Abstract
The model of damage accumulation in the material under multiaxial loading was used to develop the scheme of plotting the limiting damage surface of a structural material with regard to operating time and a stress state, which can be considered as material specifications useful for design calculations by damage criteria.
Similar content being viewed by others
REFERENCES
A. A. Lebedev, N. G. Chausov, S. A. Nedoseka, and I. O. Boginich, “Model of damage accumulation in metallic materials in static tension,” Probl. Prochn., No. 7, 31–40 (1995).
A. Ya. Nedoseka, Fundamentals of Calculation and Diagnostics of Welded Structures [in Russian], Izd. Indprom, Kiev (1998).
RD 34.17.440-96. Guidelines on the Procedure of Estimating the Individual Life of Steam Turbines and Extending Their Service Life Beyond the Design Limit [in Russian], Moscow (1996).
A. A. Lebedev, B. I. Koval'chuk, S. É. Umanskii, et al., Handbook on Strength Calculations of Engineering Structures [in Russian], Tekhnika, Kiev (1990).
P. G. Cheremskoi, Methods of Studying Porous Solids [in Russian], Énergoatomizdat, Moscow (1985).
P. G. Cheremskoi, V. V. Slezov, and V. I. Betekhtin, Pores in Solids [in Russian], Énergoatomizdat, Moscow (1990).
DNAOP 0.00-8.15-97. Procedure for Inspection of Gas Handling Equipment [in Ukrainian], Kiev (1997).
VBN V.2.3-00018201.04-2000. Strength Analysis of Operating Defect-Containing Mains [in Ukrainian], Kiev (2000).
A. A. Lebedev, N. G. Chausov, and L. V. Zaitseva, “Effect of a stress state on fracture kinetics and crack resistance of martensitic-aging steel. Part 1. Studies on fracture process stages,” Probl. Prochn., No. 8, 3–13 (1991).
N. G. Chausov, A. A. Lebedev, L. V. Zaitseva, and A. V. Getmanchuk, “Effect of a stress state on damage accumulation kinetics and crack resistance of a 15Kh2MFA structural steel in different states. Part 1. Fracture stages of a KP60 steel,” Probl. Prochn., No. 3, 3–9 (1993).
N. G. Chausov, A. A. Lebedev, L. V. Zaitseva, and A. V. Getmanchuk, “Effect of a stress state on damage accumulation kinetics and crack resistance of a 15Kh2MFA structural steel in different states. Part 2. Fracture stages of KP80 and KP100 steels,” Probl. Prochn., No. 5, 13–20 (1993).
A. A. Lebedev, N. G. Chausov, and L. V. Zaitseva, “Effect of a stress state on fracture kinetics and crack resistance of martensitic-aging steel. Part 2. Evaluation of the crack resistance of steel,” Probl. Prochn., No. 8, 14–18 (1991).
A. A. Lebedev, N. G. Chausov, and I. O. Boginich, “Model of damage accumulation in metallic materials in the complex stress state,” Probl. Prochn., No. 3, 55–63 (1997).
A. A. Lebedev, N. G. Chausov, I. O. Boginich, and S. A. Nedoseka, “Complex evaluation of the damage in material upon plastic deformation,” Probl. Prochn., No. 5, 23–30 (1996).
D. Holland, X. Kong, N. Schluter, and W. Dahl, “Investigation concerning quantitative determination of local damage in ductile materials,” Steel Research, 63, No. 8, 361–367 (1992).
N. Schluter, D. Holland, X. Kong, and W. Dahl, Quantitative Beschreibung des Schadigungszustandes bei Duktilen Werkstoffen, Institut für Eisenhüttenkunde der RWTH Aachen, Aachen (1993).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lebedev, A.A., Chausov, N.G. & Bogdanovich, A.Z. Assessment of Limiting Damage in Materials under Static Loading with the Account of a Stress State. Strength of Materials 34, 131–134 (2002). https://doi.org/10.1023/A:1015354224871
Issue Date:
DOI: https://doi.org/10.1023/A:1015354224871