Upcycling of BPA-PC into trimethylene carbonate by solvent assisted organocatalysed depolymerisation †

In this study, a solvent assisted organocatalysed method for the depolymerisation of bisphenol A-based polycarbonate (BPA-PC) at low temperature is described. It is shown that the selection of a suitable organic catalyst combined with mild conditions allows for the selective formation of trimethylene carbonate (TMC) in high yields (up to 80%) from the depolymerisation of BPA-PC. The key role of 1-methylimidazole as solvent and imidazole as catalyst is demonstrated and the depolymerisation mechanism is elucidated by 1 H NMR spectroscopy. It is also demonstrated that this methodology could be extended to other nucleophiles, leading to the synthesis of di ﬀ erent cyclic carbonyl-containing intermediates. Such selective depolymerisation processes under mild conditions represent a unique and interesting approach for valorising plastic waste into complex molecules that are otherwise di ﬃ cult to synthesise.


Introduction
][7][8] Unfortunately, the routine synthesis of cyclic carbonates involves the use of highly toxic reagents, such as phosgene surrogates, chlorinated chemicals, or carbon monoxide. 9,10While intensive research has been directed to the coupling reaction of CO 2 with diols or oxetanes to form the corresponding cyclic carbonate, this reaction requires not only high-performance catalysts but also high temperatures and/or pressures.][13] Recently, the depolymerisation of bisphenol A-based polycarbonate (BPA-PC), a commodity thermoplastic which is the material of choice for a wide range of applications, 14,15 has been investigated to recover not only the initial monomerbisphenol A (BPA)but also cyclic carbonates.Through the chemical scission of the carbonate linkage, the depolymerisation of BPA-PC represents an alternative source of carbonyl groups to obtain high added-value molecules.In the open literature, articles have reported the deconstruction of BPA-PC into BPA and 5-or 6-member cyclic carbonates with both metallic 16,17 and organic 18,19 catalysts.However, none of these approaches allowed the production of the simplest but one of the most important cyclic carbonates, trimethylene carbonate (TMC).
4][25] More recently, it has been also investigated as a polymer electrolyte in batteries, demonstrating an excellent stability window and good conductivity values. 26,27owever, because of the high reactivity of TMC, care must be taken during its preparation to avoid uncontrolled polymerisation into PTMC.Reports have demonstrated that an optimised catalytic system as well as low temperatures are essential for obtaining high yields of TMC. 13 Consequently, the usual harsh conditions required for chemical recycling (high temperatures, pressures, and the use of non-specific catalysts) impede the recovery of the monomer.From this perspective, a selective system able to depolymerise BPA-PC into BPA and TMC while avoiding the side ROP into PTMC is both challenging and of great interest.
Our group has explored the potential of a thermally stable organic catalyst, formed out of an organic base, 1,5,7-triazabi-cyclo [4.4.0]dec-5-ene (TBD) and an organic acid, methanesulfonic acid (MSA), namely TBD:MSA, to obtain a wide range of cyclic, carbonyl-containing molecules in high yields. 29,30nfortunately, while employing 1,3-propanediol as nucleophile in bulk at 130 °C, only the corresponding linear carbonate could be synthesised.A previous study based on the use of CO 2 as a carbonyl source has demonstrated that cyclisation into TMC was only favoured over the linear PTMC formation (obtaining TMC in yields up to 94%) under mild temperature conditions (i.e.< 60 °C). 28Thus, we hypothesised that the depolymerisation of BPA-PC should similarly be carried out at the lowest possible temperature to obtain reasonable yields of TMC.
Herein, TMC is synthesised from the depolymerisation of BPA-PC using a solvent-assisted procedure.While in the bulk depolymerisation of BPA-PC, high temperatures (100-160 °C) were necessary to complete the reaction, 29 it is demonstrated in this study that the use of an appropriate solvent leads to higher polymer solubilisation, allowing for solvent-assisted depolymerisation of BPA-PC at low temperatures (50 °C) (Fig. 1).Combined with an optimised organocatalytic system, this method renders possible the upcycling of BPA-PC waste into highly valuable TMC.

Screening of solvents and catalysts for the depolymerisation of BPA-PC under mild conditions
With the objective of obtaining trimethylene carbonate (TMC) in high yields, the depolymerisation of Bisphenol A-based polycarbonate (BPA-PC) was performed with 1,3-propanediol as nucleophile at a temperature unfavourable for the ringopening polymerisation (ROP) of the molecule into poly(trimethylene carbonate) (PTMC), i.e.50 °C, for 3 h (Scheme 1).The effect of the solvent and catalyst were first investigated to assess the optimum reaction conditions.The depolymerisation ratio, corresponding to Bisphenol A (BPA) yield, and the TMC and PTMC yields were determined through 1 H NMR spectroscopy (DMSO-d 6 , 400 MHz, 298 K) (Table 1).
The selection of solvents was performed based on the affinity of BPA-PC using the Hansen Solubility Parameters (HSP). 31This approach assumes that the interaction of the polymer with a given solvent is described by the sum of three partial solubility parameters corresponding to the nonpolar (dispersion), polar (dipole-dipole), and hydrogen bonding interactions.With the HSP values, the Relative Energy Difference (RED) parameter was calculated (Tables S1 & S2 †).The RED value indicates how strong the interaction between the solvent and the polymer is.Good solvents for a given polymer have a RED value inferior to 1, while values superior to 1 indicate low affinity.From this initial screening, tetrahydrofuran (THF), chloroform, 2-methyltetrahydrofuran (methyl-THF), toluene and 1-methylimidazole were selected to evaluate their impact on the depolymerisation of BPA-PC mediated with different organic bases as catalyst.
The different results obtained demonstrate that the reaction is highly solvent-dependent.At 50 °C, the reaction in bulk -1,3-propanediol used as solventdid not lead to any depolymerisation, which is consistent with the very poor solubility of BPA-PC in 1,3-propanediol -RED value of 2.329 -(Table 1 entry 1).On the contrary, all reactions in solvent led to the solvolysis of the polymer, although in very different proportions.Methyl-THF and toluene, for which the RED values are superior to 1, showed low reactivity, with 30 and 43% of depolymerisation after 3 h, respectively (Table 1 entries 5 & 6).THF, which has a RED value close to 1, provided better performance reaching 64% of depolymerisation.The best result was obtained with 1-methylimidazole which led to the complete depolymerisation of BPA-PC after 3 h (Table 1 entries 2 & 3).1-Methylimidazole is the only solvent analysed which has a RED value lower than 1, which confirms its higher solubility compared to common solvents and leads to a system in which the solvent dissolves the surface of the material, thus reducing the mass transfer limitations of heterogeneous systems. 32onetheless, one anomaly can be noted; even though chloroform has a RED value of 1.295, it performed rather well, with 83% of depolymerisation after 3 h (Table 1 entry 4).The extent of the undesired ring opening of TMC was also very different depending on the solvent.While methyl-THF and 1-methylimidazole promoted the formation of TMC over PTMC, the use of toluene favoured the polymerisation into PTMC.Finally, the basicity of 1-methylimidazole may play an additional role in the depolymerisation of BPA-PC as it potentially activates the nucleophilic attack of 1,3-propanediol.In the corresponding 1 H NMR spectra, the characteristic signals of 1,3-propanediol methylene groups' show a slight shift to higher positionsi.e. from δ = 1.56 to 1.61 ppm and from δ = 3.44 to 3.51 ppmwhile the signal corresponding to the intensity of the proton of the hydroxyl group is clearly reduced in comparison with the lone compound and the multiplicity of the adjacent methylene group changed from a quadruplet to a triplet (Fig. S3 †).These observations suggest the formation of hydrogen bonds between the diol and the moderately basic 1-methylimidazole, thus creating a partial negative charge on the oxygen of 1,3-propanediol which could enhance its reactivity and contribute to the efficiency of this system.
After demonstrating the importance of 1-methylimidazole as a solvent to favour the depolymerisation of BPA-PC, the impact of the catalyst on both the depolymerisation ratio and the TMC/PTMC ratio was investigated.Imidazole and derivatives, including benzimidazole, 1,2,4-triazole and benzotriazole, were explored for the reaction.4][35] 1,5,7-triazabicyclo[4.4.0]dec-5-ene (TBD), which is a strong base which has already shown excellent performance for the depolymerisation of BPA-PC, 19 was investigated for comparison (Table 1, entries 7-10).The reaction catalysed by imidazole was the most efficient compared to the depolymerisation mediated by imidazole derivatives.Benzimidazole and 1,2,4-triazole showed good to very good Scheme 1 Depolymerisation of BPA-PC with different solvents (10 eq.) and catalysts (1 eq.) for 3 h at 50 °C.
As expected, the depolymerisation mediated by TBD was much faster, full depolymerisation was attained after only 1 h, but meanwhile the TMC content only reached 26% while PTMC was the major product obtained (72%).This result suggests that strong bases usually employed for such reactions are unselective and promote both the depolymerisation of BPA-PC and the polymerisation of TMC into PTMC.
Optimisation of the reaction conditions with 1-methylimidazole as solvent and imidazole as catalyst After demonstrating the importance of 1-methylimidazole as solvent and imidazole as catalyst in the depolymerisation process, the effect of temperature, nucleophile load, solvent-topolymer ratio as well as the effect of the catalyst concentration were investigated.To evaluate the effect of the temperature on the depolymerisation, the reaction was performed at 40, 50, 60 and 90 °C.The results demonstrate that with increasing temperature, both the depolymerisation ratio and the content of PTMC increases.At 40°C, the depolymerisation ratio only reached 71% while reactions at 50, 60 and 90 °C led to full conversion after 3 h (Fig. 2a).Continuing the reaction towards 24 h did not further improve the depolymerisation degree of the reactioni.e.73%while PTMC ratio increased up to 9%.As temperature increased, the formation of PTMC also increased; at 50 °C only 18% of PTMC were produced while this value raised up to 84% at 90 °C.These results are in good agreement with previous studies reporting the detrimental effect of temperature (over 55 °C) on the synthesis of TMC from the organocatalysed coupling of oxetane and CO 2 . 28onsidering that increased temperatures promote the ROP of TMC, a minimum temperature is required.For completing the reaction in a reasonable amount of timeless than 3 hthe best balance between the final yield and the TMC/PTMC ratio was obtained for the reaction at 50 °C.The impact of the quantity of 1,3-propanediol on the formation of TMC and PTMC during the depolymerisation of BPA-PC was also evaluated.The quantity of nucleophile in excess (1.05, 1.25, 1.5 and 1.75 eq.) did not demonstrate any significant impact on the depolymerisation rate, after h, all reactions reached full conversion (Fig. However, an excess of nucleophile seemed to slightly promote the formation of PTMC.Thus, the TMC/PTMC was 81:18 with 1.05 eq. of 1,3propanediol vs. 72:32 with 1.75 eq.The 1,3-propanediol may act as an initiator for the polymerisation of TMC, which would explain why an excess of diol leads to higher PTMC content. Different quantities of solvent were also investigatedi.e.2.5., 5, 10 and 20 eq. of 1-methylimidazole compared to BPA-PC monomeric unitto evaluate the effect of the dilution on the depolymerisation (Fig. 2c).The results showed that although a minimum of 1-methylimidazole is needed to promote efficient depolymerisation, increasing the solvent content above 10 eq.does not improve the depolymerisation degree.However, the side polymerisation of TMC seemed disfavoured while 20 eq. of solvent were employed with only 3% of PTMC formed.Higher concentration favours the ROP of TMC, but higher dilution slows down the depolymerisation reaction.A compromise between these two effects can be found with 10 eq. of solvent for which complete depolymerisation is observed while only 18% of PTMC are obtained.
To gain an insight into the efficiency of the process mediated by imidazole, the effect of the catalyst loading was evaluated, with 0.5, 1 or 2 eq. of imidazole usedcompared to the BPA-PC monomeric unit.The depolymerisation yield was only 83% with 0.5 eq. of imidazole while the reactions operating with 1 or 2 eq.reached completion after 3 h (Fig. 2d).These results suggest that stoichiometric amounts of imid-azole are required to complete the depolymerisation which raises questions on the mechanism.

Mechanism of depolymerisation in the presence of azole catalysts
Mechanisms for imidazole-catalysed reactions have traditionally been described through basic interactions between the nucleophile and the lone pair orbitals of the nitrogen atom with weak activation of the carbonyl group by hydrogen bonding of the amine of imidazole. 36However, this type of mechanism usually exhibits a maximum reaction ratio with 0.1 to 0.2 eq. of catalyst and further increases usually don't lead to improvements in the reaction kinetics or yields.In contrast, with the present system, the maximum catalytic activity occurs at 1 eq.This behaviour suggests that a different mechanism is being followed.To gain an insight into the mechanism, the kinetics of the depolymerisation catalysed by benzimidazole were monitored by 1 H NMR spectroscopy in DMSO-d 6 .
Benzimidazole was selected over imidazole because it leads to a more stabilised carboxylate intermediate which facilitates the identification of the characteristic signals of the different steps of the reaction in the 1 H NMR spectra.
The 1 H NMR spectrum for the reaction at t 0 only presents the characteristic signals of the benzimidazole (the catalyst) and 1-methylimidazole (the solvent).BPA-PC is insoluble in the solvent which means that no signals of the polymer can be observed in the spectra.Over time a decrease of the benzimidazole signal intensity can be noted while new signals of low intensity arise in the aromatic region (δ = 8.91, 8.05 and 7.84 ppm) that be attributed to the products.at t f , these signals completely disappeared and the intensity of the characteristic signals of benzimidazole were restored while the signal intensity for the characteristic moieties of TMC and BPA reached a maximum (Fig. S8 †).This result suggests the formation of stable intermediates between the catalyst and BPA-PC (Scheme 2).A proposed mechanism consistent with these observations can be described as follows; first performs a nucleophilic attack on the carbonyl BPA-PC to form an unstable benzimidazole carboxylate chain-end (intermediate 1).The nucleophilic attack of 1,3propanediol is then favoured by the highly activated carbonyl which leads to the formation of intermediate 2. The catalyst then attacks intermediate 2 to form a carboxylate intermediate composed of 1,3-propanediol and benzimidazole (intermediate 3).The cyclisation of intermediate 3 leads to the formation of TMC while releasing the molecule of benzimidazole.
To examine this hypothesis, the depolymerisation was divided into two model reactions.In the first stage, BPA-PC was mixed with benzimidazole in the absence of 1,3-propanediol under the same conditions as previously described with the objective of characterising the covalent intermediate formed (Intermediate 1) (Fig. 3A).In the second stage, after complete depolymerisation of BPA-PC, 1,3-propanediol was added to the crude reaction to observe the disappearance of the intermediate and the formation of TMC and BPA (Fig. 3B).Reactions were monitored by quantitative 1 H NMR spectroscopy and COSY spectra were recorded to complete the characterisation of the intermediates (Fig. S24  However, the presence of intermediate 2 can be reasonably asserted considering previous works which have demonstrated that for such structures, imidazoleor in this case benzimidazolewould be a far better leaving group than a phenol. 37fter 30 min of reaction, the concentration of benzimidazole catalyst was completely restored while BPA and TMC were present in similar yields compared to the depolymerisation performed in one step under the same conditions, i.e. 96% and 79% respectively, which confirms the proposed mechanism.

Purification and isolation of TMC
After optimizing the depolymerisation process to obtain the highest depolymerisation ratios and the highest TMC/PTMC ratios, different approaches for the purification and isolation of TMC were investigated.Precipitation in solvent as well as liquid-liquid extraction were both unsuccessful because of the immiscibility of 1-methylimidazole in organic solvents.Following previous work of Hedrick and co-workers, an ionic  exchange column was investigated as a separation method by employing acidic resin -Amberlyst 37 First, the crude product of the depolymerisation reaction containing BPA, TMC, the catalyst and the solvent was dissolved in an excess of dichloromethane before addition to the separation column which retains imidazole and 1-methylimidazole by forming a salt with the attached sulphuric acid of the column.This salt formation being exothermic, to avoid the ring opening of TMC, the column was refrigerated with cold water to preserve a temperature below 45 °C.After concentrating, the solution was precipitated in diisopropyl ether obtaining only moderate yields, up to 30% of TMC.
Evaluating the potential of the optimised reaction for the preparation of other cyclic carbonates At this point it has been proven that the depolymerisation of BPA-PC through the presented pathway leads to TMC.To demonstrate the versatility of this methodology, other nucleophiles were investigated to obtain different carbonyl-containing cycles using the previously optimised depolymerisation conditions (Scheme 3).More precisely, carbonates, thiocarbonates and ureas were prepared using diols, dithiols, and diamines as nucleophiles, respectively.For diols such as 2,2dimethyl-1,3-propanediol, butane-1,3-diol, and trimethylolpropane allyl ether, (Table 2 entries 1 to 3), the corresponding 6-member cyclic carbonates were obtained in high yields ->80%after 3 h of reaction.The reaction with 1,2ethanedithiol and 1,2-ethanediamine also gave high yields with 98% and 81% of cyclic compounds, respectively, obtained after only 30 min (

Conclusion
In this work, a novel procedure for performing the depolymerisation of BPA-PC at low temperature was described.It was demonstrated that the success of this approach lies in the use of a solvent that favours the interaction of the catalyst with BPA-PC and a catalytic system that promotes the cyclisation into TMC over the polymerisation into PTMC.It was found that using 1-methylimidazole as solvent and imidazole as catalyst, complete depolymerisation of BPA-PC is attained with a high yield of TMCi.e. 81%at 50 °C in 3 h.To date, sustainable routes for the preparation of TMC are scarce and quite inefficient, mainly because of the high tendency of TMC to ring open.The procedure was extended to other nucleophiles demonstrating the potential of this process to prepare various carbonyl-containing cyclic molecules.Although further work is needed to enhance the isolated yield (currently up to 30%), this study demonstrates the efficiency of solvent-assisted depolymerisation which allows for the preparation of complex molecules from plastic waste through a controlled depolymerisation process under mild conditions.

Fig. 1
Fig.1Previous study on the depolymerisation of BPA-PC in bulk (interfacial catalysis) and the reaction presented in this study in appropriate solvent (volumetric catalysis).

Fig. 2
Fig. 2 Screening of different parameters for the depolymerisation of BPA-PC with 1,3-propanediol as nucleophile, 1-methylimidazole as solvent and imidazole as catalyst, at different (A) temperatures, (B) nucleophile loads, (C) solvent quantity and (D) catalyst load.Yields were determined by 1 H NMR spectroscopy in DMSO-d 6 at ambient temperature (Fig. S12 to S23 †).

Fig. 3
Fig. 3 Model reactions for studying the covalent mechanism of the depolymerisation, (A) reaction between BPA-PC and benzimidazole and (B) reaction between the formed intermediate and 1,3-propanediol.
& S25 †).After 30 min of reaction 1, complete disappearance of BPA-PC was observed, and the characteristic signals of intermediate 1 appeared in the 1 H NMR spectra.While signals at δ = 8.23, 7.61 and 7.20 ppm corresponding to benzimidazole gradually decreased, new signals appeared in the aromatic regions corresponding to the benzimidazole moiety, -δ = 8.91, 8.05 and 7.84 ppm.Furthermore, multiplets characteristic of the bisphenol moiety at δ = 7.08-6.99and 6.75-6.67ppm appeared as well as a signal corresponding to both methyl of the bisphenol synthon at δ = 1.74-1.54ppm.After the addition of 1,3-propanediol to the crude reaction mixturereaction 2the characteristic signals for intermediate 1 gradually decrease, while signals at δ = 8.02, 7.78 and 4.54 ppm corresponding to intermediate 3 (Fig. S24 †) can be identifiedmainly at 20 minbefore their complete disappearance as the characteristic signals of the final products appeared -δ = 4.39 and 2.04 ppm for TMC and δ = 6.98, 6.67 and 1.54 ppm for BPA.Intermediate 2 was not visible in the 1 H NMR spectra, likely because it is rapidly transformed into intermediate 3.

Scheme 3
Scheme 3 Depolymerisation of BPA-PC with different nucleophiles to obtain carbonyl-containing cyclic molecules.

Table 2
entries14 & 5).These examples support the versatility of the depolymerisation process for different types of nucleophile.