R-curves for two liquid-phase sintered α-SiC (SC-A and SC-B), of different microstructures, were characterized using indentation-strength method. Silicon carbide SC-B, with its coarser microstructure and 8 MPa · m1/2 toughness, showed higher resistance to crack growth and more damage tolerance than silicon carbide SC-A, with its finer microstructure and 4.5 MPa · m1/2 toughness. These results suggest that a coarse microstructure is beneficial to toughening and damage tolerance while a fine microstructure is beneficial to strengthening.
Similar content being viewed by others
References
P. Becher, J. Amer. Ceram. Soc. 74 (1991) 255.
R. Knehans and R. W. Steinbrech, J. Mater. Sci. Lett. 1 (1982) 327.
P. L. Swanson, C. J. Fairbanks, B. R. Lawn, Y.-W. Mai and B. J. Hockey, J. Amer. Ceram. Soc. 70 (1987) 279.
C. W. Li and J. Yamanis, Ceram. Eng. Sci. Proc. 10 (1989) 632.
S. R. Choi, J. A. Salem and W. A. Sanders, J. Amer. Ceram. Soc. 75 (1992) 1508.
Y.-W. Kim, M. Mitomo and N. Hirosaki, J. Mater. Sci. 30 (1995) 4043.
N. P. Padture and B. R. Lawn, J. Amer. Ceram. Soc. 77 (1994) 2518.
S. K. Lee, D. K. Kim and C. H. Kim, ibid. 78 (1995) 65.
C. J. Gilbert, J. J. Cao, L. C. De Jonghe and R. O. Ritchie, ibid. 80 (1997) 2253.
R. F. Cook and D. R. Clarke, Acta Metall. 36 (1988) 555.
D. K. Shetty and J. S. Wang, J. Amer. Ceram. Soc. 72 (1989) 1158.
S. J. Bennison and B. R. Lawn, J. Mater. Sci. 24 (1989) 3169.
Y.-W. Kim, M. Mitomo, H. Emoto and J. G. Lee, J. Amer. Ceram. Soc. 81 (1998) 3136.
J. Y. Kim, Y.-W. Kim, J. G. Lee and K. S. Cho, J. Mater. Sci. 34 (1999) 2325.
J. Y. Kim, Y.-W. Kim, M. Mitomo, G. D. Zhan and J. G. Lee, J. Amer. Ceram. Soc. 82 (1999) 441.
Y.-W. Kim, M. Mitomo and H. Hirotsuru, ibid. 80 (1997) 99.
R. F. Krause, ibid. 71 (1988) 338.
L. S. Sigl and H. J. Kleebe, ibid. 76 (1993) 773.
N. P. Padture, ibid. 77 (1994) 519.
N. Hirosaki, Y. Akimune and M. Mitomo, J. Ceram. Soc. Jpn. 101 (1993) 1239.
M. A. Mulla and V. D. Krstic, Acta Metall. Mater. 77 (1994) 303.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kim, JY., An, HG., Kim, YW. et al. R-curve behaviour and microstructure of liquid-phase sintered α-SiC. Journal of Materials Science 35, 3693–3697 (2000). https://doi.org/10.1023/A:1004894906697
Issue Date:
DOI: https://doi.org/10.1023/A:1004894906697