Vacuum-assisted decellularization: an accelerated protocol to generate tissue-engineered human tracheal scaffolds

Patients with large tracheal lesions unsuitable for conventional endoscopic or open operations may require a tracheal replacement but there is no present consensus of how this may be achieved. Tissue engineering using decellularized or synthetic tracheal scaffolds offers a new avenue for airway reconstruction. Decellularized human donor tracheal scaffolds have been applied in compassionate-use clinical cases but naturally derived extracellular matrix (ECM) scaffolds demand lengthy preparation times. Here, we compare a clinically applied detergent-enzymatic method (DEM) with an accelerated vacuum-assisted decellularization (VAD) protocol. We examined the histological appearance, DNA content and extracellular matrix composition of human donor tracheae decellularized using these techniques. Further, we performed scanning electron microscopy (SEM) and biomechanical testing to analyze decellularization performance. To assess the biocompatibility of scaffolds generated using VAD, we seeded scaffolds with primary human airway epithelial cells in vitro and performed in vivo chick chorioallantoic membrane (CAM) and subcutaneous implantation assays. Both DEM and VAD protocols produced well-decellularized tracheal scaffolds with no adverse mechanical effects and scaffolds retained the capacity for in vitro and in vivo cellular integration. We conclude that the substantial reduction in time required to produce scaffolds using VAD compared to DEM (approximately 9 days vs. 3–8 weeks) does not compromise the quality of human tracheal scaffold generated. These findings might inform clinical decellularization techniques as VAD offers accelerated scaffold production and reduces the associated costs.


Introduction
Tracheal tissue engineering has been at the forefront of efforts to generate bioengineered organs because of the lack of therapeutic options available for patients with severe tracheal disease [1e5]. Both decellularized and synthetic scaffolds have been transplanted in compassionate-use cases [6e10] and subsequent work has turned to improving the functionality of these transplants. Techniques to improve the quality of cells for transplantation, either through adult stem cell isolation and expansion [11] or induced pluripotent stem (iPS) cell technology [12e16], are being investigated but the scaffolds onto which cells are seeded also need to be refined. There is currently little consensus on the optimal scaffold for tracheal bioengineering purposes with decellularized [6,8], synthetic [17] and hybrid stent-based [18] scaffolds at various stages of development.
Clearly, a scaffold that closely mimics normal airway physiology in terms of structure and function is highly desirable [19]. For this reason, decellularization of donor organs is an attractive approach in tracheal bioengineering because the full complexity of human tracheal architecture, extracellular matrix (ECM) and regional structural variation are not yet mimicked by synthetic scaffolds [20]. Ideally, these properties should be retained whilst simultaneously removing all donor cells from the trachea to avoid complications involving immune reaction and rejection after transplantation [21,22]. Achieving this delicate balance between cell removal and ECM ultrastructure disruption causes decellularization protocols to take longer than may be ideal for the clinical needs of some tracheal stenosis patients. Clinically applied protocols have required many weeks for decellularization [8,10,23], a timeframe that rules out the use of a decellularized scaffold in more urgent clinical scenarios such as tracheal agenesis or atresia where the entire trachea is absent and full replacement is required soon after birth [24,25].
Methods to accelerate the decellularization process are being developed [26] but as yet no direct comparison of the scaffolds produced by different methods has been performed using human tracheae, particularly in terms of their in vivo responses [27]. We developed an accelerated vacuum-assisted decellularization (VAD) protocol, which reduces the time required for decellularization from several weeks [8,10,28] to just nine days (Fig. 1). We hypothesized that VAD would effectively decellularize human tracheal scaffolds and that the resulting scaffolds would retain similar biomechanical properties and key extracellular matrix components to those obtained with the clinically applied detergent-enzymatic method (DEM). Further, we hypothesized that both VAD and DEM scaffolds would support the engraftment of primary human airway epithelial cells in vitro and would vascularize to similar extents following in vivo implantation.

Materials and methods
2.1. Decellularization of human tracheae 2.1.1. Tissue procurement Human tracheae were obtained from cadaveric donors (30e80 years age) identified through the National Health Service Blood and Transplant (NHSBT) tissue retrieval team, by agreement and with appropriate consent, following the current clinical practice for nonliving tissue retrieval in the U.K. Ethical approval was obtained through the National Research Ethics Committee (REC reference 11/ LO/1522). Tracheae were retrieved less than 48 h post mortem and were removed in their entirety from cricoid to carina. Donor tracheae were immediately rinsed in 1 L 0.9% normal saline and surrounding tissue was dissected away. The tracheae were immersed in 20% chlorhexidine solution for 5 min followed by a further three rinses in 0.9% saline. Intact tracheae were divided into two equal halves and these matched donor pairs were processed for either the clinically applied standard protocol [23] of repeated cycles of detergent and enzyme (detergent-enzymatic method; DEM) or frozen and then decellularized using the vacuum-assisted decellularization (VAD) protocol [26] such that decellularization using both procotols finished simultaneously. A matched donor design was chosen due to the difficulties in obtaining large numbers of human donor organs for research purposes and to minimize the effect of inter-individual variability on results.

Detergent-enzymatic method (DEM) decellularization
Tracheae were subjected to 25 cycles of distilled water for 72 h at 4 C, 4% sodium deoxycholate (Sigma) for 4 h and 2000 kU DNase I in 1 M sodium chloride (Sigma) for 3 h. Tracheae were continuously rotated on a roller throughout the decellularization process and were stored at 4 C in PBS until use.

Vacuum-assisted decellularization (VAD)
Tracheae to be processed by VAD were aspirated dry and frozen at À80 C. Tissue was thawed to room temperature for 24 h and rinsed in PBS. Decellularization was performed in an autoclaved stainless steel Ricordi chamber. Luer locks with 3-way ports and a pressure gauge were attached to the chamber such that a vacuum (1 Torr) could be generated. All decellularization steps were performed under vacuum on a tissue agitator at 140 rpm at 37 C unless otherwise indicated. All solutions were supplemented with 1% penicillin/streptomycin (Sigma). Tracheae were incubated in detergent solution containing 0.25% sodium deoxycholate (Sigma) and 0.25% Triton X-100 (Sigma) in HBBS for 24 h at 37 C. Tracheae were then rinsed twice in sterile water for 2 h and incubated for a further 44 h in sterile water at 4 C on a tissue agitator at 20 rpm. Following the wash step, tracheae were incubated in DNase I (2 kU/ ml) and RNase (4 U/ml) at 37 C for 24 h, followed by another 24 h wash step in sterile water at 4 C as described above. The DNase/ RNase step and wash was repeated once prior to a final wash step of sterile water for 48 h at 4 C as described above. Tracheae were then stored at 4 C in PBS until use.

Whole-mount immunocytochemistry
For whole-mount imaging, cell-seeded scaffolds were fixed in 4% PFA for 30 min and blocked for 1 h in blocking buffer (10% fetal bovine serum in PBS containing 0.01% Triton X-100). CK5 primary antibody (Abcam; ab17130) incubation was overnight at 4 C in blocking buffer without Triton X-100. Scaffolds were washed three times in PBS for 5 min and species-appropriate secondary antibody (AlexaFluor dyes; Molecular Probes) was added for 2 h at room temperature. Scaffolds were washed three times in PBS and DAPI (1:10,000 in PBS) was applied to counterstain scaffolds before imaging. Scaffolds were oriented luminal-side down on a low-profile chamber-well slide (Ibidi; #80826) for image acquisition using a LSM700 confocal microscope (Zeiss).

DNA quantification
Isolation of DNA from tracheal samples was performed using a PureLink DNA extraction kit (Invitrogen) according to the manufacturer's instructions. Briefly, samples were digested overnight in proteinase K and DNA was isolated using the supplied buffers and mini-columns. Quantification of eluted DNA was carried out by spectrophotometry using a NanoDrop 8000 (Thermo Scientific). All samples had a 260/280 ratio of between 1.8 and 2.0.

Extracellular matrix quantification
Collagen, elastin and glycosoaminglycans were quantified as previously described [29]. Collagen content was determined using a total collagen assay kit (QuickZyme Biosciences) according to the manufacturer's instructions. Representative whole tracheal samples of native and decellularized trachea were weighed and directly hydrolyzed in 6 M HCl for 20 h at 95 C. Samples were allowed to cool to room temperature and centrifuged to remove debris. To detect hydroxyproline residues, supernatants were mixed with a chromogen solution for 1 h at 60 C. Absorbance for each sample was read using a colorimetric reader (555 nm). Standards were generated by serial dilution of rat tail collagen I (BD Biosciences) from 300 mg/ml. Elastin quantification was performed using an elastin assay kit (FASTIN, Biocolor). Representative whole tracheal samples of both native and decellularized tissue were homogenized and solubilized twice with 0.25 M oxalic acid incubated at 95 C. Extracts were combined with FASTIN dye reagent (5,10,15,20-tetraphenyl-21H,23H-porphine tetrasulfonate (TPPS)) and the absorbance was determined at 555 nm. Concentrations were determined using alaminin standards.
The sulphated glycosaminoglycan (sGAG) content was quantified according to the Blyscan GAG Assay Kit (Biocolor). Representative wet tissue samples were incubated in 1 ml of papain digestion buffer at 65 C for 18 h. Aliquots of each sample were mixed with 1,9-dimethyl-methylene blue dye and the reagents from the GAG assay kit. The absorbance was read at 656 nm and quantified according to standards generated from bovine tracheal chondroitin-4-sulphate.

Scanning electron microscopy
Scanning electron microscopy (SEM) images show the luminal surface of decellularized human donor tracheal scaffolds. Scaffolds were fixed in 2.5% glutaraldehyde in 0.1 M phosphate buffer, washed with 0.1 M phosphate buffer (pH 7.4), post fixed with 1% osmium tetraoxide and 1.5% potassium ferrocyanine in 0.1 M phosphate buffer and rinsed with distilled water. Specimens were then dehydrated to 100% ethanol using a graded ethanol-water series and critical-point dried using carbon dioxide. Samples were mounted onto aluminum stubs with sticky carbon tabs. A Gatan ion beam coater was used to coat scaffolds with a layer of Au/Pd (approx. 2 nm thickness). Images were obtained using a 7401 FEG scanning electron microscope (Jeol, USA).

Mechanical testing
All decellularized tracheal samples were equilibrated to room temperature prior to testing and kept hydrated in PBS for mechanical testing. Each trachea was cut into 3 cm sections and compressed with antero-posterior and lateral compressive forces. The load (N) exerted by the scaffold was calculated when the scaffold was compressed to 50% of the starting diameter. Further tracheal samples were cut into dumbbell sections with a template cutter such that vertical (axial) forces across tracheal rings and trachealis could be applied. A further dumbbell section was horizontally cut across a tracheal ring. The load required to pull apart the sample until breaking point was measured using an Instron 5565 tensile tester (Instron Ltd., UK). The tensile stress versus strain properties were assessed at a displacement rate of 50e100 mm/ min. The Young's modulus is a measure of material stiffness and was calculated using Bluehill software (Instron, U.K.) as the slope of the straight line portion between 0 and 5 mm.

Primary epithelial cell seeding
Primary human bronchial epithelial cells (HBECs) were obtained either by enzymatic digestion from donor human trachea or from explant biopsy outgrowth [30]. Primary HBECs were maintained for up to three passages in bronchial epithelial growth medium (BEGM; Lonza, UK) as previously described [31]. Decellularized human tracheal scaffolds were cut into 5 mm discs using a biopsy punch, such that they fitted into 96-well plate wells. Prior to epithelial seeding, scaffolds were oriented with luminal/mucosalsurface side up in a low-adhesion 96-well plate (Nunc) and incubated overnight in 200 ml of BEGM medium. Epithelial cells were seeded at 0.25 Â 10 6 cells/cm 2 , 0.5 Â 10 6 cells/cm 2 or 1.0 Â 10 6 cells/ cm 2 and allowed to adhere overnight. Scaffolds were transferred to new low-adhesion plates with the same orientation maintained. Subsequently, medium was changed every 48 h.

Generation of luciferase-tagged immortalized HBECs
Immortalized human bronchial epithelial cells (iHBECs; a gift from Dr. Gisli Jenkins, University of Nottingham, U.K.) were transduced with mStrawberry-Luc lentivirus to create a stable iHBEC cell line co-expressing mStrawberry fluorescent protein and luciferase. Lentivirus production was as previously described [32] but created with the pLV-LS1 transfer vector and the packaging and envelope vectors pCMV-dR8.74 and pMD.G2 (Plasmid Factory). Briefly, viral supernatants were created by co-transfecting 293T HEK cells with the above plasmids using JetPEI (Polyplus Transfection). Supernatant containing lentivirus was collected at 48 and 72 h and was concentrated by ultracentrifugation. Each collection underwent ultracentrifugation to concentrate virus. To generate a transduced cell line, iHBECs were grown in LHC9 medium (Gibco), seeded at 1 Â 10 5 cells in a T25 flask and transduced at an MOI of 7.5 with 4 mg/ml polybrene (Sigma). After 8 h, medium was changed and cells were passaged when approximately 80% confluent. To obtain a pure luciferase-expressing population, mStrawberry fluorescent protein-expressing cells were sorted by fluorescence-activated cell sorting (FACS) using a BD Aria flow cytometer.

In vitro cell tracking using IVIS imaging
IVIS imaging (Caliper Life Sciences) was used as a non-invasive in vitro method of tracking luciferase-tagged iHBECs on decellularized human tracheal scaffolds by detecting a luminescence signal from cells in the presence of the luciferase substrate luciferin. Scaffolds were fashioned into 5 mm discs and placed into 96-well plate wells with the luminal surface facing upwards. Scaffolds were incubated in LHC9 medium (Gibco) overnight at 37 C and 5% CO 2 . Cells were seeded on the scaffolds and transferred to a new low adhesion plate prior to imaging. D-luciferin was added to the medium at 150 m-g/ml and scaffolds were imaged within the plates at position 'C' using automatic acquisition times.

Chick chorioallantoic membrane (CAM) assay
Fertilized chicken eggs (Henry Stewart and Co., UK) were incubated at 37 C. After 3 days of incubation, an approximately 3 cm diameter window was cut into the shell using dissecting scissors, revealing the embryo and CAM vasculature. Windows were sealed with tape and eggs were returned to the incubator for 5 days. At day 8 of incubation, decellularized human tracheal scaffolds (approximately 2e3 mm 3 ) and pieces of absorbable gelatin sponge (Gelfoam; Pfizer; a negative control) were placed on the CAM between blood vessels. Scaffolds were checked daily for 6 days, when scaffolds were photographed in ovo with a stereomicroscope (Leica). Vessel ingrowth was quantified blindly as previously described [33].

Xenotransplantation of decellularized human trachea
Human tracheal scaffolds were prepared as described above and cut into full thickness 5e7 mm 2 pieces, irradiated with 10,000 Gy to ensure sterility and stored in PBS prior to implantation. Adult CD1 mice were used for subcutaneous implantation of scaffolds. Live animal work was ethically approved and carried out under Home Office Project Licence PPL 70/7504. Briefly, CD1 mice were anaesthetized with a 2e5% isoflorane:oxygen gas mix for induction and maintenance. Under aseptic conditions, the dorsum of the mouse was shaved and chlorhexidine was applied to the skin. 5 mm transverse incisions over each dorsal flank were made and subcutaneous pockets created. One scaffold was inserted in each pocket and these were closed with buried 4/0 Vicryl interrupted sutures. Scaffolds were implanted for 56 days and the experiments were terminated accordingly. Scaffolds were retrieved en bloc for histopathological analysis.

Statistical analysis
Results are presented as mean ± standard deviation. Data were analyzed in Microsoft Excel and GraphPad Prism 6.0. Statistical tests are indicated in figure legends and significance was accepted at the 5% level.

Histological assessment
To assess the efficacy of vacuum-assisted decellularization (VAD) we compared this protocol with the clinically applied detergent-enzymatic method (DEM). Histologically, VAD removed nuclei from the epithelium, the submucosal glands and the tracheal cartilage but cartilage lacunae remained intact in both scaffolds ( Fig. 2A). Periodic acid-Schiff (PAS) staining demonstrated the widespread retention of proteoglycans and glycoproteins in cartilage and also in submucosal glands, which may reflect the protection of the glandular basement membrane during decellularization ( Fig. 2A). Picrosirius red (PSR) staining demonstrated the widespread retention of collagen I and III fibers within tracheal scaffolds decellularized using both DEM and VAD, findings supported by Masson's trichrome (MT) staining ( Fig. 2A).

Scaffold composition
Reflecting the extensive decellularization by both protocols, the DNA content of scaffolds was significantly reduced in comparison to native trachea (Fig. 2B). While there was a trend towards lower DNA content in VAD tracheae as compared to DEM tracheae, consistent with results following the application of vacuum pressure to porcine tracheal decellularization [26], this did not reach statistical significance. However, the abundance of structural components of scaffolds such as elastin, collagen and sulphated glycosaminoglycans (sGAGs) was not significantly affected by either DEM or VAD decellularization (Fig. 2B).

Scanning electron microscopy
Scanning electron microscopy (SEM) of decellularized scaffolds confirmed the absence of cells in both DEM and VAD scaffolds and showed the folded macroarchitecture characteristic of human trachea. At higher magnification, a meshwork of fibers was visible on the luminal surface of both scaffolds (Fig. 2C). However, the basement membrane proteins laminin and collagen IV were not found at the luminal surface using immunofluorescence but were retained deeper within scaffolds (Fig. 2D).

Biomechanical properties of human tracheae are retained following decellularization
An important aspect of tracheal bioengineering is the structural integrity of scaffolds post-transplantation. To assess whether VAD compromises scaffold mechanical properties, we compared these scaffolds with DEM-decellularized and native tracheae. We found that decellularization did not significantly affect a scaffold's ability to resist compression in either the anterior-posterior (Fig. 3A) or lateral (Fig. 3B) axes. Further, the elastic properties of the cartilage rings (Fig. 3C), the tracheal wall (Fig. 3D) and the trachealis (Fig. 3E) were not significantly affected by VAD or DEM decellularization.

Epithelial cell attachment to decellularized scaffolds
For VAD-decellularized tracheae to be of use clinically, the scaffolds must retain the capacity to support cells in addition to retaining their mechanical properties. As airway epithelial cells represent a key functional aspect of bioengineered tracheae [34,35], we examined the adhesion of primary human bronchial epithelial cells (HBECs) to the luminal surface of DEM-and VADprepared scaffolds in vitro. By immunofluorescence staining 72 h post-seeding, we observed that HBECs adhered well to both scaffolds but that high seeding densities improved the retention of cells in both types of scaffold (Fig. 4A). Scanning electron microscopy (SEM) of scaffolds seeded at 1 Â 10 6 cells per cm 2 also demonstrated that cells had adhered to both grafts and revealed possible morphological differences between DEM-and VAD-prepared scaffolds with cells more rounded on DEM scaffolds and flatter on VAD scaffolds, a possible indication of more mature cellular adhesions to scaffolds in the VAD condition (Fig. 4B).

Cell survival on decellularized scaffolds using luciferasetagged epithelial cells
In order to monitor cells in real time on decellularized scaffolds, we monitored the bioluminescence of luciferase-transduced immortalized human bronchial epithelial cells (iHBECs) using an in vivo imaging system (IVIS). Non-invasive monitoring of cells on the decellularized scaffolds using this system demonstrated a stable signal over the 5-day period. VAD scaffolds had higher signals throughout this experiment, apparently caused by higher initial engraftment of cells on VAD scaffolds compared to DEM scaffolds ( Fig. 4C and D). However, we cannot rule out that differences between the decellularization protocols, such as enzyme concentration, affected these results as scaffolds were stored identically after decellularization and optimization of this step may be necessary for optimal cell seeding.

Chorioallantoic membrane assays
For cells seeded ex vivo to survive following transplantation, there is a clear need for rapid integration and angiogenesis in implanted decellularized scaffolds. To assess the potential of DEMand VAD-prepared scaffolds for vascular integration, we performed chick chorioallantoic membrane (CAM) assays [29,36] using fragments of either DEM-or VAD-decellularized human tracheae. Gelfoam ® acted as a negative control. Macroscopically, we observed a spoke-wheel pattern of vessels four days after implantation, which suggested that vessels were attracted to both DEM-and VAD-prepared scaffolds (Fig. 5A). Quantification of the number of vessels converging on the decellularized scaffolds revealed that decellularized scaffolds stimulated significantly more vessel ingrowth than negative controls (Fig. 5B) and that the accelerated VAD protocol did not negatively influence vessel ingrowth (Fig. 5A).

Xenotransplantation assays
Finally, we compared the behavior of DEM-and VAD-prepared human tracheal scaffolds in a xenotransplantation assay. 3 mm 3 pieces of either DEM-or VAD-prepared tracheae were implanted subcutaneously into immunocompetent CD1 mice and retrieved after 8 weeks. Throughout the experiment the mice behaved normally without evidence of inflammation, extrusion of the implanted tissue or death. At the time of retrieval, tissue surrounding the implants appeared healthy, without signs of adverse reaction. Histological analyses revealed that DEM-and VAD-prepared tracheal scaffolds showed similar cellular infiltration around the graft (Fig. 6A) and that this was predominantly macrophages  ( Fig. 6B). Evidence of vascularization was also seen in both scaffold types as demonstrated by endomucin-stained vessels within the grafts (Fig. 6C and D).

Discussion
We show that a vacuum-assisted decellularization (VAD) protocol produces human tracheal scaffolds with comparable decellularization efficiency, extracellular matrix retention, mechanical properties, cytocompatibility and in vivo integration capacity to scaffolds decellularized using the clinically applied detergentenzymatic method (DEM). However, VAD is an accelerated protocol requiring only 9 days from donor tissue procurement to final decellularized scaffold; by contrast, the DEM method takes 3e8 weeks [8,10,23]. The efficacy of decellularization reported here is in line with previously published accepted standards for tissue decellularization [37]. These results are an important step towards the use of decellularized human cadaveric donor tracheae as scaffolds for airway bioengineering because expedited preparation broadens the clinical scenarios in which decellularization is appropriate. The incorporation of a freezing step prior to decellularization is of particular importance as it suggests banking of donor tracheae as a clinically relevant strategy. An important consideration is that current protocols for storage of predecellularized tracheae mean their salient properties might deteriorate over time in storage [38] and the optimization of storage conditions for decellularized materials is a priority for the field.
Production of decellularized scaffolds that share similar biomechanical properties to native tissue is an important aim as the tracheal cartilage maintains a patent airway in healthy individuals. Previous studies suggest that decellularization using some protocols could negatively affect the structural properties of porcine tracheae [39]. Here, we comprehensively tested the biomechanical properties of VAD-decellularized human tracheae including lateral and antero-posterior compression finding that the resistance to compression and elastic properties remain similar to that of native human tracheae. It is noteworthy that donor tracheae have quite large variance between samples and this may contribute to nonsignificant differences found despite controlling for this with matched samples. In the future, particularly for clinical application, donor selection criteria may have to be more stringent than they have been for research purposes.
Scaffold preparation represents the first step in the process of generating a transplantable tissue-engineered airway. Clinically applied protocols have recellularized scaffolds with autologous cells, including epithelial cells, mesenchymal stromal cells (MSCs) and MSC-derived chondrocytes [6,8e10]. As such, it is important that, as well as maintaining the expected mechanical properties, scaffolds are able to support the adherence and survival of relevant cell types. Here, we demonstrated that human bronchial epithelial cells (HBECs) attach to and survive on both decellularized human scaffold types in vitro. However, neither the DEM or VAD decellularization method preserved the basement membrane that is normally present beneath airway epithelial cells; instead, a mesh of fibers ordinarily constrained to the stromal compartment was presented at the luminal surface [40]. This may explain the high seeding densities of HBECs required for cell retention as many cells may undergo apoptosis before basement membrane production and/or remodeling occurs. We believe that future studies should investigate the importance of the basement membrane in airway bioengineering: basement membrane retention or reconstruction could improve the cytocompatibility of both decellularized and synthetic scaffolds, which presently require huge numbers of HBECs to re-epithelialize [11]. Authors treating severe skin burns with cultured epidermal stem cells found that the application of these cells on a fibrin sheet greatly improved the 'take rate' and ease of application [41]. Similar to other tissue-engineered epithelia, it may also be possible to transplant airway epithelium as a pre-prepared sheet product [42,43] or as organoids [44]. Optimization of protocols for functional airway differentiation, to generate a ciliated epithelium on VAD human scaffolds, as has been demonstrated in rodent tracheal scaffolds [45], is also desirable. Pre-seeding and integration of stromal cells into VAD scaffolds could also be considered [46].
The mechanism, time-course and quality of vascularization of tissue-engineered constructs is presently unknown and requires further research, as highlighted at a recent international consensus meeting [47]. We believe that our data demonstrating comparable behavior of DEM and VAD scaffolds in terms of their ability to promote a rapid angiogenic response in CAM experiments and comparable vascular integration as subcutaneous implants provide reassurance that reducing the time taken to prepare scaffolds using a vacuum system does not have detrimental effects on scaffold performance.
In the trachea, translation of these protocols into clinical practice will require the development of equipment capable of delivering vacuum pressure to GMP standards. While the reagents used in the protocol reported here have previously been adapted towards GMP manufacture, the development of standard operating procedures and quality control measures for VAD will be an important step towards this. Further, the concept of VAD might be useful in clinical protocols to produce decellularized scaffolds from other organs but protocols will likely require customization to each setting.

Conclusion
This comparison between clinically used DEM decellularization and accelerated vacuum-assisted decellularization (VAD) of human tracheae shows that VAD can rapidly generate decellularized tracheal scaffolds that are comparable to those previously used for clinical transplantation in a number of key aspects. Importantly, this innovative procedure allows for banking of tracheae prior to decellularization for future applications. The similar properties of DEM and VAD scaffolds both ex vivo and in vivo provide a rationale for the use of VAD in clinical applications of tissue-engineered airway scaffolds.