Wireless wide-range pressure sensor based on graphene/PDMS sponge for tactile monitoring

We propose a flexible wireless pressure sensor, which uses a graphene/polydimethylsiloxane (GR/PDMS) sponge as the dielectric layer. The sponge is sandwiched between two surfaces of a folded flexible printed circuit with patterned Cu as the antenna and electrode. By adjusting graphene and NH4HCO3 concentrations, a composite with 20% concentration of NH4HCO3 and 2% concentration of graphene as the dielectric layer is obtained, which exhibits high sensitivity (2.2 MHz/kPa), wide operating range (0–500 kPa), rapid response time (~7 ms), low detection limit (5 Pa), and good stability, recoverability, and repeatability. In addition, the sensor is sensitive to finger bending and facial muscle movements for smile and frown, that are transmitted using wireless electromagnetic coupling; therefore, it has potential for a wide range of applications such as intelligent robots, bionic-electronic skin and wearable electronic devices.


Results and Discussion
GR/PDMS sponge preparation and characterization. The manufacturing process of the GR/PDMS sponge is shown in Fig. 1(a). The GR/PDMS sponge production steps are as follows: first, graphene was dispersed uniformly in ethanol by ultrasonic dispersion at 30 °C for 8 h to weaken the interaction between the graphene nanoparticles and obtain a good graphene suspension. Second, the PDMS main agent was added to the graphene suspension and heated at 100 °C until the ethanol was completely evaporated. After cooling, NH 4 HCO 3 powder and PDMS curing agent were added to the previous mixture using magnetic stirring to uniformly disperse NH 4 HCO 3 powder. Then, the mixture was poured on glass and heated at 150 °C until the NH 3 , CO 2 , and H 2 O were completely evaporated. According to Eq. (1) below, NH 4 HCO 3 on heating will break down into NH 3 , CO 2 , and H 2 O. The density of the PDMS was simply modified by the gas evaporation, forming a GR/PDMS sponge of high deformation with air microfeatures. Using the above approach, dielectric layers with different concentrations of NH 4 HCO 3 and graphene were fabricated. The fabricated GR/PDMS sponge can be cut into small pieces for use in the dielectric layer. The surface topography of the GR/PDMS sponge was obtained by SEM, and it was found that air holes were evenly spread across the PDMS; further, the graphene particles did not agglomerate and were uniformly distributed in PDMS, as shown in Fig. 1b.
The Raman spectrum of graphene, PDMS, and GR/PDMS sponge are shown in Fig. 1c. The Raman spectrum of the GR/PDMS sponge shows a D peak at 1344 cm −1 , a G peak at 1594 cm −1 , and two peaks within 2800 cm −1 to 3000 cm −1 , which is the superposition of the Raman spectrum of graphene and PDMS.
Sensor fabrication and working principle. The flexible pressure sensor was fabricated by folding a flexible substrate with Cu circuitry and using the GR/PDMS sponge placed between the folded surfaces as the dielectric layer 43,44 , as shown in Fig. S1. The size of the packaged sensor is 9 × 9 × 2 mm, as shown in Fig. 2a.
When external pressure is applied to the sensor, the GR/PDMS sponge is compressed, causing the air-holes to shrink. According to Eq. (2) 45 , the increase in capacitance of the GR/PDMS sponge is mainly attributed to the decrease in the distance between the two electrode plates. To better explain the pressure sensing mechanism, we assume that both air-holes and graphene distributed in the PDMS play important roles when the sensor is under pressure. The graphene particles are separated by PDMS and the air-holes to form numerous parallel capacitors (C 1 ,C 2 ,C 3 •••C n ), as depicted in Fig. 2b. The presence of the air-holes makes the sensor more susceptible to deformation when it is under pressure, resulting in a decrease in the space between the graphene particles. The total capacitance increases with the simultaneous increase in the number of parallel capacitors. www.nature.com/scientificreports www.nature.com/scientificreports/ The principle of the wireless system is shown in Fig. 2c. The LC tags based on the GR/PDMS sponge can be used for large and subtle human body motion detection, owing to the high sensitivity and wide sensing range. Figure 2d illustrates the working principle of the wireless pressure sensor. The antenna connected to the network analyser can transmit a series of sweep signals, containing the resonant frequency of the sensor. Thus, it can be seen from Fig. 2e, that the resonant frequency of the sensor decreases as the capacitance increases, which is in accordance with Eq. (3). The resonant frequencies of the sensor are wirelessly transmitted to the antenna through signal coupling. The resonant frequencies will be obtained by analysing the S11 parameters, and the relationship between the resonant frequency and the external pressure can be established.

Characterization of GR/PDMS sponge.
To characterize the performance of the GR/PDMS sponge, we measured the sensor sensitivity, response time, repeatability and detection limits using the platform we built with an impedance analyser (N4990A) and pressure gauge. The capacitance variation ratio ((C-C0)/C0, where C0 and C represent the initial capacitance and the capacitance under applied pressure) was plotted as a function of the applied pressure. The sensitivity is defined as S = δ(∆C/C0)/δP, which is a slope of the measured curve. When the NH 4 HCO 3 concentration is 20% and graphene concentration is 2%, the sensor has the highest sensitivity, as shown in Fig. S2. The sensitivity curves with PDMS and GR/PDMS sponge as a dielectric layer are shown in Fig. 3a. The fabricated sensor could operate over a wide range of 0-500 kPa, which is a large operating range when compared with other reported sensors 18 www.nature.com/scientificreports www.nature.com/scientificreports/ for 10-100 kPa, and 0.004 kPa −1 in the high-pressure range of 100-500 kPa. The pressure sensor with GR/PDMS sponge as a dielectric layer shows an improved sensitivity compared with that using PDMS as a dielectric layer. In view of elastic nature of the as-prepared GR/PMDS sponge, according to the theory of mechanics of materials, the deformation of GR/PDMS at 0-100 kPa was proportionally conformed with the pressure applied on the capacitance plate which is known as Hooke Law. Therefore, the variation of capacitance in 0-100 kPa was much more significant and the pressure sensor shows a high sensitivity in 0-100 kPa, as shown in Fig. 3a. As the pressure exceeds 100 kPa, the as-prepared GR/PMDS sponge was in yield stage and at this stage the deformation of GR/ PDMS sponge was low, which would then cause a low capacitance change and a low-level sensitivity.
In addition to the sensitivity, the stability, recoverability, and repeatability of a sensor are important parameters to characterise its performance. The sensor exhibits favourable recoverability when pressure is applied and released (Fig. S3). Figure 3b depicts the response curves with different pressure values (10, 50, and 200 kPa) when dynamic loading/unloading pressure is applied on the sensors. The fabricated sensor exhibits a consistent response value during the seven processes of loading/unloading under each pressure. This indicates that the sensor has excellent stability and repeatability. In order to further characterize the repeatability of the sensor, it was subjected to more than 5000 cycles of loading/unloading experiments under the same pressure, as shown in Fig. 3c, which confirm the high robust performance of this pressure sensor.
The parameters of the detection limit and response time were also analysed to further elucidate the performance of the fabricated sensor. A mung bean with a mass of 50 mg was used as the pressure source (~5 Pa) and placed on the surface of the pressure sensor. Figure 3d indicates that the sensor can detect a lightweight object and output a response signal because of the presence of air-holes. An endurance test was performed by hitting the sensor with a hammer. The sensor quickly restored to its initial state after each hit, as shown in Fig. 3e, which further explains that the sensor has good recovery and endurance. More information can be derived from Fig. 3e, as shown in Fig. 3f. The response time is 7 ms and the recovery time is 60 ms, which suggests an instantaneous response when compared with other reported sensors 8,13,24,27 . The sensor can sensitively detect the bending motion of a finger as shown in Fig. S4.
Characterization of resonant frequency response. From the measured results mentioned above, the GR/PDMS sponge as a dielectric layer exhibits the excellent properties of a wide operating range, rapid response time, low detection limit, good stability, recoverability, and repeatability. For further wireless testing of the practicality of the sensor, we built a wireless test system, as shown in Fig. S5. Figure 4a shows the corresponding output frequency curves under different external pressures. There is a unique minimum in the pressure range of 0-500 kPa for each curve, which corresponds to the resonant frequency of the sensor. The resonant frequency of the sensor is reduced from 367.67 to 309.19 MHz as the external pressure increases from 0 to 500 kPa. The absolute value of the difference between the initial and deformed resonant frequency points extracted from the curves with different external loading values were plotted against different pressure in Fig. 4b. The sensitivity is 2.2 MHz/kPa in the low-pressure regime (0-10 kPa), 230 kHz/kPa in the middle-pressure regime (10-100 kPa), and 37.5 kHz/kPa in the high-pressure regime (100-500 kPa). The www.nature.com/scientificreports www.nature.com/scientificreports/ variation trends of the resonant frequency and the capacitance are approximately the same under the same pressure, which establishes the correctness and feasibility of the wireless detection method, as shown in Fig. S6.
To verify the practicality of the fabricated wireless pressure sensor, it was attached onto a finger to measure the finger bending movements. Each finger movement state corresponds to a resonant curve. When the finger was bent from the horizontal state (0°) to the vertical state (90°) at intervals of approximately 30°, the resonant frequency was changed from 363.91 to 333.89 MHz, as shown in Fig. 4c. That is because the bending of the finger causes an increase in the capacitance of the GR/PDMS sponge, resulting in a decrease in the resonant frequency of the sensor.
To further investigate the benefits of our wireless pressure sensor, we attached our sensors to the throat, face, and centre of the forehead to monitor the swallowing action, facial muscle movements for smile and frown. The demonstrations involved a healthy female volunteer with approval from the institutional review board of the North University of China. In addition, we confirmed that all experiments were performed in accordance with the relevant guidelines and regulations of the institutional review board. First, the capacitance response curve of the pressure sensor was obtained for repeated swallowing actions. Meanwhile, the resonant frequency curve (Fig. S7) was recorded by extracting the smallest point in the curve during the swallowing process, as shown in Fig. 4d. It can be concluded that there is a corresponding relationship between the capacitance response curve and the frequency response curve from Eq. (3). That is, the capacitance variation can be transformed into frequency variation in the wireless method. The capacitance and frequency response curves of the smile and frown processes were recorded using the previous method, as shown in Fig. 4e, and f. Therefore, our wireless pressure sensor can wirelessly detect finger bending and facial muscle movements, compared to other existing cabled sensors 3,[8][9][10][11][12][13][14][15][16][17][18][19][20][21][22][23][24][25][26] , which gives it the potential to be used for highly sensitive wireless detection in a wide range of applications such as intelligent robots, bionic-electronic skin and wearable electronic devices.

Conclusions
In summary, we propose a wireless flexible pressure sensor based on a GR/PDMS sponge as a dielectric layer, which is sandwiched by folding the flexible printed circuit with patterned Cu as the antenna and electrode. The GR/PDMS sponge with NH 4 HCO 3 concentration of 20% and graphene concentration of 2% as the dielectric layer exhibits high performance with high sensitivity, wide operating range (0-500 kPa), rapid response time (~7 ms), www.nature.com/scientificreports www.nature.com/scientificreports/ low detection limit (5 Pa), and good stability, recoverability, and repeatability. The sensitivity is 2.2 MHz/kPa in the low-pressure regime (0-10 kPa), 230 kHz/kPa in the middle-pressure regime (10-100 kPa), and 37.5 kHz/kPa in the high-pressure regime (100-500 kPa). In addition, the practicality of the fabricated wireless pressure sensor was confirmed by capacitance and frequency response curves mapping for finger bending and facial muscle movements for smile and frown. Moreover, the sensor has the advantages of low cost, simple testing, high stability, and battery-free, and is thus suitable for use in highly sensitive wireless detection devices in a wide range of applications such as intelligent robots, bionic-electronic skin and wearable electronic devices.
The topography of the GR/PDMS sponge was characterized by using a scanning electron microscope (SEM) (Hitachi S-4800). The Raman measurements were taken with InVia Raman Microscope. The Raman spectrum were obtained using a 5 mW, 514.5 nm laster with a 50X objective. The capacitance-characterizations of the GR/ PDMS sponge were performed using an impedance analyser (Agilent E4990A.) The frequency-characterizations of the wireless pressure sensor were performed using a vector network analyser (Agilent E5061B).
All data generated or analysed during this study are included in this published article. In this study, the experiments involved a volunteer with approval from the institutional review board of the North University of China. Their rights were protected and all subjects provided written informed consent to participate. The specific consents from the authors and volunteer have been obtained to publish the information in an open-access online publication. The authors confirmed that all experiments were performed in accordance with the relevant guidelines and regulations of the institutional review board.