Abstract
This study is concerned with the fabrication of multilayered and bulk Ti aluminide sheets by self-propagating high-temperature synthesis (SHS) reaction using hot rolling and heat treatment. A multilayered Ti/Al sheet was prepared by stacking thin Ti and Al sheets alternatively. When this sheet was hot-rolled and heat-treated at 1000°C, a multilayered sheet composed of Ti3Al and TiAl was made through the process of formation and growth of intermetallic phases at Ti/Al interfaces and porosity reduction. A bulk Ti aluminide sheet having a lamellar structure of TiAl and Ti3Al was also fabricated successfully by heat treatment at 1400°C.
Similar content being viewed by others
References
C. Bassi, J. A. Peters and J. Wittenauer, J. Metals 41 (1989) 18.
H. Clemens, W. Glatz and P. Schretter, in “Gamma Titanium Aluminides,” edited by Y. W. Kim et al. (TMS, 1995) p. 717.
S. L. Semiatin, D. C. Vollmer, S. El-Soudani and C. Su, Scripta Metall. 24 (1990) 1409.
D. E. Alman, J. A. Hawk, A. V. Petty and J. C. Rawers, J. Metals 46 (1994) 31.
D. E. Alman, J. C. Rawers and J. A. Hawk, Metall. Trans. A 26A (1995) 589.
J. C. Rawers, J. S. Hansen, D. E. Alman and J. A. Hawk, J. Mater. Sci. Lett. 13 (1994) 1357.
M. Sujata, S. Bhargava and S. Sangal, ISIJ Int'l 36 (1996) 255.
J. C. Rawers, W. R. Wrzesinski, E. K. Roub and R. R. Brown, Mater. Sci. & Tech. 6 (1990) 187.
W. J. Park, W. C. Lee, J. Y. Jung, S. Ahn and N. J. Kim, J. Kor. Inst. Met. & Mater. 36 (1998) 1570.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Oh, J., Pyo, S.G., Lee, S. et al. Fabrication of multilayered titanium aluminide sheets by self-propagating high-temperature synthesis reaction using hot rolling and heat treatment. Journal of Materials Science 38, 3647–3651 (2003). https://doi.org/10.1023/A:1025637600400
Issue Date:
DOI: https://doi.org/10.1023/A:1025637600400