Effects of Microporosity and Surface Chemistry on Separation Performances of N-Containing Pitch-Based Activated Carbons for CO2/N2 Binary Mixture

In this study, N-containing pitch-based activated carbons (NPCs) were prepared using petroleum pitch with a low softening point and melamine with a high nitrogen content. The major advantage of the preparation method is that it enables variations in chemical structures and textural properties by steam activation at high temperatures. The adequate micropore structures, appropriate chemical modifications, and high adsorption enthalpies of NPCs are favorable for CO2 adsorption onto carbon surfaces. Furthermore, the structure generates a considerable gas/N-containing carbon interfacial area, and provides selective access to CO2 molecules over N2 molecules by offering an increased number of active sites on the carbon surfaces. The highest CO2/N2 selectivity, i.e., 47.5, and CO2 adsorption capacity for a CO2/N2 (0.15:0.85) binary gas mixture, i.e., 5.30 wt%, were attained at 298 K. The NPCs also gave reversible and durable CO2-capturing performances. All the results suggest that NPCs are promising CO2 sorbents, which can meet the challenges of current CO2 capture and separation techniques.

been studied as potential CO 2 sorbents, because of their extremely high surface areas and typically high CO 2 adsorption capacities. However, potential disadvantages of using zeolites and MOFs as CO 2 sorbents include their limited physicochemical stabilities and sensitivities in the presence of water 22 . Recently, ACs have attracted interest as CO 2 sorbents, because they have high mechanical hardness, thermal stability, and water resistance in conventional CO 2 capture systems [23][24][25][26][27][28] . However, ACs are not ideal sorbents, because they have low CO 2 adsorption capacities and CO 2 /N 2 selectivities.
As in the case of ACs in general, pitch-based ACs with high-density graphitizable structures have diverse applications, including adsorption of gas-and liquid-phase pollutants, catalysts, and gas storage [29][30][31] . They are a complex blend of polyaromatic molecules and heterocyclic compounds, and can generally be obtained as by-products of petroleum industries. The use of pitch therefore has significant potential from the economic perspective.
CO 2 and N 2 are non-polar molecules with similar kinetic diameters, i.e., 3.30 and 3.64 Å, respectively. However, they have different quadrupole moments (2.85:1) and polarizabilities (1.5:1), and this enables the design of CO 2 -philic sorbents 32 . CO 2 has an electron-deficient carbon atom; therefore, it is expected to have favorable interactions with electronegative species, leading to strong acid-base interactions, whereas N 2 is not affected. This simple theory has led to the development of a plethora of nanoporous sorbents that incorporate nitrogen-rich chemical structures such as tetrazoles, triazines, imidazoles, phosphazenes, amines, and imides 33 .
In all these and many other situations, CO 2 -philicity is the main driving force for the selective capture of CO 2 over N 2 , without taking into account any favorable interactions with CO 2 that would selectively repel N 2 molecules. The preparation of pitch-based carbon materials with tailored porous textures and surface chemistry is, from this perspective, essential for achieving optimum CO 2 adsorption. The optimum pore size and a basic N-containing chemical structure are the key factors in obtaining ACs with the highest adsorption capacities and selectivities. N-containing ACs can be synthesized from solid amines with high initial nitrogen contents as the precursor, heat treatment of mixtures of ACs and nitrogen compounds, and chemical modification of carbon structures by nitrogen compounds at high temperatures 34 .
In this work, we developed a useful method for synthesizing N-containing pitch-based ACs (NPCs). It involves mixing pitch with a compound containing a large amount of nitrogen, followed by carbonization and steam activation. This method enables transformation of a mixture of raw pitch and melamine with a high nitrogen content into NPCs. The CO 2 adsorption behaviors based on the chemical transformations and textural properties of the NPCs are discussed.

Results and Discussion
An X-ray photoelectron spectroscopy (XPS) survey scan showed the presence of carbon, nitrogen, and oxygen in the samples, as shown in Figure S1. The slightly reduced intensity of the C1s peak for NPC-800 suggests that the carbon-containing groups, which were initially dominant in the raw pitch, were substituted by nitrogen-containing groups, or decomposed during activation of the pitch and melamine. The NPC-800 structure was further investigated by deconvolution of the C1s, O1s, and N1s peaks. The chemical structures of the raw pitch were altered by mixing with raw melamine and through the subsequent high-temperature activation process. Figure S2 shows that the XPS C1s spectrum of melamine is completely different from those of the other samples. This spectrum has a small peak at 288.7 eV, a sharp peak at 287.4 eV, and a third one, of lower intensity, at 284.4 eV. This distribution agrees with the structure of melamine, in which two types of carbon atoms can be distinguished, the carbon atoms in the -C= N-species [binding energy (BE) around 287 eV] being the most abundant. The peak at 288.7 eV, i.e., with the highest BE among the three peaks, is assigned to the carbon attached to an oxygen atom in C= O. These carbonyl groups are assumed to be formed by surface oxidation, which could occur during the manufacture of pristine melamine 35 . It is evident from the XPS C1s peak of raw pitch that the raw pitch sample contains large quantities of C= C and C-C bonds and trace amounts of oxygen functional groups 36 . A comparison of the spectra of raw pitch and NPC-800 clearly shows that activation at high temperatures results in considerable changes in the C1s spectrum. High-temperature activation results in broadening of the C1s peak, because of the large number and variety of oxygen functional groups formed 37 . Furthermore, the higher-BE peaks mainly arise from species with carbon atoms bound to oxygen or nitrogen atoms. The carbon atoms in C-O or C= N groups have a BE of 286.6 eV, those in C= O or C-N species have a BE of 287.8 eV, and those in carboxyl groups have a BE of 289.2 eV 38 . The formation of various types of nitrogen-carbon structures could play a key role in causing stronger interactions between CO 2 molecules and NPCs than between CO 2 and raw pitch, which has no nitrogen species in its chemical structure. Nitrogen components in a graphitic carbon structure can act as basic sites, therefore access of CO 2 molecules to the carbon surfaces is favored over access of N 2 molecules.
The NPCs were prepared by heat treatment with steam in an air flow at temperatures of 600 °C and above. During this treatment, important chemical changes take place in the pitch, which is transformed into an infusible material. At low temperatures, i.e., around 300 °C, the consumption of aliphatic hydrogen atoms occurs, whereas at higher temperatures, aromatic hydrogens react to form oxygen-containing groups. Oxygen-containing groups that decompose between 300 and 600 °C give rise to new bonds between pitch molecules; when the temperature is higher than 600 °C, typical reactions such as cyclizations and condensation of carbon rings to form graphene-like structures take place 39 .
The XPS O1s core-level spectrum of melamine ( Figure S3) shows a well-defined peak at around 532 eV corresponding to ether bond formation by oxygen atoms, i.e., C-O-C species; this is in agreement with the chemical structure shown in Fig. 1b. A peak appears at 532 eV in the spectrum of raw pitch, which is attributed to oxygen atoms forming C-O single bonds 40 . The NPC-800 sample has a slightly wider O1s peak, indicating the presence of several types of surface oxygen functional groups, with BEs for O1s electrons ranging from 529 to 535 eV 41 .
Scientific RepoRts | 6:23224 | DOI: 10.1038/srep23224 Figure 1 shows the XPS N1s core-level spectra of raw melamine and NPC-800. Fitting of the melamine peak shows three contributions at BEs of 398.7, 399.4, and 400.5 eV. The chemical structure of melamine (Fig. 1b) and XPS studies performed with similar compounds such as polyaniline 42 suggest that the three peaks can be assigned as shown in Fig. 1a. The peak at 398.7 eV can be attributed to neutral imine nitrogen atoms ( 2 N in Fig. 1b), and the peak at 399.4 eV corresponds to neutral amine nitrogen atoms ( 1 N in Fig. 1b). The peak at the highest BE (400.5 eV) can only be assigned to positively charged nitrogen species, as melamine does not contain additional nitrogenated species such as pyrroles or pyridines, which would also produce an XPS signal at this BE 43 . Figure S1 shows that the N1s XPS signal for raw pitch is almost negligible, because of the low nitrogen content. The N1s peak of NPC-800 cannot be interpreted using the same three species as those in melamine. Four peaks, at BEs of 398.1, 400.3, 401.5, and 402.8 eV, fit the N1s curve (Fig. 1c). It should be noted that the peak at the amine BE (i.e., 399.5 eV) does not appear. The peaks at BEs of 398.1 and 400.3 eV correspond to pyridine nitrogen functional groups (which are more stable than imines), and pyrrole or pyridone nitrogen functional groups, respectively. The species with a BE of 402.8 eV can be assigned to oxidized forms of nitrogen (see Fig. 1d), and the band at 401.5 eV corresponds to quaternary nitrogen 44 . The quaternary nitrogen species are located within the graphene layers that develop from condensation reactions that occur during carbonization. Similarly, when pitch is carbonized at a high temperature with melamine, chemical reactions occur between nitrogen species and the pitch molecules, resulting in the formation of cyclic nitrogen-containing structures, such as pyridines or pyrroles; these are the main nitrogen species detected when the material is carbonized, because condensation reactions take place. The chemical compositions of materials formed by activation of petroleum pitch and melamine at various temperatures are shown in Table S1. The data show that the nitrogen content decreased, whereas the carbon content increased, with increasing activation temperature from 600 to 900 °C, indicating selective removal of nitrogen during the thermal treatment. It can therefore be stated that the selective removal of nitrogen is highly dependent on the activation temperature. In addition, the graphene layered structure containing nitrogen atoms at inner positions has the excellent thermal stability of carbonaceous materials 45 . The thermogravimetric analysis (TGA) results in Figure S4 show that the NPCs are highly stable in the temperature range 30-900 °C in a N 2 flow, unlike raw melamine, which undergoes major thermal decomposition at 250-370 °C. NPC-800 maintained 93% of its original weight even after heating to 900 °C. This high value is ascribed to its synthetic process, which involves steam activation at high temperature in an air flow 46 .
The high-resolution scanning electron microscopy (HR-SEM) images in Fig. 2 show an irregular layered structure, which consists of pitch carbon chemically modified with melamine, and rough surfaces generated by steam activation. The high-resolution images show that the NPC samples have interconnected structures formed by chemically modified particles. Vacancies are formed as the activation temperature increases. These can lead to better diffusion of adsorbates and subsequently to favorable interactions with CO 2 .
The Ar adsorption isotherms at 87 K of the synthesized NPCs display typical type-I reversible adsorption profiles, indicating the presence of micropores on the carbon surfaces (Fig. 3a). Ar uptakes at 87 K by the NPC sorbents depend significantly on the sample activation temperature, implying that the textures of the carbon materials can be well controlled by changing the activation temperature. The porosity parameters are summarized in Table 1. The specific surface areas were 187, 384, 624, and 1344 m 2 g −1 for NPC-600, NPC-700, NPC-800, and NPC-900, respectively; these values were calculated using an alternative linear form of the Brunauer-Emmett-Teller (BET) equation (Figures S5 and S6) 47,48 . The BET plots for the two series of NPCs using the two equations, i.e., the alternative and standard equations, are shown in Figures S5-S8. The two sets of plots obtained using the two equations differ considerably. The plots obtained using the alternative linear form show greater deviations from linearity and show asymptotic behavior at both low and high relative pressures, whereas the plots obtained over the same relative pressure range using the standard BET form are almost linear. The relative pressure range over which the BET equation gives linear plots can therefore be determined more precisely using the alternative approach instead of the standard one. It can also be observed that the constants C calculated for the NPCs using the standard BET equation are overestimated. The results in Table 1 imply that the specific surface area increases by a factor of two as the activation temperature is increased to 100 °C. The total pore volumes determined from Ar adsorption at a relative pressure p/p 0 = 0.99 for NPC-600, NPC-700, NPC-800, and NPC-900 were 0.15, 0.21, 0.31, and 0.67 cm 3 g −1 , respectively; the micropore volumes calculated using the Dubinin-Radushkevich (DR) equation were 0.07, 0.14, 0.24, and 0.47 cm 3 g −1 , respectively. These results show that the samples prepared at higher activation temperatures have more abundant micropores, indicating that pore structure creation increases with increasing steam activation temperature. The maximum micropore sizes, obtained using the  Horváth-Kawazoe (HK) method, are centered at 0.39, 0.44, 0.39, and 0.41nm for NPC-600, NPC-700, NPC-800, and NPC-900, respectively. The micropore sizes obtained from N 2 isotherms using the HK method for NPC-600, NPC-700, NPC-800, and NPC-900 are 0.66, 0.69, 0.54, and 0.49 nm, respectively (Fig. 3c,d, Table 1). The calculated specific surface areas obtained from the N 2 adsorption-desorption isotherms of the NPCs at 77 K are commensurate with those obtained based on Ar adsorption measurements ( Fig. 3b and Table 1). NPC-900 shows broad peaks in the HK pore size distribution, suggesting an abundant and intricate microporous system. Pores larger than ~0.6 nm are only observed for NPC-900, implying that the greatest activation was achieved at the highest activation temperature (900 °C). We have also obtained HK pore size distribution using CO 2 adsorption isotherms but it is not represented. CO 2 is one of the standard molecules, along with N 2 and Ar, used to analyze the pore size distributions of carbon materials, but it gives unreliable results in the presence of basic surfaces that can interact via specific interactions. Because the surfaces of NPCs contain large amounts of basic nitrogen components in the carbon structure, the HK method is unsuitable for use with CO 2 49 . CO 2 adsorption-desorption isotherms for the NPC sorbents were also obtained at 273, 298, 313, and 333 K up to 1 bar. Figure 4 shows that the CO 2 adsorption isotherms of the NPCs are type-I, according to the IUPAC classification. They are almost reversible over the entire pressure and temperature range investigated, meaning that the CO 2 adsorbed on the NPCs can be desorbed simply by reducing the pressure. The amounts of CO 2 adsorbed at 298 K are 1.95, 2.07, 2.84, and 2.57 mmol g −1 for NPC-600, NPC-700, NPC-800, and NPC-900, respectively ( Table 2). As expected, the adsorption capacity decreases as the temperature increases. Nevertheless, the adsorption capacities at 333 K are still 1.22, 1.28, 1.39, and 1.28 mmol g −1 for NPC-600, NPC-700, NPC-800, and NPC-900, respectively; this indicates stable CO 2 capture behavior even at elevated temperatures. The CO 2 adsorption capacity of NPC-800 is higher than those of the other samples. This enhanced adsorption Specimens BET surface area (m 2 g −1 ) Total pore volume (cm 3 g −1 ) Micro pore volume (cm 3 g −1 ) Pore  Table 1. Textural and surface properties of samples studied. The specific surface areas, total pore volumes, and C values were calculated from Ar and N 2 adsorption isotherms using the alternative BET equation. The micropore volume and pore size were obtained using the D-R equation and H-K method. capacity stems from the high specific surface area, micropore volume, and C value of NPC-800. The CO 2 adsorption capacities of NPC-900 are lower than those of NPC-800 at 298, 313, and 333 K, in spite of its higher specific surface area and micropore volume, indicating that the constant C played the most important role in this case. Although C constant does not provide a quantitative estimate of the enthalpy of adsorption, it is an indication of the magnitude of the adsorbent-adsorbate interaction energy 50 . Ar is inert and has a quadrupole moment of almost zero, therefore the constants C also indicate the magnitude of the surface energy, and can therefore be used to estimate adsorption potentials for other gases, CO 2 in this case 51 . It has been reported that sorbents that consist of N-containing carbon surfaces and have an optimum pore size have the potential to adsorb increased amounts of CO 2 . In the synthesized NPCs, melamine provides nitrogen-containing groups on the carbon surfaces, and these have a good affinity for CO 2 molecules. In addition to the surface composition, the pore structures derived from the high-temperature activation process, e.g., micropores with optimum pore sizes and other sites, can affect the CO 2 adsorption potential. Figure 4 shows that the isotherms bend slightly toward the vertical axis at pressures lower than 0.5 bar, whereas the isotherms become approximately linear at pressures greater than 0.5 bar. The subtle inflections on the isotherms suggest the presence of multiple adsorption sites for CO 2 on NPCs. For the sake of simplicity, the adsorption sites are classified into two types: active adsorption sites in micropores with the optimum pore size (site 1), and other sites (site 2) 52 .
Based on the above considerations, the dual-site Langmuir (DSL) model was used to describe the adsorption equilibria of CO 2 on the NPCs. Nonlinear parameter estimation was performed using a combined fitting method. The measured isotherm data for the NPCs can be appropriately correlated with the DSL model ( Figure S9); the corresponding estimated values of the adsorption parameters are collected in Table S2. The adsorption equilibrium constant for the first site (b 1 ) is significantly larger than that for the second site (b 2 ) at all temperatures, implying a much stronger affinity for CO 2 at site 1 than site 2. The contributions of site 1 and site 2 to CO 2 adsorption on NPCs, based on the fitting data, are shown in Figure S11. CO 2 is predominantly adsorbed at site 1 at low pressures and achieves adsorption saturation at about 0.3 bar. In contrast, the amount adsorbed at site 2 continues to accumulate as the pressure increases. CO 2 adsorption at site 1 can therefore be attributed to micropore filling with appropriate pore width, whereas that at site 2 mainly involves adsorption on pores other than micropores with appropriate pore width. The data in Table S2 show that NPC-900 has the highest q sat,A value, indicating the highest saturated CO 2 adsorption capability at site 1. The pore size distribution of NPC-900, above 0.6 nm, which is about twice as large as the kinetic diameter of CO 2 (0.33 nm), is broader than those of the other NPCs. The large amount of micropores of size 0.6 nm results in strong adsorption of CO 2 molecules and such micropores has been shown to be selective for CO 2 adsorption 53 . However, the correlation between q sat,A and the CO 2 adsorption performances (e.g., adsorption capacity and selectivity) clearly shows that other factors have a greater effect on the CO 2 adsorption performances than q sat,A does. As discussed above, the differences among the surface energies, according to the activation temperatures, make the main contributions to the adsorption capacities and CO 2 /N 2 selectivities.
For post-combustion CO 2 adsorption, CO 2 must be selectively adsorbed over N 2 . The ideal adsorbed solution theory (IAST), developed by Myers and Prausnitz, is frequently used to predict multicomponent isotherms on the basis of single-component isotherms 54,55 . On this basis, the selectivities were calculated for a 0.15:0.85 CO 2 /N 2 mixture (Fig. 5a,b, Figures S12-S15, Table 2). The IAST CO 2 /N 2 selectivities of the NPCs ranged from 34 to 107 at 273 K, from 21 to 47 at 298 K, from 23 to 53 at 313 K, and from 21 to 44 at 333 K. At all temperatures, the CO 2 /N 2 Figure 5. Binary IAST isotherms and selectivities for CO 2 over N 2 for NPC-600 (a) and NPC-800 (b) in CO 2 /N 2 gas mixture (0.15:0.85), and results for NPC-600 in CO 2 /N 2 gas mixture (5:95) (c). Ideal selectivity as function of CO 2 molar fraction for NPCs at 298 K and total pressure of 1 bar (d).
selectivities of NPC-600 and NPC-700 were better than that of NPC-800, although it had the highest CO 2 adsorption capacities based on the CO 2 adsorption-desorption isotherms.
This unexpected behavior cannot be explained only by conventional CO 2 affinities. Instead, a new concept, namely N 2 -phobicity, should be considered 56 . As discussed above, NPC-800 has the highest C value and abundant micropores for CO 2 molecules, leading to a significant affinity for CO 2 molecules. However, an activation temperature greater than 700 °C leads to a considerable decrease in the amount of nitrogen, which endows the carbon surfaces with N 2 -phobicity. The data in Table S1 show that the nitrogen contents of NPC-800 and NPC-900 are much smaller than those of NPC-600 and NPC-700 (Table S1). The higher N 2 -phobicities of NPC-600 and NPC-700 (compared with that of NPC-800) result in better CO 2 /N 2 selectivities, for a CO 2 :N 2 ratio of 0.15:0.85, despite their lower CO 2 capacities based on CO 2 adsorption isotherms (compared with NPC-800) (Fig. 5a,b). These results imply that N 2 -phobicity generated by N-containing surfaces can be a dominant factor in determining CO 2 /N 2 selectivities. NPC-900 had the lowest C constant from the BET equation, and the lowest nitrogen content among all the prepared samples. This endows NPC-900 with a low CO 2 affinity and N 2 -phobicity, resulting in the lowest CO 2 /N 2 selectivities. The excellent CO 2 adsorption capacity of NPC-800, based on its CO 2 adsorption-desorption isotherm, suggests that it is potentially an excellent sorbent for CO 2 ; however, NPC-600 and NPC-700 are the best sorbents for gas separation applications, especially for selective adsorption of CO 2 over N 2 .
The ideal selectivity for CO 2 over N 2 at a pressure of 1 bar was plotted as a function of the CO 2 molar fraction; the plots are shown in Fig. 5c,d and Figures S16-S19. For all the NPCs, the selectivities for CO 2 decrease with increasing the CO 2 molar fraction (Fig. 5d). The predicted selectivity for CO 2 on NPC-600 ranges from 34.6 to 64.6, depending on the CO 2 molar fraction in the CO 2 /N 2 mixture. The other NPCs showed lower CO 2 selectivities, although they have stronger adsorption potentials for CO 2 . This is because the NPCs, except NPC-600, have higher N 2 adsorption capacities, and this decreases the CO 2 selectivity ( Figure S10). The higher nitrogen content of NPC-600 (compared with the other NPCs) contributes to its higher CO 2 adsorption selectivity over N 2 . The IAST selectivity value of NPC-600 at 298 K or similar temperatures is significantly higher than, or at least comparable to, those of recently reported porous nanomaterials 57-62 . More detailed comparisons are shown in Table S3. The probable reason is that the interactions of the NPC samples with CO 2 molecules are strong, because of the large amount of micropores with sizes that fit CO 2 molecules, and the basic surface provided by the N-containing species derived from chemical restructuring of petroleum pitch with melamine. CO 2 adsorption experiments were conducted with a CO 2 /N 2 (0.15:0.85) binary mixture, using TGA, to investigate potential applications of NPCs in post-combustion CO 2 capture. Adsorption was achieved by exposing the sorbents to a stream of 15% (v/v) CO 2 in N 2 at 298, 313, and 333 K; these conditions approximately replicate conventional CO 2 capture and sequestration systems. After adsorption, a pure N 2 stream was used to regenerate the sorbents. Figure 6a shows that the NPCs reached CO 2 adsorption equilibrium within 40 min at 298 K. CO 2 capacities of 2.68, 3.84, 5.30, and 3.30 wt% were achieved using NPC-600, NPC-700, NPC-800, and NPC-900, respectively. The NPCs were regenerated in 40 min under a N 2 flow. CO 2 capacities of 2.01, 2.50, 4.65, and 2.01 wt% were obtained with NPC-600, NPC-700, NPC-800, and NPC-900, respectively, in 20 min at 313 K; the NPCs were completely regenerated in 20 min. The CO 2 uptakes at 333 K for NPC-600, NPC-700, NPC-800, and NPC-900 were 1.23, 2.36, 3.73, and 1.67 wt%, respectively ( Figure S20 and Table S4).
The results in Fig. 6b and Table S4 show that the CO 2 adsorption capacities at all temperatures gradually decrease with increasing temperature, because of the thermodynamically unfavorable conditions at higher temperatures. Solid sorbents with high adsorption enthalpies have the advantages of high selectivities and capacities for CO 2 /N 2 (0.15:0.85) binary mixtures, although material regeneration is a concern 63 . The recycling properties of the NPCs were examined by performing 10 CO 2 adsorption-desorption cycles at 298 K for 120 min, followed by application of a pure N 2 stream at the same temperature. At every cycle, the regenerated material retained its stability (Fig. 6d). We also measured the adsorption rates of the fully activated solids in a CO 2 /N 2 (0.15:0.85) binary mixture with a flow rate of 60 mL min −1 at 298, 313, and 333 K (Fig. 6c, Table S4). NPC-800 showed the highest initial adsorption rates, i.e., 1.63, 1.66, and 0.98 wt% min −1 at 298, 313, and 333 K, respectively. The adsorption potential factor, C constant, calculated from the alternative BET equation, can provide an explanation for these adsorption rate results. The adsorption rate behaviors of the NPCs correlate well with the values of C calculated using the alternative BET equation.

Conclusions
We developed highly effective AC sorbents based on a petroleum pitch support for selective CO 2 capture over N 2 .
The synthesis of N-containing ACs by steam activation provides controllable structures, with porous textures and chemical natures that can be precisely tailored. The modified chemical and textural structures enable preferential CO 2 adsorption over N 2 , and generate considerable gas/N-containing carbon interfacial areas. The structure also provides surfaces with high CO 2 adsorption potentials. When the sorbents were evaluated for CO 2 capture applications, the as-prepared NPC-800 displayed outstanding adsorption features at all experimental temperatures. More specifically, the highest adsorption capacity obtained was 5.30 wt% for a CO 2 /N 2 (0.15:0.85) binary mixture at 298 K. Additionally, the superior IAST selectivity achieved for CO 2 /N 2 (0.15:0.85), namely 47.5 at 298 K, was also attained with NPC-600. All the results suggest that NPCs are highly sorptive, reversibly dynamic, and regenerable sorbents for selective CO 2 capture at all experimental temperatures. These NPCs therefore have potential applications in post-combustion CO 2 capture. The novel physical and chemical structures observed in this study may also represent a new type of sorbent for CO 2 , and should be the subject of further investigation.

Methods
Pre-treatment of petroleum pitch. Petroleum pitch (GS Caltex Co.) was pre-treated for use as a carbon precursor; it had a softening point of 423 K and did not contain any nitrogen. The petroleum pitch was ball-milled at 200 rpm for 5 h. The resulting powder was mixed with hydrochloric acid solution (30%, Sigma Aldrich Co.) and stirred continuously for 6 h to remove residual metal particles and other impurities. The powder was recovered and washed several times with ethanol and water. The pre-treated petroleum pitch was obtained by drying in a vacuum oven at 80 °C.

Synthesis of NPCs.
Pre-treated petroleum pitch and melamine (Sigma Aldrich Co.) were used as a supporting material and a nitrogen source, respectively. NPCs were synthesized by mixing pre-treated pitch with melamine in an organic solvent, followed by high-temperature steam activation. More specifically, pre-treated pitch (1.2 g) was dissolved in tetrahydrofuran (50 mL; Sigma Aldrich Co.), melamine (2.8 g) was added to the solution, and the mixture was continuously stirred at 300 rpm and 50 °C for 12 h. The mixture was dried in an oven at 80 °C until the solvent had completely evaporated, resulting in a dry black solid. The physical mixture was carbonized and activated by heating. The dried solid was steam-activated as follows. (1) The sample was placed in a tube furnace with a syringe for the injection of steam molecules. (2) The furnace temperature was gradually increased to the desired temperature (600, 700, 800, and 900 °C) at a rate of 2 °C min −1 . As it reached the desired temperature, steam molecules were injected from the syringe into the tube furnace at an injection rate of 6 mL h −1 . Steam injection at the desired temperature was maintained for 1 h under an air flow, while maintaining a slightly increased pressure (about 1.2 bar), to increase the activation energy of the steam molecules. A series of NPCs were obtained by varying the Figure 6. Time-dependent CO 2 adsorption curves for CO 2 /N 2 (0.15:0.85) gas mixture with NPCs at 298 K (a) and results for NPC-800 at various temperatures (298, 313, and 333 K) (b). Results for initial section for comparison of adsorption rates (c), and cycling of CO 2 adsorption from gas mixture following regeneration by N 2 purging (d).
Characterization. The morphologies of the samples were examined using HR-SEM (SU8010, Hitachi Co., Ltd., Japan). The samples were attached to the observation platform and sprayed with platinum vapor under high vacuum for about 10 min. Elemental analysis of the samples was performed using an element analyzer (Thermo EA 1112, Thermo Scientific Co., USA) to determine their carbon, hydrogen, nitrogen, and oxygen contents (%). The chemical structures of the sorbents were investigated using XPS (K-Alpha, Thermo Scientific Co., USA) with a VG Scientific ESCALAB MK-II spectrometer equipped with a Mg Kα (1253.6 eV) X-ray source and a high-performance multichannel detector, which was operated at 200 W. TGA was performed using a thermogravimetric analyzer (TG209F3, Netzsch Co., Germany) by heating the samples to 900 °C at a rate of 10 °C min −1 under an inert N 2 flow. The N 2 adsorption-desorption isotherms at 77 K were measured to investigate the textural properties such as the specific surface area and pore structure, using an automated adsorption apparatus (BELSORP, BEL Co., Japan). Before the measurements, the samples were pre-treated in a vacuum at 200 °C for 12 h to release any remaining moisture or organic species. The pore structure was examined more precisely using Ar adsorption isotherms at 87 K, because the size and quadrupole moment of Ar are lower than those of nitrogen.
The adsorption-desorption isotherms were used to obtain the pore parameters, i.e., the specific surface area, pore volume, pore size, and magnitude of the adsorption enthalpy (based on C constant). The specific surface area was calculated using the BET equation, and total pore volumes were obtained from the amount of N 2 or Ar adsorbed at a relative pressure (p/p 0 ) of 0.99. The micropore volumes were calculated using the DR equation. The pore size distributions of the NPCs were calculated using the HK method. The CO 2 and N 2 adsorption-desorption isotherms of the NPCs at 273, 298, 313, and 333 K were also measured to investigate the CO 2 adsorption behavior, using an automated adsorption apparatus (BELSORP, BEL Co., Japan).
Cycling CO 2 adsorption experiments for CO 2 /N 2 (0.15:0.85) binary mixture. The fundamental kinetics of CO 2 adsorption-desorption for a CO 2 /N 2 (0.15:0.85) binary mixture using the NPC sorbents were investigated using TGA (Pyris 1, Perkin Elmer Co., Ltd., USA). In a typical test, the sample (10 mg) was placed in a ceramic balance and dried in an inert flow of N 2 at 110 °C for 5 h before adsorption. The sample was cooled to 298, 313, or 333 K, and adsorption was performed in a stream of 15% CO 2 in N 2 , which mimics post-combustion systems. The weight of the sorbent sample and the adsorption temperature were recorded continuously. In all experiments, the flow rates of the reactant gas (CO 2 ) and inert gas (N 2 ) were set at 60 mL min −1 , and the stream of CO 2 was kept constant for 60 min to fully adsorb CO 2 on the sorbents. After adsorption, the sorbent was regenerated using a N 2 flow. The recyclabilities of the sorbents were determined by repeating the adsorption-desorption process 10 times. The adsorption rates of the NPCs were calculated at the initial point of the adsorption kinetics.