FT-IR and HPLC analysis of silver fir (Abies alba Mill.) bark compounds from different geographical provenances

Fourier Transform Infrared Spectroscopy (FT-IR) and High-Performance Liquid Chromatography (HPLC) could be applied to study the provenance of wood, specifically the differentiation of wood resources, as well as the identification of chemical compounds that are connected to the changes that occur in wood as a result of drying treatments. To test this hypothesis, the bark of silver fir (Abies alba Mill.) from trees belonging to seven different geographical provenances was studied, using samples dried at three different temperatures (60, 80, and 100 °C). FT-IR spectroscopy revealed different band assignments in the mid-infrared region depending on fir provenances, whereas the vibrational bands of the biomass functional groups tended to shift to lower wavenumbers. Significant differences were identified between the chemical compounds in the bark depending on the provenances. The largest proportion of the total phenolics was represented by the epicatechin gallate, epicatechin, catechin, and procyanidin dimer B1. Exploratory data analysis was performed using principal component analysis (PCA), hierarchical clustering, and Pearson correlations. This allowed a comparative evaluation of the samples and interpret the findings according to the geographical provenances, respectively ecological conditions in the areas of origin, but also the influence of the drying temperatures of the samples on chemical compounds. The precipitation in the areas of origin decreased total phenolics in silver fir bark samples, and total phenolics differed not only due to the geographic provenance, but also due to drying temperature.


Introduction
The life and biodiversity of the planet depend critically on forests, which also give people the necessary environmental, social, and economic circumstances for a proper life.Along with their numerous ecosystem functions and services [1][2][3][4], forests also supply raw materials and wood for a variety of industries [1,5,6].Wood is a complex lignocellulosic material composed of cellulose, hemicellulose, lignin, and various extractives.It is accepted that the wood of gymnosperms is of soft essence, and that of angiosperms is of hard essence, and they represent the main types of timber [7,8].Wood is one of the most popular building materials, as well as being used for furniture and numerous other purposes [9][10][11][12].
In the wood business, bark and branches are commonly considered waste; however, this could be a missed opportunity, because such materials can be valuable and are partially underutilized reserves [10].The bark contains components similar to those present in wood, such as cellulose, hemicellulose, pectin, lignin and various extractive substances [13].The bark and needles are used to extract the resin that is used for the production of turpentine, drugs, and cosmetics [14].
Information regarding variations in the proportions of the major organic components of wood can be obtained using the Fourier Transform Infrared Spectroscopy (FT-IR) method.It is a method that is frequently used to characterize wood and provides information on functional groups and molecular bonds [7,15], which is valuable for identifying wood components and determining the quality of wood [16][17][18][19].Furthermore, because extracts from the bark of diverse conifer species contain multiple types of polyphenols and have a diversity of actions, including pharmacological ones, reversed-phase High-Performance Liquid Chromatography (HPLC) has been commonly utilized to analyze the extracts of interest [20][21][22].
Analysis based on FT-IR spectroscopy in conjunction with multivariate statistical approaches provides numerous opportunities for study and data exploration; for example, FT-IR and principal component analysis (PCA) were effective in distinguishing between different wood species [23][24][25], to describe soil organic matter and microbial communities in forest sites [26], to identify the origin of lignin [27] and to detect pathogens, like Fusarium fungi [28].FT-IR was developed as a tool for the simultaneous and quantitative determination of organic components (e.g., proteins, carbohydrates and lipids), including chemical bonds, being used in multiple fields [29].PCA analysis has been also used to distinguish very subtle spectral changes in cell walls [30,31].Gierlinger et al. [25] were able to differentiate between European larch (Larix decidua), Japanese larch (L.kaempferi) and hybrid larch (L.eurolepis) by means of FT-IR in combination with PCA, cluster analysis and independent class analogy modelling.Schimleck et al. [32] discriminated wood from different Eucalyptus species, from distant provenances, as well as from the same species grown in different locations, by analyzing NIR spectra by PCA.
Valid, rapid and simple methods of wood identification and certification are needed in forestry for several reasons, such as accurate recognition of the wood source, evaluation of different factors affecting the quality of wood, according to its destination, or even to prevent illegal logging and trade, by identifying and correlating specific components with the ecological conditions from where the trees were developing.Furthermore, forest microclimates influence biodiversity and ecosystem processes in forest landscapes [33][34][35], most likely also at the level of wood quality and critical wood components.Therefore, the main purpose of the current study was to validate a tool for evaluation of different provenances of Romanian silver fir (Abies alba), based on FT-IR and HPLC analyses of the silver fir bark, in order to identify genotypes with a high content of useful components, in regard with the quantity and quality of any lignocellulose or resin constituent and their use within industrial or medicinal purposes.The potential of FT-IR spectroscopy in combination with different multivariate statistical methods is lately used in forestry in order to distinguish wood of the same species, but harvested from different sources.Therefore, in the present study, silver fir bark samples collected from trees grown in seven different areas in Romania, were analyzed through FT-IR and cluster analysis, to identify their biochemical composition.Even more, it was aimed to have a more complete and comprehending image of the data regarding the silver fir bark, so that HPLC was pursued to gain more detailed results, thus to perform a more qualitative and quantitative analysis of the polyphenolic profile of bark extracts.

Field sites and sampling
A. alba samples were collected from mature trees (between 60 and 80 years), chosen randomly to represent seven populations registered as seed source stands in Romania, located in different areas (Table 1).
The geographical origins of these provenances (P) were as follows: P1 -Valea Bistrei, P2 -Someșul Rece, P3 -Avrig, P4 -Budescu, P5 -Sohodol, P6 -Valea Morii, P7 -Gârda Seacȃ (Fig. 1A,B,C).Within all provenances, ten individual trees with similar growth characteristics (habitus and similar dimensions, a straight trunk, without defects, etc.) were randomly chosen for sampling.Stem bark samples were taken only from healthy trees, with no apparent damage.The samples have been taken at a trunk height of approximately 1.3 m above the ground, near the so-called 'diameter at breast height', or DBH), stored in paper tubes, and transported to the spectroscopy laboratory at the University of Agricultural Sciences and Veterinary Medicine of Cluj-Napoca.For FT-IR spectra were used ground bark, belonging to the repeated sampling of the same lot.

Analyses of silver fir bark by FT-IR
Circular incisions were made on the trunk of selected trees for each population, assuring that the proper bark for the investigation has at least 1 cm thickness.Before the FT-IR analysis, the stem bark samples were dried in the oven at different temperatures (60 • C, 80 • C and 100 • C) for a period of 2 h.The temperatures and the equal interval were established around those used in other similar studies [21,36,37].In order to generate a composite sample for each provenance, bark samples have been chopped down into small pieces and then ground together in an equal contribution; Grinder Retsch Grindomix GM 200 was used at this stage, with mesh size <300 μm.After that, samples were made by combining 3 mg of the material with two hundred grams of calcined KBr [38].In order to create a very fine powder, the sample and the KBr were both ground up together once again, until the mixture became completely homogenous.After placing the mixture in a steel spectral pellet kit, verification of the pellet was accomplished using a Specac hydraulic press.
In order to conduct the necessary measurements, each pellet was promptly inserted into a cassette of a Fourier Transform Infrared Spectometer model Jasco FT/IR 4100.The resolution was 4.0 cm − 1 , and the scanning range was between 4000 and 350 cm − 1 .Each spectrum was an average calculated from 256 scans that were carried out on a single sample pellet for each provenance.Spectra Manager was used to make five corrections for CO 2 and five corrections for H 2 O for each spectrum.In order to perform a comprehensive study, peak reading was carried out using Origin by OriginLab [39].

Preparation of extracts
For the extraction of the phenolic compounds, 1 g of ground sample was weighted and extracted with 10 mL methanol, by vortex, for 1 min (Heidolph Reax Top Vortex).After this stage, the extract was placed in an ultrasonication bath for 1 h (Elmasonic E15H).
During the final extraction step, the sample was centrifugated at 10,000 RPM, at room temperature, for 10 min (Eppendorf AG 5804).
The collected supernatants were filtered through a micro-filter (Chromafil Xtra nylon 0.45 μm) and 20 μL were injected into the HPLC system.

Phytochemical profilinganalysis of bark phenolic extracts by HPLC-DAD-ESI+
Regarding the chromatographic conditions, the separation and identification of the compounds were done by an HPLC system (HPLC Agilent 1200) equipped with a quaternary pump, solvent degasser, autosampler, a UV-VIS detector with a photodiode (DAD) and coupled with a single quadrupole mass spectrometer (Agilent Technologies 6110, CA, USA).The separation was performed on a Kinetex XB C18 column, 4.6 × 150 mm, 5 μm particle size (Phenomenex, USA), using water (A) and acetonitrile (B) as mobile phases, both containing 0.1% acetic acid (v/v), with a flow rate of 0.5 ml/min.The UV spectra were recorded in the 200-600 nm range for all the peaks, while the chromatograms were registered at the wavelength of 280 nm.The MS detector was used in ESI full positive ionization scanning mode: capillary voltage 3000 V, 350 • C, nitrogen flow 7 l/min and m/z 120-1200.
The data acquisition and interpretation of the results were performed using Agilent ChemStation software.Phenolic compounds have been identified by comparing retention time, UV-VIS and mass spectra with standard compounds and data from literature.

Reagents and standards
Hydroxybenzoic acids were quantified as gallic acid equivalents and flavanols as catechin equivalents, so that we used the two phenolic compounds (gallic acid and catechin) as representatives of the polyphenols subclasses.Ultrapure water was purified using a direct-Q UV system from Millipore (USA), and HPLC-purity acetonitrile was acquired from Merck (Germany).Purity levels of >98% HPLC were achieved by using Sigma-Aldrich (USA) gallic acid and catechin.

Data analyses
The final data were processed as mean total phenolic values.Analysis of variance (ANOVA) was utilized as a statistical test for a multifactorial experience to find possible differences between the means of the provenances and drying temperatures.Before applying the ANOVA test, the data were tested for normality.If the null hypothesis was rejected, ANOVA was completed using Duncan's test (α < 0.05) to separate and highlight the differences between means.Principal component analysis (PCA) and hierarchical clustering analyses utilizing the single linkage technique were performed using PAST software (PAleontological STatistics (PAST) Version 4.09, Natural History Museum, University of Oslo, Norway) [40].The Pearson correlations between each phenolic compound, respectively total phenolics in the bark, and the main ecological conditions (i.e., temperature, precipitation, amplitude) were computed for the set of geographical provenances, and the graphical representations were made with the NCSS 2023 Statistical Software (NCSS, LLC, Kaysville, Utah) [41].The P-values below 0.05 were considered statistically significant.

The main FT-IR bands of the silver fir bark and their assignments
The FT-IR bands for the silver fir bark exposed to three different drying temperatures (respectively 60 • C, 80 • C and 100 • C), are presented in Table 2.
One can assign the characteristic functional groups to a class of compounds.Thereafter, it can be recorded that bands in the range of 3399-3426 cm − 1 correspond to compounds containing functional hydroxyl groups (-OH), including phenolic compounds (e.g., from lignin) such as gallic acids, protocatechuic acid, p-coumaric acid or aliphatic structures or hydroxyl group for alpha-cellulose.
Bands no.13-15 match aldehyde groups (e.g., carbonyl C --O double bond stretching vibration in hemicelluloses (1850-1600 cm − 1 ); the C --O stretching vibration of unconjugated carbonyl group in hemicelluloses (xyloglucan) was identified at 1742-1746 cm − 1 (connected with the thermal treatment applied).The band no. 12, assigned to C --C vibration can be connected to aromatic ring vibrations of lignin.

Assignment of FT-IR bands according to bark drying temperature
The results obtained using the FT-IR technique and three drying temperatures (60 • C, 80 • C and 100 • C) demonstrate variations in the chemical composition of the bark within the silver fir provenances (Fig. 2).
Silver fir bark showed 18 prominent peaks in the fingerprint region of the wavenumbers from 3500 to 800 cm − 1 (Table 2), which represent major cell wall components (i.e., cellulose, hemicelluloses and lignin) [47].The populations investigated registered comparable peaks, but some migration of bands was noted, depending on the provenance and the drying temperature (Fig. 2A,B,C).The migration of the CH 2 stretching compound of cellulose and hemicelluloses from the wavenumber range of 2860-2851 cm − 1 , as well as the migration of the C --O stretch in unconjugated ketones, carbonyls, and ester groups, often originating from carbohydrates, from the wavenumber range of 1746-1742 cm − 1 , was observed in the provenance designated as Gârda Seacȃ.
FT-IR spectroscopy, which is often used to delineate the presence of the cellulose, hemicelluloses and lignin of different lingocellulosic materials [49], revealed different band assignments in the mid-infrared region depending on wood provenances.Strong absorption bands were observed in forest residues from fir bark attributed to O-H and C-H stretching vibrations (3500-3000 cm − 1 and 3000-2650 cm − 1 ), carbonyl C --O double bond vibration hemicelluloses (1850-1600 cm − 1 ), C --C from aromatic skeletal vibrations, C-H plane bending vibrations and C-O and C-C skeletal vibrations (1500-900 cm − 1 ) within lignin, cellulose and hemicellulose components.It can be noticed that the vibrational bands of the biomass functional groups had a tendency to shift (to lower wavenumbers), similar to other results [12,60].Changes observed in the FT-IR spectrum for fir bark dried at 100 • C might be due to some different changes in the biomass compared to the samples treated at 60 and 80 • C, respectively changes attributed to unidentified compounds in this study.These bands became less sharp and wider with the increase in treatment temperature.The main bands associated with lignin components were detected between 1620 and 1616 cm − 1 [7,55], while the cellulose and hemicelluloses were characterized by the bands between 2925 and 2923 cm − 1 [58].Group stretching O-H, as well as O-H in lignin, decrease significantly from 60 • C to 100 • C; for example, after the bark was exposed to 60 • C, the peak was found at 3426 cm − 1 for Valea Morii provenance and migrated to 3409 cm − 1 after 100 • C; similarly, for Budescu provenance, the band migrated from 3415 cm − 1 to 3404 cm − 1 .For nearly all components, among the drying temperature tested for silver fir bark, the bands' position migrated to lower wavenumbers from 60 • C to 100 • C. Such is the case of aromatic C-O vibration in guiacyl rings, which for the seventh provenance was located at 1272 at 60 • C treatment and shifted to 1267 at 80 • C and 100 • C.
Several studies present well-defined peaks which provide information on various functional groups present in fir wood constituents and their variation depending on the source (needles, bark) that can be identified [12,61].Differences could also be noticed among samples, according to the wood provenances.This could be explained by the degradation of the lignin, which has become significant at high temperatures.
Peaks in the interval 3399-3426 cm − 1 indicate an increase of free or only weakly H-bonded O-H groups of cellulose.These evolving O-H bands may suggest the depolymerisation of the polysaccharides and the relative resistance of cellulose crystallites.

Identification of phenolic compounds in silver fir bark samples by HPLC
Based on their MS fragmentation patterns, high-resolution mass, UV spectra, and retention times, 11 phenolic compounds in total were found in the 21 samples of powder silver fir bark.Representative chromatograms for two selective provenances, respectively P1 -Valea Bistrei and P5 -Sohodol, using the three drying temperatures: T1 = 60 • C; T2 = 80 • C; T3 = 100 • C are illustrated in Figs. 3 and  4).These two provenances have approximately average values for the total phenolics among the populations analyzed, and thus can be considered convenient representations for all chromatograms obtained in the study.Flavonols were responsible for the greatest peaks  in the HPLC traces of silver fir wood extracts, while the lower peaks were represented by hydroxybenzoic acids.
Peak number identities from all the analyzed provenances are displayed in Table 3, along with quantifications of phenolic compounds (mg/g) depending on the three drying temperature (T1 = 60 • C; T2 = 80 • C; T3 = 100 • C), in silver fir samples from seven geographic provenances, are presented in Tables 4-6.
The obtained chromatograms (21 in total, three temperatures for all seven provenances) look almost similar, whereas the amount of phenolic compounds differs depending on the area.It can be noted that the population with the highest content of phenolic compounds was represented by P3 -Avrig (35.825 mg/g at 60 • C (Table 4), 36.075mg/g at 80 • C (Table 5), 31.899mg/g at 100 • C (Table 6), while the one with the lowest content was P4 -Budescu (1.985 mg/g at 60 • C (Table 4), 2.120 mg/g at 80 • C (Table 5), 1.237 mg/g at 100 • C (Table 6).Also, the influence of temperature was marked and can be concluded that 80 • C seems to be the optimal temperature for polyphenol content analysis.
The most abundant compounds in the stem bark samples of silver pin were epicatechingallate, epicatechin, procyanidin dimer B1 and catechin, but their concentration was different depending on the drying temperature applied.Epicatechin and catechin are the first derivative products of flavan-3-ols, while gallocatechin forms polymeric tannins.
The results presented in Fig. 5A highlight the significant differences between the content of the fir bark in total phenolics depending on the interaction between provenances and treatments.Drying temperature did not influence the variation of phenolics in the bark in only two provenances, P4 -Budescu and P6 -Valea Morii, which also had the lowest amount of total phenolics (Fig. 5B).Among the provenances, it stood out with a high content of total phenolics P3 -Avrig, followed by P7 -Gârda Seacȃ and P5 -Sohodol.Unlike the influence of the geographical origin of the samples, drying temperature had significant effects on the phenolics content (Fig. 5C).It had higher values at the treatment with 80 • C and lower at 100 • C, while the treatment with the lowest temperature provided intermediate values.

Multivariate analysis for A. alba provenances related to FT-IR and HPLC bark investigation
Principal component analysis (PCA) was used to explore the three drying temperatures (T1 = 60 • C, T2 = 80 • C, and T3 = 100 • C) for A. alba bark, and the findings are displayed in Fig. A1 (A, B, and C).In the PCA dataset for the lowest drying temperature, T1 =     Hierarchical cluster analysis and the corresponding heatmap summarized the relationships between the chemical compounds, in the row dendrogram, but also between the three drying temperatures, in the column dendrogram (Fig. 6).The row dendrogram illustrates the clusters of compounds according to the grouping of observations that were made on the peaks and the levels of similarity between these.The cluster of phenolic compounds has two main branches, the lower one containing only three compounds, two of which are closely placed in a subcluster (CH and CH 2 ) and one more distant (H, O-H).The upper subcluster has two branches, one represented by a single compound, but the other with numerous branches and subclusters, some finished as four pairs in which the compounds are very close (i.The Pearson correlations calculated between the main ecological conditions (temperature, precipitation, altitude) of the silver fir geographic provenances and phenolic compounds in the bark revealed that the level of more than half of the phenolic compounds decreased significantly as precipitation increased (Fig. A2).A significant negative correlation (r = − 0.803*) was identified both between the total phenolics and precipitation (Fig. A3), illustrating that the amounts of phenolic compounds in the bark are inversely associated with the quantity of precipitation in the areas of the silver fir geographic provenances.

Discussion
The current study is a new attempt to evaluate A. alba provenances using FT-IR fingerprints and HPLC.FT-IR approach is useful for analyzing wood because it provides information about functional groups and chemical bonds [15,49,50,62], lucrative for identifying wood parts, wood type, and also wood quality assessment [16,19].
FT-IR spectra have been effectively used to characterize the chemical part of wood and bark [42,44,46,62,63], as well as the detection and further the influence of fungi on wood [44,64].Infrared spectroscopy has also been applied to distinguish tree species.Niemz et al. [65] were able to differentiate between softwoods and hardwoods based on chemical differences in the lignin composition of conifers and angiosperms which were easily detected by FT-IR analyses.However, if differences in chemical composition are small, analysis of individual chemical components is insufficient to group a set of samples by species [47,66].
Chromatography results further revealed that silver fir bark extracts contain large amounts of chemical compounds such as cellulose, hemicellulose, lignin, flavonoids, phenols with antioxidant activity and others, fact that corresponds to other studies carried out [67,68].Within the same species, genetic variation in the forest can be manifested within and among populations [69].It is of interest to uncover genetic differences that also determine phenotypic differences in trees, such as growth, resilience to stresses, and useable properties of wood [70][71][72].
Tree habitus, wood, bark, and chemical compounds can take different peculiarities within species and populations, and under specific ecological conditions, i.e. soil, climate, altitude, forest characteristics, etc. [73].Bark thickness and constitution depend on the species, the age of the tree, the ecological factors from the origin area, and slightly on different parts of the tree [20].Bark is also important because it guards trees' stems from fire and other dangers and helps them absorb nutrients, connect to water, and often fix damage [74].Bark, a non-technical name for tissues located outside the vascular cambium [75], that perform important physiological tasks in a living tree, includes the following: transport and storage of photosynthesis-derived compounds [76], as well as defence against biotic and abiotic stressors [77,78].Its function can be deduced from the chemical composition, which varies according to the quantities and proportions of structural (cellulose, hemicelluloses, lignin, and suberin) and non-structural (extracts) substances [79].Conifer bark can contain up to six times more extractives than stemwood (softwood) [78,79], and the bark comprises 10-15% of stem volume [20].The bark of the silver fir tree comprises various extractable non-structural constituents, including soluble carbohydrates, terpenes, aliphatic alcohols, fatty acids, and polyphenols such as stilbens, flavonoids, lignans, and tannins [78].The bark is comprised of various tissues encompassing the vascular cambium, encompassing both the periderm and secondary phloem, which is further divided into inner and outer bark [80].The secondary phloem, which is the layer directly surrounding the vascular cambium, contains polyphenolic parenchyma cells, where the majority of the bark secondary metabolites are produced.These cells also include lipids, carbohydrates, and polyphenolic chemicals [81].The utilization of bark from commercially cultivated softwood trees presents a promising avenue for accessing secondary metabolites, notably polyphenols such as tannins.These compounds have demonstrated utility in the production of adhesives and resins [20].A higher total extractive content of the bark was identified in the upper positions of the silver fir trunk [20].
European softwood bark-derived condensed tannins are accepted as an alternative to synthetic phenolics [82].Due to the composition of the majority of flavonols and acids, the tree bark represents an important source of materials for wood industry.Due to the hydroxyl groups' reactivity with formaldehyde, condensed tannins are ideally suited for the efficient production of adhesives, polymers and foams.Our findings reveal that a significant quantity of catechins and epicatechins (a subgroup of flavanols) were detected in the bark of some provenances, confirming the necessity for proper utilization of this resource in silver fir [11,12,78].Epicatechin and catechin have been identified in various kinds of trees, including leaf extracts from several Salix species, but also in a range of fruits, beans, and chocolate [83].In comparison to samples from the other provenances, Gârda Seacȃ contained larger concentrations of ellagic acid.This polyphenol is present in the wood and bark of several forest species, including Quercus, Eucalyptus, and Castanea [84] and has been recognized having antioxidant, anticancer, and antimutagenic activities.As a result, waste from the forestry, wood-processing, and agro-forestry industries might be used to recover some bioactive chemicals, including ellagic acid [85].
Most infrared bands cannot be traced to a single component due to the intricacy of wood.To improve FT-IR spectral analysis, multivariate statistical approaches can be applied [51].Similar to the current investigation, principal component analysis (PCA) has been used to discover chemical differences between early-wood and late-wood [86], or to discriminate between trees growing in different places [47].The hierarchical clustering method enabled the combination of multiple information gathered from detailed sample characterization into a global perspective of the system.Multivariate statistical analysis is frequently used to make clear distinctions based on band positions obtained in FT-IR [51].
In our investigation, infrared spectroscopy and HPLC, in combination with statistical interpretation of data, were valuable instruments to evaluate provenance and characterize the noted differences between the studied samples.The findings provide a potential starting point for selecting appropriate resources represented by natural forests, as well as optimal processes for the utilization of wood from renewable biomass in energy and commodities with added value.Because of the finite nature of fossil-based resources and the negative environmental impact of their use, harnessing renewable biomass is gaining popularity in sustainable forestry.However, for future studies, an in-depth method will be conceived for the assessment of factors (except geographical, respectively genetic, and ecological) that may influence the chemical compounds of interest in fir bark, including age, condition, size of trees, and different sampling heights, cardinal points, different years, but also different seasons.

Conclusions
In order to identify prospective uses as sources of significant chemicals, this study includes an in-depth investigation of silver fir bark from seven different geographic provenances in Romania.Among the assessed sources, several populations with high potential for biomass utilization were found, according to the final and compositional analysis.Interpopulation variations of Romanian silver fir caused by genetic and ecological variables appear to be sources of a variety of chemical compounds of interest in tree bark, namely considerable levels of phenolics and flavonoids.Depending on the origins of A. alba, the extractive fractions of some provenances contained a significant amount of beneficial compounds and potential antioxidant activity.A negative correlation was identified between total phenolics and precipitation, meaning that as precipitation, respectively the altitude levels increase, the amounts of phenolic compounds in silver fir bark decrease.

Fig. 1 .
Fig. 1.Location in Romania and the main parameters for investigated A. alba populations from which the bark samples were analyzed: Altitude, as m.a.s.l.(metres above sea level) (A); Amount of annual precipitation, as multiannual average, in mm (B); Average annual temperature, in • C (C).Data for mean annual temperature and mean annual precipitation are average values for a ten-year period (2012-2022) from meteorological stations.
I.M.Morar et al.
I.M.Morar et al.
e., C-O-C asymm.Stretch.and C-O-C stretch.;C-O stretch.and Aromatic C-H; C --C, C --O and C-H asym CH 3 and CH 2 ; CH 2 wagg.and C-O vibr.).The column dendrogram of drying temperatures shows a closer relationship between the 80 • C and 100 • C levels, which are grouped in a pair subcluster from which the 60 • C level appears more distant.

Fig. 6 .
Fig. 6.Hierarchical clusteringpaired group UPGMA (unweighted pair group method with arithmetic mean) for 15 components identified in bark of seven provenances of A. alba using FT-IR technique, at three different drying temperatures (60, 80, 100 • C).
I.M.Morar et al.

Table 1
Administrative details of the studied A. alba provenances (populations) in regard with their provenance from Romania.

Table 3
Peak number identities and phenolic compounds identified in silver fir samples.
I.M.Morar et al.