Abstract
Carbon rods extracted from Zn-C primary battery waste was used as raw material for graphene oxide (GO) synthesis. The synthesis used a modified Hummers method by providing potassium permanganate-sulfuric acid as the oxidizing agent. XRD analysis confirms a significant change between the graphite waste pattern and the produced graphene oxide pattern. A major peak at 2θ 27 ° which present in the graphite waste pattern is disappeared after it converts to the product, as well as a broad peak under 25 ° referring the presence of amorphous carbon. A broad peak at low angle of 12.02 ° dominantly present in the prepared GO pattern as a characteristic peak of GO. Meanwhile, some small peaks at 2θ of 17.76 °, 28.58 °, and 37.28 ° confirming the presence of manganese oxide which was used as oxidizing agent. A sharp peak at 1700 – 1500 cm-1 in the FT-IR spectrum indicates the presence of –C=O group, and at 1600 cm-1 refers to –C=C group. It confirms that this research has produced the targeted GO. Even though, the purity is need to be enhanced by removing the rest of oxidizing agent that still exist in the material.
Export citation and abstract BibTeX RIS
Content from this work may be used under the terms of the Creative Commons Attribution 3.0 licence. Any further distribution of this work must maintain attribution to the author(s) and the title of the work, journal citation and DOI.