Time Dependent Behavior of Engineered Cementitious Composite Concrete Produced from Portland Limestone Cement

Conventional concretes are nearly unbendable, and just 0.1 percent of strain potential makes them incredibly brittle and stiff. This absence of bendability is a significant cause of strain failure and has been a guiding force in the production of an elegant substance, bendable concrete, also known as engineered cement composites, abbreviated as ECC. This type of concrete is capable of displaying dramatically increased flexibility. ECC is reinforced with micromechanical polymer fibers. ECC usually uses a 2 percent volume of small, disconnected fibers. Thus, bendable concrete deforms but without breaking any further than conventional concrete. This research aims to involve this type of concrete, bendable concrete, that will give solutions for concrete deficiencies. Two types of Portland Limestone Cement were used, Karasta (CK) and Tasluja (CT). Four mixes were adopted, polypropylene fibers (PP) and polyvinyl alcohol solution (PVA) were conducted to prepare the mixes. The tests were carried out at the age of 28 days of water curing. Best results were presented for mixes containing pp fibers and PVA solution than those without fibers for drying shrinkage and creep tests.