Nanoarchitectonics of ultrafine molybdenum carbide nanocrystals into three-dimensional nitrogen-doped carbon framework for capacitive deionization

Molybdenum carbide (MoC) has emerged as a promising material for capacitive deionization (CDI), but the poor electrochemical kinetics in conventional MoC owing to the bulk structure and low electric conductivity limit its CDI performance. To address this challenge, herein, we develop a novel strategy to synthesize ultrafine MoC nanocrystals that are embedded within a three-dimensional nitrogen-doped carbon framework (NC/MoC). This synthesis method involves the space-confined pyrolysis of molybdate precursors within metal–organic frameworks (MOFs). In this process, molybdates are confined into the MOF crystalline structure, where MOFs provide a confined reactor and carbon source. The resulting NC/MoC with the uniformly distributed MoC nanocrystals provides sufficient active sites for the electrosorption of salt ions, while the MOF-derived NC matrix facilitates charge transfer and provides the space-confined effect for preventing the possible aggregations of MoC nanocrystals during the CDI process. The NC/MoC exhibits an impressive salt adsorption capacity (SAC, 84.2 mg g−1, 1.2 V), rapid desalination rate, and high cycling stability (91.4% SAC retention after 200 cycles), better than those of most previously reported carbon-based CDI materials. Besides, the possible mechanisms are systematically investigated by ex situ characterization and density functional theory calculations. This study opens up new avenues for the construction of metal carbide-based nanocrystals for CDI and other electrochemical applications.


Introduction
5][6][7] As is well known, electrode materials play indispensable roles in CDI, and the developments of advanced electrode materials have been recognized as a prospective strategy for improving desalination performance. 8So far, various carbonaceous materials, such as activated carbon (AC), 9,10 carbon aerogels, 11,12 biomass-derived carbons, 13,14 carbon nanotubes, 15 and graphene, 16 have been synthesized and utilized as CDI electrodes.However, the salt adsorption capacity (SAC) of most traditional carbonaceous CDI electrodes is still unsatisfactory, 17,18 which might have originated from their decient compositions or uncontrolled structures. 17,18Therefore, the carbonaceous materials should be further optimized through morphological/structural/compositional regulations, to improve their electronic conductivity, SAC as well as cycling stability for achieving large-scale practical CDI application.
0][21] To date, Mo x C with different crystal phases, structures, and morphologies, have been prepared using various strategies, including solid-gas reactions between molybdenum oxides and carbon-hydrogen-containing gases, 22 solid-liquid reactions involving hydrothermal and annealing processes, 23 solid-solid reactions via the carbonization of Mobased compounds and carbon sources, 24 chemical vapor deposition, 25 etc.However, the preparation of Mo x C by these previously established approaches is oen performed at elevated temperatures, which easily leads to unavoidable aggregations or structural deteriorations, thereby compromising their electrochemical kinetics and further limiting their practical performance. 26If we develop an appropriate strategy for enhancing their structural characteristics, the targeted Mo x C will emerge as full potential candidates for high-performance CDI electrodes. 27etal-organic frameworks (MOFs) possess highly ordered porous nanostructures with ne microstructures, 26,[28][29][30][31] which have demonstrated an emerging opportunity to serve as space-conned reactors in nanocrystal constructions. 32Inspired by the space-conned effect within MOFs, 26,[28][29][30][31] herein, we develop an efficient strategy to synthesize ultrane MoC nanocrystals embedded into three-dimensional (3D) nitrogen-doped carbon (NC/MoC), through functionalization of MOFs with Na 2 MoO 4 (denoted as MOF/MoO 4 ) and a subsequent carbonization process. 26The detailed synthesis route of NC/MoC is schematically illustrated in Fig. 1a.First, ZIF-8 rhombic dodecahedra (RDs) were synthesized as the precursors, which were subsequently functionalized with molybdate. 33,34Aer the thermal pyrolysis of MOF/MoO 4 , the NC/MoC containing highly dispersed MoC nanocrystals conned into the N-doped porous carbon matrix was obtained.Leveraging the structural and compositional advantages, the resulting NC/MoC demonstrates promising CDI performance with large SACs (84.2 mg g −1 at 1.2 V; 123.4 mg g −1 at 1.6 V), rapid desalination rates, low specic energy consumption (0.43 W h g −1 ), and excellent longterm cycling stability (91.4% SAC retention aer 200 cycles).Furthermore, the possible mechanisms were also systematically elaborated by the ex situ characterization and density functional theory (DFT) calculations.

Results and discussion
The morphological evolution at each step was characterized by eld-emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM).As illustrated in Fig. 1b, the initially prepared ZIF-8 RDs (average diameter, ∼500 nm) possess a well-dened rhombic dodecahedral morphology with smooth surfaces.Subsequently, a series of MOF/MoO 4 -x (where x represents the mass ratio of Na 2 MoO 4 to ZIF-8, x = 0.25, 0.5, and 1) were synthesized through functionalizing MOFs with different ratios of MoO 4 2− .The amount of MoO 4 2− was adjusted by varying the concentration of Na 2 MoO 4 while maintaining the same quantity of ZIF-8 RDs.SEM images in Fig. 1c and S1a, b † reveal that the morphologies of MOF/MoO 4 -x are similar to the original rhombic dodecahedral shape of the initial ZIF-8 RDs (Fig. 1b).However, the nanocrystal sizes of MOF/MoO 4 -x are slightly reduced, and their rhombic edges as well as corners also become less distinct, which is consistent with previous publications. 26,35The as-prepared series of MOF/ MoO 4 -x were then pyrolyzed at 800 °C under a N 2 atmosphere; during this process, the organic ligands were converted into NC, which could further react with the adjacent Mo atoms to generate Mo y C nanocrystals (where y is 1 or 2), 26 leading to the formation of NC/Mo y C heterostructures.
In contrast to the well-preserved original dodecahedral morphology of the initial ZIF-8 derived NC (Fig. 1d), the MOF/ MoO 4 -x derived NC/Mo y C-x exhibit shrunk architectures with wrinkled, bumpy surfaces, and their average sizes become smaller with increasing MoO 4 2− ratios (Fig. 1e, f and S1c, d †).
High-resolution TEM (HRTEM) images in Fig. 1g and S2a † exhibit the emergence of the single-phase MoC nanocrystals in the NC/MoC-0.25 and NC/MoC-0.5,where MoC possesses a lattice fringe spacing of ∼0.25 nm, corresponding to the (100) plane. 26However, the HRTEM image in Fig. S2b † shows that the derived NC/MoC/Mo 2 C-1 possesses two lattice fringes with inter-planar spacings of 0.25 and 0.22 nm, corresponding to the (100) plane of MoC and (101) plane of Mo 2 C, respectively.Additionally, the HRTEM images in Fig. 1g and S2a † also show the presence of ultrane MoC nanocrystals ranging from 5-10 nm in size, possibly attributed to the space-conned effect within the MOF-derived NC matrix.The high-angle annular dark-eld scanning TEM (HAADF-STEM) and corresponding element mapping images in Fig. 1h reveal a homogeneous distribution of C, N, and Mo elements in NC/MoC-0.5.
To conrm the presence of MoO 4 2− units within the frameworks of ZIF-8 RDs, Fourier transform infrared spectroscopy (FTIR) spectra of MOF/MoO 4 -x were measured and compared with those of ZIF-8 RDs.As depicted in Fig. 2a, the FTIR spectra of the three MOF/MoO 4 -x maintain the main characteristic peaks of ZIF-8, but new characteristic peaks at approximately 842 cm −1 are observed in their FTIR spectra, assigned to the vibrations of Mo-O-Mo bonds. 36The intensities of these peaks gradually increase with higher proportions of MoO .Aer pyrolysis, the MOF/MoO 4 -x derived NC/Mo y C-x with ultrane carbide nanocrystals conned in N-doped porous carbons was obtained (Fig. 1e, f and S1c, d †). 26The XRD analysis in Fig. 2d reveals that only a broad diffraction peak at around 26°, corresponding to the (002) diffraction of amorphous carbon, is observed for pure ZIF-8 derived carbon (ZIF-8-C).NC/ MoC-0.25 and NC/MoC-0.5 exhibit characteristic diffraction peaks at ∼32°, 36°, 43°, 49°, 63°, and 73°, indexed to the (100), ( 101), ( 103), ( 104), (110), and (114) diffractions of the MoC nanocrystals (JCPDS No. 06-0546), respectively.Interestingly, at a mass ratio of 1, the dual-crystalline phases of both MoC (JCPDS No. 06-0546) and Mo 2 C (JCPDS No. 35-0787) can be simultaneously recognized in the XRD pattern of NC/MoC/ Mo 2 C-1, unlike the single crystal phase of MoC observed for both NC/MoC-0.25 and NC/MoC-0.5 (Fig. 2d).These XRD results, coupled with HRTEM observations, conrm that the single phase of MoC can be obtained at relatively low mass ratios (0.25 and 0.5) of MoO 4 2− to MOF, while the dual-phases of MoC/Mo 2 C are obtained at a higher mass ratio of 1.Such single or dual-phases of carbides prepared through the regulation of the mass ratios have been also observed in other carbides, 38,39 e.g., WC/W 2 C, 26 Fe 2.2 C/Fe 5 C 2 , 38 or Fe 2 C/Fe 5 C 2 /Fe 3 C. 39 Raman spectra in Fig. 2e illustrate that two distinct peaks at approximately 1341 and 1580 cm −1 are observed for the three NC/Mo y C-x and ZIF-8-C, corresponding to the D-band associated with lattice defects, and the G-band related to the stretching vibrations of graphitic carbons, respectively. 40The I D / I G ratio of NC/MoC-x, as the evaluation for the degrees of carbon disorders/defects, are calculated to be 1.49(NC/MoC-0.25),1.43 (NC/MoC-0.5),and 1.37 (NC/MoC/Mo 2 C-1), lower than that of ZIF-8-C (2.13).The I D /I G ratio achieves a decreasing trend along with the increase in Mo y C proportions in NC/Mo y C-x, suggesting a decrease in lattice defects with the improved graphitization degree from NC/MoC-0.25 to NC/MoC/Mo 2 C-1, which might be benecial for accelerating charge transfer and stabilizing the carbide nanocrystals. 26Nitrogen adsorption-desorption isotherms in Fig. 2f further reveal the coexistence of micropores and mesopores in the three NC/Mo y C-x, with the sharp nitrogen gas adsorption at low relative pressure (P/P 0 < 0.1) and the hysteresis loops at higher relative pressures (∼0.4 to 1.0).Pore size distributions in Fig. S3b † also illustrate the hierarchical micro-mesoporous structures in the three NC/ Mo y C-x, which are different from the microporous characteristics of ZIF-8-C.The specic surface areas of NC/MoC-0.25,NC/ MoC-0.5, and NC/MoC/Mo 2 C-1 are 627.3,493.9, and 308.2 m 2 g −1 , respectively.Furthermore, the inductively coupled plasma optical emission spectrometry (ICP-OES) determinations clearly illustrate that the contents of the Mo element exhibits an increasing trend from 38.2 wt% of NC/MoC-0.25 to 67.1 wt% of NC/MoC/Mo 2 C-1, with the improvements of the MoO 4 2− units in ZIF-8 RDs (Fig. S4 †).The surface elemental compositions and valence states of the NC/Mo y C-x heterostructures were investigated using X-ray photoelectron spectroscopy (XPS) analysis.The survey spectra in Fig. 2g 3a), indicating the capacitive behaviors for ion storage. 43he three NC/Mo y C-x electrodes achieve signicantly larger integral areas of CV curves than ZIF-8-C, and in particular, NC/ MoC-0.5 exhibits the largest integral area among these electrodes, which shows its highest specic capacitance.GCD measurements were conducted to explore the charge storage capacity of these electrodes at a current density of 0.2 A g −1 over the potential range of −1.0 to 0 V (Fig. 3b).The NC/Mo y C-x electrodes display approximately symmetrical triangular shapes, with NC/MoC-0.5 also achieving the longest discharge time and therefore the highest specic capacitance 43   straight segments in the low-frequency region.Notably, the three NC/Mo y C-x electrodes possess smaller intersection values with the X-coordinates compared to ZIF-8-C, illustrating their alleviated charge-transfer impedance. 17Additionally, a simulated equivalent circuit (inset of Fig. 3f) suggests that the calculated charge transfer resistance (R ct ) value of NC/MoC-0.5 (0.12 U) is obviously lower than that of ZIF-8-C (1.01 U), indicating the enhanced charge transfer kinetics of NC/MoC-0.5 during Na + reversible desalination/regeneration.
To gain further insight into the electrochemical kinetics of NC/Mo y C-x, their surface-controlled (e.g., capacitive contribution) and diffusion-controlled processes (i.e., redox contribution) were calculated according to eqn (2) and (3) (S1.6 †). 40,44,45s illustrated in Fig. 3g, the tted curves between the logarithm of current densities (log I) and the logarithm of scan rates (log v) are straight lines for both the discharging and charging steps.Their corresponding b values range from 0.89 to 0.95, suggesting that the capacitive contributions of NC/Mo y C-x are mainly governed by the surface-controlled process rather than the diffusion-controlled process. 18The detailed contributions of surface and diffusion behaviors of NC/MoC-0.5 were calculated, and Fig. 3h manifests that the surface-contributions are gradually increased with the enhancements of the scan rates from 0.5 to 100 mV s −1 .At a scan rate of 50 mV s −1 , the contributions of surface-controlled and diffusion-controlled processes are determined to be 89.8% and 10.2%, respectively (Fig. 3i).These electrochemical measurements and analyses demonstrate that NC/MoC-0.5 exhibits a rapid and reversible ion storage process with capacitive characteristics, highlighting its signicant potential for CDI application.
The exceptional electrochemical activities of the NC/Mo y C-x electrodes are used to investigate their CDI applications.CDI experiments were carried out in a symmetric CDI cell 18 consisting of the NC/Mo y C-x electrodes as both the cathode and anode.For comparison, a bulk MoC and ZIF-8-C based CDI cells were also assembled.Desalination experiments were conducted in a 500 mg L −1 NaCl solution at an applied voltage of 1.2 V.The dynamic curves of the calculated SAC values (eqn (5), S1.7 †) versus deionization time in Fig. 4a reveal that the SAC values of these electrodes increase quickly in the initial period, indicating the rapid capture of Na + and Cl − .As deionization time progresses, the SAC values gradually increase and reach equilibrium.It is worth noting that NC/MoC-0.5 achieves an ultrahigh SAC value of 82.4 mg g −1 , markedly exceeding those of ZIF-8-C (26.7 mg g −1 ), bulk MoC (45.8 mg g −1 ), NC/MoC-0.25 (56.3 mg g −1 ) and NC/MoC/Mo 2 C-1 (67.8 mg g −1 ).The CDI Ragone plots were used to assess the deionization performance of NC/Mo y C-x, bulk MoC and ZIF-8-C, including the SAC and salt adsorption rate (SAR, eqn (6), S1.7 †).As illustrated in Fig. 4b, the NC/MoC-0.5electrode occupies the more right and upper region, indicating its larger SAC and faster SAR among these electrodes.Furthermore, the effects of the initial NaCl concentrations and working voltages on CDI performance were further veried.Fig. 4c shows that the SAC values of NC/Mo y C-x, bulk MoC and ZIF-8-C show a gradual improvement with increasing NaCl concentrations.More importantly, NC/MoC-0.5 acquires superior SAC values compared to ZIF-8-C, bulk MoC, NC/MoC-0.25 and NC/MoC/Mo 2 C-1 across all concentration ranges from 100 to 1000 mg L −1 , reaching a large SAC value of 93.8 mg g −1 at a concentration of 1000 mg L −1 .With the extension of working voltages, both the SAC and SAR values of NC/Mo y C-x, and ZIF-8-C manifest pronounced improvements with increasing voltages from 0.8 to 1.6 V (Fig. 4d and S8, S9 †), and the CDI Ragone plots shi to the upper-right domain at higher voltages, attributed to the reinforced electrosorption of ions (Na + and Cl − ) onto the electrodes driven by accelerated electrostatic force. 17he real-time current responses of the NC/Mo y C-x electrodes were also simultaneously monitored during the CDI process (Fig. 4e).These current changes originate from the cycling desalination/regeneration of Na + and Cl − by the NC/Mo y C-x electrodes at the applied voltage 46,47 (inset of Fig. 4e).The charging efficiency (L) values are calculated to be 24.5%,65.9%, and 33.6% (eqn (7), S1.7 †) for NC/MoC-0.25,NC/MoC-0.5, and NC/MoC/Mo 2 C-1, respectively (Fig. 4f).The higher charge efficiency of NC/MoC-0.5 indicates its lower energy consumption during the CDI desalination process. 46,47And the energy consumption of NC/MoC-0.5 was determined to be 0.43 W h g −1 (eqn (8), S1.7 †), 17 signicantly lower than that of NC/MoC-0.25 (1.13 W h g −1 ) and NC/MoC/Mo 2 C-1 (1.08 W h g −1 ).Additionally, the Langmuir isotherm model (eqn (9), S1.7 †) has been adopted to simulate the changes in experimental SACs for NC/ MoC-0.5 as a function of the initial NaCl concentrations ranging from 100 to 1000 mg L −1 .As illustrated in Fig. 4g, the correlation coefficient r 2 is calculated to be 0.996, revealing that the Langmuir isotherm matches well with the experimental SACs.The maximum theoretical SAC (q m ) of NC/MoC-0.5 predicted from the Langmuir isotherm is 104.9 mg g −1 .
In view of the aforementioned experimental results and discussions, the newly synthesized metal carbide, NC/MoC-0.5,exhibits several superior characteristics such as a high SAC and rapid salt adsorption rate, which evidently exceeded those of Mo-based composites like transition metal carbides/ dichalcogenides, or MOF-derived carbons (Fig. 4h and Table S1 †).Furthermore, the cycling stability, also termed as longterm desalination/regeneration performance, was also experimentally measured using an initial NaCl concentration of 500 mg L −1 at 1.2 V. Fig. 4i shows that the bulk MoC exhibits unsatisfactory SAC degradation and an increase in energy consumption only aer 50 cycles.In contrast, the NC/MoC-0.5electrode achieves a high SAC retention rate of ∼91.4% aer 200 cycles, without pronounced enhancements in energy consumption throughout the long-term CDI cycles.Additionally, the SEM, TEM, HRTRM images, and XRD patterns in Fig. S10 † aer 200 CDI cycles demonstrate the well-maintained morphology and crystal structure of NC/MoC-0.5,further illustrating its outstanding structural stability during the consecutive CDI deionization/regeneration process, which agrees well with the above CDI cycling results (Fig. 4i).The good cycling stability of NC/MoC-0.5 might be attributed to the evenly distributed MoC nanocrystals conned in the NC matrix, and the space-conned effect might efficiently avoid the possible aggregations during the long-term CDI process.
To further understand the possible desalination mechanism, ex situ XRD characterization studies [48][49][50] were performed for the NC/MoC electrode at various applied voltages, corresponding to the desalination/regeneration process of the CDI measurements.As shown in Fig. 5a, some typical diffraction peaks of the (100), (101), and (104) planes from the NC/MoC-0.5shi to lower 2q angles during the desalination process (step I to III), and subsequently return back to higher original 2q angles aer the regeneration of the NC/MoC-0.5electrode (step III to V).Such behaviors might originate from the reversible insertion/extraction of Na ions 46,51 into the frameworks of MoC crystals, 52 thereby bringing out an increase or a decrease in the crystal lattice parameters.Furthermore, DFT calculations were conducted to understand the high CDI performance of NC/MoC (S2 †), with the structural models of MoC, NC, and NC/MoC depicted in Fig. S11.† The calculated differential charge density of NC/MoC in Fig. 5b shows that the charge accumulates near the surface of MoC and depletes near the NC surface, revealing the transfer of electrons from NC to the neighboring MoC, and therefore generating interfacial electronic coupling 53,54 between the NC and MoC interfaces.The charge accumulation at the heterointerface is supposed to be benecial to facilitate electron transport during the desalination/ regeneration process. 53,54The density of states (DOS) in Fig. 5c also illustrates an obvious enhancement in charge density at the Fermi level for NC/MoC compared with pure MoC, which

Conclusion
In summary, we have successfully synthesized MoC nanocrystals embedded into MOF-derived NC via functionalization of MOFs with molybdates and a subsequent thermal carbonization strategy.Due to the unique architecture of NC/MoC, the uniformly distributed MoC nanocrystals were steadily conned within the NC matrix, therefore achieving a large salt adsorption capacity (84.2 mg g −1 , 1.2 V; 123.4 mg g −1 , 1.6 V), fast desalination rate, and good cycling stability over 200 cycles.DFT calculations and ex situ XRD characterization further elucidated that the MoC nanocrystals conned in the NC matrix could facilitate electron transport during the desalination/ regeneration process, thereby enhancing the CDI performance compared with pure MoC.These experimental and theoretical insights provide valuable guidance and inspiration for the design and fabrication of carbide-based nanocrystals, opening new avenues for CDI applications, and potentially extending to other applications such as electrochemical adsorption and energy storage conversion.
the ZIF-8 RDs.26 X-ray diffraction (XRD) patterns in Fig.2bindicate that only the ZIF-8 crystalline phase is observed in all three MOF/MoO 4 -x, and the addition of MoO 4 2− units does not signicantly affect the original crystallinity of ZIF-8.37Moreover, nitrogen adsorption/desorption isotherms in Fig.2cshow that the three MOF/MoO 4 -x present essentially identical microporous characteristics to ZIF-8 RDs, characterized by steep N 2 gas uptakes at low relative pressures (P/P 0 < 0.1).The similar pore size distributions of MOF/MoO 4 -x and ZIF-8 RDs in Fig.S3a† further indicate that the pore structures of ZIF-8 RDs are almost not expanded or blocked aer the functionalization by MoO 4 2− photoelectron spectroscopy (XPS) analysis.The survey spectra in Fig.2gevidence the co-existence of C, N, and O elements, with the absence of Mo in ZIF-8-C.Differently, the Mo 3d peak appears in the survey XPS spectra of NC/MoC-0.25,NC/MoC-0.5, and NC/ MoC/Mo 2 C-1, and its content gradually increases along with the increase in Mo y C ratios (Fig.2g).The high-resolution XPS spectra of the Mo 3d regions (Fig.2h) reveal two main characteristic pairs of peaks for both NC/MoC-0.25 and NC/MoC-0.5,where a pair of peaks at lower binding energies (228.9 eV for Mo 3d 5/2 and 232.3 eV for Mo 3d 3/2 ) are indexed to Mo(IV) (Mo-Mo or Mo-C bonds), while a pair of peaks at higher binding energies (233.5 eV for Mo 3d 5/2 and 235.7 eV for Mo 3d 3/2 ) are assigned to Mo(VI) (Mo-O bond) owing to the possible surface oxidation of NC/ Mo y C-x.26,41,42With regards to NC/MoC/Mo 2 C-1, another pair of peaks at binding energies of 228.8 eV (Mo 3d 5/2 ) and 231.6 eV (Mo 3d 3/2 ) are also obviously observed, originating from Mo(II) of Mo 2 C.42 The high-resolution N 1s spectra of ZIF-8-C and NC/ Mo y C-x (Fig.2i) can be deconvoluted into three peaks at 398.3, 399.4,and 400.6 eV, corresponding to pyridinic-N, pyrrolic-N and graphitic-N, respectively.The additional Mo 2p characteristic peaks can also be observed in the XPS spectra of NC/MoC-0.25,NC/MoC-0.5, and NC/MoC/Mo 2 C-1.The electrochemical performance of NC/MoC-0.25,NC/MoC-0.5,NC/MoC/Mo 2 C-1, and ZIF-8-C electrodes was systematically evaluated by cyclic voltammetry (CV) and galvanostatic charge/ discharge (GCD) in 1.0 M NaCl solution.All CV curves of NC/ Mo y C-x and ZIF-8-C exhibit nearly symmetrical rectangular shapes without any additional redox peaks at 100 mV s −1 (Fig.3a), indicating the capacitive behaviors for ion storage.43The three NC/Mo y C-x electrodes achieve signicantly larger
(202.4 F g −1 ) compared to the other electrodes.The detailed specic capacitances of these electrodes at different current densities are further illustrated in Fig. 3c, which suggests the highest specic capacitance of NC/MoC-0.5 across all ranges of current densities.Furthermore, Fig. 3d reveals the corresponding CV proles of the NC/MoC-0.5electrodes recorded at scan rates ranging from 0.5 to 100 mV s −1 .The CV integral area of NC/ MoC-0.5 gradually increases with higher scan rates, indicating the boosted capacitive performance of NC/MoC-0.5.The GCD curves of NC/MoC-0.5 in Fig. 3e maintain relatively symmetrical triangular shapes with the reduction of current densities ranging from 4 to 0.2 A g −1 , which indicates the rapid and reversible ion/charge storage processes even at low current densities.Similar tendencies are observed in the CV and GCD curves of ZIF-8-C, NC/MoC-0.25,and NC/MoC/Mo 2 C-1 (Fig. S5-S7 †).The Nyquist plots of NC/Mo y C-x and ZIF-8-C in Fig. 3f exhibit quasi-semicircles in the high-frequency region and

Fig. 3
Fig. 3 (a) CV curves at 100 mV s −1 , (b) GCD curves at 0.2 A g −1 , and (c) the specific capacitance values at different current densities for NC/MoC-0.25,NC/MoC-0.5,NC/MoC/Mo 2 C-1, and ZIF-8-C.(d) CV curves of NC/MoC-0.5 at the scan rates from 0.5 to 100 mV s −1 .(e) GCD curves of NC/MoC-0.5 at current densities from 0.2 to 4 A g −1 .(f) Nyquist plots of the three NC/Mo y C-x and ZIF-8-C.Inset: the equivalent circuit diagram of NC/MoC-0.5.(g) The fitted curves between current densities and the scan rates in charge and discharge processes for NC/MoC-0.25,NC/ MoC-0.5 and NC/MoC/Mo 2 C-1.(h) Normalized proportions of surface-and diffusion-controlled contributions at different scan rates for NC/ MoC-0.5.(i) Decoupling of surface-and diffusion-controlled contributions for NC/MoC-0.5 at a scan rate of 50 mV s −1 .

Fig. 4
Fig. 4 (a) Dynamic SAC versus deionization time plots, and (b) corresponding CDI Ragone plots of the three NC/Mo y C-x, bulk MoC, and ZIF-8-C in 500 mg L −1 NaCl solution at 1.2 V. (c) SAC values at different NaCl concentrations from 100 to 1000 mg L −1 for the three NC/Mo y C-x, bulk MoC, and ZIF-8-C (applied voltage: 1.2 V).(d) Dynamic SAC versus deionization time plots of NC/MoC-0.5 with an initial concentration of 500 mg L −1 using different voltages from 0.8 to 1.6 V. (e) Current response curves of the three NC/Mo y C-x, and the corresponding current variation of NC/MoC-0.5 during the desalination/regeneration cycle (inset).(f) The calculated charge efficiencies of the three NC/Mo y C-x.(g) The fitted isotherm adsorption curves of the Langmuir model (applied voltage: 1.2 V; NaCl concentration: from 100 to 1000 mg L −1 ).(h) Comparison of CDI performance between NC/MoC-0.5 and some reported transition metal carbides/dichalcogenides or MOF-derived carbons.(i) The recycling performance of bulk MoC and NC/MoC-0.5,along with their corresponding energy consumption changes over 200 cycles (applied voltage: 1.2 V; NaCl concentration: 500 mg L −1 ).