A review of weldability of carbon steel in arc-based welding processes

Abstract The weldability of carbon steel is determined by carbon equivalent (CE) for predicting/estimating preheat temperatures necessary for weld integrity of the weldment. The microstructure of the welded carbon steel at the heat affected zone (HAZ) plays an essential role in the mechanical properties of the weldment, thus, painstakingly selecting welding process and parameters to slowdown the cooling rate are ensued by sound weld quality and crack free weld (enhanced service performance). This research work reviews the effects of various welding processes and parameters on microstructure and mechanical properties of carbon steels in arc-based welding.


PUBLIC INTEREST STATEMENT
Carbon steels are widely used engineering materials because of their outstanding mechanical properties and cost-effectiveness when juxtaposed with other materials.However, the ease of welding these materials, majorly high carbon steel has been a challenge due to the metallurgical transformation at the heat affected zone (HAZ) and the fusion zone (FZ) triggered by the welding heat.The weldability of these materials depends on its carbon content which is evaluated by the carbon equivalent (CE) value.The higher the CEV, the lower the weldability and vice versa.The microstructural transformation at the HAZ in the course of welding is a key factor that determines the weld integrity which depends on the cooling rate.The cooling rate is affected by the selected welding parameters and processes and can be handled in such a way to prevent rapid cooling at the HAZ and FZ for better service performance.

Introduction
Carbon steel properties depend mainly on its carbon content which is widely used in engineering practices.It is categorized into low carbon (mild) steel widely used for heavy structural steelwork, medium carbon steel used for shaft, gearing, pressured structures and railway applications and high carbon steel used for production of springs, gear wheels, vices, cutting tools and brackets in which welding plays an essential role in their fabrication processes (Adedayo, Odebiyi, & Oseni, 2013;Mousavi & Kelishami, 2008;Poorhaydari, Patchett, & Ivey, 2005;Prasanna, Rao, & Rao, 2010).
However, weldability of carbon steel is the property that shows the ease with which they can be welded (Adedayo et al., 2013).It is a function of carbon equivalent estimated from the chemical composition of the steel (Adedayo et al., 2013;Khaled, 2014; https://www.productionmachining. com/articles/material-influences-on-the-weldability-of-carbon-steel).

Welding parameters
Welding parameters such as current, voltage, speed, thermal efficiency and heat input of welding affect the weld quality of carbon steel weldment.

Heat input
Welding Heat input is defined by Equation 13(a-c) For instantaneous energy measurements in joule For instantaneous power measurements in J/s or W Where V and I are the arc voltage (volts) and current (amp.),respectively, S is the welding speed mm/min, and K is the thermal efficiency for the welding process (Kumar et al., 2014;Liskevych & Scotti, 2015) From Figure 1, the heat affected zone of the weldment improved as the heat input of the welding process increases.
Table 1 and Figure 2 show the effect of heat input on the cooling rate of the weldment, as the heat input increases (1.46KJ/mm to 7.28KJ/mm) the cooling rate of the weldment decreases from 12.5 C/sec to 2.5 C/sec.
As the heat input increases, the microstructure of the heat affected zone (HAZ) is more refined from cold cracking (martensite formation) by slowing down the cooling rate.The grains at the fusion zone are larger for the slow cooling rate when juxtaposed with the other fusion zone (FZ) of fast and medium cooling rates weldments, respectively, as shown in Figure 3(a-c).

Welding current
Table 2 shows the effect of welding current on the heat input in the course of the welding process.It can be noted that the welding current increases from 80Amp to 100amp as the welding heat input increases from 942J/mm to 1178J/mm.The weldment hardness and heat affected zone increased up to 90amp then decreased.(Samir, 2015) (Samir, 2015).As a result of this increase in welding current up to 90 amp, the more bainitic lathe is formed in lieu of pearlite which results in increased hardness.However, with further increase in current, welding heat input increases and leads to an extra normalizing effect on the weld with a resulting decrease in hardness (Samir, 2015)

Welding voltage
As the welding arc voltage increases from 21 volts to 25 volts, the width of the weld joint and the heat input increase from 1060 J/mm to 1262 J/mm with a decrease in penetration as shown in Table 3.The arc voltage has more influences on the welding heat input than the welding current.(Samir, 2015) Figure 3. (a) Fast cooling rate, low heat input (Kumar et al., 2014), (b) Medium cooling rate, medium heat input (Kumar et al., 2014), (c) Slow cooling rate, high heat input (Kumar et al., 2014).(a-c): Macrographs of weldment at a different cooling rate and heat input at 7x magnification.(Kumar et al., 2014).
Table 2. Effect of heat input controlled by a change in welding current (Samir, 2015) Specimen no.

Current in
Amp.There exist a maximum difference in the change in hardness of the workpiece at 21 volts, with greater hardness value at the heat affected zone in all the workpieces as depicted in Figure 5(a).The hardness of the weld joint decreases in all the three regions (HAZ, weld metal, and base metal) as the arc voltage increases and the cooling rate, decreased with an increase in arc voltage as depicted in Figure 5(b).the solidification time of the weld increases as the welding arc voltage increases in a linear pattern as shown in Figure 5(c) (Samir, 2015)

Welding speed
Welding heat input decreases as the welding speed increases as a result of the reduction in time for arcing during welding.The hardness values of both the heat affected zone and the weldment were increased with an increase in welding speed as shown in Figure 6(a) and Table 4 respectively (Samir, 2015).Cooling rate increases with increase in welding speed and solidification time decreased abruptly, thus giving room for martensitic transformation at the heat affected zone  (Samir, 2015).(b) Change in cooling rate.(Samir, 2015).(c) Change in solidification time.(Samir, 2015).and weldment hardness increases with increase in welding speed as shown in Figure 6(b,c) respectively.Additionally, penetration of the weld increases up to optimum welding speed and then decreases while the width of the weld joint decreases with an increase in welding speed (Samir, 2015)

Thermal efficiency
Welding processes performance is measured by thermal efficiency, high weld deposit quality, penetration and productivity of the processes.The thermal efficiency also called arc efficiency, process efficiency and heat transfer efficiency can be calculated as given in Equation 14; Where Q weld is the calorimetric energy input to the plate, Q nom is the nominal energy input from the power supply (arc energy)  (Samir, 2015).(b) Change in cooling rate (Samir, 2015).(c) Change in solidification time (Samir, 2015).
The thermal efficiency for consumable electrode processes is generally higher than the noconsumable processes.(Dupunt & Marder, 1995;Pépe, Egerland, Colegrove, & Yapp, 2011;Stenbacka, Choquet, & Hurtig, 2012) Figure 7 shows the schematic representation of the qualitative energy balance of the welding process that describes the melting efficiency and the process arc.The welding arc provides the bulk of the total energy in the welding process, and a small portion is provided by the welding electrode.The summation of these generated energies is transferred to the weld metal while a portion is lost to the welding surrounding (Dupunt & Marder, 1995).Mathematically, this energy balance is given as; Since the left hand is the total energy transferred to the weld metal, the arc efficiency (μ a Þ and melting efficiency (μ m Þ can be expressed as in Equations 16-17;  (Samir, 2015).(b) Change in cooling rate.(Samir, 2015).(c) Change in solidification time.(Samir, 2015).
The fusion zone (FZ) is melted by a portion of the total energy transferred to the weldment while the remaining energy lost is responsible for metallurgical transformation of part of the weldment next to the fusion zone (FZ) (formation of the heat affected zone) and heating up of the remaining parts of the weldment above the room temperature (Dupunt & Marder, 1995;Pépe et al., 2011;Stenbacka et al., 2012).
Figures 8 and 9 show GMAW and SAW with good arc efficiency and maximum travel speed follow by GTAW and PAW of the considered processes.

Parallel heating
Parallel heating is the operation of heating weldment at the outer boundary to some pre-determined temperature concurrently with the welding process as depicted in Figure 10, whereas preheating involves heating workpiece to some pre-determined temperature before commencing the real welding process.The microstructure of high carbon steel is vulnerable to cold cracking (martensitic microstructure) as a result of rapid cooling of the weldment HAZ can be altered by parallel heating which is more pronounced as the boundary heater temperatures increases.(Adedayo et al., 2013;Graville, 1973;Khaled, 2014).
The boundary heating with high temperatures gave minimum cooling rates as shown in Table 5.Thus, the application of transient heat simultaneously with the welding process slows down the cooling rates, and thus, the applied heat refines the microstructures of the weldment by preventing the formation martensite (cold cracking) (Adedayo et al., 2013;Asibeluo & Emifonye, 2015).(Dupunt & Marder, 1995).

Weldment thickness
The thickness of the weldment to be joined modifies the cooling rate which as a result induces the hardening and cracking tendency (Kumarkhamari et al., 2018;Liskevych & Scotti, 2015).Considering the thickness of weld metal, the carbon equivalent value is modified to achieve compensated carbon equivalent related as per Equation 18.
Where' t' is the thickness of the plate in mm.
For large weld metals, vast amounts of austenite may be available after welding if preheat temperature ðT PH Þ and interpass temperature (T IPÀMin ) are notably higher than M 90 (90% martensite transformation temperature) for the work piece.As cooling progresses, this austenite can transform to martensite thereby increasing the risk of cold cracking and for large base metal T PH and T IPÀMin should be below M 90 (90% martensite transformation temperature).Thicker sections generally require higher T PH because of the greater heat-sinking capacity of thicker sections; heat sinking increases cooling rates producing smaller τ 8 = 5 values (Hinton & Wiswesser, 2008;Khaled, 2014).
The cooling rate τ 8=5 À Á is related to the thickness as per Equation 19 (Samir, 2015) t1 Where t is the weldment thickness, ρ is the density of the weldment in g=mm 3 Where k is the thermal conductivity in J=mms C T 0 is the initial temperature of the plate to be welded in C T c the temperature near the pearlite nose on TTT diagram Where ρC is volumetric specific heat in J=mm 3 C The cooling rate slows down as the thickness requires more heat input as depicted in Figure 11-Figure 13 3. Arc-based welding processes Sir Humphrey Davy in 1800 was credited for the manufacturing of an arc between two carbon electrodes using the battery as a source of power supply in the 19 th century (https://weldguru.com/OLDSITE/welding-history.html; https://www.interfacewelding.com;https://www.totalmateria.com/page.aspx?ID=CheckArticle&site=kts&NM=186).The popular arc-based welding processes are Shielded Metal Arc Welding (SMAW), Gas Metal Arc Welding (GMAW/MIG), Flux Cored Arc Welding (FCAW), Submerged Arc Welding (SAW), Gas Tungsten Arc Welding (GTAW/TIG) and a variant of GTAW process called Activated Flux Gas Tungsten Arc Welding (A-GTAW) Figure 11.Heat cyclic on HAZ of plates with different thicknesses (Dong et al., 2017).(Balasubramanian et al., 2009;Cao, Jahazi, Immarigeon, & Wallace, 2006;Khaled, 2014;Khurmi & Gupta, 1997;Pamnani et al., 2016;Tsuei, 2000; https://nptel.ac.in/courses/112107090/module1/ lecture2/lecture2.pdf).
process which requires a constant voltage and direct current power source.The arc is struck between the consumable electrode and the base metal.The four basic methods of metal transfers are spay, globular, pulsed-spray and short-circulating in which the shielding gas usually Helium, Argon or a combination of the two is externally supplied.The consumable electrode (filler wire) is fed continuously into the fusion zone automatically.MIG can be semiautomatic or automatic.In the latter, the torch or the base metal is moved relative to other mechanically while in semiautomatic MIG, the torch is manipulated manually.

Shielded metal arc welding (SMAW)
In 1950 s SMAW was developed (https://weldguru.com/OLDSITE/welding-history.html;https://www.interfacewelding.com;https://www.totalmateria.com/page.aspx?ID=CheckArticle&site=kts&NM= 186).This welding process is frequently utilized for welding ferrous metals in the steel structures construction and industrial fabrications.It is popularly called stick/covered electrode welding which follows a manual process in which the covered electrode uses an electric current to generate an electric arc between the base metal and the consumable electrode/stick.The molten weldment is shielded by fluxing elements provided by gas produced by the flux coating decomposition.

Submerged arc welding (SAW)
SAW was invented in Pennsylvania in the course of the defense buildup at Mckeesport in the late 1930 s and early 1940 s by the National Tube Company for a new pipe mill (https://weldguru.com/OLDSITE/welding-history.html; https://www.interfacewelding.com;https://www.totalmateria.com/page.aspx?ID=CheckArticle&site=kts&NM=186).The arc is between the base metal and cored consumable electrode in which the arc is being shielded by a layer of fusible granular flux (blankets and protects the fusion zone and nearby area from contamination upon melting).The weldment modification is done by the alloying ingredients present in the flux, and more than one cored electrode can be concurrently fed into the weld pool to increase rates of deposition.

Gas tungsten arc welding (GTAW)
This is also known as tungsten inert Gas (TIG) welding in which the arc is between the tungsten electrode (non-consumable) and base metal.GTAW was developed in 1890 by C.L. Coffin and later refined by Hobart in the late 1920s (https://weldguru.com/OLDSITE/welding-history.html;https://www.totalmateria.com/page.aspx?ID=CheckArticle&site=kts&NM=186).It is used to weld thick sections of high alloy steel or nonferrous metals.This process employs more time and complex than other processes.However, a variant of TIG called activated flux gas tungsten arc welding (A-GTAW) has been reported to surmount the major drawbacks of low productivity and shallow penetration in the TIG welding process.GTAW is similar to Plasma Arc Welding (PAW) developed by Robert M. Gage in 1957.More welding heat is produced in PAW than GTAW by the ionized gas.(https://weldguru.com/OLDSITE/welding-history.html;https://www.totalmateria.com/page.aspx?ID=CheckArticle&site=kts&NM=186)

Flux cored arc welding (FCAW)
FCAW was developed in 1954 by Bernard and later patented and refined by National Cylinder Gas Co. in 1957 (https://weldguru.com/OLDSITE/welding-history.html;https://www.totalmateria.com/page.aspx?ID=CheckArticle&site=kts&NM=186).This is a portable and high welding speed process developed as an alternative to shield welding.The arc is struck between the consumable cored electrode containing internally packed flux and the base metal.This welding process can be automatic or semiautomatic.The shielding gas is produced in the process by decomposition of the internal flux as in the SMAW process.A supporting shielding gas usually carbon dioxide may be added externally to supplement the flux gas which makes this process to resemble GMAW.
The selection of arc-based welding processes highlighted in 3.1-3.5 depends on the thickness of materials, cost-effectiveness, welding speed required, deposition rate, ease of automation, depth penetration and the arc efficiency.However, the laser welding process is the recent and newest welding process used because of the huge concentration of energy in a small space that serves as a power source.Laser welding equipment is exorbitant and bulky when compared to arc-based welding processes (https://weldguru.com/OLDSITE/welding-history.html;https://www.totalmateria.com/page.aspx?ID=CheckArticle&site=kts&NM=186).Another recent welding process is the inertia or friction welding (FRW) process developed in the soviet union.FRW is a solid-state welding process that produces welding heat via the rotational friction between the welded plates in relative motion and the upset pressure.Due to tooling and initial expense of equipment in FRW, it is applicable where a sufficient volume of similar parts is to be joined (https://weldguru.com/OLDSITE/welding-history.html; https://www.interfacewelding.com;https://www.totalmateria.com/page.aspx?ID=CheckArticle&site=kts&NM=186).

Preheating, interpass temperature, and post weld heat treatment
These three processes distinguish single weld from the multipass weld.Single-pass weld is defined by heating the workpiece to a predetermined temperature prior to actual welding process (Preheating) and giving heat treatment to the weldment after the welding (post-weld heat treatment) while Multipass weld involves controlling the interpass temperature in addition to preheating and post-weld heat treatment (Adedayo et al., 2013;Khaled, 2014;Stenbacka et al., 2012).Generally, carbon steels are expected to be preheated to some temperature (T PH ), before the actual welding process.It has been suggested that (T PH ) for any given steel should be about 50 F above the martensite start temperature for the particular steel being welded.However, most alloy steels have fairly high martensite start (M s ) temperatures, making welding at or above them somewhat cumbersome for the welder, thereby potentially compromising weld quality.For such steels, therefore, manufacturers often opt for preheat (T PH ) temperatures below Ms (martensite start) temperatures.Preheating removes moisture and other contaminants off the joint; moisture, lubricants and other contaminants are sources of hydrogen.More importantly preheating serves, to reduce the rate at which the metal cools down from the welding temperature to preheat temperature (T PH ) (Hinton & Wiswesser, 2008;Khaled, 2014).The hardness equivalent (HE) of the heat affected zone can be defined as (Hinton & Wiswesser, 2008;Khaled, 2014;Rizvi et al., 2013); Where HE is the hardness equivalent, PH is the Preheat Temperature, maximum heat affected zone Brinell hardness number (Max.HAZ BHN) and M 90 is the 90% martensite completion transformation temperature.
Thus, it can be inferred that; CE < 0:45 Required no PH 0:45 < CE < 0:5200 C À 500 CPH may be required CE >0:7 can not be welded cold cracking ð Þ Post weld heat treatment (PWHT) refers to the heat treatments carried out on the weldment after the completion of the welding process.This is to prevent residual stresses and hydrogen present in the weld that can lead to cold cracking which could either be post heating (weldment is not allowed to cool to room temperature) or stress relief (carried out after the weldment had cooled to room temperature).Most carbon steels are susceptible to cold cracking, weld cracking occurs when allowed to cool to room temperature, thus this could be prevented by allowing the hydrogen in the weld pool to diffuse from the weld at some elevated temperatures before the completed weld cools to room temperature, this is called post heating PWHT (Adedayo et al., 2013;Graville, 1973;Hinton & Wiswesser, 2008;Khaled, 2014;Khurmi & Gupta, 1997;Rizvi et al., 2013;Scott Funderburk, 1998).
The interpass temperature (T IP ) applies to multipass welds; it is the temperature of the weld zone between consecutive weld passes in multiple pass weld.This temperature can be specified as a minimum, a maximum or both depending on the metal being welded (Hinton & Wiswesser, 2008;Scott Funderburk, 1998).The minimum specified interpass temperature is typically equal to the minimum specified preheating temperature, both less than martensite starts temperature (M s ).To reduce or eradicate the risk of cold weld cracking, the weld temperature is maintained above the minimum specified interpass temperature between the passes (Khaled, 2014;Scott Funderburk, 1998).
The higher the preheat temperature, the higher the cooling rate (slow down cooling rate); however, as the thickness of the weldment increases, high heat input is required (Dong et al., 2017).
Table 6 shows the analysis of the effects of welding parameters on the properties of welds obtained from different welding processes in arc-based welding of carbon steels.
Table 6 shows that the primary welding parameters that influence the process heat input are the arc voltage, welding current and travel speed.Increase heat input means increase arc voltage and current but decrease travel speed and vice versa.
The mechanical properties such as the toughness and tensile strength increase with a decrease in hardness as the heat input increase regardless of the welding processes and carbon steels.
Parallel heat temperature and initial elevated temperature influence the microstructures at the heat affected zone and increase the tensile and toughness properties of the carbon steels but decrease the hardness value.The effect of Parallel boundary heat and initial elevated temperatures is more pronounced in high carbon steels as there is more rapid cooling at the HAZ (formation of martensite) when compared to other carbon steels.
Initial elevated temperature and parallel boundary heat temperatures slowdown the cooling rates regardless of the welding process and parameters.

Analytical method of temperature distribution in arc-based welding process of carbon steel
Predicting the weld flaws such as residual stresses, deformations, and weld solidifications cracking induced in a weldment is a critical first step which requires accurate computation of the transient temperature fields during the arc welding process (Nassef & Abdallah, 2012;Sykora, 2015).
Transient temperature field is essential because the temperature has a first order effect on the microstructure, mechanical properties and mostly on the welds defects formation.(Adedayo et al., 2013;Nassef & Abdallah, 2012) The accurate prediction of the thermal history is of key importance to effective simulation strategy for weld analysis (Nassef & Abdallah, 2012).Also, the effects of various welding processes and welding parameters on the transient temperature states must be accurately known (Nassef & Abdallah, 2012) From the diagram in Figure 14, Let the new coordinate system with respect to the tip of the electrode have the coordinate (; y; z) (Nunes, 1983)     x ¼ þ vt making the subject (25) Differentiating equation with respect to x and t The temperature distribution T is a function of and t, thus; Differentiating T with respect to t T ¼ f ð; tÞ (26) @T @t ¼ @T @ Á @ @t @T @t Á @t @t Similarly, The temperature field T varies in space coordinates x, y, z and time t in agreement with the differential equation of heat transfer in Equation 28.(Nunes, 1983) Where α is the heat diffusivity of the material in m 2 /sec, C p is the specific heat of material at constant pressure in J/KgK, ρ is the density of the material of a cubic element in Kg/m 3 and K is the heat conductivity of the material in W/mk.
Wieslawa et al. (Piekarska, Saga, Kroliszewka, Domanski, & Kopaj, 2018) determined the hardness distribution in a welded joint made of S1100QL steel using an analytical method.They determined the mechanical properties of the heat affected zone (HAZ) from the structural composition and mechanical properties of each of the structure (Piekarska & Dorota, 2016;Slezak & Sniezek, 2014).Having known the phase composition in the HAZ, such as pearlite martensite, and bainite, the mechanical properties of the entire welded zone are given as in Equation 32 (Piekarska & Dorota, 2016;Piekarska et al., 2018): Where W i is the properties of the structural components W, can be the mean hardness, yield strength, tensile strength, impact strength, elongation, and contraction.i is Martensite, Bainite, Ferrite, and Pearlite.
The phase composition and hardness of each of the structure of phases determine the hardness properties of the heat affected zone (HAZ).
Figure 15 depicts the results of the numerical simulation marking the region of the weld, HAZ, base metal and the direction of the welding heat source in the finite element analysis using ABAQUS software.The hardness properties of HAZ and the weld were predicted from Equations ( 32) and (34) for the 42 selected points of the weldment.The phase volume fraction on the function of time t 8 = 5 was obtained analytically as shown in Figure 16 (Piekarska et al., 2018).The experimental and analytical results for hardness distribution in the weldment for root and face show similar trend as shown in Figures 17-18.
The thermal cycles at different points in the weldment are a key factor in determining the microstructure and properties and can provide clear information on how the welding residual stresses occur in the course of the welding process as shown in Figure 19 (Malik et al., 2007).

Result and discussion
Estimating the carbon Equivalent (CE) value of carbon steels before welding design/procedure will go a long way in determining the preheat/interpass temperature and weldability of the material.Having known this, pertinent welding design can be put in place to prevent weld failure.
The choice of the welding process, optimum primary welding parameters (current, arc voltage, and travel speed) can ensure the estimation of carbon equivalent value of the material in question.The Figure 18.Hardness distribution in the cross section of weldment for root (Piekarska et al., 2018).
primary cause of cold cracking at the heat affected zone is rapid cooling, a metallurgical transformation triggered by the welding heat.Parallel boundary heat temperature, preheat Initial elevated temperature and can be used to enhance the microstructure for better toughness and tensile strength by slowing down the cooling rate.Additionally, post weld heat treatment influences the mechanical properties after welding before the occurrence of cold cracking as it is the time-dependent martensitic transformation of the microstructure at the heat affected zone.Thick workpiece requires high heat input and shows a slow cooling rate when compared to the thin workpiece.Thin metal coolings rapidly at HAZ as it requires low heat input.
Rosenthal's equation assumed initial temperature to be at room temperature; this will be modified for boundary heat temperatures in the future research.

Conclusion
The heat input of the selected welding process depends on the welding current, voltage, speed and thermal efficiency of the process which in turn affects the cooling rate.However, the cooling rate is also directly affected by parallel boundary heat transient temperatures, the thickness of the weldment, welding speed, post-weld heat treatment, interpass (multipass weld) and preheat temperatures.Thus, to achieve sound and crack free weld quality of carbon steel in the arc-based welding process, appropriate selection of welding process and parameters would produce high sound weld quality in carbon steel weldment.
Optimization of the process and its parameters for sound weld integrity and modified Rosenthal's equation for temperature distribution with boundary heat would be examined in the future research.

Figure 4
Figure 4(a) shows an increase in hardness at the heat affected zone of the weldment compare to weld joint and base metal in all the specimens.The cooling rate decreases in parabolic pattern with an increase in current as shown in Figure 4(b) with the solidification time increasing in a straight line as shown in Figure 4(c).

Figure 14 .
Figure 14.Schematic diagram of moving point welding heat source in SMAW.

Table 1 .
Calculated heat input and cooling rate(Kumar et al., 2014)

Table 5 .
(Adedayo et al., 2013)rent parallel boundary heating temperatures (BHT)(Adedayo et al., 2013) C is the specific heat of solid metal in J=g C T c is the temperature near the pearlite nose on TTT diagram T 0 is the initial temperature of the plate to be welded in C H net is the heat input in J=min for t1 > 0:75 τ 8=5

Table 6 .
The microstructure and mechanical properties of carbon steels under different welding processes and parameters

Table 6
volumetric heat source power distribution was used as given in Equation35