Preparation of size-controlled (30–100 nm) magnetite nanoparticles for biomedical applications

https://doi.org/10.1016/j.jmmm.2006.10.795Get rights and content

Abstract

Size-controlled magnetite nanoparticles (MNPs) with several dozen nanometers (nm) were synthesized for biomedical applications. Nanoparticles of single-phase magnetite, as revealed by X-ray analyses and magnetic measurements, were prepared by oxidizing ferrous hydroxide (Fe(OH)2) with a weak oxidant NaNO3 in an N2-deaerated aqueous NaOH solution (pH=12–13) at various temperatures below 37 °C. As the synthesis temperature increases from 4 to 37 °C, the MNPs are decreased in size (d) from 102±5.6 to 31.7±4.9 nm and widened in size distribution, Δd/d increases from 5.5% to 15%. Prepared without using any surfactant, the MNPs are advantageous for immobilizing functional molecules stably on the surfaces for biomedical applications.

Introduction

Magnetite (Fe3O4) nanoparticles (MNPs) have been used as magnetic carriers for a variety of biomedical applications [1]. Recently, we have developed magnetic nanobeads with submicron size having a core/shell structure of MNPs (40 nm in size)/polymer for use as magnetic carriers of bio-screening [2]. In order to attain high throughput and high accuracy in bioscreening, the core MNPs must be rather large and their size should be precisely controlled with several dozen nanometers (nm). MNPs synthesized by conventional wet process, well known as co-precipitation method, are smaller than 8 nm and are widely dispersed. Sugimoto and Matijevic [3] synthesized MNPs at 90 °C with regulating their size ranging between 30 and 1.1 μm by a sophisticated chemical route. However, size of their MNPs was dispersed with coefficient of variation larger than ca. 15%. Recent progress enabled us to synthesize MNPs with sharp size distribution, but the size has been limited to smaller than 20 nm [4], [5]. Since organic solvent and/or surfactant are involved in their methods, organic solvent, and/or surfactant remained on the MNPs surface and tend to make it difficult to encapsulate them in a hydrophilic polymer shell for biomedical use. In this study, we have successfully prepared MNPs with sharply dispersed size ranging between 30 and 100 nm in aqueous solution at relatively low temperatures (4–37 °C) without any surfactant.

Section snippets

Experimental procedure

MNPs were synthesized by surfactant-free oxidation process in an aqueous solution. Into a 21 mM aqueous NaOH solution (475 ml, pH=12,13), which was sufficiently deaerated by N2 gas, sodium nitrate (NaNO3) (0.75 g, 8.80 mmol) as an oxidant was added. Deaerated 0.1 M ferrous chloride aqueous solution (25 ml) was added to the alkaline solution, which was kept at 4, 15, 25, and 37 °C for 24 h, respectively. MNPs thus synthesized were separated from the solution with a magnet and washed several times with

Results and discussion

As a typical example is shown in Fig. 1, all the synthesized nanoparticles exhibited X-ray diffraction lines ascribed only to the spinel structure. The nanoparticles were essentially magnetite because they had a lattice constant quite near to that reported for bulk Fe3O4. This was also confirmed by their saturation magnetization close to that (92 emu/g) reported for bulk Fe3O4, as shown in Table 1. All the MNPs had a residual magnetization because their sizes were larger than the

Concluding remarks

We succeeded in carrying out the synthesis of strictly size-controlled MNPs (d=30∼100 nm and Δd/d<15%) by a simple chemical process without any surfactant. Our synthesized MNPs are suitable for coating by functional molecules. Now, we apply these MNPs as a magnetic core for magnetic nanobeads [2] and confirm that prepared magnetic nanobeads perform a quick and effective responsibility of a magnet.

Acknowledgements

This work was financially supported by a grant for R&D Projects in Cooperation with Academic Institutions from the New Energy and Industrial Technology Development Organization (NEDO), by a Grant-in-Aid (A) for Scientific Research Priority Areas, No. 18209019, from the Ministry of Education, Culture, Sports, Science and Technology (MEXT), and by Special Coordination Funds for Promoting Science and Technology from MEXT.

References (5)

  • T. Sugimoto et al.

    J. Colloid Interface Sci.

    (1980)
  • H. Urs et al.

    Scientific and Clinical Applications of Magnetic Carriers

    (1997)
There are more references available in the full text version of this article.

Cited by (0)

View full text