Synthesis of TS-1 by microwave heating of template-impregnated SiO2–TiO2 xerogels

Abstract

TS-1 was prepared by microwave heating of a SiO₂–TiO₂ xerogel dry-impregnated with the template, TPAOH. A highly crystalline product was obtained within 30 min after microwave irradiation with yields over 90%. These are significant advantages over the TS-1 obtained by conventional oven heating using alkoxide precursors in liquid phase, which requires 1–2 day crystallization time with low product yields. Characterization of the TS-1 obtained was carried out using XRD, SEM, FT-IR, and UV-vis spectroscopy, and catalytic activity was examined for 1-hexene epoxidation using H₂O₂ as oxidant. These studies revealed that the material obtained by microwave heating of the mixed oxide gel shows essentially identical physicochemical properties to those prepared by conventional means.