Preconcentration of Trace Amounts of Pb(II) Ions without Any Chelating Agent by Using Magnetic Iron Oxide Nanoparticles prior to ETAAS Determination

This work investigates the potential of magnetic Fe3O4 nanoparticles as an adsorbent for separation and preconcentration of trace amounts of lead from water samples prior to electrothermal atomic absorption spectrometry (ETAAS) determination. No chemical modifier is required in graphite furnace. Pb(II) ion was adsorbed on magnetic Fe3O4 nanoparticles in the pH range of 5.5–6.5, and then magnetic nanoparticles (MNPs) were easily separated from the aqueous solution by applying an external magnetic field; so, no filtration or centrifugation was necessary. After extraction and collection of MNPs, the analyte ions were eluted using HNO3 1.0 mol L−1. Several factors that may affect the preconcentration and extraction process, such as pH, type, and volume of eluent, amount of MNPs, sample volume, salting out effect, and interference ions were studied and optimized. Under the best experimental conditions, linearity was maintained between 0.005–0.5 ng mL−1. Detection limits for lead were 0.8 ng L−1 based on 3Sb. The relative standard deviation of seven replicate measurements of 0.05 ng mL−1 of Pb(II) ions was 3.8%. Finally, the method was successfully applied to extraction and determination of lead ions in the water and standard samples.


Introduction
In recent years, water pollution caused by heavy metals is one of the major economic and environmental problems all over the world. Among heavy metal ions, Pb(II) is considered to be a non-biodegrade-like organic pollutant in water and attracted more attention due to its toxicity, persistent in nature particularly, even at low concentrations [1][2][3]. Consequently, the development of reliable methods for the removal and determination of lead in environmental and biological samples is of particular significance [4].
Several techniques have been used to determinate the levels of lead in environmental and biological samples. These include electrothermal atomic absorption spectrometry (ETAAS) [5], inductively coupled plasma mass spectroscopy [6], inductively coupled plasma optical emission spectroscopy (ICP-OES) [7], and flame atomic absorption spectroscopy (FAAS) [8]. However, their sensitivity and selectivity are usually insufficient for direct determination of the Pb(II) ions at a very low concentration level in complex sample matrices [9]. In order to overcome these problems, separation and preconcentration of Pb(II) ions become necessary, particularly when it exists at trace levels of concentration. A number of separation/preconcentration procedures have been used for trace metal determinations: these include precipitation/coprecipitation [10], liquid-liquid extraction [11], and solid phase extraction (SPE) [12].
Nowadays, SPE is a well-established technique and has been applied for the preconcentration and cleaning-up of numerous different classes of compounds in a variety of 2 The Scientific World Journal  120  10  20  250  Pyrolysis  400  10  40  250  Atomization  1200  0  3  0  Cleaning  2000  1  2  250 matrices by virtue of its high enrichment factor, high recovery, rapid phase separation, low consumption of organic solvents, and compatibility with different detection techniques [13][14][15][16][17][18][19]. In some cases, however, due to the limited rate of diffusion and mass transfer, extraction time of ordinary SPE processes is usually long [20], it is particularly evident when extracting very low amount of the target analytes from large volumes of samples. Thus, novel SPE modes that can facilitate mass transfer are highly desirable. It is commonly acknowledged that the sorbent plays a very important role in the SPE technique, which is related to the analytical sensitivity, precision, and selectivity. Recently, various types of solid-phase sorbent have been developed [21]. Magnetic nanoparticles such as magnetite (Fe 3 O 4 ) and maghemite (γ-Fe 2 O 3 ) can be used as novel and excellent adsorbents due to their unique advantages over traditional microsized adsorbents [22]; they possess not only high surface area which can exhibit higher adsorption capacity for analytes, but also strong superparamagnetic properties which can meet the need of rapid extraction of large volume samples by employing a strong external magnetic field. In recent years, MIONs have been applied for the separation of trace organic compounds and metal ions in various samples [23][24][25][26][27][28][29].
To the best of our knowledge, there has been no study conducted on the use of magnetic iron oxide nanoparticles (MIONs) for the separation and preconcentration of trace metals without addition of chelating agent and without any modification of MIONs. Therefore, the main objective of this study is to investigate the preconcentration of Pb(II) on MIONs, prior to ETAAS determination in water and certified environmental samples.

Reagents and Solutions.
All chemicals were of analyticalreagent grade, and all solutions were prepared with deionized water. The laboratory glassware was kept overnight in a 1.4 mol L −1 HNO 3 solution. Before using, all the glassware was washed with deionized water and dried. Stock solution of lead at a concentration of 1000.0 μg mL −1 was prepared from Merck (Darmstadt, Germany). Working reference solutions were obtained daily by stepwise dilution from stock solution. A solution of 10% (w/v) NaCl (Merck) was prepared by dissolving of 10 g of NaCl in 100 mL of de-ionized water. Buffer solution was prepared from 0.1 mol L −1 sodium dihydrogen phosphate and 0.1 mol L −1 disodium hydrogen phosphate for pH 6. The solution of alkali metal salts (1% w/v) and various metal salts (0.1% w/v) was used to study the interference ions.

Instrumentation.
The measurements for lead determination were performed with a Shimadzu AA-680G atomic absorption spectrometer equipped with GFA-4A graphite furnace and deuterium background corrector. Lead hollowcathode lamp was used for absorbance measurements at wavelength of 283.3 nm and operated at 7.0 mA, with a spectral bandwidth of 0.3 nm. Peak area absorbance values were measured. Pyrolytically coated graphite tubes (Schunk, Germany) with a preinstalled pyrolytic graphite L'vov platform were used. Argon was used as sheathing gas; the internal gas flow in the graphite tube was interrupted during the atomization step. The instrumental parameters for ETAAS determination of lead are given in Table 1. A Metrohm 692 pH (Herisau, Switzerland) was used for pH measurements.

Preparation of MIONs.
The MIONs were synthesized by coprecipitation of a stoichiometric mixture of ferrous and ferric chlorides (molar ratio 1 : 2) in an ammonium hydroxide solution with constant stirring [30]. The nanoparticles were collected by the magnet and thoroughly washed with deionized water to remove excess amounts of ammonium hydroxide.

Characterization of MIONPs.
The microstructure of the MIONs was observed by transmission electron micrograph (TEM) image and showed that the adsorbent had a regular surface with an average size less than 50 nm.
Relative magnetization curve was determined at room temperature using a Quantum Design MPMS 5 superconducting quantum interface device magnetometer. The magnetic MIONs were characterized by a high magnetic moment when placed under a high magnetic field. The magnetic moment in the absence of an applied field was subtracted from the result. The magnetization curve exhibited zero magnetization upon the removal of magnetic field, which is a characteristic behavior of superparamagnetic particles. Magnetic MIONs did not retain any magnetization after the removal of an external magnetic field which proved the superparamagnetic characteristic of these nanoparticles.
Another important parameter for practical applications of synthesized Fe 3 O 4 is their magnetization. Due to the asymptotic increase of magnetization for high fields, the saturation magnetization value can be obtained from the fitting of the M versus 1/H curves, extrapolating the magnetization value of 1/H to 0 [31]. The results were shown that the saturation magnetization for uncoated-NPs is 55.7 emu g −1 , which is lower than that of bulk magnetite (92 emu g −1 ) [32]. This reduction might suggest a mixture with the maghemite phase. Conditions were the same as Figure 1.

General
Procedure. The extraction procedure was carried out in a batch process mode. Fifty mL of each standard and sample was placed in a beaker. To each beaker, 2 mL of 0.1 mol L −1 phosphate buffer (pH 6), 1 mL of 10% (w/v) NaCl, and 100 mg MIONs were added. Then, beakers were stirred for 5 min. The beaker was placed on the magnet, and nanoparticles were collected. After decanting the supernatant solution, the collected MIONs were washed with 1.0 mL of 1.0 mol L −1 HNO 3 solution in order to desorb the adsorbed ions. Then, analyte ions in the eluent were determined by ETAAS.

Sample Preparation.
Tap, river, mineral, and seawater samples were collected in acid-leached polyethylene bottles. The only pretreatment was acidification to pH 2 with nitric acid, which was performed immediately after collection, in order to prevent adsorption of the metal ions on the flask walls. The samples were filtered before analyses through a cellulose membrane (Millipore, Bedford, MA) of 0.45 μm pore size. Ten milliliter of each water sample was transfered to calibrated flask and was made to 250.0 mL with deionized water in a calibrated flask. Twenty milliliter of urine samples was given and heated for 1 h after addition of 15 mL concentrated HNO 3 and 4 mL HClO 4 70%. The content of the flasks was diluted with deionized water and filtered through a Whatman no. 40 filter paper into a 100 mL calibrated flask, and its pH was adjusted to 6 [18].

Results and Discussion
In this study, a combination of SPE and ETAAS was developed for determination of trace amounts of lead. Several factors that may affect the preconcentration and extraction process, including pH, type, and volume of eluent, sample volume and matrix effect were optimized. The optimizations were carried out on 50 mL of aqueous solution containing 2.5 ng of lead ions.

Effect of pH.
Since the pH of the aqueous sample solutions is an important analytical factor in the SPE studies of metal ions, the influence of pH on the preconcentration of lead ions was examined in the pH range of 3-9, keeping the other parameters constant. It was found that the lead was quantitatively adsorbed on the sorbent in the pH range 5.5-6.5. The pH curves for adsorption of Pb(II) ions are shown in Figure 1. In subsequent studies, the pH was maintained at approximately 6. Addition of 1-6 mL of buffer did not have any effect on the adsorption. Therefore, 2 mL of 0.1 mol L −1 phosphate buffer solution was used in all subsequent experiments. The results were showed that the extraction efficiency was increased to 0.75 mL and then remained constant in the range of 0.75 to 1.5 mL. Therefore, 1 mL NaCl 10% was used in all further experiments. The Scientific World Journal

Effect of Interference.
Various salts and metal ions were added individually to a solution containing 2.5 ng of Pb(II) ions, and the general procedure was applied. The tolerance limit was set as the concentration of the diverse ion required to cause ±5% error. The results obtained are given in Table 2. Most of the ions examined did not interfer. Thus, the proposed method is selective and can be used for determination of Pb(II) ions in complex samples without any prior separation.

Adsorption Capacity.
To determine adsorption capacity of MIONs, 50 mL of aqueous solution containing 3.0 mg of Pb(II) ion at pH 6 was added to 100 mg of MIONs. After shaking for 30 min, the MIONs were separated and the supernatant solution was determined by FAAS. The capacity of MIONs for Pb(II) ions was found to be 28.6 mg g −1 .

Analytical Figures of Merit.
Under the optimized conditions, calibration curves were constructed for the determination lead according to the general procedure. Linearity in the original solution was maintained between 0.005-0.5 ng mL −1 with a correlation coefficient of 0.9985 (A = 1.481C + 0.002, where A is the absorbance value of the eluent and C is the concentration of Pb (ng mL −1 )). Seven replicate determinations of 0.05 ng mL −1 of Pb(II) ions in the original solution gave a mean absorbance of 0.078 with a relative standard deviation 3.8%. The detection limit was determined as three times the standard deviation (7 replicate measurements) of the absorbance of a blank sample.
The detection limit for lead in the original solution was 0.8 ng L −1 .

3.10.
Accuracy of the Method. The accuracy and applicability of the proposed method has been applied to the determination of Pb(II) ions in NIST CRM 1643e (National Institute of Standard and Technology, Trace elements in water). The amount of lead in NIST CRM 1643e was found to be 19.47 ± 0.26 ng mL −1 . It was found that there is no significant difference between the result obtained by the general procedure and the certified result (19.63 ± 0.21). The t-test was applied to both sets of results and showed that there was no significant difference at the 95% confidence level.
3.11. Application to Real Samples. The general procedure has been applied to the determination of Pb(II) ion content in tap water, seawater, mineral water, and urine samples by using 50.0 mL of each sample. The results are given in Table 3. Also, the recovery of Pb(II) ions from samples spiked with known amounts of lead ions was studied. The results are shown in Table 3. As can be seen from the results in Table 3, the added lead ions were quantitatively recovered from the water samples by the general procedure. These results demonstrate the applicability of the procedure for lead determination in water samples.

Comparison.
A comparison between the proposed method and the other reported preconcentration methods [5,[33][34][35][36] for the Pb(II) ion extraction from water samples is given in Table 4. The obtained detection limits by the proposed method are comparable to most of those reported in the literature.

Conclusions
It can be concluded from the results that MIONs are an effective sorbent for separation and preconcentration of trace amounts of lead from various water samples. The greatest advantage of this method is that desired materials are separated from solution by a simple and compact process while less secondary wastes are produced. Other advantages are avoidance of channeling effects that are common in packed The Scientific World Journal 5 beds; simple, rapid, reproducible, and low analysis cost. Also, MIONs did not retain any magnetization after the removal of an external magnetic field which proved the superparamagnetic characteristic of these nanoparticles.