Abstract
In order to provide an effective prevention to 316L implants, a synthesized bioceramic was coated by using electrophoretic deposition (EPD). The effect of boron addition into hydroxyapatite (HA) on surface morphology, adhesion and corrosion resistance of the implant has been examined. Boron doped HA (B–HA) was synthesized by a simple chemical acid-base method with 5, 10, and 15 wt % boron additions to coat on 316L implants. The synthesized B-HA was coated on the substrates and the coated surfaces with and without B additions. Sintering took place at different temperatures and sintering rates. The coatings were characterized by X-ray diffractometer (XRD), Fourier transform infrared spectroscopy (FT–IR) and scanning electron microscope (SEM). Furthermore, adhesion and in vitro corrosion tests were conducted. The influence of boron additons on adhesion and corrosion resistance of 316L have been revealed for the coated substrates at different B additions. It was shown that boron addition increased the adhesion and corrosion resistance of the bioceramic coatings. Furthermore, the sintering effect on adhesion was also evaluated and the highest adhesion as 25.8 MPa has been reached at 750°C for 90 s and 5°C min–1 sintering conditions. It was found that using iodine as EPD dispersant has increased the charging ability of the B–HA powders in the suspension and hence eased deposition rate. The study revealed that boron-containing hydroxyapatite coatings can provide crack-free surfaces that providing high adhesion and hence increase the corrosion resistance of metallic implants. Through the results, it was also shown that the network between powders was improved and hence adhesion was increased with increasing B addition.
Similar content being viewed by others
REFERENCES
Williams, D.F., J. Mater. Sci., 1987, vol. 22, no. 10, pp. 3421–3445.
Burny, F., Donkerwolcke, M., and Muster, D., Mater. Sci. Eng., A, 1995, vol. 199, no. 1, pp. 53–59. https://doi.org/10.1016/0921-5093(95)09907-7
Hsu, R.W.W., Yang, C.C., Huang, C.A., and Chen, Y.S., Mater. Chem. Phys., 2005, vol. 93, nos. 2–3, pp. 531–538. https://doi.org/10.1016/j.matchemphys.2005.04.007
Say, Y. and Aksakal, B., J. Mater. Res. Technol., 2020, vol. 9, no. 2, 1742–1749.
Aksakal, B., Say, Y., Buyukpinar, Ç., and Bakirdere, S., Ceram. Int., 2017, vol. 43, pp. 12609–12615.
Bronzino, J.D., Biomedical Engineering Handbook, Boca Raton, FL: CRC Press, 2000.
Bogdanoviciene, I., Beganskiene, A., Tonsuaadu, K., Glaser, J., Meyer, H.J., and Kareiva, A., Mater. Res. Bull., 2006, vol. 41, pp. 1754–1762.
Murugan, R. and Ramakrishna, S., Compos. Sci. Technol., 2005, vol. 65, pp. 2385–2406.
Aksakal, B. and Demirel, M., Proc. Inst. Mech. Eng., Part H, 2018, vol. 232, no. 10, pp. 1039–1047.
Barheine, S., Hayakawa, S., Jäger, C., Shirosaki, Y., and Osaka, A., J. Am. Ceram. Soc., 2011, vol. 94, no. 8, pp. 2656–2662.
Ong, J.L. and Chan, D.C., Crit. Rev. Biomed. Eng., 2000, vol. 28, nos. 5–6, pp. 28–35.
Aksakal, B., Kom, M., Tosun, H.B., and Demirel, M., Eur. J. Orthop. Surg. Traumatol., 2014, vol. 24, no. 5, pp. 813–819.
Say, Y., Aksakal, B., and Dikici, B., Ceram. Int., 2016, vol. 42, no. 8, pp. 10151–10158.
Say, Y. and Aksakal, B., J. Mater. Sci.: Mater. Med., 2016, vol. 27, no. 6, p. 105.
Mavrogenis, A., Dimitriou, R., Parvizi, J., and Babis, G., J. Musculoskeletal Neuronal Interact., 2009, vol. 9, no. 2, pp. 61–71. https://doi.org/10.1016/j.joms.2007.05.013
Mucalo, M., Hydroxyapatite (HAp) for Biomedical Applications, Amsterdam: Woodhead Publ., 2015.
Hakki, S.S., Bozkurt, B.S., and Hakki, E.E., J. Trace Elem. Med. Biol., 2010, vol. 24, pp. 243–250. https://doi.org/10.1016/j.jtemb.2010.03.003
Ternane, R., Cohen-Adad, M.T., Panczer, G., et al., J. Alloys Compd., 2002, vol. 333, pp. 62–71. https://doi.org/10.1016/S0925-8388(01)01558-4
Devirian, T.A. and Volpe, S.L., Crit. Rev. Food Sci. Nutr., 2003, vol. 43, no. 2, pp. 219–231. https://doi.org/10.1080/10408690390826491
Yesilbag, D., J. Uludag Univ. Fac. Vet. Med., 2008, vol. 27, nos. 1–2, pp. 61–68. https://dergipark.org.tr/ tr/pub/uluvfd/issue/13525/163617.
Aksakal, B. and Boccaccini, A.R., Mater. Lett., 2012, vol. 76, pp. 177–180. https://doi.org/10.1016/j.matlet.2012.02.059
Mohseni, E., Zalnezhad, E., and Bushroa, A.R., Int. J. Adhes. Adhes., 2014, vol. 48, pp. 238–257. https://doi.org/10.1016/j.ijadhadh.2013.09.030
Williams, R., Mater. Today, 2011, vol. 14, no. 6, p. 290.
Wennerberg, A., Hallgren, C., Johansson, C., and Danelli, S., Clin. Oral Implants Res., 1998, vol. 9, no. 1, pp. 11–19.
Tozar, A. and Karahan, I.H., Surf. Coat. Technol., 2018, vol. 340, pp. 167–176.
Göncü, Y., Geçgin, M., Bakan, F., and Ay, N., Mater. Sci. Eng., C, 2017, vol. 79, no. 1, pp. 343–353.
Kokubo, T. and Takadama, H., Biomaterials, 2006, vol. 27, pp. 2907–2915.https://doi.org/10.1016/j.biomaterials.2006.01.017
Papavinasam, S., Boca Raton, FL: CRC Press, 2008, pp. 49–83.
Albayrak, Ö., Mater. Charact., 2020, vol. 113, pp. 82–89.
Khoshsima, S., Alshemary, A.Z., Tezcaner, A., Surdem, S., and Evis, Z., Process. Appl. Ceram., 2018, vol. 12, no. 2, pp. 143–152.
Güler, H., Gündoǧmaz, G., Kurtuluş, F., Çelik, G., and Gacanoǧlu, Ş.S., Solid State Sci., 2011, vol. 13, pp. 1916–1920. https://doi.org/10.1016/j.solidstatesciences.2011.08.016
Wang, Y.C., Leu, I.C., and Hon, M.H., J. Am. Ceram. Soc., 2004, vol. 87, no. 1, pp. 84–88. https://doi.org/10.1111/j.1551-2916.2004.00084.x
Wei, M., Ruys, A.J., Milthorpe, B.K., Sorrell, C.C., and Evans, J.H., J. Sol-Gel Sci. Technol., 2001, vol. 21, pp. 39–48. https://doi.org/10.1023/A:1011201414651
Askari, N., Yousefpour, M., and Rajabi, M., J. Aust. Ceram. Soc., 2020, vol. 56, pp. 1053–1059.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Aksoy, M.E., Aksakal, B., Aslan, N. et al. Enhanced Adhesion and Corrosion Properties of Boron Doped Bioceramic Coated 316L Implants. Prot Met Phys Chem Surf 57, 1040–1050 (2021). https://doi.org/10.1134/S2070205121050026
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S2070205121050026