Data for phase angle shift with frequency

Phase angle shift between the current and voltage with frequency has been reported for a single phosphoric acid fuel cell in the cell temperature from 100 °C to 160 °C and the humidifier temperature from 40 °C to 90 °C. An electrochemical workbench is employed to find the shift. The figure of phase angle shift shows a peak in high humidifier temperatures. The peak in phase angle shift directs to lower frequency side with decreasing humidifier temperature. The estimation of electrochemical reaction time is also evaluated in the humidifier temperature zone from 50 °C to 90 °C.


a b s t r a c t
Phase angle shift between the current and voltage with frequency has been reported for a single phosphoric acid fuel cell in the cell temperature from 100°C to 160°C and the humidifier temperature from 40°C to 90°C. An electrochemical workbench is employed to find the shift. The figure of phase angle shift shows a peak in high humidifier temperatures. The peak in phase angle shift directs to lower frequency side with decreasing humidifier temperature. used to find the data. The entire datum was taken at cell temperatures of 100-160°C and humidifier temperatures of 40-90°C. The experimental error in the phase angle measurement is within 7 0.01°.

Experimental features
A single phosphoric acid fuel cell was constructed and an electrochemical workbench was connected using two probe configuration method.

Data source location
Jadavpur University, Kolkata, India Data accessibility Data is with this article

Value of the data
Phase angle shift with frequency is commonly used yet powerful technique for electrochemical analysis.
Other researchers can use the data as guidelines to select these parameters for their fabricated fuel cell without rigorous trials and errors.
The designed technique can also be applicable for polymer electrolyte membrane fuel cells as well as solid oxide fuel cell.

Data
Shift in phase angle between the current and voltage is evaluated by applying sinusoidal excitation of 10 mV across the single phosphoric acid fuel cell. Figures depicting the variation of phase angle with frequency are shown here in wide cell temperatures and humidifier temperatures.

Experimental design, materials and methods
A single unit of phosphoric acid fuel cell (PAFC) consists of anode, electrolyte and cathode. Here, 88 wt% phosphoric acid (Merck, India) was used as an electrolyte. The details of the experimental set up were also reported elsewhere [1,2]. A glass mat soaked in the phosphoric acid was used as a solid electrolyte. Two electrodes were composed of thin layers of 20 wt% Pt/C, as deposited on to carbon plate. The electrolyte/electrode assembly was placed between two grooved graphite plates. Pure H 2 was passed through a humidifier to humidify the gas and fed to the anode through the grooved graphite plates. In the cathode, the O 2 gas was fed. The outlets of the grooved graphite plates from both cathode and anode were connected to an adsorber to collect moisture. Two stainless steel plates were placed at the two ends and were used as current collectors. A heating plate was placed on the lower current collector to maintain the cell temperature. The total arrangement was kept intact by using two pusher plates. Throughout all the experiments the inflows of H 2 and O 2 gases were maintained at 100 and 50 cc/min, respectively using rotameters. Measurement of phase angle shift between the current and voltage using the electrochemical workbench was performed after 3 h of starting the gas flow. This time is given so that the open circuit potential was generated after the electrochemical reactions inside the cell. As parameters both the cell temperature and humidifier temperature were varied. The variation of phase angle shift with frequency is shown in Fig. 1. A welldefined peak in phase angle shift is observed for higher humidification [ Fig. 1(a)-(e)]. The peak shifts towards lower frequency region as the humidifier temperature decreases in Fig. 1(a)-(e). It is observed from Fig. 1(f) that the peak vanishes at 40°C humidifier temperature. Scattering of datum in extreme low frequency indicates the uncertainty of measurement beyond the experimental error [ Fig. 1(d)-(f)]. The electrochemical reaction time (τ) is evaluated using the peak of phase angle shift at the investigated temperatures [3]. The electrochemical reaction time is also presented in Table 1. It is found that τ has maximum 0.8 ms and minimum 1.45 s for higher humidifier temperature and lower humidifier temperature respectively.