Abstract
The Sr0.8Ce0.2Mn1 – yCoyO3 – δ (y = 0.2, 0.3, 0.4, 0.5, and 0.6) complex oxides with the perovskite structure obtained from simple oxides by the solid–state reaction technique have been examined using structural analysis and magnetic measurements. Substitution of Co for Mn in the dilute Sr0.8Ce0.2MnO3 antiferromagnet with a Néel temperature of TN = 210 K leads to a decrease in the degree of tetragonal distortion of the crystal structure and transition to the cubic cell. The degeneracy of the antiferromagnetic interaction (TN = 138 K at y = 0.2) observed at the first stage of the substitution of Co for Mn changes for its gradual enhancement with an increase in the magnetic transformation temperature up to 239 K at y = 0.6. An increase in the Co content weakens the competition between the ferromagnetic and antiferromagnetic couplings and reduces the temperature of the transition to the spin-glass-like state. The magnetic inhomogeneity and formation of Co2+–Mn4+ ferromagnetic clusters in Sr0.8Ce0.2Mn0.4Co0.6O2.69 at 140 K have been observed.
Similar content being viewed by others
REFERENCES
A. Urushibara, Y. Moritomo, T. Arima, A. Asamitsu, G. Kido, and Y. Tokura, Phys. Rev. B 51, 14103 (1995).
M. Imada, A. Fujimori, and Y. Tokura, Rev. Mod. Phys. 70, 1039 (1998).
S. Balamurugan, K. Yamaura, A. B. Karki, D. P. Young, M. Arai, and E. Takayama Muromachi, Phys. Rev. B 74, 172406 (2006).
J. S. Srikiran, A. Das, P. L. Paulose, and S. K. Paranjpe, Appl. Phys. A 74, S814 (2002).
N. Gayathri, A. K. Raychaudhuri, and S. K. Tiwary, Phys. Rev. B 56, 1345 (1997).
G. V. Bazuev, A. V. Korolyov, M. A. Melkozyorova, and T. I. Chupakhina, J. Magn. Magn. Mater. 322, 494 (2010).
A. Sundaresan, J. L. Tholence, A. Maignan, C. Martin, M. Hervieu, B. Raveau, and E. Suard, Eur. Phys. J. B 14, 431 (2000).
W. J. Lu, B. C. Zhao, R. Ang, W. H. Song, J. J. Du, and Y. P. Sun, Phys. Lett. 346, 321 (2005).
P. Mandal, A. Hassen, and A. Loidl, Phys. Rev. B 69, 224418 (2004).
H. Gu, H. Chen, L. Gao, Y. Zheng, X. Zhu, and L. Guo, Electrochem. Acta 54, 3532 (2009).
S. Balamurugan, K. Yamaura, M. Arai, and E. Taka-yama Muromachi, Phys. Rev. B 76, 014414 (2007).
A. Maignan, B. Raveau, S. Hebert, V. Pralong, V. Caignaert, and D. Pelloquin, J. Phys.: Condens. Matter 18, 4305 (2006).
P. D. Battle, T. C. Gibb, and C. W. Jones, J. Solid State Chem. 74, 60 (1988).
H. Wu. K. Zhu, G. Xu, and H. Wang, Phys. B (Amsterdam, Neth.) 407, 770 (2012).
Z. Zhang, C. J. Howard, D. Kennedy, M. Matsuda, and M. Miyake, J. Phys.: Condens. Matter 21, 124218 (2009).
T. I. Chupakhina and G. V. Bazuev, Inorg. Mater. 47, 1361 (2011).
S. N. Shamin, V. V. Mesilov, M. S. Udintseva, A. V. Ko-rolev, T. I. Chupakhina, G. V. Bazuev, and V. R. Galakhov, Curr. Appl. Phys. 16, 1597 (2016).
G. V. Bazuev and A. V. Korolyev, J. Magn. Magn. Mater. 320, 2262 (2008).
G. V. Bazuev, Russ. Chem. Rev. 75, 749 (2006).
A. Maignan, S. Hebert, N. Nguyen, V. Pralong, D. Pelloquin, and V. Caignaert, J. Magn. Magn. Mater. 303, 197 (2006).
R. D. Shannon, Acta Crystallogr., A 32, 75 (1976).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated by E. Bondareva
Rights and permissions
About this article
Cite this article
Bazuev, G.V., Chupakhina, T.I. & Korolev, A.V. Effect of Cobalt on the Crystal Structure and Magnetism of Electron-Doped Sr0.8Ce0.2MnO3 Oxide. Phys. Solid State 60, 2491–2497 (2018). https://doi.org/10.1134/S1063783418120089
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1063783418120089