66 V (indicated as * in Fig. 4) has been observed also by other authors: it describes a still not completely clear irreversible processes only occurring during first discharge. 32,33 The peak at 1.10 V (A) is consistent with the pre-lithiation of the iron oxide phase, 34  Then, the sharp peak at 0.70 V (B), describes the first-cycle reduction of the oxide nanoparticles to Fe metal 20,35 by the conversion reaction, leading to the formation of an amorphous composite of Fe 0 dispersed in a Li 2 O matrix. 4 In the first anodic sweep a shoulder labeled as (C) is visible at E = 1.15 V, was assigned to Li + deinsertion from the PAN-derived carbon nanofibers, then a couple of broad and partially overlapped peaks are visible at 1.58 V and 1.82 V (D), which are attributed to the oxidation of the Fe 0 nanoparticles to Fe 2+ and Fe 3+ , respectively. These results are consistent with literature data reported for liquid systems. 36,37 In the following cathodic sweep a pronounced hysteresis appears, following a well-known electrochemical behavior typical for conversion anode materials, 3 and the peak (B) shifts to 0.8 V, now labeled as peak (D). On the other hand, the anodic oxidation process, peak (D), remains substantially unchanged. From Cycle#2, another electrochemical process is activated at E = 2.45 V and was labeled as (E). It is of interest to investigate the presence of an additional reversible redox couple related to peak (E), visible in the successive voltammetry cycles, and labeled as peaks F and G, respectively, see Fig. S2.
Galvanostatic cycling were performed using a current of 250 mA g −1 (current density 0.32 mA cm −2 ) in the voltage range between 0.100 V < E < 3.000 V, the same used for the cyclic voltammetry experiment, to ensure both reproducibility and to limit Li + insertion into the PAN-derived carbon fibers at very low potentials. 38 The obtained results are reported in Fig. 5. The panel (a) reports the prolonged cycling performance of the Fe 3 O 4 nanoparticles highlighting a first discharge capacity of 1049 mAhg −1 and a subsequent charge at 643 mAhg −1 , with coulombic efficiency around 61%. The first-cycle irreversible capacity is attributed to irreversible processes which could be associated to the formation of a passivation layer on the active material particles, as already evidenced by the CV experiment of Fig. 4. During the following 15 cycles, the capacity is stabilized at around 506 mAhg −1 for the remaining 335 cycles, with coulombic efficiency steadily exceeding 99.5%.
The galvanostatic E vs Q profiles of the first discharge step, Fig. 5b, reveal two short sloping plateaus at 1.93 V and 1.65 V, a short sloping plateau at 1.02 V, and a larger one at 0.76 V. The profile associated with the subsequent charge step presents a sloping plateau which extends from 1.5 V to 1.90 V. The profiles are almost consistent with the cycling voltammetry experiment. From the second charge/ discharge cycle, any sign of definite plateaus disappears in favor of a more sloped line around 1.0 V during the discharge steps, and from 1.6 V to 1.75 V during the charge steps. Additionally, with increasing cycle number a reversible short sloping plateau is visible at 2.45 V, which is assigned to a broad potential interval in which can be present both the Li 2 S and the Li 3 PS 4 electrochemical reactions. 39 Furthermore, the presence of a Li 2 S related peak, could be associated with some amorphous unreacted Li 2 S, left over during the electrolyte ball-milling preparation step and introduced into the electrodic composite formulation mixture. This behavior has not been fully understood yet. The data showed in Fig. 5b, is even clearer in the differential plots shown in Fig. 5c, in which all the signals present in the cyclic voltammetry are present, showing a highly stable and reversible behavior up to cycle 300.   The large voltage hysteresis after the first discharge and visible changes in the shape of voltage profiles, are typical features of conversion materials. This has been reported by several authors, associating parallel-occurring processes, such as: (I) the increase in surface area in Fe 3 O 4 nanoparticles-based electrodes during the first discharge, with the pristine oxide to the Li 2 O/M composite formation 40 ; (II) possible different reaction pathways during the conversion reaction. 41,42 Rate capability tests for the Fe 3 O 4 /C composite using different current rate, ranging from 100 mA g −1 to 2000 mA g −1 are reported in Fig. 6 and detailed in Table I. The delivered capacity ranges from 984 mAh g −1 at 100 mA g −1 to 236 mAh g −1 at 2000 mA g −1 , while, the ability to recover the original specific capacity is evaluated after 150 cycles at 250 mAg −1 . Average reversible capacity values of 660 mAhg −1 were obtained, with a coulombic efficiency constantly exceeding 99.8%, see Table I. Specific capacity profiles of the rate capability test are shown in Fig. S4. At higher currents, the profiles become almost featureless, and this polarization effect could hint at a slower kinetic response of the conversion mechanism for stronger polarizations.
The good performance at high current rate and the outstanding electrochemical stability in the following 150 cycles at lower current rate, in which most of the original specific capacity is recovered, is due to different factors. First, the very small size of active material particles and the fibrous nature of the carbon material create a high conducting network favoring electronic transport. Secondly, the preparation procedure through ball milling of both the composite material and the electrode powder mix ensures a very close contact among the composite nanoparticles, the solid-state electrolyte and the conductive additive which benefit to the Li + diffusion and charge transfer kinetics.
Further extended galvanostatic cycling experiments were conducted using two high current-rate of at 500 mA g −1 (current density 0.65 mA cm −2 ) and 1000 mA g −1 (current density 1.31 mA cm −2 ) for over 1000 cycles, with the aim to check the prolonged stability of the solid-state cell, which are depicted in Fig. 7. In both experiments, the system shows an impressive cycling stability by reaching 1000 cycles mark without any failure. Considering the current rate of 500 mA g −1 , marked as (a) in the graph, the electrode highlights a capacity retention of 39.10% at the last cycle and an average capacity value of 240 mAhg −1 , while for the experiment at 1000 mA g −1 , marked as (b), the electrode has a capacity retention of 51.46% during the last cycle and an average capacity value of 193 mAh g −1 . It is to notice that the first cycles are crucial for a correct activation of the material. Indeed, in this initial phase of the experiment, it is concentrated most of the irreversible capacity loss, which is then followed by a stabilization over a high number of cycles. Figures S3 and S4 report details of the voltage profiles and differential analyses during these two experiments, which show    consistent electrochemical features with the rest of the electrochemical characterization. Nyquist plots, in Fig. 8, have been acquired after full charge (3.000 V) by EIS measurements at selected cycle numbers (1,5,10,50,100,200). All the EIS spectra are characterized by very large depressed semicircles in the medium frequency range, related to charge transfer processes (see in inset of Fig. 8), and a sloping line at low frequency related to diffusion processes. As a general trend, the overall impedance of the electrodes tends to a slight increase upon cycling. At the same time, an increase of impedance values upon cycling, mostly during the initial cycles, is a signal of a worsening of the charge-transfer kinetics, which may be related to partial nanoparticles re-aggregation, loss of electric contact, and interfacial degradation.

Conclusions
Fe 3 O 4 nanoparticles have been synthesized by a simple basepromoted method, and mechanically mixed with PAN derived electrospun carbon nanofibers. The characterization was performed using different techniques while the electrode powders have been prepared by ball milling of the composite material with Li 3 PS 4 -LiI sulfide solid-state electrolyte and conductive carbon additive.
Their electrochemical characterization revealed a very stable cycling performance showing features consistent with Fe 3 O 4 conversion oxide and Li 2 S(Li 3 PS 4 ) electrochemical mechanisms for a high number of galvanostatic cycles, with specific capacities of 506 mAh g −1 after 350 cycles using 250 mA g −1 current rate. Rate capability experiments showed very good performance with a remarkable capacity recovery during the long cycling at the end of the experiment. Prolonged cycling experiments at high current rate, 500 and 1000 mA g −1 showed outstanding performance for over 1000 cycles. Preliminary electrochemical impedance spectroscopy experiments showed a quite stable interface. In conclusion, the use of all-solid-state cell configuration combined with the synthesis of inexpensive oxide like Fe 3 O 4 , easily synthesizable electrolyte and electrospun carbon fibers is very promising for the building of future LiBs with improved cycle-life and safety.