Sodium beta-alumina thin films as gate dielectrics for AlGaN/GaN metal—insulator—semiconductor high-electron-mobility transistors

Sodium beta-alumina (SBA) is deposited on AlGaN/GaN by using a co-deposition process with sodium and Al₂O₃ as the precursors. The X-ray diffraction (XRD) spectrum reveals that the deposited thin film is amorphous. The binding energy and composition of the deposited thin film, obtained from the X-ray photoelectron spectroscopy (XPS) measurement, are consistent with those of SBA. The dielectric constant of the SBA thin film is about 50. Each of the capacitance—voltage characteristics obtained at five different frequencies shows a high-quality interface between SBA and AlGaN. The interface trap density of metal—insulator—semiconductor high-electron-mobility transistor (MISHEMT) is measured to be (3.5∼9.5)×10¹⁰ cm⁻²·eV⁻¹ by the conductance method. The fixed charge density of SBA dielectric is on the order of 2.7×10¹² cm⁻². Compared with the AlGaN/GaN metal—semiconductor heterostructure high-electron-mobility transistor (MESHEMT), the AlGaN/GaN MISHEMT usually has a threshold voltage that shifts negatively. However, the threshold voltage of the AlGaN/GaN MISHEMT using SBA as the gate dielectric shifts positively from −5.5 V to −3.5 V. From XPS results, the surface valence-band maximum (VBM-EF) of AlGaN is found to decrease from 2.56 eV to 2.25 eV after the SBA thin film deposition. The possible reasons why the threshold voltage of AlGaN/GaN MISHEMT with the SBA gate dielectric shifts positively are the influence of SBA on surface valence-band maximum (VBM-EF), the reduction of interface traps and the effects of sodium ions, and/or the fixed charges in SBA on the two-dimensional electron gas (2DEG).