Abstract
The quenching and partitioning (Q&P) process was experimentally investigated on the thermomechanical simulator (Gleeble3800). The microstructure and fracture mechanism of the sheets were investigated by means of TEM. It was found that the microstructure of quenched and partitioned steel consists of fine lath martensite and thin inter-lath austenite films. The optimum quenching temperature of producing the maximum amount of retained austenite after final quenching at room temperature was predicted by Matlab software package. It was found that the calculations by Matlab software can provide guidance for experimental processing design reliably. The volume fraction of retained austenite at room temperature was approximately 8%, which was measured easily by the software VC6.0++ programming. The results verified that quenched and partitioned steel possesses a good combination of strength and plasticity due to its fine microstructure. This steel exhibited high ultimate tensile strength (exceeding 1000 MPa) and good elongation of 25%. The results showed that the fracture mechanism of the sheets is typical tough fracture under the condition of tensile failure.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
MI Zhen-li, TANG Di, YAN Ling, et al. High-Strength and High-Plasticity TWIP Steel for Modern Vehicle [J]. Material Science and Technology, 2005, 21(4): 451.
Speer J G, Streicher A M, Matlock D K, et al. Quenching and Partitioning: a Fundamentally New Process to Create High Strength TRIP Sheet Microstructures [A]. The Thermodynamics, Kinetics, Characterization and Modeling of Austenite Formation and Decomposition [C]. Chicago: Minerals Metals and Mater, 2003. 502.
Gerdemann F L H, Speer J G, Matlock D K. Microstructure and Hardness of Steel Grade 9260 Heat-Treated by the Quenching and Partitioning (Q&P) Process [A]. Materials Science and Technology [C]. New Orleans: Association for Iron and Steel Technology, 2004. 439.
Speer J G, Edmonds D V, Rizzo F C. Partitioning of Carbon From Supersaturated Plates of Ferrite, With Application to Steel Processing and Fundamentals of the Bainite Transformation [J]. Current Opinion in Solid State and Materials Science, 2004, 8(3): 219.
Clarke A, Speer J G, Matlock D K, et al. Microstructure and Carbon Partitioning in a 0.19% C-1.59% Mn-1. 63% Si Trip Sheet Steel Subjected to Quenching and Partitioning [A]. Proceedings of an International Conference on Solid-Solid Phase Transformations in Inorganic Materials [C]. Phoenix: TMS, 2005. 99.
Matlock D K, Bräutigam V E, Speer J G. Application of the Quenching and Partitioning (Q&P) Process to a Medium-Carbon, High-Si Micro-Alloyed Bar Steel [J]. Materials Science Forum, 2003, 426–432(2): 1089.
Speer J G, Rizzo F C, Matlock D K, et al. The “Quenching and Partitioning” Process: Background and Recent Progress [J]. Materials Research, 2005, 8(4): 417.
Matlock D K, De Cooman B C, Schroth J G, et al. Carbon Partitioning Into Austenite After Martensite Transformation [J]. Acta Materialia, 2003, 51(9): 2611.
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation Item: Item Sponsored by National Natural Science Foundation of China (50575022)
Rights and permissions
About this article
Cite this article
Zhao, C., Tang, D., Jiang, Ht. et al. Process simulation and microstructure analysis of low carbon Si-Mn quenched and partitioned steel. J. Iron Steel Res. Int. 15, 82–85 (2008). https://doi.org/10.1016/S1006-706X(08)60149-1
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1016/S1006-706X(08)60149-1