Influence of heat treatment on corrosion behavior of laser welded Mg-Gd-Y fusion zones

This paper aims to evaluate the corrosion resistance of fusion zones in different heat treated condition from laser welded Mg-Gd-Y alloys and analyze their intrinsic corrosion mechanism.

The corrosion behavior of fusion zone from laser-welded Mg-Gd-Y alloy joints in the as-welded, ageing and solution + ageing conditions was investigated in the 3.5 wt.% NaCl solution by immersion tests.

The corroded surface of as-welded fusion zone consists of dark and bright regions, and the bright regions were composed of high-density needle-like products, whereas some different extended direction of the cracks with lots of long ultrafine needle-shaped corrosion products appeared in the dark regions. The corrosion resistance of the fusion zone is slightly decreased after the ageing treatment.

The solution + ageing treated fusion zone exhibits the highest corrosion resistance than that of the as-welded and ageing treated state because of the full dissolution of the cathodic coarse eutectic compound, grains growth and relatively compact protective films. The inhomogeneous distribution of the β′ can somewhat improve the corrosion rate of solution + ageing treated fusion zone when compared with base metal.