Dataset on leaching properties of coal ashes from Malaysian coal power plant

Coal combustion by-products (CCPs) (i.e. fly (FA) and bottom (BA) ashes) generated by power plants contain heavy metals. This research presents leaching properties of coal ashes (FA and BA) collected from Jimah coal-fired power station, Port Dickson, Negeri Sembilan using USEPA standard methods namely toxicity characteristic leaching procedure (TCLP), and synthetic precipitation leaching procedure (SPLP). Heavy metals like lead (Pb), zinc (Zn), copper (Cu) and arsenic (As) were quantified using atomic absorption spectrometer (AAS). The leached of heavy metals fluxes were Cu < Zn < Pb < As. As leached the most whilst indicating of possible contamination from As. Overall, the ranges of leached concentration were adhered to permissible limits of hazardous waste criteria for metal (Pb and As) and industrial effluent (Zn and Cu). The presented data has potential reuse as reference for the coal ash concrete mixed design application in construction industries.

Keywords: Leaching properties Coal ashes Power plant Toxicity characteristic leaching procedure Synthetic precipitation leaching procedure Heavy metals a b s t r a c t Coal combustion by-products (CCPs) (i.e. fly (FA) and bottom (BA) ashes) generated by power plants contain heavy metals. This research presents leaching properties of coal ashes (FA and BA) collected from Jimah coal-fired power station, Port Dickson, Negeri Sembilan using USEPA standard methods namely toxicity characteristic leaching procedure (TCLP), and synthetic precipitation leaching procedure (SPLP). Heavy metals like lead (Pb), zinc (Zn), copper (Cu) and arsenic (As) were quantified using atomic absorption spectrometer (AAS). The leached of heavy metals fluxes were Cu < Zn < Pb < As. As leached the most whilst indicating of possible contamination from As. Overall, the ranges of leached concentration were adhered to permissible limits of hazardous waste criteria for metal (Pb and As) and industrial effluent (Zn and Cu). The presented data has potential reuse as reference for the coal ash concrete mixed design application in construction industries.
© 2020 The Author(s

Value of the data
• The data can be used by civil engineers as reference for the application of concrete mix design containing coal ash in construction industries. • The leaching properties data will benefit scientific community and public authority on hazardous waste management like coal ashes via a strict monitoring and legislated guidelines. • The data will give an additional value for further spatial temporal studies on leaching properties of heavy metals infused in concrete mixed designs before application in the construction industries to prevent any environmental impact from the use of CCPs.

Data description
Coal fired power plant generates mass production of coal combustion by-products such as fly (FA) and bottom (BA) ashes [1] . The leaching of heavy metals fluxes may contribute to adverse environmental and health impacts due to bioaccumulation in soft tissues, toxic at certain level of concentration and period of exposure [ 2 -5 ]. Therefore, the dataset presented leaching properties of four heavy metals namely lead (Pb), zinc (Zn), copper (Cu) and arsenic (As) in coal ashes.
The permissible limit of heavy metals for leaching test is categorized as hazardous waste criteria (mg/L) and hazardous waste limit (mg/L) [6] . Hazardous waste criteria a refers (mg/L) to limits that are allowed in solid waste or soil for disposal in a landfill (i.e. Pb: 100.0 mg/L, and; As: 100 mg/L). The hazardous waste limits b (mg/L) are the limits allowed to leach out of soil or solid waste in a landfill (i.e. Pb: 5.0 mg/L, and; As: 5.0 mg/L). However, limits for Zn and Cu are not available. Therefore, limits for industrial effluents regulations [7] and national standards for drinking water quality by Malaysia government [8] are included in this study. The limits for industrial effluent are Standard A (Pb: 0.1 mg/L; Zn: 1.0 mg/L; Cu: 0.2 mg/L and; As: 0.05 mg/L) and Standard B (Pb: 0.5 mg/L; Zn: 1.0 mg/L; Cu: 1.0 mg/L and; As: 0.01 mg/L) [7] . The concentration of heavy metals leached from coal ashes (FA, BA, and FA + BA) after the acidic leaching tests along with standards for hazardous waste are shown in Table 1  The H + ion in aqueous acidic solution will remove the cations (heavy metals) from their binding sites (FA and BA) causing cations leaching due to the reduction of cation exchange capacity (CEC) [9] . Cation exchange capacity is a capacity of cations to be attached on matrix surfaces [10] . Therefore, concentration of heavy metals in the matrix system were found in both TCLP and SPLP tests.
The dataset on leaching properties of coal ashes presented is essentially important. Overall, the ranges of concentration in FA, BA and FA + BA for Pb complied with permissible limits for metals ab : Hazardous waste criteria a (mg/L) and TCLP hazardous waste limits b (mg/L). The ranges of concentration for As complied with permissible limits for metal a : Hazardous waste criteria a (mg/L). The concentration for Zn and Cu complied with limit for industrial effluent (Standard A and Standard B) and national drinking water quality standards. The evaluation on leaching of heavy metals (Pb, Zn, Cu, and As) in FA, BA and FA + BA showed that As leached the most whilst indicating of possible contamination from As. The leached of heavy metals fluxes were Cu < Zn < Pb < As. Nevertheless, the leachability of mixed samples of FA + BA was found to be higher than those of pure FA or BA in case of Pb, Cu and As. Therefore, the mixed of these samples may expose threat to the environment. Further investigation to understand the physico-chemical and leaching properties of mixed samples are highly recommended.

Experimental design, materials, and methods
The leaching properties of coal ashes (FA , BA , and FA + BA, 1:1, v/v of dry weight) was determined via two USEPA standard procedures namely toxicity characteristic leaching procedure (TCLP) and synthetic precipitation leaching procedure (SPLP) [ 11 , 12 ].
The TCLP is to determine the leaching properties of organic and inorganic substance in liquid, solid and multiphase wastes simulating landfill leachate (Method 1311) [11] . Two extraction fluid namely extraction fluid No.1 (5.7 mL glacial acetic acid (CH 3 CH 2 OOH) in 500 mL of deionized water, additional of 64.3 mL of 1 M sodium hydroxide (NaOH) and diluted to 1 L, pH: 4.93 ± 0.05) and extraction fluid No. 2 (5.7 mL CH 3 CH 2 OOH diluted to 1 L with deionized water, pH: 2.88 ± 0.05) were used.
The sample ratio to extraction fluid was equivalent to 1:20 (v/v). Samples (5.0 g of each FA, BA and FA + BA) were transferred into a 500 mL Erlenmeyer flask containing 96.5 mL of deionized water and stirred for 5 min. The extraction fluid No. 1 would be added if observed pH was below 5. If the pH was more than 5.0, 3.5 mL 1N HCl would be added. Next, the solutions were heated to 50 °C for 10 min, left to room temperature with agitation at 30 rpm for 18 h.
The synthetic precipitation leaching procedure (SPLP) is to determine the leaching properties of organic and inorganic compounds in liquids, soils, and wastes simulating acid rain from airborne nitric and sulfuric oxides (Method 1312) [12] . Following the same procedure as TCLP, sulfuric acids were used in the extraction fluid instead of acetic acid (5.7 mL sulfuric acid (H 2 SO 4 ) in 500 mL of deionized water, additional of 64.3 mL of 1 M sodium hydroxide (NaOH) and diluted to 1 L, pH: 4.20 ± 0.05).
The solutions (contained FA, BA and FA + BA) were filtered using glass fiber filters (0.7 μm) for Atomic Absorption Spectrometry analysis (SHIMADZU, AA-6800). The furnace method assisted with acethylene gas was used for Pb, Cu, and Zn quantification. The graphite method assisted with acethylene gas was used for As quantification.

Declaration of Competing Interest
The authors declare that they have no known competing financial interests or personal relationships which have, or could be perceived to have, influenced the work reported in this article.