Abstract
Fracture initiated from a sharp crack or wedge shaped notch in a homogeneous material, subjected to different loading is considered. Singularities in the stress fields at edges and vertices are discussed. A point-stress criterion is used to predict fracture for sharp cracks as well as 90° wedge notches in expanded PVC foam. The point-stress criterion is formulated in a manner allowing failure predictions in general 3D stress situations. The influence of nonsingular T-stress at cracks is discussed and substantiated by experimental results.
Similar content being viewed by others
References
Andersson, B., Falk, U., Babuska, I. and von Petersdorff, T. (1995). Reliable stress and fracture mechanics analysis of complex components using a h-p version of FEM. International Journal for Numerical Methods in Engineering 38, 2135–2163.
Benthem, J.P. (1977). State of stress at the vertex of a quarter-infinite crack in a half-space. International Journal of Solids and Structures 13, 479–492
Divinycell® Technical Manual, H Grade (1991).
Falk, L. (1994). Foam core sandwich panels with interface disbonds. Composite Structures 28, 481–490.
Grenestedt, J.L., Hallström, S. and Kuttenkeuler, J. (1996). On cracks emanating from wedges in expanded PVC foam. Engineering Fracture Mechanics (4)54, 445–456.
Grenestedt, J.L. and Hallström, S. (1997). Crack initiation from homogeneous and bimaterial corners. Journal of Applied Mechanics (4)64, 811–818.
Larsson, S.G. and Carlsson, A.J. (1973). Influence of non-singular stress terms and specimen geometry on small-scale yielding at crack tips in elastic-plastic materials. Journal of the Mechanics and Physics of Solids 21, 263–277.
Severyn, A. (1994). Brittle fracture criterion for structures with sharp notches. Engineering Fracture Mechanics (5)47, 673–681.
Whitney, J.M. and Nuismer, R.J. (1994). Stress fracture criteria for laminated composites containing stress concentrations. Journal of Composite Materials 8, 253–265.
Zenkert, D. (1989). PVC sandwich core materials: Fracture behaviour under mode II loading and mixed mode conditions. Materials Science and Engineering A 108, 233–240.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hallström, S., Grenestedt, J. Mixed Mode Fracture of Cracks and Wedge Shaped Notches in Expanded PVC Foam. International Journal of Fracture 88, 343–358 (1997). https://doi.org/10.1023/A:1007439409625
Issue Date:
DOI: https://doi.org/10.1023/A:1007439409625